Biomimetic coating of organic polymers with a protein-functionalized layer of calcium phosphate: the surface properties of the carrier influence neither the coating characteristics nor the incorporation mechanism or release kinetics of the protein

Polymers that are used in clinical practice as bone-defect-filling materials possess many essential qualities, such as moldability, mechanical strength and biodegradability, but they are neither osteoconductive nor osteoinductive. Osteoconductivity can be conferred by coating the material with a layer of calcium phosphate, which can be rendered osteoinductive by functionalizing it with an osteogenic agent. We wished to ascertain whether the morphological and physicochemical characteristics of unfunctionalized and bovine-serum-albumin (BSA)-functionalized calcium-phosphate coatings were influenced by the surface properties of polymeric carriers. The release kinetics of the protein were also investigated. Two sponge-like materials (Helistat® and Polyactive®) and two fibrous ones (Ethisorb and poly[lactic-co-glycolic acid]) were tested. The coating characteristics were evaluated using state-of-the-art methodologies. The release kinetics of BSA were monitored spectrophotometrically. The characteristics of the amorphous and the crystalline phases of the coatings were not influenced by either the surface chemistry or the surface geometry of the underlying polymer. The mechanism whereby BSA was incorporated into the crystalline layer and the rate of release of the truly incorporated depot were likewise unaffected by the nature of the polymeric carrier. Our biomimetic coating technique could be applied to either spongy or fibrous bone-defect-filling organic polymers, with a view to rendering them osteoconductive and osteoinductive.

Endothelial-cell-binding aptamer for coating of intracoronary stents

Oligonucleotides capturing CD31 endothelial cells (= aptamer) were used for coating of intracoronary stents to improve endothelialization and vascular healing.

Value of the SYNTAX score for risk assessment in the all-comers population of the randomized multicenter LEADERS (Limus Eluted from A Durable versus ERodable Stent coating) trial

OBJECTIVES: We aimed to assess the predictive value of the SYNTAX score (SXscore) for major adverse cardiac events in the all-comers population of the LEADERS (Limus Eluted from A Durable versus ERodable Stent coating) trial. BACKGROUND: The SXscore has been shown to be an effective predictor of clinical outcomes in patients with multivessel disease undergoing percutaneous coronary intervention. METHODS: The SXscore was prospectively collected in 1,397 of the 1,707 patients enrolled in the LEADERS trial (patients after surgical revascularization were excluded). Post hoc analysis was performed by stratifying clinical outcomes at 1-year follow-up, according to 1 of 3 SXscore tertiles. RESULTS: The 1,397 patients were divided into tertiles based on the SXscore in the following fashion: SXscore8 and 16 (SXhigh) (n=461). At 1-year follow-up, there was a significantly lower number of patients with major cardiac event-free survival in the highest tertile of SXscore (SXlow=92.2%, SXmid=91.1%, and SXhigh=84.6%; p<0.001). Death occurred in 1.5% of SXlow patients, 2.1% of SXmid patients, and 5.6% of SXhigh patients (hazard ratio [HR]: 1.97, 95% confidence interval [CI]: 1.29 to 3.01; p=0.002). The myocardial infarction rate tended to be higher in the SXhigh group. Target vessel revascularization was 11.3% in the SXhigh group compared with 6.3% and 7.8% in the SXlow and SXmid groups, respectively (HR: 1.38, 95% CI: 1.1 to 1.75; p=0.006). Composite of cardiac death, myocardial infarction, and clinically indicated target vessel revascularization was 7.8%, 8.9%, and 15.4% in the SXlow, SXmid, and SXhigh groups, respectively (HR: 1.47, 95% CI: 1.19 to 1.81; p<0.001). CONCLUSIONS: The SXscore, when applied to an all-comers patient population treated with drug-eluting stents, may allow prospective risk stratification of patients undergoing percutaneous coronary intervention. (LEADERS Trial Limus Eluted From A Durable Versus ERodable Stent Coating; NCT00389220).

