Push-out bond strength of CAD/CAM-ceramic luted to dentin with self-adhesive resin cements

OBJECTIVES: This study evaluated the initial and the artificially aged push-out bond strength between ceramic and dentin produced by one of five resin cements. METHODS: Two-hundred direct ceramic restorations (IPS Empress CAD) were luted to standardized Class I cavities in extracted human molars using one of four self-adhesive cements (SpeedCEM, RelyX Unicem Aplicap, SmartCem2 and iCEM) or a reference etch-and-rinse resin cement (Syntac/Variolink II) (n=40/cement). Push-out bond strength (PBS) was measured (1) after 24h water storage (non-aged group; n=20/cement) or (2) after artificial ageing with 5000 thermal cycles followed by 6 months humid storage (aged group; n=20/cement). Nonparametrical ANOVA and pairwise Wilcoxon rank-sum tests with Bonferroni-Holm adjustment were applied for statistical analysis. The significance level was set at alpha=0.05. In addition, failure mode and fracture pattern were analyzed by stereomicroscope and scanning electron microscopy. RESULTS: Whereas no statistically significant effect of storage condition was found (p=0.441), there was a significant effect of resin cement (p<0.0001): RelyX Unicem showed significantly higher PBS than the other cements. Syntac/Variolink II showed significantly higher PBS than SmartCEM2 (p<0.001). No significant differences were found between SpeedCEM, SmartCem2, and iCEM. The predominant failure mode was adhesive failure of cements at the dentin interface except for RelyX Unicem which in most cases showed cohesive failure in ceramic. SIGNIFICANCE: The resin cements showed marked differences in push-out bond strength when used for luting ceramic restorations to dentin. Variolink II with the etch-and-rinse adhesive Syntac did not perform better than three of the four self-adhesive resin cements tested.

Teeth restored using fiber-reinforced posts: in vitro fracture tests and finite element analysis

In dentistry the restoration of decayed teeth is challenging and makes great demands on both the dentist and the materials. Hence, fiber-reinforced posts have been introduced. The effects of different variables on the ultimate load on teeth restored using fiber-reinforced posts is controversial, maybe because the results are mostly based on non-standardized in vitro tests and, therefore, give inhomogeneous results. This study combines the advantages of in vitro tests and finite element analysis (FEA) to clarify the effects of ferrule height, post length and cementation technique used for restoration. Sixty-four single rooted premolars were decoronated (ferrule height 1 or 2 mm), endodontically treated and restored using fiber posts (length 2 or 7 mm), composite fillings and metal crowns (resin bonded or cemented). After thermocycling and chewing simulation the samples were loaded until fracture, recording first damage events. Using UNIANOVA to analyze recorded fracture loads, ferrule height and cementation technique were found to be significant, i.e. increased ferrule height and resin bonding of the crown resulted in higher fracture loads. Post length had no significant effect. All conventionally cemented crowns with a 1-mm ferrule height failed during artificial ageing, in contrast to resin-bonded crowns (75% survival rate). FEA confirmed these results and provided information about stress and force distribution within the restoration. Based on the findings of in vitro tests and computations we concluded that crowns, especially those with a small ferrule height, should be resin bonded. Finally, centrally positioned fiber-reinforced posts did not contribute to load transfer as long as the bond between the tooth and composite core was intact.

The influence of toothbrushing and coffee staining on different composite surface coatings

The aim of our study is to evaluate the performance of surface sealants and conventional polishing after ageing procedures. Eighty circular composite restorations were performed on extracted human molars. After standardised roughening, the restorations were either sealed with one of three surface sealants (Lasting Touch (LT), BisCover LV (BC), G-Coat Plus (GP) or a dentin adhesive Heliobond (HB)) or were manually polished with silicon polishers (MP) (n = 16). The average roughness (Ra) and colourimetric parameters (CP) (L*a*b*) were evaluated. The specimens underwent an artificial ageing process by thermocycling, staining (coffee) and abrasive (toothbrushing) procedures. After each ageing step, Ra and CP measurements were repeated. A qualitative surface analysis was performed with SEM. The differences between the test groups regarding Ra and CP values were analysed with nonparametric ANOVA analysis (α = 0.05). The lowest Ra values were achieved with HB. BC and GP resulted in Ra values below 0.2 μm (clinically relevant threshold), whereas LT and MP sometimes led to higher Ra values. LT showed a significantly higher discolouration after the first coffee staining, but this was normalised to the other groups after toothbrushing. The differences between the measurements and test groups for Ra and CP were statistically significant. However, the final colour difference showed no statistical difference among the five groups. SEM evaluation showed clear alterations after ageing in all coating groups. Surface sealants and dentin adhesives have the potential to reduce surface roughness but tend to debond over time. Surface sealants can only be recommended for polishing provisional restorations.