Electronic transport in the heavy fermion superconductors UPd 2 Al 3 and UNi 2 Al 3

This work addresses the electronical properties of the superconductors UPd2Al3 and UNi2Al3 on the basis of thin film experiments. These isotructural compounds are ideal candiates to study the interplay of magnetism and superconductivity due to the differences of their magnetically ordered states, as well as the experimental evidence for a magnetic pairing mechanism in UPd2Al3. Epitaxial thin film samples of UPd2Al3 and UNi2Al3 were prepared using UHV Molecular Beam Epitaxy (MBE). For UPd2Al3, the change of the growth direction from the intrinsic (001) to epitaxial (100) was predicted and sucessfully demonstrated using LaAlO3 substrates cut in (110) direction. With optimized deposition process parameters for UPd2Al3 (100) on LaAlO3 (110) superconducting samples with critical temperatures up to Tc = 1.75K were obtained. UPd2Al3-AlOx-Ag mesa junctions with superconducting base electrode were prepared and shown to be in the tunneling regime. However, no signatures of a superconducting density of states were observed in the tunneling spectra. The resistive superconducting transition was probed for a possible dependence on the current direction. In contrast to UNi2Al3, the existence of such feature was excluded in UPd2Al3 (100) thin films. The second focus of this work is the dependence of the resisitive transition in UNi2Al3 (100) thin films on the current direction. The experimental fact that the resisitive transition occurs at slightly higher temperatures for I║a than for I║c can be explained within a model of two weakly coupled superconducting bands. Evidence is presented for the key assumption of the two-band model, namely that transport in and out of the ab-plane is generated on different, weakly coupled parts of the Fermi surface. Main indications are the angle dependence of the superconducting transition and the dependence of the upper critical field Bc2 on current and field orientation. Additionally, several possible alternative explanations for the directional splitting of the transition are excluded in this work. An origin due to scattering on crystal defects or impurities is ruled out, likewise a relation to ohmic heating or vortex dynamics. The shift of the transition temperature as function of the current density was found to behave as predicted by the Ginzburg-Landau theory for critical current depairing, which plays a significant role in the two-band model. In conclusion, the directional splitting of the resisitive transition has to be regarded an intrinsic and unique property of UNi2Al3 up to now. Therefore, UNi2Al3 is proposed as a role model for weakly coupled multiband superconductivity. Magnetoresistance in the normalconducting state was measured for UPd2Al3 and UNi2Al3. For UNi2Al3, a negative contribution was observed close to the antiferromagnetic ordering temperature TN only for I║a, which can be associated to reduced spin-disorder scattering. In agreement with previous results it is concluded that the magnetic moments have to be attributed to the same part of the Fermi surface which generates transport in the ab-plane.

Electronic structure and physical properties of Heusler compounds for thermoelectric and spintronic applications

This thesis focuses on synthesis as well as investigations of the electronic structure and properties of Heusler compounds for spintronic and thermoelectric applications.rnThe first part reports on the electronic and crystal structure as well as the mechanical, magnetic, and transport properties of the polycrystalline Heusler compound Co2MnGe. The crystalline structure was examined in detail by extended X-ray absorption fine structure spectroscopy and anomalous X-ray diffraction. The low-temperature magnetic moment agrees well with the Slater-Pauling rule and indicates a half-metallic ferromagnetic state of the compound, as is predicted by ab-initio calculations. Transport measurements and hard X-ray photoelectron spectroscopy (HAXPES) were performed to explain the electronic structure of the compound.rnA major part of the thesis deals with a systematical investigation of Heusler compounds for thermoelectric applications. Few studies have been reported on thermoelectric properties of p-type Heusler compounds. Therefore, this thesis focuses on the search for new p-type Heusler compounds with high thermoelectric efficiency. The substitutional series NiTi1−xMxSn and CoTi1−xMxSb (where M = Sc, V and 0 ≤ x ≤ 0.2) were synthesized and investigated theoretically and experimentally with respect to electronic structure and transport properties. The results show the possibility to create n-type and p-type thermoelectrics within one Heusler compound. The pure compounds showed n-type behavior, while under Sc substitution the system switched to p-type behavior. A maximum Seebeck coefficient of +230 μV/K (at 350 K) was obtained for NiTi0.26Sc0.04Zr0.35Hf0.35Sn, which is one of the highest values for p-type thermoelectric compounds based on Heusler alloys up to now. HAXPES valence band measurement show massive in gap states for the parent compounds NiTiSn, CoTiSb and NiTi0.3Zr0.35Hf0.35Sn. This proves that the electronic states close to the Fermi energy play a key role for the behavior of the transport properties. Furthermore, the electronic structure of the gapless Heusler compounds PtYSb, PtLaBi and PtLuSb were investigated by bulk sensitive HAXPES. The linear behavior of the spectra close to εF proves the bulk origin of Dirac-cone type density of states. Furthermore, a systematic study on the optical and transport properties of PtYSb is presented. The compound exhibits promising thermoelectric properties with a high figure of merit (ZT = 0.2) and a Hall mobility μh of 300 cm2/Vs at 350 K.rnThe last part of this thesis describes the linear dichroism in angular-resolved photoemission from the valence band of NiTi0.9Sc0.1Sn and NiMnSb. High resolution photoelectron spectroscopy was performed with an excitation energy of hν = 7.938 keV. The linear polarization of the photons was changed using an in-vacuum diamond phase retarder. Noticeable linear dichroism is found in the valence bands and this allows for a symmetry analysis of the contributing states. The differences in the spectra are found to be caused by symmetry dependent angular asymmetry parameters, and these occur even in polycrystalline samples without preferential crystallographic orientation.rnIn summary, Heusler compounds with 1:1:1 and 2:1:1 stoichiometry were synthesized and examined by chemical and physical methods. Overall, this thesis shows that the combination of first-principle calculations, transport measurements and high resolution high energy photoelectron spectroscopy analysis is a very powerful tool for the design and development of new materials for a wide range of applications from spintronic applications to thermoelectric applications.rn