The influence of saliva on the dissolution of calcium fluoride after application of different fluoride gels in vitro

OBJECTIVE: To determine the formation and dissolution of calcium fluoride on the enamel surface after application of two fluoride gel-saliva mixtures. METHOD AND MATERIALS: From each of 80 bovine incisors, two enamel specimens were prepared and subjected to two different treatment procedures. In group 1, 80 specimens were treated with a mixture of an amine fluoride gel (1.25% F-; pH 5.2; 5 minutes) and human saliva. In group 2, 80 enamel blocks were subjected to a mixture of sodium fluoride gel (1.25% F; pH 5.5; 5 minutes) and human saliva. Subsequent to fluoride treatment, 40 specimens from each group were stored in human saliva and sterile water, respectively. Ten specimens were removed after each of 1 hour, 24 hours, 2 days, and 5 days and analyzed according to potassium hydroxide-soluble fluoride. RESULTS: Application of amine fluoride gel resulted in a higher amount of potassium hydroxide-soluble fluoride than did sodium fluoride gel 1 hour after application. Saliva exerted an inhibitory effect according to the dissolution rate of calcium fluoride. However, after 5 days, more than 90% of the precipitated calcium fluoride was dissolved in the amine fluoride group, and almost all potassium hydroxide-soluble fluoride was lost in the sodium fluoride group. Calcium fluoride apparently dissolves rapidly, even at almost neutral pH. CONCLUSION: Considering the limitations of an in vitro study, it is concluded that highly concentrated fluoride gels should be applied at an adequate frequency to reestablish a calcium fluoride-like layer.

Regulation of Cx45 hemichannels mediated by extracellular and intracellular calcium

Connexin45 (Cx45) hemichannels (HCs) open in the absence of Ca(2+) and close in its presence. To elucidate the underlying mechanisms, we examined the role of extra- and intracellular Ca(2+) on the electrical properties of HCs. Experiments were performed on HeLa cells expressing Cx45 using electrical (voltage clamp) and optical (Ca(2+) imaging) methods. HCs exhibit a time- and voltage-dependent current (I(hc)), activating with depolarization and inactivating with hyperpolarization. Elevation of [Ca(2+)](o) from 20 nM to 2 μM reversibly decreases I(hc), decelerates its rate of activation, and accelerates its deactivation. Our data suggest that [Ca(2+)](o) modifies the channel properties by adhering to anionic sites in the channel lumen and/or its outer vestibule. In this way, it blocks the channel pore and reversibly lowers I(hc) and modifies its kinetics. Rapid lowering of [Ca(2+)](o) from 2 mM to 20 nM, achieved early during a depolarizing pulse, led to an outward I(hc) that developed with virtually no delay and grew exponentially in time paralleled by unaffected [Ca(2+)](i). A step increase of [Ca(2+)](i) evoked by photorelease of Ca(2+) early during a depolarizing pulse led to a transient decrease of I(hc) superimposed on a growing outward I(hc); a step decrease of [Ca(2+)](i) elicited by photoactivation of a Ca(2+) scavenger provoked a transient increase in I(hc). Hence, it is tempting to assume that Ca(2+) exerts a direct effect on Cx45 hemichannels.

Poly(ethylene oxide)-b-poly(3-sulfopropyl methacrylate) block copolymers for calcium phosphate mineralization and biofilm inhibition.

Poly(ethylene oxide) (PEO) has long been used as an additive in toothpaste, partly because it reduces biofilm formation on teeth. It does not, however, reduce the formation of dental calculus or support the remineralization of dental enamel or dentine. The present article describes the synthesis of new block copolymers on the basis of PEO and poly(3-sulfopropyl methacrylate) blocks using atom transfer radical polymerization. The polymers have very large molecular weights (over 10(6) g/mol) and are highly water-soluble. They delay the precipitation of calcium phosphate from aqueous solution but, upon precipitation, lead to relatively monodisperse hydroxyapatite (HAP) spheres. Moreover, the polymers inhibit the bacterial colonization of human enamel by Streptococcus gordonii, a pioneer bacterium in oral biofilm formation, in vitro. The formation of well-defined HAP spheres suggests that a polymer-induced liquid precursor phase could be involved in the precipitation process. Moreover, the inhibition of bacterial adhesion suggests that the polymers could be utilized in caries prevention.

Fluoride varnishes with calcium glycerophosphate: fluoride release and effect on in vitro enamel demineralization

The aims of this study were (1) to assess the amount of fluoride (F) released from varnishes containing calcium glycerophosphate (CaGP) and (2) to assess the effect of the experimental varnishes on in vitro demineralization. Six test groups using 5 varnishes: base varnish (no active ingredients); Duraphat® (2.26% NaF); Duofluorid® (5.63% NaF/CaF2); experimental varnish 1 (1% CaGP/5.63% NaF/CaF2); experimental varnish 2 (5% CaGP/5.63% NaF/CaF2); and no varnish were set up. In stage 1, 60 acrylic blocks were randomly distributed into 6 groups (n = 10). Then 300 µg of each varnish was applied to each block. The blocks were immersed in deionized water, which was changed after 1, 8, 12, 24, 48 and 72 hours. Fluoride concentration in the water was analyzed using a fluoride electrode. In stage 2, 60 bovine enamel samples were distributed into 6 groups (n = 10), and treated with 300 µg of the respective varnish. After 6 h the varnish was removed and the samples were subjected to a 7-day in vitro pH cycle (6 h demineralization/18 h remineralization per day). The demineralization was measured using surface hardness. The results showed that both experimental varnishes released more fluoride than Duofluorid® and Duraphat® (p < 0.05), but Duraphat® showed the best preventive effect by decreasing enamel hardness loss (p < 0.05). Therefore, we conclude that even though (1) the experimental varnishes containing CaGP released greater amounts of F, (2) they did not increase in the preventive effect against enamel demineralization.

Osteoclast-like cells on deproteinized bovine bone mineral and biphasic calcium phosphate: light and transmission electron microscopical observations.

OBJECTIVES The occurrence of multinucleated giant cells (MNGCs) on bone substitute materials has been recognized for a long time. However, there have been no studies linking material characteristics with morphology of the MNGCs. The aim was to analyze the qualitative differences of MNGCs on two commercially available calcium phosphate bone substitute materials retrieved from bone defects. MATERIAL AND METHODS Six defects were prepared bilaterally in the mandibular body of three mini pigs. The defects were randomly grafted with either deproteinized bovine bone mineral (DBBM) or biphasic calcium phosphate (BCP). After a healing period of four weeks, bone blocks were embedded in LR White resin. Three consecutive sections per defect were analyzed as follows: two with light microscopy using toluidine blue and tartrate-resistant acid phosphatase (TRAP) staining and one with transmission electron microscopy. RESULTS Multinucleated giant cells appeared on both biomaterials. On BCP, MNGCs had a flat morphology and were not observed in resorption lacunae. On DBBM, the MNGCs appeared more round and were often found in shallow concavities. MNGCs on both biomaterials demonstrated a varying degree of TRAP staining, with a tendency toward higher staining intensity of MNGCs on BCP. At the ultrastructural level, signs of superficial dissolution of BCP together with phagocytosis of minor fragments were observed. MNGCs on the surface of DBBM demonstrated sealing zones and ruffled borders, both features of mature osteoclasts. CONCLUSION MNGCs demonstrated distinctly different histological features depending on the bone substitute material used. Further research is warranted to understand the clinical implications of these morphological observations.