Combined effect of a fluoride-, stannous- and chitosan-containing toothpaste and stannous-containing rinse on the prevention of initial enamel erosion-abrasion.

OBJECTIVES The aim of this study was to assess the preventive effect of a fluoride-, stannous- and chitosan-containing (F/Sn/chitosan-) toothpaste (TP) on initial enamel erosion and abrasion. METHODS In total, 150 human premolar enamel specimens were ground, polished and divided into 5 toothpaste/rinse groups (n=30): (G1) placebo-TP/tap water, (G2) sodium fluoride (NaF-) TP/tap water, (G3) F/Sn/chitosan-TP/tap water, (G4) F/Sn/chitosan-TP/Sn-rinse, (G5) NaF-TP/NaF-rinse. The 8-day erosion-abrasion cyclic treatment (one cycle/day) consisted of incubating the samples in artificial saliva (30min), then submitting the samples to toothbrush abrasion (2min incubation in toothpaste slurry; brushing with 20 toothbrush strokes) and rinsing (2min; 10ml) with the respective solution: tap water (G1-G3), Sn-rinse (G4) or NaF-rinse (G5). Afterwards, the samples were submitted to erosion (2min; 30ml 1% citric acid, pH=3.6). Surface microhardness (SMH) was measured initially and after every abrasion and erosion treatment. Enamel substance loss was calculated after each abrasion. Non-parametric ANOVA followed by Wilcoxon rank tests were used for analysis. RESULTS G1 presented the greatest SMH decrease, while G4 presented the least SMH decrease (p<0.001). G3 had a similar SMH decrease to G2 and G5. Substance loss was significantly lower in G4 than all other groups (p<0.05), closely followed by G3. Both G2 and G5 showed similar calculated enamel substance loss to G1. CONCLUSION The treatment with F/Sn/chitosan-TP and tap water provided a similar SMH decrease to both NaF-TP groups, but significantly lower substance loss. F/Sn/Chitosan-TP and Sn-rinse showed a better preventive effect, which promoted less SMH decrease and reduced substance loss. CLINICAL SIGNIFICANCE The toothpaste containing fluoride, stannous and chitosan shows promising results in reducing substance loss from erosion and abrasion. The combination of this toothpaste with the stannous-containing rinse showed even better prevention against erosion-abrasion.

The influence of saliva on the dissolution of calcium fluoride after application of different fluoride gels in vitro

OBJECTIVE: To determine the formation and dissolution of calcium fluoride on the enamel surface after application of two fluoride gel-saliva mixtures. METHOD AND MATERIALS: From each of 80 bovine incisors, two enamel specimens were prepared and subjected to two different treatment procedures. In group 1, 80 specimens were treated with a mixture of an amine fluoride gel (1.25% F-; pH 5.2; 5 minutes) and human saliva. In group 2, 80 enamel blocks were subjected to a mixture of sodium fluoride gel (1.25% F; pH 5.5; 5 minutes) and human saliva. Subsequent to fluoride treatment, 40 specimens from each group were stored in human saliva and sterile water, respectively. Ten specimens were removed after each of 1 hour, 24 hours, 2 days, and 5 days and analyzed according to potassium hydroxide-soluble fluoride. RESULTS: Application of amine fluoride gel resulted in a higher amount of potassium hydroxide-soluble fluoride than did sodium fluoride gel 1 hour after application. Saliva exerted an inhibitory effect according to the dissolution rate of calcium fluoride. However, after 5 days, more than 90% of the precipitated calcium fluoride was dissolved in the amine fluoride group, and almost all potassium hydroxide-soluble fluoride was lost in the sodium fluoride group. Calcium fluoride apparently dissolves rapidly, even at almost neutral pH. CONCLUSION: Considering the limitations of an in vitro study, it is concluded that highly concentrated fluoride gels should be applied at an adequate frequency to reestablish a calcium fluoride-like layer.

Fluoride in dental erosion

Dental erosion develops through chronic exposure to extrinsic/intrinsic acids with a low pH. Enamel erosion is characterized by a centripetal dissolution leaving a small demineralized zone behind. In contrast, erosive demineralization in dentin is more complex as the acid-induced mineral dissolution leads to the exposure of collagenous organic matrix, which hampers ion diffusion and, thus, reduces further progression of the lesion. Topical fluoridation inducing the formation of a protective layer on dental hard tissue, which is composed of CaF(2) (in case of conventional fluorides like amine fluoride or sodium fluoride) or of metal-rich surface precipitates (in case of titanium tetrafluoride or tin-containing fluoride products), appears to be most effective on enamel. In dentin, the preventive effect of fluorides is highly dependent on the presence of the organic matrix. In situ studies have shown a higher protective potential of fluoride in enamel compared to dentin, probably as the organic matrix is affected by enzymatical and chemical degradation as well as by abrasive influences in the clinical situation. There is convincing evidence that fluoride, in general, can strengthen teeth against erosive acid damage, and high-concentration fluoride agents and/or frequent applications are considered potentially effective approaches in preventing dental erosion. The use of tin-containing fluoride products might provide the best approach for effective prevention of dental erosion. Further properly designed in situ or clinical studies are recommended in order to better understand the relative differences in performance of the various fluoride agents and formulations.

