Mechanical insertion properties of calcium-phosphate implant coatings

Abstract Objectives: To investigate the influence of protein incorporation on the resistance of biomimetic calcium-phosphate coatings to the shear forces that are generated during implant insertion. Materials and Methods: Thirty-eight standard (5 x 13 mm) Osseotite((R)) implants were coated biomimetically with a layer of calcium phosphate, which either lacked or bore a co-precipitated (incorporated) depot of the model protein bovine serum albumin (BSA). The coated implants were inserted into either artificial bone (n=18) or the explanted mandibles of adult pigs (n=12). The former set-up was established for the measurement of torque and of coating losses during the insertion process. The latter set-up was established for the histological and histomorphometric analysis of the fate of the coatings after implantation. Results: BSA-bearing coatings had higher mean torque values than did those that bore no protein depot. During the insertion process, less material was lost from the former than from the latter type of coating. The histological and histomorphometric analysis revealed fragments of material to be sheared off from both types of coating at vulnerable points, namely, at the tips of the threads. The sheared-off fragments were retained within the peri-implant space. Conclusion: The incorporation of a protein into a biomimetically prepared calcium-phosphate coating increases its resistance to the shear forces that are generated during implant insertion. In a clinical setting, the incorporated protein would be an osteogenic agent, whose osteoinductive potential would not be compromised by the shearing off of coating material, and the osteoconductivity of an exposed implant surface would not be less than that of a coated one. To cite this article: Hägi TT, Enggist L, Michel D, Ferguson SJ, Liu Y, Hunziker EB. Mechanical insertion properties of calcium-phosphate implant coatings. Clin. Oral Impl. Res. xx, 2010; 000-000. doi: 10.1111/j.1600-0501.2010.01916.x.

Biomimetic Coatings and Their Biological Functionalization

The biomimetic coating technique can be used to deposit layers of calcium phosphate (CaP) on medical devices to improve their osteoconductivity and osseointegration.The inorganic layer generated is akin to mineralized bone matrix and can be degraded as such. The biomimetic coating technique involves the nucleation and growth of bone-like crystals on a pretreated substrate by immersing it in a supersaturated solution of CaP under physiological conditions of temperature (37°C) and pH (7.4). The method, originally developed by Kokubo and his co-workers in 1990, has since undergone improvement and refinement by several groups of investigators. Biomimetic coatings are valuable in that they can serve as a vehicle for the slow, sustained release of osteogenic agents at the site of implantation. This attribute is rendered possible by the near-physiological conditions under which these coatings are prepared, which permits the incorporation of bioactive agents into the inorganic crystal latticework rather than their superficial adsorption on preformed layers. In addition, the biomimetic coating technique can be applied to implants of an organic as well as of a metallic nature and to those with irregular surface geometries, which is not possible using conventional methodologies.

BMP-2 liberated from biomimetic implant coatings induces and sustains direct ossification in an ectopic rat model

INTRODUCTION: Using a rat model, we evaluated the kinetics and histomorphometry of ectopic bone formation in association with biomimetic implant coatings containing BMP-2. MATERIALS AND METHODS: One experimental and three control groups were set up: titanium-alloy discs coated with a biomimetically co-precipitated layer of calcium phosphate and BMP-2 [1.7 microg per disc (incorporated-BMP group)]; uncoated discs (control); discs biomimetically coated with a layer of calcium phosphate alone (control); and discs biomimetically coated with a layer of calcium phosphate bearing superficially adsorbed BMP-2 [0.98 microg per disc (control)]. Discs (n = 6 per group) were implanted subcutaneously in rats and retrieved at 7-day intervals over a period of 5 weeks for kinetic, histomorphometrical, morphological and histochemical analyses. RESULTS: In the incorporated-BMP-2 group, osteogenic activity was first observed 2 weeks after implantation and thereafter continued unabated until the end of the monitoring period. The net weekly rates of bone formation per disc were 5.8 mm3 at 2 weeks and 3.64 mm3 at 5 weeks. The total volumes of bone formed per disc at these junctures were 5.8 mm3 and 10.3 mm3, respectively. Bone tissue, which was formed by a direct ossification mechanism, was deposited at distances of up to 340 microm from the implant surfaces. The biomimetic coatings were degraded gradually, initially by foreign body giant cells alone and then also by osteoclasts. Forty percent of the coating material (and thus presumably of the incorporated BMP-2) remained at the end of the monitoring period. Hence, 60% of the incorporated BMP-2 had been released. At this 5-week juncture, no bone tissue was associated with any of the control implants. CONCLUSION: BMP-2 incorporated into biomimetic calcium phosphate coatings is capable not only of inducing bone formation at an ectopic site in vivo but also of doing so with a very high potency at a low pharmacological level, and of sustaining this activity for a considerable period of time. The sustainment of osteogenic activity is of great clinical importance for the osseointegration of dental and orthopedic implants.