Shear bond strength of resin cements to human dentin

OBJECTIVES: The objectives of this in vitro study were (1) to assess the bond strength of the universal cement RelyX Unicem to dentin and to compare it with three conventional resin cements, (2) to test the influence of aging on their bonding capacity and (3) to test the influence of the operator on bonding quality by performing the same test in two different centers. METHODS: 160 third molars, divided into 80 for tests at the University of Zurich (Z) and 80 for tests at the University of Berne (B), were assigned to 2 x 8 subgroups of 10 teeth each. The specimens were prepared with the corresponding bonding agents and acrylic rods were luted either with RelyX Unicem (U), RelyX ARC (A), Multilink (M) or Panavia 21 (P). All specimens were stored in water for 24h (W) and half of the specimens were subjected to 1500 cycles of thermocycling (5 degrees C and 55 degrees C) (T). Bond strength was measured by means of a shear test. RESULTS: After water storage RelyX Unicem exhibited lowest bond strength (UWZ: 9.2+/-1.6 MPa, UWB: 9.9+/-1.2 MPa, AWZ: 15.3+/-6.0 MPa, AWB: 12.2+/-4.3 MPa, MWZ: 15.6+/-3.3 MPa, MWB: 12.4 MPa+/-2.4, PWZ: 13.4+/-2.9 MPa, PWB: 14.9+/-2.6 MPa). Thermocycling affected the bonding performance of all four cements. However, bond strength of RelyX Unicem was least influenced by thermocycling (UTZ: 9.4+/-2.9 MPa, UTB: 8.6+/-1.3 MPa, ATZ: 11.4+/-6.3 MPa, ATB: 13.3+/-3.7 MPa, MTZ: 15.4+/-3.1 MPa, MTB: 10.3+/-2.4 MPa, PTZ: 11.1+/-2.8 MPa, PTB: 11.3+/-2.8 MPa). SIGNIFICANCE: Although the bond strength of RelyX Unicem to dentin was lower in comparison to RelyX ARC, Multilink and Panavia 21, its bond strength was less sensitive to variations in handling and aging.

Light curing through glass ceramics: effect of curing mode on micromechanical properties of dual-curing resin cements

OBJECTIVES The aim of this study was to investigate micromechanical properties of five dual-curing resin cements after different curing modes including light curing through glass ceramic materials. MATERIALS AND METHODS Vickers hardness (VH) and indentation modulus (Y HU) of Panavia F2.0, RelyX Unicem 2 Automix, SpeedCEM, BisCem, and BeautiCem SA were measured after 1 week of storage (37 °C, 100 % humidity). The resin cements were tested following self-curing or light curing with the second-generation light-emitting diode (LED) curing unit Elipar FreeLight 2 in Standard Mode (1,545 mW/cm(2)) or with the third-generation LED curing unit VALO in High Power Mode (1,869 mW/cm(2)) or in XtraPower Mode (3,505 mW/cm(2)). Light curing was performed directly or through glass ceramic discs of 1.5 or 3 mm thickness of IPS Empress CAD or IPS e.max CAD. VH and Y HU were analysed with Kruskal-Wallis tests followed by pairwise Wilcoxon rank sum tests (α = 0.05). RESULTS RelyX Unicem 2 Automix resulted in the highest VH and Y HU followed by BeautiCem SA, BisCem, SpeedCEM, and finally Panavia F2.0. Self-curing of RelyX Unicem 2 Automix and SpeedCEM lowered VH and Y HU compared to light curing whereas self-curing of Panavia F2.0, BisCem, and BeautiCem SA led to similar or significantly higher VH and Y HU compared to light curing. Generally, direct light curing resulted in similar or lower VH and Y HU compared to light curing through 1.5-mm-thick ceramic discs. Light curing through 3-mm-thick discs of IPS e.max CAD generally reduced VH and Y HU for all resin cements except SpeedCEM, which was the least affected by light curing through ceramic discs. CONCLUSIONS The resin cements responded heterogeneously to changes in curing mode. The applied irradiances and light curing times adequately cured the resin cements even through 1.5-mm-thick ceramic discs. CLINICAL RELEVANCE When light curing resin cements through thick glass ceramic restorations, clinicians should consider to prolong the light curing times even with LED curing units providing high irradiances.

