Synthese und Strukturierung von funktionalisierten Oligothiophenen

AbstractIn this thesis t-BOC and methacrylate functionalisedoligothiophenes with 3 – 5 thiophene units where synthesizedby Stille coupling. The material was structured by methodslike stamping and photolithography.The polymerizability of the methacrylates was proved by thepolymerization in solution with AIBN and subsequent analysisby gel permeation chromatography and differential scanningcalorimetry. The conductivities of the doped polymer filmswere in the range published for oligothiophenes.The optical and electrochemical properties of the compoundswere measured and compared to known compounds.The cleavage of the t-BOC groups was followed bythermogravimetry and infrared spectroscopy. The cleavagetemperature can be lowered by up to 100 °C by the use ofphoto acid generators. The cleavage is complete after 2hours annealing.The methacrylates were structured by microinjection mouldingin capillaries (MIMIC), stamping with soft silicone moulds,filling of patterned substrates and preperation of an opalreplica. By MIMIC line patterns with 5- 50 µm line widthswere obtained. The stamping succeeded in structures with 500nm line width only, on which liquid crystals wereorientated. This shows the possible application asorientation layers in LED’s with polarized emission. Withsilica opal templates the three-dimensional structuring ofthe oligomers succeeded.ZusammenfassungIn dieser Arbeit wurden neue funktionalisierteOligothiophene hergestellt und unter Anwendung verschiedenerVerfahren wie Stempeltechniken oder Photolithographiestrukturiert. Dazu wurden Oligothiophene mit drei bis fünfThiopheneinheiten durch Stille-Kupplung synthetisiert. Alsfunktionelle Gruppen wurden t-BOC-Ester undMethacrylsäureester eingeführt.Die Polymerisierbarkeit der Methacrylate wurde durch diePolymerisation mit AIBN in Lösung und anschließendeGelpermeationschromatographie und Differentialkalorimetrienachgewiesen. Die Leitfähigkeiten der dotierten Polymerfilmelagen im Bereich der für Oligothiophene bekannten Werte.Die optischen und elektrochemischen Eigenschaften derVerbindungen wurden untersucht und mit den Eigenschaftenbekannter Verbindungen verglichen. Die Abspaltung der t-BOC-Gruppen wurde thermogravimetrischund infrarotspektroskopisch verfolgt. Es wurde gezeigt, daßdie Abspaltungstemperatur durch den Zusatz einesPhotosäuregenerators um bis zu 100°C gesenkt wird und dieAbspaltung nach zweistündigem Tempern vollständig ist.Die methacrylatfunktionalisierten Verbindungen wurdenstrukturiert durch Micro Injection Moulding in Capillaries(MIMIC), Prägen mit weichen Silikonstempeln, Füllen vonstrukturierten Substraten und die Herstellung einerOpalreplika. Durch die Strukturierung mit MIMIC wurdenLinienstrukturen mit Linienbreiten von 5-50 µm erhalten.Durch Prägen wurden Strukturen mit Linienbreiten von nur 500nm erreicht, auf diesen gelang die Orientierung vonFlüssigkristallen. Dies zeigt die mögliche Anwendung alsOrientierungsschichten in Leuchtdioden mit polarisierterEmission. Durch die Verwendung von Siliziumoxidopalen alsTemplate gelang die dreidimensionale Strukturierung derOligomere.

Functional silicones and silicone-containing block copolymers

Polysiloxanes can be synthesized and subsequently modified (i) by the attachment of small molecules that change the properties of the silicone in such a way that it becomes more hydrophilic, but under the premise that this does not go together with a loss of the silicone-specific features. This can be done by adding hydrophilic sidechains to a polysiloxane. Polyethers like poly(ethylene glycol) or hyperbranched polyether-polyols are suitable in this regard. In order to assure that the silicone properties retain, these side groups can be attached to only one part of the polysiloxane backbone, which results in a block copolymer that consists of a common polysiloxane and a second block of the modified structure. (ii) Polysiloxanes can be equipped with functional groups that are capable of initializing polymerization of a different monomer (macroinitiator approach). For example, hydroxyl groups are used to initiate the ring opening polymerization of cyclic esters, or ATRP macroinitiators can be synthesized to add a second block via controlled radical polymerization. Stimuli responsive polymers like poly(oligoethylene glycol methacrylate) (POEGMA) can be added via this route to create “smart” siloxane-containing block copolymers that respond to certain stimuli. rnAn important premise for all synthetic routes is to achieve the targeted structure in a process as simple as possible, because facile availability of the material is crucial with regard to industrial applicability of the invented products. rnConcerning characterization of the synthesized macromolecules, emphasize is put on their (temperature dependent) aggregation behavior, which can be investigated by several microscopic and scattering methods, their behavior at the interface between silicone oils and water and their thermal properties.rnrn

Mechanical properties and structure of gel systems

Understanding the origins of the mechanical properties and its correlation withrnthe microstructure of gel systems is of great scientific and industrial interest. Inrngeneral, colloidal gels can be classified into chemical and physical gels, accordingrnto the life time of the network bonds. The characteristic di↵erences in gelationrndynamics can be observed with rheological measurements.rnAs a model system, a mixture of sodium silicate and low concentration sulfuric acidrnwas used. Nano-sized silica particles grow and aggregate to a system-spanning gelrnnetwork. The influence of the finite solubility of silica at high pH on the gelationrnwas studied with classical and piezo rheometer. The storage modulus of therngel grew logarithmically with time with two distinct growth laws. A relaxationrnat low frequency was observed in the frequency dependent measurements. I attributernthese two behaviors as a sign of structural rearrangements due to the finiternsolubility of silica at high pH. The reaction equilibrium between formation andrndissolution of bonds leads to a finite life time of the bonds and behavior similar tornphysical gel. The frequency dependence was more pronounced for lower water concentrations,rnhigher temperatures and shorter reaction times. With two relaxationrnmodels, I deduced characteristic relaxation times from the experimental data. Besidesrnrheology, the evolution of silica gels at high pH on di↵erent length scales wasrnstudied by NMR and dynamic light scattering. The results revealed that the primaryrnparticles existed already in sodium silicate and aggregated after the mixingrnof reactants due to a chemical reaction. Throughout the aggregation process thernsystem was in its chemical reaction equilibrium. Applying large oscillatory shearrnstrain to the gel allowed for modifying the gel modulus. The e↵ect of shear andrnshear history on the rheological properties of the gel were investigated. The storagernmodulus of the final gel increased with increasing strain. This behavior can be explained with (i) shear-induced aggregate compaction and (ii) combination ofrnbreakage and new formation of bonds.rnIn comparison with the physical gel-like behavior of the silica gel at high pH, typicalrnchemical gel features were exhibited by other gels formed from various chemicalrnreactions. Influences of the chemical structure modification on the gelation wererninvestigated with the piezo-rheometer. The external stimuli can be applied to tunernthe mechanical properties of the gel systems.