Push-out bond strength of CAD/CAM-ceramic luted to dentin with self-adhesive resin cements

OBJECTIVES: This study evaluated the initial and the artificially aged push-out bond strength between ceramic and dentin produced by one of five resin cements. METHODS: Two-hundred direct ceramic restorations (IPS Empress CAD) were luted to standardized Class I cavities in extracted human molars using one of four self-adhesive cements (SpeedCEM, RelyX Unicem Aplicap, SmartCem2 and iCEM) or a reference etch-and-rinse resin cement (Syntac/Variolink II) (n=40/cement). Push-out bond strength (PBS) was measured (1) after 24h water storage (non-aged group; n=20/cement) or (2) after artificial ageing with 5000 thermal cycles followed by 6 months humid storage (aged group; n=20/cement). Nonparametrical ANOVA and pairwise Wilcoxon rank-sum tests with Bonferroni-Holm adjustment were applied for statistical analysis. The significance level was set at alpha=0.05. In addition, failure mode and fracture pattern were analyzed by stereomicroscope and scanning electron microscopy. RESULTS: Whereas no statistically significant effect of storage condition was found (p=0.441), there was a significant effect of resin cement (p<0.0001): RelyX Unicem showed significantly higher PBS than the other cements. Syntac/Variolink II showed significantly higher PBS than SmartCEM2 (p<0.001). No significant differences were found between SpeedCEM, SmartCem2, and iCEM. The predominant failure mode was adhesive failure of cements at the dentin interface except for RelyX Unicem which in most cases showed cohesive failure in ceramic. SIGNIFICANCE: The resin cements showed marked differences in push-out bond strength when used for luting ceramic restorations to dentin. Variolink II with the etch-and-rinse adhesive Syntac did not perform better than three of the four self-adhesive resin cements tested.

Clinical and Histological Evaluation of a Granular Bovine Bone Biomaterial Used as an Adjunct to Guided Tissue Regeneration With a Bioresorbable Bovine Pericardium Collagen Membrane in the Treatment of Intrabony Periodontal Defects

The aim of the present study is to evaluate the clinical and histologic healing of deep intrabony defects treated with guided tissue regeneration (GTR) with a collagen membrane from bovine pericardium and implantation of granular bovine bone biomaterial.

Effect of systemic tetracycline on the degradation of tetracycline-impregnated bilayered collagen membranes: an animal study

BACKGROUND: Premature collagen membrane degradation may compromise the outcome of osseous regenerative procedures. Tetracyclines (TTCs) inhibit the catalytic activities of human metalloproteinases. Preprocedural immersion of collagen membranes in TTC and systemic administration of TTC may be possible alternatives to reduce the biodegradation of native collagen membranes. AIM: To evaluate the in vivo degradation of collagen membranes treated by combined TTC immersion and systemic administration. MATERIALS AND METHODS: Seventy-eight bilayered porcine collagen membrane disks were divided into three groups and were immersed in 0, 50, or 100 mg/mL TTC solution. Three disks, one of each of the three groups, were implanted on the calvaria of each of 26 Wistar rats. Thirteen (study group) were administered with systemic TTC (10 mg/kg), while the remaining 13 received saline injections (control group). Calvarial tissues were retrieved after 3 weeks, and histological sections were analyzed by image analysis software. RESULTS: Percentage of remaining collagen area within nonimpregnated membranes was 52.26 ± 20.67% in the study group, and 32.74 ± 13.81% in the control group. Immersion of membranes in 100 mg/mL TTC increased the amount of residual collagen to 63.46 ± 18.19% and 42.82 ± 12.99% (study and control groups, respectively). Immersion in 50 mg/mL TTC yielded maximal residual collagen values: 80.75 ± 14.86% and 59.15 ± 8.01% (study and control groups, respectively). Differences between the TTC concentrations, and between the control and the study groups were statistically significant. CONCLUSIONS: Immersion of collagen membranes in TTC solution prior to their implantation and systemic administration of TTC significantly decreased the membranes' degradation.

Evaluation of cartilage repair tissue after matrix-associated autologous chondrocyte transplantation using a hyaluronic-based or a collagen-based scaffold with morphological MOCART scoring and biochemical T2 mapping: preliminary results

In cartilage repair, bioregenerative approaches using tissue engineering techniques have tried to achieve a close resemblance to hyaline cartilage, which might be visualized using advanced magnetic resonance imaging.