Effect of tin-chloride pretreatment on bond strength of two adhesive systems to dentin

OBJECTIVES: To determine the effect on resin composite-to-dentin bond strength of incorporation of an acidic tin-chloride pretreatment in two adhesive systems. MATERIALS AND METHODS: Human molars were ground to expose mid-coronal dentin. For microtensile bond strength (μTBS) testing, dentin was treated with Optibond FL or Clearfil SE according to one of six protocols (n = 22/group). Group 1: Phosphoric acid etching, Optibond FL Prime, Optibond FL Adhesive (manufacturer's instructions; control); Group 2: Tin-chloride pretreatment, Optibond FL Prime, Optibond FL Adhesive; Group 3: Phosphoric acid etching, tin-chloride pretreatment, Optibond FL Prime, Optibond FL Adhesive; Group 4: Clearfil SE Primer, Clearfil SE Bond (manufacturer's instructions; control); Group 5: Phosphoric acid etching, Clearfil SE Primer, Clearfil SE Bond; and Group 6: Tin-chloride pretreatment, Clearfil SE Primer, Clearfil SE Bond. The molars were then built up with resin composite (Clearfil Majesty Esthetic). After storage (1 week, 100  % humidity, 37 °C) the μTBS was measured and failure mode was determined. Additionally, pretreated dentin surfaces were evaluated using SEM and EDX. The μTBS results were analyzed statistically by a Welch Two Sample t-test and a Kruskal-Wallis test followed by exact Wilcoxon rank sum tests with Bonferroni-Holm adjustment for multiple testing (α = 0.05). RESULTS: When Optibond FL was used, partial or total replacement of phosphoric acid with tin-chloride decreased μTBS significantly. In contrast, when Clearfil SE was used, inclusion of a tin-chloride pretreatment in the adhesive procedure increased μTBS significantly. CONCLUSIONS: Tin-chloride pretreatment had a beneficial influence on the bond promoting capacity of the MDP-containing adhesive system Clearfil SE.

Cement-augmented anterior screw fixation of Type II odontoid fractures in elderly patients with osteoporosis

BACKGROUND CONTEXT: Closed reduction and internal fixation by an anterior approach is an established option for operative treatment of displaced Type II odontoid fractures. In elderly patients, however, inadequate screw purchase in osteoporotic bone can result in severe procedure-related complications. PURPOSE: To improve the stability of odontoid fracture screw fixation in the elderly using a new technique that includes injection of polymethylmethacrylat (PMMA) cement into the C2 body. STUDY DESIGN: Retrospective review of hospital and outpatient records as well as radiographs of elderly patients treated in a university hospital department of orthopedic surgery. PATIENT SAMPLE: Twenty-four elderly patients (8 males and 16 females; mean age, 81 years; range, 62-98 years) with Type II fractures of the dens. OUTCOME MEASURES: Complications, cement leakage (symptomatic/asymptomatic), operation time, loss of reduction, pseudarthrosis and revision surgery, patient complaints, return to normal activities, and signs of neurologic complications were all documented. METHODS: After closed reduction and anterior approach to the inferior border of C2, a guide wire is advanced to the tip of the odontoid under biplanar fluoroscopic control. Before the insertion of one cannulated, self-drilling, short thread screws, a 12 gauge Yamshidi cannula is inserted from anterior and 1 to 3 mL of high-viscosity PMMA cement is injected into the anteroinferior portion of the C2 body. During polymerization of the cement, the screws are further inserted using a lag-screw compression technique. The cervical spine then is immobilized with a soft collar for 8 weeks postoperatively. RESULTS: Anatomical reduction of the dens was achieved in all 24 patients. Mean operative time was 64 minutes (40-90 minutes). Early loss of reduction occurred in three patients, but revision surgery was indicated in only one patient 2 days after primary surgery. One patient died within the first eight postoperative weeks, one within 3 months after surgery. In five patients, asymptomatic cement leakage was observed (into the C1-C2 joint in three patients, into the fracture in two). Conventional radiologic follow-up at 2 and 6 months confirmed anatomical healing in 16 of the19 patients with complete follow-up. In two patients, the fractures healed in slight dorsal angulation; one patient developed a asymptomatic pseudarthrosis. All patients were able to resume their pretrauma level of activity. CONCLUSIONS: Cement augmentation of the screw in Type II odontoid fractures in elderly patients is technically feasible in a clinical setting with a low complication rate. This technique may improve screw purchase, especially in the osteoporotic C2 body.