Functionalization of deproteinized bovine bone with a coating-incorporated depot of BMP-2 renders the material efficiently osteoinductive and suppresses foreign-body reactivity

The repair of critical-sized bony defects remains a challenge in the fields of implantology, maxillofacial surgery and orthopaedics. As an alternative bone-defect filler to autologous bone grafts, deproteinized bovine bone (DBB) is highly osteoconductive and clinically now widely used. However, this product suffers from the disadvantage of not being intrinsically osteoinductive. In the present study, this property was conferred by coating DBB with a layer of calcium phosphate into which bone morphogenetic protein 2 (BMP-2) was incorporated. Granules of DBB bearing a coating-incorporated depot of BMP-2--together with the appropriate controls (DBB bearing a coating but no BMP-2; uncoated DBB bearing adsorbed BMP-2; uncoated DBB bearing no BMP-2)--were implanted subcutaneously in rats. Five weeks later, the implants were withdrawn for a histomorphometric analysis of the volume densities of (i) bone, (ii) bone marrow, (iii) foreign-body giant cells and (iv) fibrous capsular tissue. Parameters (i) and (ii) were highest, whilst parameters (iii) and (iv) were lowest in association with DBB bearing a coating-incorporated depot of BMP-2. Hence, this mode of functionalization not only confers DBB with the property of osteoinductivity but also improves its biocompatibility--thus dually enhancing its clinical potential in the repair of bony defects.

Comparison of biolimus eluted from an erodible stent coating with bare metal stents in acute ST-elevation myocardial infarction (COMFORTABLE AMI trial): rationale and design

Compared with bare metal stents (BMS), early generation drug-eluting stents (DES) reduce the risk of revascularisation in patients with ST-elevation myocardial infarction (STEMI) at the expense of an increased risk of very late stent thrombosis (ST). Durable polymer coatings for controlled drug release have been identified as a potential trigger for these late adverse events and this has led to the development of newer generation DES with durable and biodegradable polymer surface coatings with improved biocompatibility. In a recent all-comers trial, biolimus-eluting stents with a biodegradable polymer surface coating were found to reduce the risk of very late ST by 80% compared with sirolimus-eluting stents with durable polymer, which also translated into a lower risk of cardiac death and myocardial infarction (MI) beyond one year.

Pulmonary surfactant coating of multi-walled carbon nanotubes (MWCNTs) influences their oxidative and pro-inflammatory potential in vitro

Background Increasing concern has been expressed regarding the potential adverse health effects that may be associated with human exposure to inhaled multi-walled carbon nanotubes (MWCNTs). Thus it is imperative that an understanding as to the underlying mechanisms and the identification of the key factors involved in adverse effects are gained. In the alveoli, MWCNTs first interact with the pulmonary surfactant. At this interface, proteins and lipids of the pulmonary surfactant bind to MWCNTs, affecting their surface characteristics. Aim of the present study was to investigate if the pre-coating of MWCNTs with pulmonary surfactant has an influence on potential adverse effects, upon both (i) human monocyte derived macrophages (MDM) monocultures, and (ii) a sophisticated in vitro model of the human epithelial airway barrier. Both in vitro systems were exposed to MWCNTs either pre-coated with a porcine pulmonary surfactant (Curosurf) or not. The effect of MWCNTs surface charge was also investigated in terms of amino (−NH2) and carboxyl (−COOH) surface modifications. Results Pre-coating of MWCNTs with Curosurf affects their oxidative potential by increasing the reactive oxygen species levels and decreasing intracellular glutathione depletion in MDM as well as decreases the release of Tumour necrosis factor alpha (TNF-α). In addition, an induction of apoptosis was observed after exposure to Curosurf pre-coated MWCNTs. In triple cell-co cultures the release of Interleukin-8 (IL-8) was increased after exposure to Curosurf pre-coated MWCNTs. Effects of the MWCNTs functionalizations were minor in both MDM and triple cell co-cultures. Conclusions The present study clearly indicates that the pre-coating of MWCNTs with pulmonary surfactant more than the functionalization of the tubes is a key factor in determining their ability to cause oxidative stress, cytokine/chemokine release and apoptosis. Thus the coating of nano-objects with pulmonary surfactant should be considered for future lung in vitro risk assessment studies. Keywords: Multi-walled carbon nanotubes (MWCNTs); Pulmonary surfactant (Curosurf); Macrophages; Epithelial cells; Dendritic cells; Triple cell co-culture; Pro-inflammatory and oxidative reactions

