Maxillary sinus grafting with a synthetic, nanocrystalline hydroxyapatite-silica gel in humans: histologic and histomorphometric results.

The aim of this study was to evaluate in humans the amount of new bone after sinus floor elevation with a synthetic bone substitute material consisting of nanocrystalline hydroxyapatite embedded in a highly porous silica gel matrix. The lateral approach was applied in eight patients requiring sinus floor elevation to place dental implants. After elevation of the sinus membrane, the cavities were filled with 0.6-mm granules of nanocrystalline hydroxyapatite mixed with the patient's blood. A collagen membrane (group 1) or a platelet-rich fibrin (PRF) membrane (group 2) was placed over the bony window. After healing periods between 7 and 11 months (in one case after 24 months), 16 biopsy specimens were harvested with a trephine bur during implant bed preparation. The percentage of new bone, residual filler material, and soft tissue was determined histomorphometrically. Four specimens were excluded from the analysis because of incomplete biopsy removal. In all other specimens, new bone was observed in the augmented region. For group 1, the amount of new bone, residual graft material, and soft tissue was 28.7% ± 5.4%, 25.5% ± 7.6%, and 45.8% ± 3.2%, respectively. For group 2, the values were 28.6% ± 6.90%, 25.7% ± 8.8%, and 45.7% ± 9.3%, respectively. All differences between groups 1 and 2 were not statistically significant. The lowest and highest values of new bone were 21.2% and 34.1% for group 1 and 17.4% and 37.8% for group 2, respectively. The amount of new bone after the use of nanocrystalline hydroxyapatite for sinus floor elevation in humans is comparable to values found in the literature for other synthetic or xenogeneic bone substitute materials. There was no additional beneficial effect of the PRF membrane over the non-cross-linked collagen membrane.

Osteoblast responses to different oxide coatings produced by the sol-gel process on titanium substrates

In order to improve the osseointegration of endosseous implants made from titanium, the structure and composition of the surface were modified. Mirror-polished commercially pure (cp) titanium substrates were coated by the sol-gel process with different oxides: TiO(2), SiO(2), Nb(2)O(5) and SiO(2)-TiO(2). The coatings were physically and biologically characterized. Infrared spectroscopy confirmed the absence of organic residues. Ellipsometry determined the thickness of layers to be approximately 100nm. High resolution scanning electron microscopy (SEM) and atomice force microscopy revealed a nanoporous structure in the TiO(2) and Nb(2)O(5) layers, whereas the SiO(2) and SiO(2)-TiO(2) layers appeared almost smooth. The R(a) values, as determined by white-light interferometry, ranged from 20 to 50nm. The surface energy determined by the sessile-drop contact angle method revealed the highest polar component for SiO(2) (30.7mJm(-2)) and the lowest for cp-Ti and 316L stainless steel (6.7mJm(-2)). Cytocompatibility of the oxide layers was investigated with MC3T3-E1 osteoblasts in vitro (proliferation, vitality, morphology and cytochemical/immunolabelling of actin and vinculin). Higher cell proliferation rates were found in SiO(2)-TiO(2) and TiO(2), and lower in Nb(2)O(5) and SiO(2); whereas the vitality rates increased for cp-Ti and Nb(2)O(5). Cytochemical assays showed that all substrates induced a normal cytoskeleton and well-developed focal adhesion contacts. SEM revealed good cell attachment for all coating layers. In conclusion, the sol-gel-derived oxide layers were thin, pure and nanostructured; consequent different osteoblast responses to those coatings are explained by the mutual action and coadjustment of different interrelated surface parameters.