Does tin pre-treatment enhance the bond strength of adhesive systems to enamel?

OBJECTIVES The study investigated the modification of composite-to-enamel bond strength by pre-treatment of enamel with a concentrated, acidic SnCl2-solution. METHODS Six groups of flat human enamel specimens (n=44 per group) were treated as follows: OB-H: H3PO4 etching, Optibond FL application (primer+adhesive; manufacturer's instructions); OB-S: SnCl2 pre-treatment, Optibond FL application (primer+adhesive); OB-HS: H3PO4 etching+SnCl2 pre-treatment, Optibond FL application (primer+adhesive); CF-N: Clearfil SE application (primer+bond; manufacturer's instructions); CF-H: H3PO4 etching, Clearfil SE application (primer+bond); CF-S: SnCl2 pre-treatment, Clearfil SE application (primer+bond). Enamel specimens were then built up with resin composite (Clearfil Majesty Esthetic) and stored (100% humidity, 37 °C, 1 week). μTBS-measurement and failure mode analysis of one-half of the specimens were performed immediately after storage, while the other half was analysed after a thermocycling procedure (8500 cycles; 5 °C and 55 °C; dwell time 30s). Additional specimens were prepared for SEM- and EDX-analysis. RESULTS Highest values were measured for OB-H before and after thermocycling, lowest values for CF-N. Compared to OB-H treatment, OB-S treatment reduced μTBS before/after thermocycling by 23%/28% and OB-HS treatment by 8%/24% (except for OB-SH before (n.s.), all p≤0.001 compared to OB-H). In the Clearfil SE treated groups pre-treatment increased μTBS significantly compared to CF-N (before/after: CF-H: +46%/+70%; CF-S: +51%/42%; all p≤0.001). CONCLUSION Pre-treatment with H3PO4 or SnCl2 markedly increased the μTBS of Clearfil SE to enamel. However, thermocycling partly reduced the gain in μTBS obtained by SnCl2 pre-treatment. CLINICAL SIGNIFICANCE The application of an acidic and highly concentrated SnCl2 solution is a good option to increase the μTBS between enamel and a resin composite mediated by an adhesive system containing the multifunctional monomer MDP.

Bonding of simplified adhesive systems to caries-affected dentin of primary teeth.

PURPOSE To evaluate the bonding of simplified adhesive systems to sound and caries-affected dentin of primary teeth with microtensile (µTBS) and nanoleakage (NL) tests. MATERIALS AND METHODS Occlusal cavities were prepared in 36 sound second primary molars. Half of the specimens were submitted to pH cycling to simulate caries-affected dentin. Teeth were randomly restored with one of three materials: the etch-and-rinse adhesive system Adper Single Bond 2 (SB), the two-step self-etching adhesive system Adper SE Plus (SE), and the one-step self-etching adhesive system Adper Easy One (EASY). After storage for 24 h, specimens with cross-sectional areas of 0.8 mm2 were prepared for microtensile testing (1 mm/min). One stick from each tooth was immersed in silver nitrate solution (24 h) and allowed to develop for 8 h in order to score the nano leakage with SEM. The fracture pattern was evaluated using a stereomicroscope (400X). The µTBS means were analyzed by two-way ANOVA and Tukey's post-hoc test. For NL, the Kruskal- Wallis and Mann-Whitney tests were used (α < 0.05). RESULTS SB (35.5 ± 3.5) showed the highest µTBS value to sound dentin, followed by EASY (26.3 ± 1.9) and SE (18.2 ± 6.5) (p < 0.05). No difference among materials was observed for caries-affected dentin (SB: 17.8 ± 4.2; SE: 13.9 ± 3.2; EASY: 14.4 ± 4.2, p > 0.05). For all groups, adhesive/mixed fracture prevailed. Caries affected dentin promoted silver nitrate uptake into the adhesive interface; however, with SE, the nano leakage was more pronounced than in the other adhesive systems, even in sound dentin. CONCLUSION Caries-affected dentin negatively influences the bond strength and nano leakage of the two-step etch-and-rinse and one-step self-etching adhesive systems tested in primary teeth.