Effect of a plasmaelectrolytic coating on the strength retention of in vivo and in vitro degraded magnesium implants

The strength decrease in magnesium implants was studied in vitro and in vivo, with and without a protective plasmaelectrolytic coating. In vivo, degradation was examined by implanting rectangular plates on top of the nasal bone of miniature pigs. The presence of gas pockets in the soft tissue surrounding the implants was evaluated with intermediate X-rays and computed X-ray tomography scans before euthanasia. After 12 and 24weeks of in vivo degradation, the large rectangular plates were removed and mechanically tested in three-point bending. In vitro, identical plates were immersed in simulated body fluid for 4, 8 and 12weeks. In vitro and in vivo results showed that onset of gas release can be delayed by the plasmaelectrolytic coating. Mass loss and strength retention during in vivo degradation is about four times slower than during in vitro degradation for the chosen test conditions. Despite the slow degradation of the investigated WE43 alloy, the occurrence of gas pockets could not be completely avoided. Nevertheless, uniformity of degradation and reliable strength retention make this alloy a prime candidate for the use of magnesium in cranio-maxillofacial surgery.

Polymer stent coating for prevention of neointimal hyperplasia

AIMS: Restenosis has been the principal limitation of bare metal stents. Based upon the presumption that platelet and inflammatory cell recruitment initiate neointimal proliferation, we explored a novel polymer coating that reduces cell-stent interactions. The purpose of the present study was to investigate the effect of poly(L-lysine)-graft-poly(ethyleneglycol) (PLL-g-PEG) adsorbed to stent surfaces to reduce neointimal hyperplasia in the porcine restenosis model. METHODS AND RESULTS: Seven animals were instrumented each with 2 stainless steel stents (15 mm length, 2.5-3.5 mm diameter), randomly implanted in 1 major epicardial coronary artery. One stent was dip-coated with PLL-g-PEG, whereas the other stent served as the uncoated control stent. All animals were sacrificed after 6 weeks for histological examination. Neointimal hyperplasia was significantly less (-51%) in the PLL-g-PEG-coated stents (1.15 +/- 0.59 mm2) than in the uncoated control stents (2.33 +/- 1.01 mm2; p < 0.001). Conversely, lumen size was larger in the PLL-g-PEG-coated stents (2.91 +/- 1.17 mm2) than in the uncoated stents (2.04 +/- 0.64 mm2; p < 0.001). High magnification histomorphologic examination revealed no signs of inflammation or thrombus formation in either stent group. CONCLUSIONS: Polymeric steric stabilization of stents with PLL-g-PEG significantly reduces neointimal hyperplasia in the porcine restenosis model. Reduction of cell-stent interactions mediated by PLL-g-PEG appear to improve biocompatibility of stainless steel stents without evidence of adverse inflammatory or prothrombotic effects.

Improved neo-endothelialization of small diameter ePTFEgrafts with titanium coating

BACKGROUND: Patency of small synthetic bypass grafts is inferior compared to autologous grafts for revascularization procedures. Titanium coating of foreign surfaces has shown to decrease thrombogenicity, enhance biocompatibility and promote adhesion of endothelial cells. The aim of this study was to test the effect of titanium coating of small diameter ePTFE grafts on short term patency, neo-endothelialization and neointimal proliferation. METHODS: Bilateral carotid graft interposition was performed in 5 pigs with uncoated (n=5) and titanium-coated (n=5) ePTFE grafts (internal diameter=4 mm, length=5 cm), thus each pig served as its own control. At the end of the study (30 +/- 3 days), patency and stenosis severity was assessed by carotid angiography. Animals were sacrificed and grafts were excised for histology and scanning electron microscopy. Morphometry of histologic sections was carried out to determine neointimal proliferation and percentage of neo-endothelial coverage. RESULTS: Patency rate was 80% for uncoated and titanium-coated grafts. Quantitative angiography did not show any significant difference in lumen size between two groups. Morphometry revealed a significantly higher cellular coverage with CD31 positive endothelial cells for titanium-coated (84 +/- 19%) than uncoated grafts (48 +/- 26%, p<0.001). There was a non significant trend (p=0.112) towards increased neointimal proliferation in titanium-coated (94 +/- 61 micron2/micron) compared to uncoated grafts (60 +/- 57 micron2/micron). CONCLUSIONS: Patency rate in uncoated and titanium-coated ePTFE grafts is similar at one month. However, titanium coated grafts show a significant improvement in neo-endothelialization compared to uncoated grafts.

