Efficacy of fluoride compounds and stannous chloride as erosion inhibitors in dentine

The aim of this study was to evaluate the anti-erosive effects of different fluoride compounds and one tin compound in the context of the complex pathohistology of dentine erosion, with particular emphasis on the role of the organic portion. Samples were subjected to two experiments including erosive acid attacks (0.05 molar citric acid, pH 2.3; 6 x 2 min/day) and applications (6 x 2 min/day) of the following test solutions: SnCl(2) (815 ppm Sn), NaF (250 ppm F), SnF(2) (250 ppm F, 809 ppm Sn), amine fluoride (AmF, 250 ppm F), AmF/NaF (250 ppm F), and AmF/SnF(2) (250 ppm F, 409 ppm Sn). The demineralised organic fraction was enzymatically removed either at the end of the experiment (experiment 1) or continuously throughout the experiment (experiment 2). Tissue loss was determined profilometrically after 10 experimental days. In experiment 1, the highest erosive tissue loss was found in the control group (erosion only); the AmF- and NaF-containing solutions reduced tissue loss by about 60%, reductions for SnCl(2), AmF/SnF(2), and SnF(2) were 52, 74 and 89%, respectively. In experiment 2, loss values generally were significantly higher, and the differences between the test solutions were much more distinct. Reduction of tissue loss was between 12 and 34% for the AmF- and NaF-containing preparations, and 11, 67 and 78% for SnCl(2), AmF/SnF(2), and SnF(2), respectively. Stannous fluoride-containing solutions revealed promising anti-erosive effects in dentine. The strikingly different outcomes in the two experiments suggest reconsidering current methodologies for investigating anti-erosive strategies in dentine.

Radical Chain Reduction of Alkylboron Compounds with Catechols

The conversion of alkylboranes to the corresponding alkanes is classically performed via protonolysis of alkylboranes. This simple reaction requires the use of severe reaction conditions, that is, treatment with a carboxylic acid at high temperature (>150 degrees C). We report here a mild radical procedure for the transformation of organoboranes to alkalies. 4-tert-Butylcatechol, a well-established radical inhibitor and antioxidant, is acting as a source of hydrogen atoms. An efficient chain reaction is observed due to the exceptional reactivity of phenoxyl radicals toward alkylboranes. The reaction has been applied to a wide range of organoboron derivatives such as B-alkylcatecholboranes, trialkylboranes, pinacolboronates, and alkylboronic acids. Furthermore, the so far elusive rate constants for the hydrogen transfer between secondary alkyl radical and catechol derivatives have been experimentally determined. Interestingly, they are less than 1 order of magnitude slower than that of tin hydride at 80 degrees C, making catechols particularly attractive for a wide range of transformations involving C-C bond formation.

Randomised in situ study on the efficacy of a tin/chitosan toothpaste on erosive-abrasive enamel loss

Tin is a notable anti-erosive agent, and the biopolymer chitosan has also shown demineralisation-inhibiting properties. Therefore, the anti-erosive/anti-abrasive efficacy of the combination of both compounds was tested under in situ conditions. Twenty-seven volunteers were included in a randomised, double-blind, three-cell crossover in situ trial. Enamel specimens were recessed on the buccal aspects of mandibular appliances, extraorally demineralised (6 × 2 min/day) and intraorally treated with toothpaste slurries (2 × 2 min/day). Within the slurry treatment time, one-half of the specimens received additional intraoral brushing (5 s, 2.5 N). The tested toothpastes included a placebo toothpaste, an experimental NaF toothpaste (1,400 ppm F(-)) and an experimental F/Sn/chitosan toothpaste (1,400 ppm F(-), 3,500 ppm Sn(2+), 0.5% chitosan). The percentage reduction of tissue loss (slurry exposure/slurry exposure + brushing) compared to placebo was 19.0 ± 47.3/21.3 ± 22.4 after use of NaF and 52.5 ± 30.9/50.2 ± 34.3 after use of F/Sn/chitosan. F/Sn/chitosan was significantly more effective than NaF (p ≤ 0.001) and showed good efficacy against erosive and erosive-abrasive tissue loss. This study suggests that the F/Sn/chitosan toothpaste could provide good protection for patients who frequently consume acidic foodstuffs.