Identification of a fibronectin interaction site in the extracellular matrix protein ameloblastin

Mammalian teeth are composed of hydroxyapatite crystals that are embedded in a rich extracellular matrix. This matrix is produced by only two cell types, the mesenchymal odontoblasts and the ectodermal ameloblasts. Ameloblasts secrete the enamel proteins amelogenin, ameloblastin, enamelin and amelotin. Odontoblasts secrete collagen type I and several calcium-binding phosphoproteins including dentin sialophosphoprotein, dentin matrix protein, bone sialoprotein and osteopontin. The latter four proteins have recently been grouped in the family of the SIBLINGs (small integrin-binding ligand, N-linked glycoproteins) because they display similar gene structures and because they contain an RGD tripeptide sequence that binds to integrin receptors and thus mediates cell adhesion. We have prepared all the other tooth-specific proteins in recombinant form and examined whether they might also promote cell adhesion similar to the SIBLINGs. We found that only ameloblastin consistently mediated adhesion of osteoblastic and fibroblastic cells to plastic or titanium surfaces. The activity was dependent on the intact three-dimensional structure of ameloblastin and required de novo protein synthesis of the adhering cells. By deletion analysis and in vitro mutagenesis, the active site could be narrowed down to a sequence of 13 amino acid residues (VPIMDFADPQFPT) derived from exon 7 of the rat ameloblastin gene or exons 7-9 of the human gene. Kinetic studies and RNA interference experiments further demonstrated that this sequence does not directly bind to a cell surface receptor but that it interacts with cellular fibronectin, which in turn binds to integrin receptors. The identification of a fibronectin-binding domain in ameloblastin might permit interesting applications for dental implantology. Implants could be coated with peptides containing the active sequence, which in turn would recruit fibronectin from the patient's blood. The recruited fibronectin should then promote cell adhesion on the implant surface, thereby accelerating osseointegration of the implant.

Percutaneous collagen induction-regeneration in place of cicatrisation?

Ablative procedures that are used for the improvement of a degenerative process that leads to a loss of skin elasticity and integrity, injure or destroy the epidermis and its basement membrane and lead to fibrosis of the papillary dermis. It was recently shown in clinical and laboratory trials that percutaneous collagen induction (PCI) by multiple needle application is a method for safely treating wrinkles and scars and smoothening the skin without the risk of dyspigmentation. In our study, we describe the effect of PCI on epidermal thickness and the induction of genes relevant for regenerative processes in the skin in a small animal model.

Percutaneous collagen induction therapy: an alternative treatment for burn scars

This study aims to evaluate percutaneous collagen induction (PCI) in post-burn scarring.

Different collagen types define two types of idiopathic epiretinal membranes

To identify differences in extracellular matrix contents between idiopathic epiretinal membranes (IEM) of cellophane macular reflex (CMRM) or preretinal macular fibrosis (PMFM) type.

Bonding of restorative materials to dentin with various luting agents

The aim was to compare eight types of luting agents when used to bond six indirect, laboratory restorative materials to dentin. Cylinders of the six restorative materials (Esteticor Avenir [gold alloy], Tritan [titanium], NobelRondo [feldspathic porcelain], Finesse All-Ceramic [leucite-glass ceramic], Lava [zirconia], and Sinfony [resin composite]) were ground and air-abraded. Cylinders of feldspathic porcelain and glass ceramic were additionally etched with hydrofluoric acid and were silane-treated. The cylinders were luted to ground human dentin with eight luting agents (DeTrey Zinc [zinc phosphate cement], Fuji I [conventional glass ionomer cement], Fuji Plus [resin-modified glass ionomer cement], Variolink II [conventional etch-and-rinse resin cement], Panavia F2.0 and Multilink [self-etch resin cements], and RelyX Unicem Aplicap and Maxcem [self-adhesive resin cements]). After water storage at 37°C for one week, the shear bond strength of the specimens (n=8/group) was measured, and the fracture mode was stereomicroscopically examined. Bond strength data were analyzed with two-factorial analysis of variance (ANOVA) followed by Newman-Keuls' Multiple Range Test (?=0.05). Both the restorative material and the luting agent had a significant effect on bond strength, and significant interaction was noted between the two variables. Zinc phosphate cement and glass ionomer cements produced the lowest bond strengths, whereas the highest bond strengths were found with the two self-etch and one of the self-adhesive resin cements. Generally, the fracture mode varied markedly with the restorative material. The luting agents had a bigger influence on bond strength between restorative materials and dentin than was seen with the restorative material.

Micromorphology and adhesive performance of Er:YAG laser-treated dentin of primary teeth

This study evaluated (1) the micromorphology by scanning electron microscopy (SEM) and (2) the adhesive performance by microtensile bond strength (μTBS) of diamond bur-treated dentin compared to Er:YAG laser-treated dentin of human primary teeth. (1) For qualitative SEM evaluation, dentin of 18 second primary molars (n = 3/method) was treated with either diamond bur as a control (group 1a: 40 μm diamond bur only (clinical situation); group 1b: grinding + 40 μm diamond bur) or with Er:YAG laser (group 2a (clinical situation, manufacturer's settings): 200 mJ/25 Hz (5 W) + 100 mJ/35 Hz (3.5 W) laser only; group 2b (experimental setting "high"): grinding + 400 mJ/20 Hz (8 W); group 2c (manufacturer's setting "finishing"): grinding + 100 mJ/35 Hz (3.5 W); group 2d (experimental setting "low"): grinding + 50 mJ/35 Hz (1.75 W)). (2) For evaluation of adhesive performance, 64 second primary molars were divided into four groups and treated as described for group 1b and groups 2b/c/d (n = 16/method), and μTBS of Clearfil SE/Clearfil Majesty Esthetic to dentin was measured. The SEM micrographs were qualitatively analyzed. The μTBS values were compared with a Kruskal-Wallis test. The significance level was set at α = 0.05. SEM micrographs showed the typical micromorphologies with a smear layer for the diamond bur groups and open dentin tubules for all laser-treated groups. However, in group 2d, the laser beam had insufficiently irradiated the dentin area, rendering the underlying ground surface partly visible. There were no statistically significant differences between μTBS values of the four groups (p = 0.394). This suggests that Er:YAG laser treatment of dentin of primary molars provides bond strengths similar to those obtained following diamond bur treatment.