Effect on infection resistance of a local antiseptic and antibiotic coating on osteosynthesis implants: an in vitro and in vivo study

The purpose of this study was to acquire information about the effect of an antibacterial and biodegradable poly-L-lactide (PLLA) coated titanium plate osteosynthesis on local infection resistance. For our in vitro and in vivo experiments, we used six-hole AO DC minifragment titanium plates. The implants were coated with biodegradable, semiamorphous PLLA (coating about 30 microm thick). This acted as a carrier substance to which either antibiotics or antiseptics were added. The antibiotic we applied was a combination of Rifampicin and fusidic acid; the antiseptic was a combination of Octenidin and Irgasan. This produced the following groups: Group I: six-hole AO DC minifragment titanium plate without PLLA; Group II: six-hole AO DC minifragment titanium plate with PLLA without antibiotics/antiseptics; Group III: six-hole AO DC minifragment titanium plate with PLLA + 3% Rifampicin and 7% fusidic acid; Group IV: six-hole AO DC minifragment titanium plate with PLLA + 2% Octenidin and 8% Irgasan. In vitro, we investigated the degradation and the release of the PLLA coating over a period of 6 weeks, the bactericidal efficacy of antibiotics/antiseptics after their release from the coating and the bacterial adhesion of Staphylococcus aureus to the implants. In vivo, we compared the infection rates in white New Zealand rabbits after titanium plate osteosynthesis of the tibia with or without antibacterial coating after local percutaneous bacterial inoculations at different concentrations (2 x 10(5)-2 x 10(8)): The plate, the contaminated soft tissues and the underlying bone were removed under sterile conditions after 28 days and quantitatively evaluated for bacterial growth. A stepwise experimental design with an "up-and-down" dosage technique was used to adjust the bacterial challenge in the area of the ID50 (50% infection dose). Statistical evaluation of the differences between the infection rates of both groups was performed using the two-sided Fisher exact test (p < 0.05). Over a period of 6 weeks, a continuous degradation of the PLLA coating of 13%, on average, was seen in vitro in 0.9% NaCl solution. The elution tests on titanium implants with antibiotic or antiseptic coatings produced average release values of 60% of the incorporated antibiotic or 62% of the incorporated antiseptic within the first 60 min. This was followed by a much slower, but nevertheless continuous, release of the incorporated antibiotic and antiseptic over days and weeks. At the end of the test period of 42 days, 20% of the incorporated antibiotic and 15% of the incorporated antiseptic had not yet been released from the coating. The antibacterial effect of the antibiotic/antiseptic is not lost by integrating it into the PLLA coating. The overall infection rate in the in vivo investigation was 50%. For Groups I and II the infection rate was both 83% (10 of 12 animals). In Groups III and IV with antibacterial coating, the infection rate was both 17% (2 of 12 animals). The ID50 in the antibacterial coated Groups III and IV was recorded as 1 x 10(8) CFU, whereas the ID50 values in the Groups I and II without antibacterial coating were a hundred times lower at 1 x 10(6) CFU, respectively. The difference between the groups with and without antibacterial coating was statistically significant (p = 0.033). Using an antibacterial biodegradable PLLA coating on titanium plates, a significant reduction of infection rate in an in vitro and in vivo investigation could be demonstrated. For the first time, to our knowledge, we were able to show, under standardized and reproducible conditions, that an antiseptic coating leads to the same reduction in infection rate as an antibiotic coating. Taking the problem of antibiotic-induced bacterial resistance into consideration, we thus regard the antiseptic coating, which shows the same level of effectiveness, as advantageous.