Effectiveness of a calcium sodium phosphosilicate-containing prophylaxis paste in reducing dentine hypersensitivity immediately and 4 weeks after a single application: a double-blind randomized controlled trial

AIMS The aim of this single-site, randomized, controlled, double-blind, 3-arm parallel study was to determine the effectiveness of a prophylaxis paste containing 15% calcium sodium phosphosilicate (CSPS; NovaMin(®) ) with and without fluoride in reducing dentine hypersensitivity immediately after a single application and 28 days following dental scaling and root planing. MATERIALS & METHODS Overall, 151 subjects were enrolled in this study. All subjects received a scaling and root planing procedure followed by a final prophylaxis step using one of three different prophylaxis pastes: Test-A (15% NovaMin(®) and NaF), Test-B (15% NovaMin(®) ) and a control. Dentine hypersensitivity was assessed by tactile stimulus (Yeaple Probe(®) ) and by air blast (Schiff scale) at baseline, immediately after and 28 days after a prophylaxis procedure. One hundred and forty-nine subjects completed the study. RESULTS Subjects having received the test prophylaxis pastes showed statistically lower (anova, p < 0.05) dentine hypersensitivity compared with the control group immediately after the prophylaxis procedure (Yeaple Probe(®) : Test-A = 20.9 ± 12.6, Test-B = 22.7 ± 12.9, Control=11.2 ± 3.1; Schiff score: Test-A = 1.1 ± 0.6, Test-B = 1.1 ± 0.6, Control = 2.0 ± 0.7) and after 28 days (Yeaple probe: Test-A = 21.5 ± 11.9, Test-B = 20.6 ± 11.3, Control = 11.8 ± 6.0; Schiff score: Test-A = 1.0 ± 0.6, Test-B = 1.0 ± 0.6, Control = 2.0 ± 0.7). CONCLUSIONS In conclusion, the single application of both fluoridated and non-fluoridated prophylaxis pastes containing 15% CSPS (NovaMin(®) ) provided a significant reduction of dentine hypersensitivity up to at least 28 days.

The effect of monoalkyl phosphates and fluoride on dissolution of hydroxyapatite, and interactions with saliva

The aims were to investigate the effect of monoalkyl phosphates (MAPs) and fluoride on dissolution rate of native and saliva-coated hydroxyapatite (HA). Fluoride at 300 mg/l (as NaF) inhibited dissolution of native HA by 12%, while potassium and sodium dodecyl phosphates (PDP, SDP), at 0.1% or higher, inhibited dissolution by 26-34%. MAPs, but not fluoride, also showed persistence of action. MAPs at 0.5% and fluoride at 300 mg/l were then tested separately against HA pre-treated with human saliva for 2 or 18 h. Agents were applied with brushing to half the specimens, and without brushing to the other half. In control (water-treated) specimens, pre-treatment of HA with human saliva reduced dissolution rate on average by 41% (2 h) and 63% (18 h). Brushing did not have a statistically significant effect on dissolution rate of saliva-coated specimens. In brushed specimens, fluoride significantly increased the inhibition due to 2- or 18-hour saliva pre-treatment. It is hypothesised that brushing partially removes the salivary film and allows KOH-soluble calcium fluoride formation at the surfaces of HA particles. Inhibition was reduced by PDP in 2-hour/non-brushed specimens and in 18-hour/brushed specimens. PDP did not affect dissolution rates in the remaining groups and SDP did not affect dissolution rate in any group. Possible reasons for these variable results are discussed. The experiments show that pre-treatment with saliva can significantly modify results of tests on potential anti-erosive agents and it is recommended that saliva pre-treatment should be a routine part of testing such agents.

