Osteo-odonto-keratoprosthesis (OOKP) and the testing of three different adhesives for bonding bovine teeth with optical poly-(methyl methacrylate) (PMMA) cylinder.

AIM Preparation of the lamina during osteo-odonto-keratoprosthesis (OOKP) design is complex, and its longevity and watertightness important. To date, only acrylic bone cements have been used for bonding the optical cylinder to the tooth dentine. Our aim was to evaluate different dental adhesives for OOKP preparation. METHODS Specimens of bovine teeth were produced by preparing 1.5-mm thick dentine slices with holes having a diameter of 3.5 mm. Each group (n=10 per group) was luted with either classic poly-(methyl methacrylate) (PMMA) bone cement, universal resin cement or glass ionomer cement. All specimens underwent force measurement using a uniaxial traction machine. RESULTS The highest mean force required to break the bond was measured for PMMA bone cement (128.2 N) followed by universal resin cement (127.9 N), with no statistically significant difference. Glass ionomer cement showed significantly lower force resistance (78.1 N). CONCLUSIONS Excellent bonding strength combined with easy application was found for universal resin cement, and thus, it is a potential alternative to acrylic bone cement in OOKP preparation.

BPA qualtitative and quantitative assessment associated with orthodontic bonding in vivo

OBJECTIVE To assess the in vivo amount of BPA released from a visible light-cured orthodontic adhesive, immediately after bracket bonding. METHODS 20 orthodontic patients were recruited after obtaining informed consent. All patients received 24 orthodontic brackets in both dental arches. In Group A (11 patients), 25 ml of tap water were used for mouth rinsing, whereas in Group B (9 patients) a simulated mouth rinse formulation was used: a mixture of 20 ml de-ionized water plus 5 ml absolute ethanol. Rinsing solutions were collected before, immediately after placing the orthodontic appliances and after washing out the oral cavity and were then stored in glass tubes. Rinsing was performed in a single phase for 60s with the entire volume of each liquid. The BPA analysis was performed by gas chromatography-mass spectrometry. RESULTS An increase in BPA concentration immediately after the 1st post-bonding rinse was observed, for both rinsing media, which was reduced after the 2nd post-bonding rinse. Water exhibited higher levels of BPA concentration than water/ethanol after 1st and 2nd post-bonding rinses. Two-way mixed Repeated Measures ANOVA showed that the primary null hypothesis declaring mean BPA concentration to be equal across rinsing medium and rinsing status was rejected (p-value <0.001). The main effects of the rinsing medium and status, as well as their interaction were found to be statistically significant (p-values 0.048, <0.001 and 0.011 respectively). SIGNIFICANCE A significant pattern of increase of BPA concentration, followed by a decrease that reached the initial values was observed. The amount of BPA was relatively low and far below the reference limits of tolerable daily intake.