Improved safety and reduction in stent thrombosis associated with biodegradable polymer-based biolimus-eluting stents versus durable polymer-based sirolimus-eluting stents in patients with coronary artery disease: final 5-year report of the LEADERS (Limus Eluted From A Durable Versus ERodable Stent Coating) randomized, noninferiority trial

OBJECTIVES This study sought to report the final 5 years follow-up of the landmark LEADERS (Limus Eluted From A Durable Versus ERodable Stent Coating) trial. BACKGROUND The LEADERS trial is the first randomized study to evaluate biodegradable polymer-based drug-eluting stents (DES) against durable polymer DES. METHODS The LEADERS trial was a 10-center, assessor-blind, noninferiority, "all-comers" trial (N = 1,707). All patients were centrally randomized to treatment with either biodegradable polymer biolimus-eluting stents (BES) (n = 857) or durable polymer sirolimus-eluting stents (SES) (n = 850). The primary endpoint was a composite of cardiac death, myocardial infarction (MI), or clinically indicated target vessel revascularization within 9 months. Secondary endpoints included extending the primary endpoint to 5 years and stent thrombosis (ST) (Academic Research Consortium definition). Analysis was by intention to treat. RESULTS At 5 years, the BES was noninferior to SES for the primary endpoint (186 [22.3%] vs. 216 [26.1%], rate ratio [RR]: 0.83 [95% confidence interval (CI): 0.68 to 1.02], p for noninferiority <0.0001, p for superiority = 0.069). The BES was associated with a significant reduction in the more comprehensive patient-orientated composite endpoint of all-cause death, any MI, and all-cause revascularization (297 [35.1%] vs. 339 [40.4%], RR: 0.84 [95% CI: 0.71 to 0.98], p for superiority = 0.023). A significant reduction in very late definite ST from 1 to 5 years was evident with the BES (n = 5 [0.7%] vs. n = 19 [2.5%], RR: 0.26 [95% CI: 0.10 to 0.68], p = 0.003), corresponding to a significant reduction in ST-associated clinical events (primary endpoint) over the same time period (n = 3 of 749 vs. n = 14 of 738, RR: 0.20 [95% CI: 0.06 to 0.71], p = 0.005). CONCLUSIONS The safety benefit of the biodegradable polymer BES, compared with the durable polymer SES, was related to a significant reduction in very late ST (>1 year) and associated composite clinical outcomes. (Limus Eluted From A Durable Versus ERodable Stent Coating [LEADERS] trial; NCT00389220).

Halitosis and tongue coating in patients with erosive gastroesophageal reflux disease versus nonerosive gastroesophageal reflux disease

OBJECTIVE The aim of this study was to investigate whether patients with diagnosed erosive gastroesophageal reflux disease (ERD) have an increased probability of halitosis and tongue coating compared to patients with nonerosive gastroesophageal reflux disease (NERD). MATERIALS AND METHODS Sixty-six patients (33 males and 33 females) were recruited for the study and received an upper gastrointestinal endoscopy. The presence of ERD (n = 31) and NERD (n = 35) was classified based on the Los Angeles classification for erosive changes in the esophagus. Additionally, the patients filled in a questionnaire regarding their subjective assessment of halitosis, and an organoleptic assessment of halitosis, a measurement of oral volatile sulfur compounds (VSC) with the Halimeter, and a tongue coating index were performed. ERD and NERD subjects were compared with regard to Halitosis-related clinical and anamnestic findings. RESULTS No statistically significant difference could be found between ERD and NERD patients regarding tongue coating index, organoleptic scores, and VSC values as well as self-perceived bad taste, tongue coating, and bad breath. CONCLUSIONS These data suggest that halitosis is not typically associated with erosive gastroesophageal reflux disease and the presence of esophageal mucosal damage (ERD patients). CLINICAL RELEVANCE The data of this investigation support the findings of interdisciplinary bad breath clinics that gastroesophageal reflux disease is not a leading cause for halitosis.