Synthesis and characterization of polymers containing oligothiophenes

In the present work a series of thiophene oligomers of three and six thiophene units were synthesized, starting from thiophene, and characterized. Polymers containing these electroative side groups were then prepared by two strategies. The oligomers were attached to existing polymer systems and were connected to a polymerizable unit leading to monomer containing the oligothiophenes as side groups. Subsequently the properties of the monomers and the polymers were investigated. A butylcellulose derivative carrying terthienyl side chains (BCTTE, 26) was synthesized starting from cellulose acetate and 5-(2-chloroethyl)-2,2':5',2'-terthiophene (4). The polymer had a degree of substitution (DS) of the butyl and terthienyl side chains of DSbutyl = 1.9 and DSterth = 0.35, respectively. It was successfully spread on a Langmuir-Blodgett (LB) trough and then transferred to several solid substrates. X-rays reflectometry showed an ordered architecture of the cellulose backbones. However, the terthiophene side groups were found as isotropically aligned by polarized UV-Vis spectroscopy. When used as anode material in the electropolymerization of 3-pentylthiophene (28), polythiophene was grafted onto the cellulose backbone through the terthienyl side groups. The polythiophene chains showed an average anisotropic alignment of 20 % along the LB dipping direction, calculated by means of polarized UV-Vis spectroscopy. A second butylcellulose derivative carrying sexithienyl side chains (BCST) was synthesized and investigated, starting from butylcellulose and 2-[b ', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2': 5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl p-toluensulfonate (7). The polymer showed formation of stable LB monolayers at the air-water interface, but its transfer onto solid substrates was not successful. A poly(p-phenylene-ethynylene) bearing sexithienyl side chains (BzAcST, 31) was prepared by reaction of the two monomers 2-[b ', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2': 5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl 2,5-diiodobenzoate (15) and 2-[b', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2':5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl 2,5-diethynylbenzoate (18). The polymer was obtained as insoluble product. Upon oxidation with FeCl3 (doping) of the polymer suspension, BzAcST showed an electrical conductivity of ó = 2.5 . 10 -6 S/cm, a typical value for semiconductors. The IR spectrum of the doped polymer presented the diagnostic bands of oxidized sexithiophene in good agreement with literature results. Along with the monomer and polymer synthesis, an a,a '-disubstituted sexithiophene, b ', b ''-dipentyl-5,5'''-bis-(2-hydroxyethyl)-2,2':5',2':5',2'':5'',2'':5'',2'''-sexithiophene (6a),was synthesized and characterized. The UV-Vis absorption of the chromophore wasinvestigated as a function of temperature and different solvents, showing a blue-shift of the absorption maximum with increasing temperature and a red-shift changing the solvent from hexane to ethanol to toluene. Monitoring the change of the UV-Vis spectrum upon electrochemical oxidation, the oxidized chromophore showed a new broad absorption band, red shifted with respect to the p -p* transition of the neutral state. Upon reduction, the new band disappeared and the UV-Vis spectrum of the chromophore was restored. Such oxidation-reduction cycles were totally reversible. This feature, together with the absorption maximum falling in the visible region, makes this chromophore a suitable compound for the development of an electrochemical sensor.Attempts to polymerize acrylic monomers carrying sexythienyl side chains both via radical polymerization, as in the case of 2-[b ', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2': 5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl acrylate (8), and anionic polymerization, as in the case of 2-{b ', b ''-dipentyl-5'''-[2-(tertbutyldimethylsiloxy)ethyl]-2,2':5',2':5',2'':5'',2'': 5'',2''' -sexithiophen-5-yl}-ethylacrylate (29), were not successful, probably due to the steric hindrance of the oligothiophene side group. However, due to the time consuming and therefore restricted availability of the monomers, a screening of the polymerization conditions towards the formation of polymeric material was not possible.

