Comparative study of biphasic calcium phosphates with different HA/TCP ratios in mandibular bone defects. A long-term histomorphometric study in minipigs

Three biphasic calcium phosphate (BCP) bone substitute materials with hydroxyapatite (HA)/tricalcium phosphate (TCP) ratios of 20/80, 60/40, and 80/20 were compared to coagulum, particulated autogenous bone, and deproteinized bovine bone mineral (DBBM) in membrane-protected bone defects. The defects were prepared in the mandibles of 24 minipigs that were divided into four groups of six with healing times of 4, 13, 26, and 52 weeks, respectively. The histologic and histomorphometric evaluation focused on differences in amount and pattern of bone formation, filler degradation, and the interface between bone and filler. Collapse of the expanded polytetrafluoroethylene barrier membrane into the coagulum defects underlined the necessity of a filler material to maintain the augmented volume. Quantitatively, BCP 20/80 showed bone formation and degradation of the filler material similar to autografts, whereas BCP 60/40 and BCP 80/20 rather equaled DBBM. Among the three BCP's, the amount of bone formation and degradation of filler material seemed to be inversely proportional to the HA/TCP ratio. The fraction of filler surface covered with bone was highest for autografts at all time points and was higher for DBBM than BCP 80/20 and 60/40 at the early healing phase. TRAP-positive multinucleated cells were identified on BCP and DBBM surfaces without showing typical signs of resorption lacunae.

Evaluation of HA-fibrin-based hydrogel for restoration of degenerated intervertebral disc

Introduction: Intervertebral disc degeneration is associated with loss of nucleus pulposus (NP) tissue and reduced disc height[1]. A number of therapies, including synthetic and natural biomaterials, have been developed to restore full disc function and to minimize the pain and disability caused by this disease. Fibrin-based biomaterials are used as a replacement for NP or as a cell carrier for tissue engineering approaches[2]. While the behavior of such gels is well-characterized from a material point of view, little is known about their contribution to intervertebral disc (IVD) restoration under dynamic loads. The aim of the present study is the evaluation of a hyaluronic acid fibrin-based hydrogel (ProCore) used to repair an in vitro model of disc degeneration under dynamic loading. Methods: In vitro model of disc degeneration was induced in intact coccygeal bovine IVD by papain digestion of the NP as previously described[3]. In order to characterize fibrin hydrogels, four experimental groups were considered: 1) intact IVD (control), 2) IVD injected with PBS, 3) injection of hydrogels in degenerative IVD and 4) injection of hydrogels in combination with human bone marrow-derived mesenchymal stem cells (MSC) in degenerative IVD. All of the groups were subjected to dynamic loading protocols consisting of 0.2MPa static compression superimposed with ±2° torsion at 0.2Hz for 8h per day and maintained for 7 days. Additionally, one group consisted of degenerative IVD injected with hydrogel and subjected to static compression. Disc heights were monitored after the duration of the loading and compared to the initial disc height. The macrostructure of the formed tissue and the cellular distribution was evaluated by histological means. Results: After one week of loading, the degenerative IVD filled with hydrogel in combination with MSC (dynamic load), hydrogels (dynamic load) and hydrogels (static load) showed a reduction in height by 30%, 15% and 20%, respectively, as compared to their initial disc height. Histological sections showed that the HA-fibrin gel fully occupied the nucleotomized region of the disc and that fibrin was effective in filling the discontinuities of the cavity region. Furthermore, the cells were homogenously distributed along the fibrin hydrogels after 7 days of loading. Discussion: In this study, we showed that fibrin hydrogels showed a good integration within the papain-induced model of disc degeneration and can withstand the applied loads. Fibrin hydrogels can contribute to disc restoration by possibly maintaining adequate stiffness of the tissue and thus preventing disorganization of the surrounding IVD. References: 1. Jarman, J.P., Arpinar, V.E., Baruah, D., Klein, A.P., Maiman, D.J., and Tugan Muftuler, L. (2014). Intervertebral disc height loss demonstrates the threshold of major pathological changes during degeneration. Eur Spine J . 2. Colombini, A., Ceriani, C., Banfi, G., Brayda-Bruno, M., and Moretti, M. (2014). Fibrin in intervertebral disc tissue engineering. Tissue Eng Part B Rev . 3. Chan, S.C., Bürki, A., Bonél, H.M., Benneker, L.M., and Gantenbein-Ritter, B. (2013). Papain-induced in vitro disc degeneration model for the study of injectable nucleus pulposus therapy. Spine J 13, 273-283. Acknowledgement We thank the Swiss National Science Foundation SNF #310030_153411 for funding.