Origin of the high upconversion green luminescence efficiency in -NaYF4:2% Er3+,20% Yb3+

Site-selective spectroscopy in hexagonal beta-NaYF4:Er3+,Yb3+ has revealed different environments for Er3+ ions (multisite formation). The low-temperature S-4(3/2) -> (I15/2Er3+)-I-4 green emission depends on the excitation wavelength associated with the F-4(7/2) Er3+ level. We have studied the effect of hydrostatic pressure on the green, red, and blue Er3+ emission upon NIR excitation at similar to 980 nm, in order to establish the role played by energy resonance conditions and the multiple Er3+ sites due to the disordered structure for the upconversion (UC) process (energy tuning). The variation of photoluminescence spectra and lifetimes as a function of pressure and temperature reveals that the origin of the high green UC efficiency of the beta-NaYF4:Er3+,Yb3+ compound is mainly due to the multisite distribution, and the low phonon energy of the host lattice.

Optimizing infrared to near infrared upconversion quantum yield of β-NaYF4:Er3+ in fluoropolymer matrix for photovoltaic devices

The present study reports for the first time the optimization of the infrared (1523 nm) to near-infrared (980 nm) upconversion quantum yield (UC-QY) of hexagonal trivalent erbium doped sodium yttrium fluoride (β-NaYF4:Er3+) in a perfluorocyclobutane (PFCB) host matrix under monochromatic excitation. Maximum internal and external UC-QYs of 8.4% ± 0.8% and 6.5% ± 0.7%, respectively, have been achieved for 1523 nm excitation of 970 ± 43 Wm−2 for an optimum Er3+ concentration of 25 mol% and a phosphor concentration of 84.9 w/w% in the matrix. These results correspond to normalized internal and external efficiencies of 0.86 ± 0.12 cm2 W−1 and 0.67 ± 0.10 cm2 W−1, respectively. These are the highest values ever reported for β-NaYF4:Er3+ under monochromatic excitation. The special characteristics of both the UC phosphor β-NaYF4:Er3+ and the PFCB matrix give rise to this outstanding property. Detailed power and time dependent luminescence measurements reveal energy transfer upconversion as the dominant UC mechanism.

Highly Efficient IR to NIR Upconversion in Gd2O2S: Er3+ for Photovoltaic Applications

Upconversion (UC) is a promising option to enhance the efficiency of solar cells by conversion of sub-bandgap infrared photons to higher energy photons that can be utilized by the solar cell. The UC quantum yield is a key parameter for a successful application. Here the UC luminescence properties of Er3+-doped Gd2O2S are investigated by means of luminescence spectroscopy, quantum yield measurements, and excited state dynamics experiments. Excitation into the maximum of the 4I15/2 → 4I13/2 Er3+ absorption band around 1500 nm induces very efficient UC emission from different Er3+ excited states with energies above the silicon bandgap, in particular, the emission originating from the 4I11/2 state around 1000 nm. Concentration dependent studies reveal that the highest UC quantum yield is realized for a 10% Er3+-doping concentration. The UC luminescence is compared to the well-known Er3+-doped β-NaYF4 UC material for which the highest UC quantum yield has been reported for 25% Er3+. The UC internal quantum yields were measured in this work for Gd2O2S: 10%Er3+ and β-NaYF4: 25%Er3+ to be 12 ± 1% and 8.9 ± 0.7%, respectively, under monochromatic excitation around 1500 nm at a power of 700 W/m2. The UC quantum yield reported here for Gd2O2S: 10%Er3+ is the highest value achieved so far under monochromatic excitation into the 4I13/2 Er3+ level. Power dependence and lifetime measurements were performed to understand the mechanisms responsible for the efficient UC luminescence. We show that the main process yielding 4I11/2 UC emission is energy transfer UC.

Relation between Excitation Power Density and Er3+ Doping Yielding the Highest Absolute Upconversion Quantum Yield

The upconversion quantum yield (UCQY) is one of the most significant parameters for upconverter materials. A high UCQY is essential for a succesful integration of upconversion in many applications, such as harvesting of the solar radiation. However, little is known about which doping level of the rare-earth ions yields the highest UCQY in the different host lattices and what are the underlying causes. Here, we investigate which Er3+ doping yields the highest UCQY in the host lattices β-NaYF4 and Gd2O2S under 4I15/2 → 4I13/2 excitation. We show for both host lattices that the optimum Er3+ doping is not fixed and it actually decreases as the irradiance of the excitation increases. To find the optimum Er3+ doping for a given irradiance, we determined the peak position of the internal UCQY as a function of the average Er−Er distance. For this purpose, we used a fit on experimental data, where the average Er−Er distance was calculated from the Er3+ doping of the upconverter samples and the lattice parameters of the host materials. We observe optimum average Er−Er distances for the host lattices β-NaYF4 and Gd2O2S with differences <14% at the same irradiance levels, whereas the optimum Er3+ doping are around 2× higher for β-NaYF4 than for Gd2O2S. Estimations by extrapolation to higher irradiances indicate that the optimum average Er−Er distance converges to values around 0.88 and 0.83 nm for β-NaYF4 and Gd2O2S, respectively. Our findings point to a fundamental relationship and focusing on the average distance between the active rare-earth ions might be a very efficient way to optimize the doping of rare-earth ions with regard to the highest achievable UCQY.