Thin nanostructured crystalline TiO 2 films and their applications in solar cells

Research on thin nanostructured crystalline TiO2 films has attracted considerable interests because of their intriguing physical properties and potential applications in photovoltaics. Nanostructured TiO2 film plays an important role in the TiO2 based dye-sensitized solar cells because they act as a substrate for the adsorption of dye molecules and a matrix for the transportation of electrons as well. Thus they can influence the solar cell performance significantly. Consequently, the control of the morphology including the shape, size and size distribution of the TiO2 nanostructures is critical to tune and optimize the performance of the solar cells. To control the TiO2 morphology, a strategy using amphiphilic block copolymer as templating agent coupled with sol-gel chemistry has been applied. Especially, a good-poor solvent pair induced phase separation process has been developed to guide the microphase separation behavior of the block copolymers. The amphiphilic block copolymers used include polystyrene-block-poly (ethylene oxide) (PS-b-PEO), poly (methyl methacrylate)-block-poly (ethylene oxide) (PMMA-b-PEO), and poly (ethylene oxide)-block-polystyrene-block-poly (ethylene oxide) (PEO-b-PS-b-PEO). The block copolymer undergoes a good-poor-solvent pair induced phase separation in a mixed solution of 1, 4-dioxane or N, N’-dimethyl formamide (DMF), concentrated hydrochloric acid (HCl) and Titanium tetraisopropoxide (TTIP). Specifically, in the system of PS-b-PEO, a morphology phase diagram of the inorganic-copolymer composite films was mapped by adjusting the weight fractions among 1, 4-dioxane, HCl, and TTIP in solution. The amorphous TiO2 within the titania-block copolymer composite films was crystallized by calcination at temperatures above 400C, where the organic block copolymer was simultaneously burned away. This strategy is further extended to other amphiphilic block copolymers of PMMA-b-PEO and PEO-b-PS-b-PEO, where the morphology of TiO2 films can also be controlled. The local and long range structures of the titania films were investigated by the combination of imaging techniques (AFM, SEM) and x-ray scattering techniques (x-ray reflectivity and grazing incidence small-angle x-ray scattering). Based on the knowledge of the morphology control, the crystalline TiO2 nanostructured films with different morphologies were introduced into solid state dye-sensitized solar cells. It has been found that all of the morphologies help to improve the performance of the solar cells. Especially, clustered nanoparticles, worm-like structures, foam-like structures, large collapsed nanovesicles show more pronounced performance improvement than other morphologies such as nanowires, flakes, and nanogranulars.

Uptake mechanism, intracellular trafficking and endo-lysosomal pH monitoring of polystyrene nanoparticles

What is the intracellular fate of nanoparticles (NPs) taken up by the cells? This question has been investigated for polystyrene NPs of different sizes with a set of molecular biological and biophysical techniques.rnTwo sets of fluorescent NPs, cationic and non-ionic, were synthesized with three different polymerization techniques. Non-ionic particles (132 – 846 nm) were synthesized with dispersion polymerization in an ethanol/water solution. Cationic NPs with 120 nm were synthesized by miniemulsion polymerization Particles with 208, 267 and 603 nm were produced by seeding the 120 nm particle obtained by miniemulsion polymerization with drop-wise added monomer and polymerization of such. The colloidal characterization of all particles showed a comparable amount of the surface groups. In addition, particles were characterized with regard to their size, morphology, solid content, amount of incorporated fluorescent dye and zeta potential. The fluorescent intensities of all particles were measured by fluorescence spectroscopy for calibration in further cellular experiments. rnThe uptake of the NPs to HeLa cells after 1 – 24 h revealed a much higher uptake of cationic NPs in comparison to non-ionic NPs. If the same amount of NPs with different sizes is introduced to the cell, a different amount of particles is present in the cell medium, which complicates a comparison of the uptake. The same conclusion is valid for the particles’ overall surface area. Therefore, HeLa cells were incubated with the same concentration, amount and surface area of NPs. It was found that with the same concentration always the same polymer amount is taking up by cells. However, the amount of particles taken up decreases for the biggest. A correlation to the surface area could not be found. We conclude that particles are endocytosed by an excavator-shovel like mechanism, which does not distinguish between different sizes, but is only dependent on the volume that is taken up. For the decreased amount of large particles, an overload of this mechanism was assumed, which leads to a decrease in the uptake. rnThe participation of specific endocytotic processes has been determined by the use of pharmacological inhibitors, immunocytological staining and immunofluorescence. The uptake of NPs into the endo-lysosomal machinery is dominated by a caveolin-mediated endocytosis. Other pathways, which include macropinocytosis and a dynamin-dependent mechanism but exclude clathrin mediated endocytosis, also occur as competing processes. All particles can be found to some extent in early endosomes, but only bigger particles were proven to localize in late endosomes. No particles were found in lysosomes; at least not in lysosomes that are labeled with Lamp1 and cathepsin D. However, based on the character of the performed experiment, a localization of particles in lysosomes cannot be excluded.rnDuring their ripening process, vesicles undergo a gradual acidification from early over late endosomes to lysosomes. It is hypothesized that NPs in endo-lysosomal compartments experience the same change in pH value. To probe the environmental pH of NPs after endocytosis, the pH-sensitive dye SNARF-4F was grafted onto amino functionalized polystyrene NPs. The pH value is a ratio function of the two emission wavelengths of the protonated and deprotonated form of the dye and is hence independent of concentration changes. The particles were synthesized by the aforementioned miniemulsion polymerization with the addition of the amino functionalized copolymer AEMH. The immobilization of SNARF-4F was performed by an EDC-coupling reaction. The amount of physically adsorbed dye in comparison to covalently bonded dye was 15% as determined by precipitation of the NPs in methanol, which is a very good solvent for SNARF-4F. To determine influences of cellular proteins on the fluorescence properties, a intracellular calibration fit was established with platereader measurements and cLSM imaging by the cell-penetrable SNARF-4F AM ester. Ionophores equilibrated the extracellular and intracellular pH.rnSNARF-4F NPs were taken up well by HeLa cells and showed no toxic effects. The pH environment of SNARF-4F NPs has been qualitatively imaged as a movie over a time period up to 1 h in pseudo-colors by a self-written automated batch program. Quantification revealed an acidification process until pH value of 4.5 over 24 h, which is much slower than the transport of nutrients to lysosomes. NPs are present in early endosomes after min. 1 h, in late endosomes at approx. 8 h and end up in vesicles with a pH value typical for lysosomes after > 24 h. We therefore assume that NPs bear a unique endocytotic mechanism, at least with regards to the kinetic involvedrn