Effect of reduced oxygen tension and long-term mechanical stimulation on chondrocyte-polymer constructs

We have investigated the influence of long-term confined dynamic compression and surface motion under low oxygen tension on tissue-engineered cell-scaffold constructs. Porous polyurethane scaffolds (8 mm x 4 mm) were seeded with bovine articular chondrocytes and cultured under normoxic (21% O(2)) or hypoxic (5% O(2)) conditions for up to 4 weeks. By means of our joint-simulating bioreactor, cyclic axial compression (10-20%; 0.5 Hz) was applied for 1 h daily with a ceramic ball, which simultaneously oscillated over the construct surface (+/-25 degrees; 0.5 Hz). Culture under reduced oxygen tension resulted in an increase in mRNA levels of type II collagen and aggrecan, whereas the expression of type I collagen was down-regulated at early time points. A higher glycosaminoglycan content was found in hypoxic than in normoxic constructs. Immunohistochemical analysis showed more intense type II and weaker type I collagen staining in hypoxic than in normoxic cultures. Type II collagen gene expression was slightly elevated after short-term loading, whereas aggrecan mRNA levels were not influenced by the applied mechanical stimuli. Of importance, the combination of loading and low oxygen tension resulted in a further down-regulation of collagen type I mRNA expression, contributing to the stabilization of the chondrocytic phenotype. Histological results confirmed the beneficial effect of mechanical loading on chondrocyte matrix synthesis. Thus, mechanical stimulation combined with low oxygen tension is an effective tool for modulating the chondrocytic phenotype and should be considered when chondrocytes or mesenchymal stem cells are cultured and differentiated with the aim of generating cartilage-like tissue in vitro.

Proliferation, differentiation and gene expression of osteoblasts in boron-containing associated with dexamethasone deliver from mesoporous bioactive glass scaffolds

Boron is one of the trace elements in the human body which plays an important role in bone growth. Porous mesopore bioactive glass (MBG) scaffolds are proposed as potential bone regeneration materials due to their excellent bioactivity and drug-delivery ability. The aims of the present study were to develop boron-containing MBG (B-MBG) scaffolds by sol-gel method and to evaluate the effect of boron on the physiochemistry of B-MBG scaffolds and the response of osteoblasts to these scaffolds. Furthermore, the effect of dexamethasone (DEX) delivery in B-MBG scaffold system was investigated on the proliferation, differentiation and bone-related gene expression of osteoblasts. The composition, microstructure and mesopore properties (specific surface area, nano-pore volume and nano-pore distribution) of B-MBG scaffolds have been characterized. The effect of boron contents and large-pore porosity on the loading and release of DEX in B-MBG scaffolds were also investigated. The results have shown that the incorporation of boron into MBG scaffolds slightly decreases the specific surface area and pore volume, but maintains well-ordered mesopore structure and high surface area and nano-pore volume compared to non-mesopore bioactive glass. Boron contents in MBG scaffolds did not influence the nano-pore size distribution or the loading and release of DEX. B-MBG scaffolds have the ability to maintain a sustained release of DEX in a long-term span. Incorporating boron into MBG glass scaffolds led to a controllable release of boron ions and significantly improved the proliferation and bone-related gene expression (Col I and Runx2) of osteoblasts. Furthermore, the sustained release of DEX from B-MBG scaffolds significantly enhanced alkaline phosphatase (ALP) activity and gene expressions (Col I, Runx2, ALP and BSP) of osteoblasts. These results suggest that boron plays an important role in enhancing osteoblast proliferation in B-MBG scaffold system and DEX-loaded B-MBG scaffolds show great potential as a release system to enhance osteogenic property for bone tissue engineering application.

Construction of skeletal myoblast-based polyurethane scaffolds for myocardial repair

Intramyocardial transplantation of skeletal myoblasts augments postinfarction cardiac function. However, poor survival of injected cells limits this therapy. It is hypothesized that implantation of myoblast-based scaffolds would result in greater cell survival. Rat skeletal myoblasts were seeded on highly porous polyurethane (PU) scaffolds (7.5 x 7.5 x 2.0 mm). The effect of several scaffold pretreatments, initial cell densities, and culture periods was tested by DNA-based cell count and viability assessment. Seeded PU scaffolds were implanted on infarcted hearts and immunohistology was performed 4 weeks later. Precoating with laminin allowed the most favorable cell attachment. An initial inoculation with 5 x 10(6) cells followed by a 15-day culture period resulted in optimal myoblast proliferation. Four weeks after their implantation in rats, numerous myoblasts were found throughout the seeded patches although no sign of differentiation could be observed. This myoblast seeding technique on PU allows transfer of a large number of living myoblasts to a damaged myocardium.

Maxillary sinus grafting with a synthetic, nanocrystalline hydroxyapatite-silica gel in humans: histologic and histomorphometric results.

The aim of this study was to evaluate in humans the amount of new bone after sinus floor elevation with a synthetic bone substitute material consisting of nanocrystalline hydroxyapatite embedded in a highly porous silica gel matrix. The lateral approach was applied in eight patients requiring sinus floor elevation to place dental implants. After elevation of the sinus membrane, the cavities were filled with 0.6-mm granules of nanocrystalline hydroxyapatite mixed with the patient's blood. A collagen membrane (group 1) or a platelet-rich fibrin (PRF) membrane (group 2) was placed over the bony window. After healing periods between 7 and 11 months (in one case after 24 months), 16 biopsy specimens were harvested with a trephine bur during implant bed preparation. The percentage of new bone, residual filler material, and soft tissue was determined histomorphometrically. Four specimens were excluded from the analysis because of incomplete biopsy removal. In all other specimens, new bone was observed in the augmented region. For group 1, the amount of new bone, residual graft material, and soft tissue was 28.7% ± 5.4%, 25.5% ± 7.6%, and 45.8% ± 3.2%, respectively. For group 2, the values were 28.6% ± 6.90%, 25.7% ± 8.8%, and 45.7% ± 9.3%, respectively. All differences between groups 1 and 2 were not statistically significant. The lowest and highest values of new bone were 21.2% and 34.1% for group 1 and 17.4% and 37.8% for group 2, respectively. The amount of new bone after the use of nanocrystalline hydroxyapatite for sinus floor elevation in humans is comparable to values found in the literature for other synthetic or xenogeneic bone substitute materials. There was no additional beneficial effect of the PRF membrane over the non-cross-linked collagen membrane.