Synthese und Strukturierung von funktionalisierten Oligothiophenen

AbstractIn this thesis t-BOC and methacrylate functionalisedoligothiophenes with 3 – 5 thiophene units where synthesizedby Stille coupling. The material was structured by methodslike stamping and photolithography.The polymerizability of the methacrylates was proved by thepolymerization in solution with AIBN and subsequent analysisby gel permeation chromatography and differential scanningcalorimetry. The conductivities of the doped polymer filmswere in the range published for oligothiophenes.The optical and electrochemical properties of the compoundswere measured and compared to known compounds.The cleavage of the t-BOC groups was followed bythermogravimetry and infrared spectroscopy. The cleavagetemperature can be lowered by up to 100 °C by the use ofphoto acid generators. The cleavage is complete after 2hours annealing.The methacrylates were structured by microinjection mouldingin capillaries (MIMIC), stamping with soft silicone moulds,filling of patterned substrates and preperation of an opalreplica. By MIMIC line patterns with 5- 50 µm line widthswere obtained. The stamping succeeded in structures with 500nm line width only, on which liquid crystals wereorientated. This shows the possible application asorientation layers in LED’s with polarized emission. Withsilica opal templates the three-dimensional structuring ofthe oligomers succeeded.ZusammenfassungIn dieser Arbeit wurden neue funktionalisierteOligothiophene hergestellt und unter Anwendung verschiedenerVerfahren wie Stempeltechniken oder Photolithographiestrukturiert. Dazu wurden Oligothiophene mit drei bis fünfThiopheneinheiten durch Stille-Kupplung synthetisiert. Alsfunktionelle Gruppen wurden t-BOC-Ester undMethacrylsäureester eingeführt.Die Polymerisierbarkeit der Methacrylate wurde durch diePolymerisation mit AIBN in Lösung und anschließendeGelpermeationschromatographie und Differentialkalorimetrienachgewiesen. Die Leitfähigkeiten der dotierten Polymerfilmelagen im Bereich der für Oligothiophene bekannten Werte.Die optischen und elektrochemischen Eigenschaften derVerbindungen wurden untersucht und mit den Eigenschaftenbekannter Verbindungen verglichen. Die Abspaltung der t-BOC-Gruppen wurde thermogravimetrischund infrarotspektroskopisch verfolgt. Es wurde gezeigt, daßdie Abspaltungstemperatur durch den Zusatz einesPhotosäuregenerators um bis zu 100°C gesenkt wird und dieAbspaltung nach zweistündigem Tempern vollständig ist.Die methacrylatfunktionalisierten Verbindungen wurdenstrukturiert durch Micro Injection Moulding in Capillaries(MIMIC), Prägen mit weichen Silikonstempeln, Füllen vonstrukturierten Substraten und die Herstellung einerOpalreplika. Durch die Strukturierung mit MIMIC wurdenLinienstrukturen mit Linienbreiten von 5-50 µm erhalten.Durch Prägen wurden Strukturen mit Linienbreiten von nur 500nm erreicht, auf diesen gelang die Orientierung vonFlüssigkristallen. Dies zeigt die mögliche Anwendung alsOrientierungsschichten in Leuchtdioden mit polarisierterEmission. Durch die Verwendung von Siliziumoxidopalen alsTemplate gelang die dreidimensionale Strukturierung derOligomere.

Charge transport in organic photovoltaic cells

Die vorliegende Dissertation dient dazu, das Verständnis des Ladungstransportes in organischen Solarzellen zu vertiefen. Mit Hilfe von Computersimulationen wird die Bewegung von Ladungsträgern in organischen Materialien rekonstruiert, und zwar ausgehend von den quantenmechanischen Prozessen auf mikroskopischer Ebene bis hin zur makroskopischen Skala, wo Ladungsträgermobilitäten quantifizierbar werden. Auf Grundlage dieses skalenübergreifenden Ansatzes werden Beziehungen zwischen der chemischen Struktur organischer Moleküle und der makroskopischen Mobilität hergestellt (Struktur-Eigenschafts-Beziehungen), die zu der Optimierung photovoltaischer Wirkungsgrade beitragen. Das Simulationsmodell beinhaltet folgende drei Schlüsselkomponenten. Erstens eine Morphologie, d. h. ein atomistisch aufgelöstes Modell der molekularen Anordnung in dem untersuchten Material. Zweitens ein Hüpfmodell des Ladungstransportes, das Ladungswanderung als eine Abfolge von Ladungstransferreaktionen zwischen einzelnen Molekülen beschreibt. Drittens ein nichtadiabatisches Modell des Ladungstransfers, das Übergangsraten durch drei Parameter ausdrückt: Reorganisationsenergien, Lageenergien und Transferintegrale. Die Ladungstransport-Simulationen richten sich auf die Materialklasse der dicyanovinyl-substituierten Oligothiophene und umfassen Morphologien von Einkristallen, Dünnschichten sowie amorphen/smektischen Mesophasen. Ein allgemeiner Befund ist, dass die molekulare Architektur, bestehend aus einer Akzeptor-Donor-Akzeptor-Sequenz und einem flexiblen Oligomergerüst, eine erhebliche Variation molekularer Dipolmomente und damit der Lageenergien bewirkt. Diese energetische Unordnung ist ungewöhnlich hoch in den Kristallen und umso höher in den Mesophasen. Für die Einkristalle wird beobachtet, dass Kristallstrukturen mit ausgeprägter π-Stapelung und entsprechend großer Transferintegrale zu verhältnismäßig niedrigen Mobilitäten führen. Dieses Verhalten wird zurückgeführt auf die Ausbildung bevorzugter Transportrichtungen, die anfällig für energetische Störungen sind. Für die Dünnschichten bestätigt sich diese Argumentation und liefert ein mikroskopisches Verständnis für experimentelle Mobilitäten. In der Tat korrelieren die Simulationsergebnisse sowohl mit gemessenen Mobilitäten als auch mit photovoltaischen Wirkungsgraden. Für die amorphen/smektischen Systeme steigt die energetische Unordnung mit der Oligomerlänge, sie führt aber auch zu einer unerwarteten Mobilitätsabnahme in dem stärker geordneten smektischen Zustand. Als Ursache dafür erweist sich, dass die smektische Schichtung der räumlichen Korrelation der energetischen Unordnung entgegensteht.