Synthesis and characterization of metal-chalcogenide MQ 2-Nanoparticles (M = Mo, W, Zr; Q = S, O)

Here, we present the adaptation and optimization of (i) the solvothermal and (ii) the metal-organic chemical vapor deposition (MOCVD) approach as simple methods for the high-yield synthesis of MQ2 (M=Mo, W, Zr; Q = O, S) nanoparticles. Extensive characterization was carried out using X-ray diffraction (XRD), scanning and transmission electron micros¬copy (SEM/TEM) combined with energy dispersive X-ray analysis (EDXA), Raman spectroscopy, thermal analyses (DTA/TG), small angle X-ray scattering (SAXS) and BET measurements. After a general introduction to the state of the art, a simple route to nanostructured MoS2 based on the decomposition of the cluster-based precursor (NH4)2Mo3S13∙xH2O under solvothermal conditions (toluene, 653 K) is presented. Solvothermal decomposition results in nanostructured material that is distinct from the material obtained by decomposition of the same precursor in sealed quartz tubes at the same temperature. When carried out in the presence of the surfactant cetyltrimethyl¬ammonium bromide (CTAB), the decomposition product exhibits highly disordered MoS2 lamellae with high surface areas. The synthesis of WS2 onion-like nanoparticles by means of a single-step MOCVD process is discussed. Furthermore, the results of the successful transfer of the two-step MO¬CVD based synthesis of MoQ2 nanoparticles (Q = S, Se), comprising the formation of amorphous precursor particles and followed by the formation of fullerene-like particles in a subsequent annealing step to the W-S system, are presented. Based on a study of the temperature dependence of the reactions a set of conditions for the formation of onion-like structures in a one-step reaction could be derived. The MOCVD approach allows a selective synthesis of open and filled fullerene-like chalcogenide nanoparticles. An in situ heating stage transmission electron microscopy (TEM) study was employed to comparatively investigate the growth mechanism of MoS2 and WS2 nanoparticles obtained from MOCVD upon annealing. Round, mainly amorphous particles in the pristine sample trans¬form to hollow onion-like particles upon annealing. A significant difference between both compounds could be demonstrated in their crystallization conduct. Finally, the results of the in situ hea¬ting experiments are compared to those obtained from an ex situ annealing process under Ar. Eventually, a low temperature synthesis of monodisperse ZrO2 nanoparticles with diameters of ~ 8 nm is introduced. Whereas the solvent could be omitted, the synthesis in an autoclave is crucial for gaining nano-sized (n) ZrO2 by thermal decomposition of Zr(C2O4)2. The n-ZrO2 particles exhibits high specific surface areas (up to 385 m2/g) which make them promising candidates as catalysts and catalyst supports. Co-existence of m- and t-ZrO2 nano-particles of 6-9 nm in diameter, i.e. above the critical particle size of 6 nm, demonstrates that the particle size is not the only factor for stabilization of the t-ZrO2 modification at room temperature. In conclusion, synthesis within an autoclave (with and without solvent) and the MOCVD process could be successfully adapted to the synthesis of MoS2, WS2 and ZrO2 nanoparticles. A comparative in situ heating stage TEM study elucidated the growth mechanism of MoS2 and WS2 fullerene-like particles. As the general processes are similar, a transfer of this synthesis approach to other layered transition metal chalcogenide systems is to be expected. Application of the obtained nanomaterials as lubricants (MoS2, WS2) or as dental filling materials (ZrO2) is currently under investigation.

Multifunctional water-soluble phosphorus dendrimers

Dendrimers are polymeric macromolecules with a regularly branched structure and are synthesised in an iterative fashion. Due to their monodispersity, well-defined shape and extremely high functionality, dendrimers are ideal nano-sized objects for functional and biocompatible surface coatings, biosensing and biomedicine. This dissertation describes the synthesis of ten novel water-soluble phosphorus containing dendrimers and their application in different biological and biomimetic systems. The dendrimers can be divided into two classes; the first type contains either a ferrocene at the core or 24 ferrocenes in the branches. They showed reversible reduction-oxidation behaviour and might be applied in electronic multilayered architectures. Dendrimers of the second class carry a dithiolane functionalised core that can strongly bind to noble metals, like gold substrates. Although such dendrimer coated substrates were unable to tether defect-free lipid bilayer membranes, the coatings were successfully applied for culturing Human Osteoblast cells. The cell adhesion to a coating of polycationic dendrimers was so strong that cell division could not take place, specifically evoking apoptosis. The polyanionic dendrimers, however, promoted excellent cell adhesion and proliferation. Therefore, the practical application of such macromolecular architectures can be envisioned, such as in dendrimer coatings for tissue engineering and or medical implants.

