[The stamp technique for direct composite restoration]

The indications for direct resin composite restorations are nowadays extended due to the development of modern resin materials with improved material properties. However, there are still some difficulties regarding handling of resin composite material, especially in large restorations. The reconstruction of a functional and individual occlusion is difficult to achieve with direct application techniques. The aim of the present publication was to introduce a new "stamp"-technique for placing large composite restorations. The procedure of this "stamp"-technique is presented by three typical indications: large single-tooth restoration, occlusal rehabilitation of a compromised occlusal surface due to erosions and direct fibre-reinforced fixed partial denture. A step-by-step description of the technique and clinical figures illustrates the method. Large single-tooth restorations can be built-up with individual, two- piece silicone stamps. Large occlusal abrasive and/or erosive defects can be restored by copying the wax-up from the dental technician using the "stamp"-technique. Even fiber-reinforced resin-bonded fixed partial dentures can be formed with this intraoral technique with more precision and within a shorter treatment time. The presented "stamp"-technique facilitates the placement of large restoration with composite and can be recommended for the clinical use.

The long-term mechanical integrity of non-reinforced PEEK-OPTIMA polymer for demanding spinal applications: experimental and finite-element analysis

Polyetheretherketone (PEEK) is a novel polymer with potential advantages for its use in demanding orthopaedic applications (e.g. intervertebral cages). However, the influence of a physiological environment on the mechanical stability of PEEK has not been reported. Furthermore, the suitability of the polymer for use in highly stressed spinal implants such as intervertebral cages has not been investigated. Therefore, a combined experimental and analytical study was performed to address these open questions. A quasi-static mechanical compression test was performed to compare the initial mechanical properties of PEEK-OPTIMA polymer in a dry, room-temperature and in an aqueous, 37 degrees C environment (n=10 per group). The creep behaviour of cylindrical PEEK polymer specimens (n=6) was measured in a simulated physiological environment at an applied stress level of 10 MPa for a loading duration of 2000 hours (12 weeks). To compare the biomechanical performance of different intervertebral cage types made from PEEK and titanium under complex loading conditions, a three-dimensional finite element model of a functional spinal unit was created. The elastic modulus of PEEK polymer specimens in a physiological environment was 1.8% lower than that of specimens tested at dry, room temperature conditions (P<0.001). The results from the creep test showed an average creep strain of less than 0.1% after 2000 hours of loading. The finite element analysis demonstrated high strain and stress concentrations at the bone/implant interface, emphasizing the importance of cage geometry for load distribution. The stress and strain maxima in the implants were well below the material strength limits of PEEK. In summary, the experimental results verified the mechanical stability of the PEEK-OPTIMA polymer in a simulated physiological environment, and over extended loading periods. Finite element analysis supported the use of PEEK-OPTIMA for load-bearing intervertebral implants.