Efficacy of fluoride compounds and stannous chloride as erosion inhibitors in dentine

The aim of this study was to evaluate the anti-erosive effects of different fluoride compounds and one tin compound in the context of the complex pathohistology of dentine erosion, with particular emphasis on the role of the organic portion. Samples were subjected to two experiments including erosive acid attacks (0.05 molar citric acid, pH 2.3; 6 x 2 min/day) and applications (6 x 2 min/day) of the following test solutions: SnCl(2) (815 ppm Sn), NaF (250 ppm F), SnF(2) (250 ppm F, 809 ppm Sn), amine fluoride (AmF, 250 ppm F), AmF/NaF (250 ppm F), and AmF/SnF(2) (250 ppm F, 409 ppm Sn). The demineralised organic fraction was enzymatically removed either at the end of the experiment (experiment 1) or continuously throughout the experiment (experiment 2). Tissue loss was determined profilometrically after 10 experimental days. In experiment 1, the highest erosive tissue loss was found in the control group (erosion only); the AmF- and NaF-containing solutions reduced tissue loss by about 60%, reductions for SnCl(2), AmF/SnF(2), and SnF(2) were 52, 74 and 89%, respectively. In experiment 2, loss values generally were significantly higher, and the differences between the test solutions were much more distinct. Reduction of tissue loss was between 12 and 34% for the AmF- and NaF-containing preparations, and 11, 67 and 78% for SnCl(2), AmF/SnF(2), and SnF(2), respectively. Stannous fluoride-containing solutions revealed promising anti-erosive effects in dentine. The strikingly different outcomes in the two experiments suggest reconsidering current methodologies for investigating anti-erosive strategies in dentine.

Conventional and anti-erosion fluoride toothpastes: effect on enamel erosion and erosion-abrasion

New toothpastes with anti-erosion claims are marketed, but little is known about their effectiveness. This study investigates these products in comparison with various conventional NaF toothpastes and tin-containing products with respect to their erosion protection/abrasion prevention properties. In experiment 1, samples were demineralised (10 days, 6 × 2 min/day; citric acid, pH 2.4), exposed to toothpaste slurries (2 × 2 min/day) and intermittently stored in a mineral salt solution. In experiment 2, samples were additionally brushed for 15 s during the slurry immersion time. Study products were 8 conventional NaF toothpastes (1,400-1,490 ppm F), 4 formulations with anti-erosion claims (2 F toothpastes: NaF + KNO(3) and NaF + hydroxyapatite; and 2 F-free toothpastes: zinc-carbonate-hydroxyapatite, and chitosan) and 2 Sn-containing products (toothpaste: 3,436 ppm Sn, 1,450 ppm F as SnF(2)/NaF; gel: 970 ppm F, 3,030 ppm Sn as SnF(2)). A mouth rinse (500 ppm F as AmF/NaF, 800 ppm Sn as SnCl(2)) was the positive control. Tissue loss was quantified profilometrically. In experiment 1, most NaF toothpastes and 1 F-free formulation reduced tissue loss significantly (between 19 and 42%); the Sn-containing formulations were the most effective (toothpaste and gel 55 and 78% reduction, respectively). In experiment 2, only 4 NaF toothpastes revealed significant effects compared to the F-free control (reduction between 29 and 37%); the F-free special preparations and the Sn toothpaste had no significant effect. The Sn gel (reduction 75%) revealed the best result. Conventional NaF toothpastes reduced the erosive tissue loss, but had limited efficacy regarding the prevention of brushing abrasion. The special formulations were not superior, or were even less effective.

The effect of a tin-containing fluoride mouth rinse on the bond between resin composite and erosively demineralised dentin

OBJECTIVES To evaluate the effect of a tin-containing fluoride (Sn/F) mouth rinse on microtensile bond strength (μTBS) between resin composite and erosively demineralised dentin. MATERIALS AND METHODS Dentin of 120 human molars was erosively demineralised using a 10-day cyclic de- and remineralisation model. For 40 molars, the model comprised erosive demineralisation only; for another 40, the model included treatment with a NaF solution; and for yet another 40, the model included treatment with a Sn/F mouth rinse. In half of these molars (n = 20), the demineralised organic matrix was continuously removed by collagenase. Silicon carbide paper-ground, non-erosively demineralised molars served as control (n = 20). Subsequently, μTBS of Clearfil SE/Filtek Z250 to the dentin was measured, and failure mode was determined. Additionally, surfaces were evaluated using SEM and EDX. RESULTS Compared to the non-erosively demineralised control, erosive demineralisation resulted in significantly lower μTBS regardless of the removal of demineralised organic matrix. Treatment with NaF increased μTBS, but the level of μTBS obtained by the non-erosively demineralised control was only reached when the demineralised organic matrix had been removed. The Sn/F mouth rinse together with removal of demineralised organic matrix led to significantly higher µTBS than did the non-erosively demineralised control. The Sn/F mouth rinse yielded higher μTBS than did the NaF solution. CONCLUSIONS Treatment of erosively demineralised dentin with a NaF solution or a Sn/F mouth rinse increased the bond strength of resin composite. CLINICAL RELEVANCE Bond strength of resin composite to eroded dentin was not negatively influenced by treatment with a tin-containing fluoride mouth rinse.

Preparation and optimization of calcium fluoride particles for dental applications.

