Microhardness and marginal adaptation of pre-warmed composites

Objectives: The aim of this study was to examine the effect of pre-warmed composite on the microhardness and marginal adaptation. Methods: Ninety six identical class II cavities were prepared in extracted human molars and filled/cured in three 2 mm increments using a metal matrix. Two composites (Tetric Evo Ceram (IvoclarVivadent) and ELS(Saremco)) were cured with a LED curing unit (Bluephase (IvoclarVivadent)) using curing cycles of 20 and 40 seconds. The composite was used at room temperature or pre-warmed at 54.5ºC (Calset(AdDent)). Twelve teeth were filled for every composite-curing time-composite temperature combination. The teeth were thermocycled (1000 cycles at 5º and 55ºC) and then stored at 37° C for seven days . Dye penetration (basic fuchsine 5% for 8 hours) was measured using a score scale. Knoop microhardness was determined 100, 200, 500, 1000, 1500, 2500, 3500, 4500 and 5500µm from the occlusal surface at a distance of 150 and 1000µm from the metal matrix. The total degree of polymerization of a composite specimen was determined by calculating the area under the hardness curve. Results: Statistical analyses showed no difference in marginal adaptation (p>0.05). Hardness values at 150µm from the matrix were lower than those at 1000µm. There was an increase of the microhardness at the top of each increment and decrease towards the bottom of each increment. Longer curing times resulted in harder composite samples. Multiple linear regression showed that only the curing time (p<0.001) and composite material (p<0.001) had a significant association with the degree of polymerization. The degree of polymerization was not influenced by pre-warming the composite at a temperature of 54.5ºC (p=4.86). Conclusion: Polymerization time can not be reduced by pre-warming the composite on a temperature of 54.5ºC. The marginal adaptation is not compromised by pre-warming the composite.