Irregularities below the Enamel-Dentin Junction May Predispose for Fissure Caries

This study investigated the structure of the fissure fundus on occlusal surfaces with respect to the detection of possible irregularities below the enamel-dentin junction (EDJ). Occlusal surfaces were examined by micro-computed tomography (µCT). In total, 203 third molars with clinically sound occlusal fissures or non-cavitated lesions were selected. All specimens were scanned with µCT. Subsequently, each tooth was sectioned, and each slice was investigated by stereomicroscopy. In 7 of 203 molars (3.4%), demarcated radiolucencies below the EDJ were detected by µCT. These defects were obviously of non-carious origin, because the µCT images revealed no gradient of demineralization in the dentin. In all cases, a direct pathway between the oral cavity and the dentin was evident. The comparison of the µCT sites with conventional histological images also revealed defects in the dentin. These results demonstrate that demarcated radiolucencies below the EDJ may not necessarily be caries lesions according to µCT images and may be classified as possible developmental irregularities. To avoid misinterpreting µCT data, dental researchers should carefully consider this condition when analyzing µCT images. The clinical significance of this finding is that these defects may predispose molar teeth to early-onset caries in occlusal pits and fissures.

Long-term bonding to eroded dentin requires superficial bur preparation

This study aims to evaluate the influence of different surface preparation techniques on long-term bonding effectiveness to eroded dentin.

Treatment of soft tissue recessions at titanium implants using a resorbable collagen matrix: a pilot study

OBJECTIVES: To histologically assess the effectiveness of a porcine-derived collagen matrix (CM) and a subepithelial connective tissue graft (CTG) for the coverage of single mucosal recessions at osseointegrated dental implants. MATERIALS AND METHODS: Chronic-type mucosal Miller Class I-like recessions (mean clinical defect height: 0.67 ± 0.33-1.16 ± 0.19 mm) were established at the buccal aspect of titanium implants with platform switch in six beagle dogs. The defects were randomly allocated to either (1) coronally advanced flap surgery (CAF) + CM, (2) CAF + CTG or (3) CAF alone. At 12 weeks, histomorphometrical measurements were made (e.g.) between the implant shoulder (IS) and the mucosal margin (PM) and IS and the outer contour of the adjacent soft tissue (mucosal thickness [MT]). RESULTS: All treatment procedures investigated were associated with an almost complete soft tissue coverage of the defect area (i.e. coronal positioning of PM relative to IS). Mean IS-PM and MT values tended to be increased in both CAF + CM (1.04 ± 0.74 mm/0.71 ± 0.55 mm) and CAF + CTG (0.88 ± 1.23 mm/0.62 ± 0.66 mm) groups when compared with CAF (0.16 ± 0.28 mm/0.34 ± 0.23 mm) alone. These differences, however, did not reach statistical significance. CONCLUSIONS: Within the limits of this pilot study, it was concluded that all treatment procedures investigated were effective in covering soft tissue recessions at titanium implants.

Bovine pericardium based non-cross linked collagen matrix for successful root coverage, a clinical study in human

Introduction The aim of this study was to clinically assess the capacity of a novel bovine pericardium based, non-cross linked collagen matrix in root coverage. Methods 62 gingival recessions of Miller class I or II were treated. The matrix was adapted underneath a coronal repositioned split thickness flap. Clinical values were assessed at baseline and after six months. Results The mean recession in each patient was 2.2 mm at baseline. 6 Months after surgery 86.7% of the exposed root surfaces were covered. On average 0,3 mm of recession remained. The clinical attachment level changed from 3.5 ± 1.3 mm to 1,8 ( ± 0,7) mm during the observational time period. No statistically significant difference was found in the difference of probing depth. An increase in the width of gingiva was significant. With a baseline value of 1.5 ± 0.9 mm an improvement of 2.4 ± 0.8 mm after six month could be observed. 40 out of 62 recessions were considered a thin biotype at baseline. After 6 months all 62 sites were assessed thick. Conclusions The results demonstrate the capacity of the bovine pericardium based non-cross linked collagen matrix for successful root coverage. This material was able to enhance gingival thickness and the width of keratinized gingiva. The percentage of root coverage achieved thereby is comparable to existing techniques. This method might contribute to an increase of patient's comfort and an enhanced aesthetical outcome.