Fluorides are used in dental care due to their beneficial effect in tooth enamel de-/remineralization cycles. To achieve a desired constant supply of soluble fluorides in the oral cavity, different approaches have been followed. Here we present results on the preparation of CaF2 particles and their characterization with respect to a potential application as enamel associated fluoride releasing reservoirs. CaF2 particles were synthesized by precipitation from soluble NaF and CaCl2 salt solutions of defined concentrations and their morphology analyzed by scanning electron microscopy. CaF2 particles with defined sizes and shapes could be synthesized by adjusting the concentrations of the precursor salt solutions. Such particles interacted with enamel surfaces when applied at fluoride concentrations correlating to typical dental care products. Fluoride release from the synthesized CaF2 particles was observed to be largely influenced by the concentration of phosphate in the solution. Physiological solutions with phosphate concentration similar to saliva (3.5 mM) reduced the fluoride release from pure CaF2 particles by a factor of 10-20 × as compared to phosphate free buffer solutions. Fluoride release was even lower in human saliva. The fluoride release could be increased by the addition of phosphate in substoichiometric amounts during CaF2 particle synthesis. The presented results demonstrate that the morphology and fluoride release characteristics of CaF2 particles can be tuned and provide evidence of the suitability of synthetic CaF2 particles as enamel associated fluoride reservoirs.

Fluoride varnishes with calcium glycerophosphate: fluoride release and effect on in vitro enamel demineralization

The aims of this study were (1) to assess the amount of fluoride (F) released from varnishes containing calcium glycerophosphate (CaGP) and (2) to assess the effect of the experimental varnishes on in vitro demineralization. Six test groups using 5 varnishes: base varnish (no active ingredients); Duraphat® (2.26% NaF); Duofluorid® (5.63% NaF/CaF2); experimental varnish 1 (1% CaGP/5.63% NaF/CaF2); experimental varnish 2 (5% CaGP/5.63% NaF/CaF2); and no varnish were set up. In stage 1, 60 acrylic blocks were randomly distributed into 6 groups (n = 10). Then 300 µg of each varnish was applied to each block. The blocks were immersed in deionized water, which was changed after 1, 8, 12, 24, 48 and 72 hours. Fluoride concentration in the water was analyzed using a fluoride electrode. In stage 2, 60 bovine enamel samples were distributed into 6 groups (n = 10), and treated with 300 µg of the respective varnish. After 6 h the varnish was removed and the samples were subjected to a 7-day in vitro pH cycle (6 h demineralization/18 h remineralization per day). The demineralization was measured using surface hardness. The results showed that both experimental varnishes released more fluoride than Duofluorid® and Duraphat® (p < 0.05), but Duraphat® showed the best preventive effect by decreasing enamel hardness loss (p < 0.05). Therefore, we conclude that even though (1) the experimental varnishes containing CaGP released greater amounts of F, (2) they did not increase in the preventive effect against enamel demineralization.

Fluoride varnishes containing calcium glycerophosphate: fluoride uptake and the effect on in vitro enamel erosion

OBJECTIVES Calcium glycerophosphate (CaGP) was added to fluoride varnishes to analyze their preventive effect on initial enamel erosion and fluoride uptake: potassium hydroxide (KOH)-soluble and KOH-insoluble fluoride bound to enamel. MATERIALS AND METHODS This study was carried out in two parts. Part 1: 108 enamel samples were randomly distributed into six varnish groups: base varnish (no active ingredients); Duraphat® (2.26 %NaF); Duofluorid® (5.63 %NaF/CaF2); experimental varnish 1 (1 %CaGP/5.63 %NaF/CaF2); experimental varnish 2 (5 %CaGP/5.63 %NaF/CaF2); and no varnish. Cyclic demineralization (90 s; citric acid, pH = 3.6) and remineralization (4 h) was made once a day, for 3 days. Change in surface microhardness (SMH) was measured. Part 2: 60 enamel samples were cut in half and received no varnish (control) or a layer of varnish: Duraphat®, Duofluorid®, experimental varnishes 1 and 2. Then, KOH-soluble and KOH-insoluble fluoride were analyzed using an electrode. RESULTS After cyclic demineralization, SMH decreased in all samples, but Duraphat® caused less hardness loss. No difference was observed between varnishes containing CaGP and the other varnishes. Similar amounts of KOH-soluble and insoluble fluoride was found in experimental varnish 1 and Duofluorid®, while lower values were found for experimental varnish 2 and Duraphat®. CONCLUSION The addition of CaGP to fluoride varnishes did not increase fluoride bound to enamel and did not enhance their protection against initial enamel erosion. CLINICAL RELEVANCE We observe that the fluoride varnishes containing CaGP do not promote greater amounts of fluoride bound to enamel and that fluoride bound to enamel may not be closely related to erosion prevention.