Influence of curing rate on softening in ethanol, degree of conversion, and wear of resin composite

PURPOSE: To investigate the effect of curing rate on softening in ethanol, degree of conversion, and wear of resin composites. METHOD: With a given energy density and for each of two different light-curing units (QTH or LED), the curing rate was reduced by modulating the curing mode. Thus, the irradiation of resin composite specimens (Filtek Z250, Tetric Ceram, Esthet-X) was performed in a continuous curing mode and in a pulse-delay curing mode. Wallace hardness was used to determine the softening of resin composite after storage in ethanol. Degree of conversion was determined by infrared spectroscopy (FTIR). Wear was assessed by a three-body test. Data were submitted to Levene's test, one and three-way ANOVA, and Tukey HSD test (alpha = 0.05). Results: Immersion in ethanol, curing mode, and material all had significant effects on Wallace hardness. After ethanol storage, resin composites exposed to the pulse-delay curing mode were softer than resin composites exposed to continuous cure (P< 0.0001). Tetric Ceram was the softest material followed by Esthet-X and Filtek Z250 (P< 0.001). Only the restorative material had a significant effect on degree of conversion (P< 0.001): Esthet-X had the lowest degree of conversion followed by Filtek Z250 and Tetric Ceram. Curing mode (P= 0.007) and material (P< 0.001) had significant effect on wear. Higher wear resulted from the pulse-delay curing mode when compared to continuous curing, and Filtek Z250 showed the lowest wear followed by Esthet-X and Tetric Ceram.

Curing capability of halogen and LED light curing units in deep class II cavities in extracted human molars

Class II cavities were prepared in extracted lower molars filled and cured in three 2-mm increments using a metal matrix. Three composites (Spectrum TPH A4, Ceram X mono M7 and Tetric Ceram A4) were cured with both the SmartLite PS LED LCU and the Spectrum 800 continuous cure halogen LCU using curing cycles of 10, 20 and 40 seconds. Each increment was cured before adding the next. After a seven-day incubation period, the composite specimens were removed from the teeth, embedded in self-curing resin and ground to half the orofacial width. Knoop microhardness was determined 100, 200, 500, 1000, 1500, 2500, 3500, 4500 and 5500 microm from the occlusal surface at a distance of 150 microm and 1000 microm from the metal matrix. The total degree of polymerization of a composite specimen for any given curing time and curing light was determined by calculating the area under the hardness curve. Hardness values 150 microm from the metal matrix never reached maximum values and were generally lower than those 1000 microm from the matrix. The hardest composite was usually encountered between 200 microm and 1000 microm from the occlusal surface. For every composite-curing time combination, there was an increase in microhardness at the top of each increment (measurements at 500, 2500 and 4500 microm) and a decrease towards the bottom of each increment (measurements at 1500, 3500 and 5500 microm). Longer curing times were usually combined with harder composite samples. Spectrum TPH composite was the only composite showing a satisfactory degree of polymerization for all three curing times and both LCUs. Multiple linear regression showed that only the curing time (p < 0.001) and composite material (p < 0.001) had a significant association with the degree of polymerization. The degree of polymerization achieved by the LED LCU was not significantly different from that achieved by the halogen LCU (p = 0.54).