The effect of dissolved magnesium on diffusion creep in calcite

We experimentally tested a series of synthetic calcite marbles with varying amounts of dissolved magnesium in a standard triaxial deformation machine at 300 MPa confining pressure, temperatures between 700 and 850°C, stresses between 2 and 100 MPa, and strain rates between 10−7 and 10−3 s−1. The samples were fabricated by hot isostatic pressing of a mixture of calcite and dolomite at 850°C and 300 MPa. The fabrication protocol resulted in a homogeneous, fine-grained high-magnesian calcite aggregate with minimal porosity and with magnesium contents between 0.07 and 0.17 mol% MgCO3. At stresses below 40 MPa the samples deformed with linear viscosity that depended inversely on grain size to the 3.26±0.51 power, suggesting that the mechanisms of deformation were some combination of grain boundary diffusion and grain boundary sliding. Because small grain sizes tended to occur in the high-magnesium calcite, the strength also appeared to vary inversely with magnesium content. However, the strength at constant grain size does not depend on the amount of dissolved magnesium, and thus, the impurity effect seems to be indirect. At stresses higher than 40 MPa, the aggregates become non-linearly viscous, a regime we interpret to be dislocation creep. The transition between the two regimes depends on grain size, as expected. The activation energy for diffusion creep is 200±30 kJ/mol and is quite similar to previous measurements in natural and synthetic marbles deformed at similar conditions with no added magnesium.

Atomistic Modeling of Effect of Mg on Oxygen Vacancy Diffusion in α-Alumina

Oxygen diffusion plays an important role in grain growth and densification during the sintering of alumina ceramics and governs high-temperature processes such as creep. The atomistic mechanism for oxygen diffusion in alumina is, however, still debated; atomistic calculations not being able to match experimentally determined activation energies for oxygen vacancy diffusion. These calculations are, however, usually performed for perfectly pure crystals, whereas virtually every experimental alumina sample contains a significant fraction of impurity/dopants ions. In this study, we use atomistic defect cluster and nudged elastic band (NEB) calculations to model the effect of Mg impurities/dopants on defect binding energies and migration barriers. We find that oxygen vacancies can form energetically favorable clusters with Mg, which reduces the number of mobile species and leads to an additional 1.5 eV energy barrier for the detachment of a single vacancy from Mg. The migration barriers of diffusive jumps change such that an enhanced concentration of oxygen vacancies is expected around Mg ions. Mg impurities were also found to cause destabilization of certain vacancy configurations as well as enhanced vacancy–vacancy interaction.