Photo-induced reversible assembly of colloidal polymer nanoparticles

Polymer nanoparticles functionalized on the surface with photo-responsive labels were synthesized. In a first synthetic step, polystyrene was copolymerized with the cross-linker divinylbenzene and poly(ethylene glycol) acrylate in a miniemulsion, to produce nano-sized spheres (~ 60 nm radius) with terminal hydroxyl groups, which were functionalized in a subsequent synthetic step with photo-responsive labels. For this purpose, two photo-active molecular structures were separately used: anthracene, which is well known to form covalently bonded dimers upon photo-excitation; and pyrene, which only forms short lived excited state dimers (excimers). Acid derivatives of these labels (9-anthracene carboxylic acid and 1-pyrene butyric acid) were bonded to the hydroxyl terminal groups of the nanoparticles through an esterification reaction, via the intermediate formation of the corresponding acid chloride.rnThe obtained labeled nanoparticles appeared to be highly hydrophobic structures. They formed lyophobic suspensions in water, which after analysis by dynamic light scattering (DLS) and ultramicroscopic particle tracking, appeared to equilibrate as a collection of singly dispersed nanoparticles, together with a few nanoparticle aggregates. The relative amount of aggregates decreased with increasing amounts of the surfactant sodium dodecyl sulfate (SDS), thus confirming that aggregation is an equilibrated state resulting from lyophobicity. The formation of such aggregates was corroborated using scanning electron microscopy (SEM). The photo-irradiation of the lyophobic aqueous suspensions of anthracene labeled nanoparticles (An-NP) resulted in the formation of higher aggregates, as evidenced by DLS and ultramicroscopy. The obtained state of aggregation could be reverted by sonication. The possibility to re-aggregate the system in subsequent photo-excitation and sonication cycles was established. Likewise, the photo-irradiation of lyophobic aqueous suspensions of pyrene-labeled nanoparticles (Py-NP) resulted in the formation of higher aggregates, as evidenced by DLS and ultramicroscopy. These appeared to remain aggregated due to hydrophobic interactions. This system could also be re-dispersed by sonication and re-aggregated in subsequent cycles of photo-excitation and sonication.

The role of dendritic cells (DC) in Friend retrovirus-induced immunosuppression and immunotherapeutic applications of functionalized nanoparticles

Friend murine leukemia Virus (FV) infection of immunocompetent mice is a well- established model to acquire further knowledge about viral immune suppression mechanisms, with the aim to develop therapeutics against retrovirus-induced diseases. Interestingly, BALB/c mice are infected by low doses of FV and die from FV-induced erythroleukemia, while C57/BL6 mice are infected by FV only at high viral dose, and remain persistently infected for their whole life. Due to the central role of dendritic cells (DC) in the induction of anti-viral responses, we asked for their functional role in the genotype-dependent sensitivity towards FV infection. In my PhD study I showed that bone marrow (BM)-derived DC differentiated from FV-infected BM cells obtained from FV-inoculated BALB/c (FV susceptible) and C57BL/6 (FV resistant) mice showed an increased endocytotic activity and lowered expression of MHCII and of costimulatory receptors as compared with non-infected control BMDC. FV-infected BMDC from either mouse strain were partially resistant towards stimulation-induced upregulation of MHCII and costimulators, and accordingly were poor T cell stimulators in vitro and in vivo. In addition, FV-infected BMDC displayed an altered expression profile of proinflammator cytokines and favoured Th2 polarization. Ongoing work is focussed on elucidating the functional role of proteins identified as differentially expressed in FV-infected DC in a genotype-dependent manner, which therefore may contribute to the differential course of FV infection in vivo in BALB/c versus C57BL/6 mice. So far, more than 300 proteins have been identified which are differently regulated in FV-infected vs. uninfected DC from both mouse strains. One of these proteins, S100A9, was strongly upregulated specifically in BMDC derived from FV-infected C57BL/6 BM cells. S100A9-/- mice were more sensitive towards inoculation with FV than corresponding wild type (WT) mice (both C57BL/6 background), which suggests a decisive role of this factor for anti-viral defense. In addition, FV-infected S100A9-/- BMDC showed lower motility than WT DC. The future work is aimed to further elucidate the functional importance of S100A9 for DC functions. To exploit the potential of DC for immunotherapeutic applications, in another project of this PhD study the usability of different types of functionalized nanoparticles

Mechanical properties and structure of gel systems

Understanding the origins of the mechanical properties and its correlation withrnthe microstructure of gel systems is of great scientific and industrial interest. Inrngeneral, colloidal gels can be classified into chemical and physical gels, accordingrnto the life time of the network bonds. The characteristic di↵erences in gelationrndynamics can be observed with rheological measurements.rnAs a model system, a mixture of sodium silicate and low concentration sulfuric acidrnwas used. Nano-sized silica particles grow and aggregate to a system-spanning gelrnnetwork. The influence of the finite solubility of silica at high pH on the gelationrnwas studied with classical and piezo rheometer. The storage modulus of therngel grew logarithmically with time with two distinct growth laws. A relaxationrnat low frequency was observed in the frequency dependent measurements. I attributernthese two behaviors as a sign of structural rearrangements due to the finiternsolubility of silica at high pH. The reaction equilibrium between formation andrndissolution of bonds leads to a finite life time of the bonds and behavior similar tornphysical gel. The frequency dependence was more pronounced for lower water concentrations,rnhigher temperatures and shorter reaction times. With two relaxationrnmodels, I deduced characteristic relaxation times from the experimental data. Besidesrnrheology, the evolution of silica gels at high pH on di↵erent length scales wasrnstudied by NMR and dynamic light scattering. The results revealed that the primaryrnparticles existed already in sodium silicate and aggregated after the mixingrnof reactants due to a chemical reaction. Throughout the aggregation process thernsystem was in its chemical reaction equilibrium. Applying large oscillatory shearrnstrain to the gel allowed for modifying the gel modulus. The e↵ect of shear andrnshear history on the rheological properties of the gel were investigated. The storagernmodulus of the final gel increased with increasing strain. This behavior can be explained with (i) shear-induced aggregate compaction and (ii) combination ofrnbreakage and new formation of bonds.rnIn comparison with the physical gel-like behavior of the silica gel at high pH, typicalrnchemical gel features were exhibited by other gels formed from various chemicalrnreactions. Influences of the chemical structure modification on the gelation wererninvestigated with the piezo-rheometer. The external stimuli can be applied to tunernthe mechanical properties of the gel systems.