Influence of curing rate on softening in ethanol, degree of conversion, and wear of resin composite

PURPOSE: To investigate the effect of curing rate on softening in ethanol, degree of conversion, and wear of resin composites. METHOD: With a given energy density and for each of two different light-curing units (QTH or LED), the curing rate was reduced by modulating the curing mode. Thus, the irradiation of resin composite specimens (Filtek Z250, Tetric Ceram, Esthet-X) was performed in a continuous curing mode and in a pulse-delay curing mode. Wallace hardness was used to determine the softening of resin composite after storage in ethanol. Degree of conversion was determined by infrared spectroscopy (FTIR). Wear was assessed by a three-body test. Data were submitted to Levene's test, one and three-way ANOVA, and Tukey HSD test (alpha = 0.05). Results: Immersion in ethanol, curing mode, and material all had significant effects on Wallace hardness. After ethanol storage, resin composites exposed to the pulse-delay curing mode were softer than resin composites exposed to continuous cure (P< 0.0001). Tetric Ceram was the softest material followed by Esthet-X and Filtek Z250 (P< 0.001). Only the restorative material had a significant effect on degree of conversion (P< 0.001): Esthet-X had the lowest degree of conversion followed by Filtek Z250 and Tetric Ceram. Curing mode (P= 0.007) and material (P< 0.001) had significant effect on wear. Higher wear resulted from the pulse-delay curing mode when compared to continuous curing, and Filtek Z250 showed the lowest wear followed by Esthet-X and Tetric Ceram.

Halogen lamp and led activation of resin-modified glass ionomer restorative material. In vitro microhardness after long term storage

AIM: The purpose of this study was to evaluate the activation of resin-modified glass ionomer restorative material (RMGI, Vitremer-3M-ESPE, A3) by halogen lamp (QTH) or light-emitting diode (LED) by Knoop microhardness (KHN) in two storage conditions: 24hrs and 6 months and in two depths (0 and 2 mm). MATERIALS AND METHODS: The specimens were randomly divided into 3 experimental groups (n=10) according to activation form and evaluated in depth after 24h and after 6 months of storage. Activation was performed with QTH for 40s (700 mW/cm2) and for 40 or 20 s with LED (1,200 mW/scm2). After 24 hrs and 6 months of storage at 37°C in relative humidity in lightproof container, the Knoop microhardness test was performed. Statistics Data were analysed by three-way ANOVA and Tukey post-tests (p<0.05). RESULTS: All evaluated factors showed significant differences (p<0.05). After 24 hrs there were no differences within the experimental groups. KHN at 0 mm was significantly higher than 2 mm. After 6 months, there was an increase of microhardness values for all groups, being the ones activated by LED higher than the ones activated by QTH. CONCLUSION: Light-activation with LED positively influenced the KHN for RMGI evaluated after 6 months.