Influence of increment thickness on microhardness and dentin bond strength of bulk fill resin composites

OBJECTIVES To investigate the influence of increment thickness on Vickers microhardness (HV) and shear bond strength (SBS) to dentin of a conventional and four bulk fill resin composites. METHODS HV and SBS were determined on specimens of the conventional resin composite Filtek Supreme XTE (XTE) and the bulk fill resin composites SDR (SDR), Filtek Bulk Fill (FBF), x-tra fil (XFIL), and Tetric EvoCeram Bulk Fill (TEBF) after 24h storage. HV was measured either as profiles at depths up to 6mm or at the bottom of 2mm/4mm/6mm thick resin composite specimens. SBS of 2mm/4mm/6mm thick resin composite increments was measured to dentin surfaces of extracted human molars treated with the adhesive system OptiBond FL, and the failure mode was stereomicroscopically determined at 40× magnification. HV profiles and failure modes were descriptively analysed whereas HV at the bottom of resin composite specimens and SBS were statistically analysed with nonparametric ANOVA followed by Wilcoxon rank sum tests (α=0.05). RESULTS HV profiles (medians at 2mm/4mm/6mm): XTE 105.6/88.8/38.3, SDR 34.0/35.5/36.9, FBF 36.4/38.7/37.1, XFIL 103.4/103.9/101.9, TEBF 63.5/59.7/51.9. HV at the bottom of resin composite specimens (medians at 2mm/4mm/6mm): XTE (p<0.0001) 105.5>85.5>31.1, SDR (p=0.10) 25.8=21.9=26.0, FBF (p=0.16) 26.6=25.3=28.9, XFIL (p=0.18) 110.5=107.2=101.9, TEBF (p<0.0001) 63.0>54.9>48.2. SBS (MPa, medians at 2mm/4mm/6mm): XTE (p<0.0001) 23.9>18.9=16.7, SDR (p=0.26) 24.6=22.7=23.4, FBF (p=0.11) 21.4=20.3=22.0, x-tra fil (p=0.55) 27.0=24.0=23.6, TEBF (p=0.11) 21.0=20.7=19.0. The predominant SBS failure mode was cohesive failure in dentin. SIGNIFICANCE At increasing increment thickness, HV and SBS decreased for the conventional resin composite but generally remained constant for the bulk fill resin composites.

Influence of polymers on microstructure and adhesive strength of cementitious tile adhesive mortars

The impact of polymer modification on the physical properties of cementitious mortars is investigated using a multimethod approach. Special emphasis is put on the identification and quantification of different polymer components within the cementitious matrix. With respect to thin-bed applications, particularly tile adhesives, the spatial distributions of latex, cellulose ether (CE), polyvinyl alcohol (PVA), and cement hydration products can be quantified. It is shown that capillary forces and evaporation induce water fluxes in the interconnected part of the pore system, which transport CE, PVA, and cement ions to the mortar interfaces. In contrast, the distribution of latex remains homogeneous. In combination with results from qualitative experiments, the quantitative findings allow reconstruction of the evolution from fresh to hardened mortar, including polymer film formation, cement hydration, and water migration. The resulting microstructure and the failure modes can be correlated with the final adhesive strength of the tile adhesive. The results demonstrate that skinning prior to tile inlaying can strongly reduce wetting properties of the fresh mortar and lower final adhesive strength.