Synthesis and surface modification of semiconductor nanocrystals

The last decade has witnessed an exponential growth of activities in the field of nanoscience and nanotechnology worldwide, driven both by the excitement of understanding new science and by the potential hope for applications and economic impacts. The largest activity in this field up to date has been in the synthesis and characterization of new materials consisting of particles with dimensions in the order of a few nanometers, so-called nanocrystalline materials. [1-8] Semiconductor nanomaterials such as III/V or II/VI compound semiconductors exhibit strong quantum confinement behavior in the size range from 1 to 10 nm. Therefore, preparation of high quality semiconductor nanocrystals has been a challenge for synthetic chemists, leading to the recent rapid progress in delivering a wide variety of semiconducting nanomaterials. Semiconductor nanocrystals, also called quantum dots, possess physical properties distinctly different from those of the bulk material. Typically, in the size range from 1 to 10 nm, when the particle size is changed, the band gap between the valence and the conduction band will change, too. In a simple approximation a particle in a box model has been used to describe the phenomenon[9]: at nanoscale dimensions the degenerate energy states of a semiconductor separate into discrete states and the system behaves like one big molecule. The size-dependent transformation of the energy levels of the particles is called “quantum size-effect”. Quantum confinement of both the electron and hole in all three dimensions leads to an increase in the effective bandgap of the material with decreasing crystallite size. Consequently, both the optical absorption and emission of semiconductor nanaocrystals shift to the blue (higher energies) as the size of the particles gets smaller. This color tuning is well documented for CdSe nanocrystals whose absorption and emission covers almost the whole visible spectral range. As particle sizes become smaller the ratio of surface atoms to those in the interior increases, which has a strong impact on particle properties, too. Prominent examples are the low melting point [8] and size/shape dependent pressure resistance [10] of semiconductor nanocrystals. Given the size dependence of particle properties, chemists and material scientists now have the unique opportunity to change the electronic and chemical properties of a material by simply controlling the particle size. In particular, CdSe nanocrystals have been widely investigated. Mainly due to their size-dependent optoelectronic properties [11, 12] and flexible chemical processibility [13], they have played a distinguished role for a number of seminal studies [11, 12, 14, 15]. Potential technical applications have been discussed, too. [8, 16-27] Improvement of the optoelectronic properties of semiconductor nanocrystals is still a prominent research topic. One of the most important approaches is fabricating composite type-I core-shell structures which exhibit improved properties, making them attractive from both a fundamental and a practical point of view. Overcoating of nanocrystallites with higher band gap inorganic materials has been shown to increase the photoluminescence quantum yields by eliminating surface nonradiative recombination sites. [28] Particles passivated with inorganic shells are more robust than nanocrystals covered by organic ligands only and have greater tolerance to processing conditions necessary for incorporation into solid state structures or for other applications. Some examples of core-shell nanocrystals reported earlier include CdS on CdSe [29], CdSe on CdS, [30], ZnS on CdS, [31] ZnS on CdSe[28, 32], ZnSe on CdSe [33] and CdS/HgS/CdS [34]. The characterization and preparation of a new core-shell structure, CdSe nanocrystals overcoated by different shells (CdS, ZnS), is presented in chapter 4. Type-I core-shell structures as mentioned above greatly improve the photoluminescence quantum yield and chemical and photochemical stability of nanocrystals. The emission wavelengths of type-I core/shell nanocrystals typically only shows a small red-shift when compared to the plain core nanocrystals. [30, 31, 35] In contrast to type-I core-shell nanocrystals, only few studies have been conducted on colloidal type-II core/shell structures [36-38] which are characterized by a staggered alignment of conduction and valence bands giving rise to a broad tunability of absorption and emission wavelengths, as was shown for CdTe/CdSe core-shell nanocrystals. [36] The emission of type-II core/shell nanocrystals mainly originates from the radiative recombination of electron-hole pairs across the core-shell interface leading to a long photoluminescence lifetime. Type-II core/shell nanocrystals are promising with respect to photoconduction or photovoltaic applications as has been discussed in the literature.[39] Novel type-II core-shell structures with ZnTe cores are reported in chapter 5. The recent progress in the shape control of semiconductor nanocrystals opens new fields of applications. For instance, rod shaped CdSe nanocrystals can enhance the photo-electro conversion efficiency of photovoltaic cells, [40, 41] and also allow for polarized emission in light emitting diodes. [42, 43] Shape control of anisotropic nanocrystals can be achieved by the use of surfactants, [44, 45] regular or inverse micelles as regulating agents, [46, 47] electrochemical processes, [48] template-assisted [49, 50] and solution-liquid-solution (SLS) growth mechnism. [51-53] Recently, formation of various CdSe nanocrystal shapes has been reported by the groups of Alivisatos [54] and Peng, [55] respectively. Furthermore, it has been reported by the group of Prasad [56] that noble metal nanoparticles can induce anisotropic growth of CdSe nanocrystals at lower temperatures than typically used in other methods for preparing anisotropic CdSe structures. Although several approaches for anisotropic crystal growth have been reported by now, developing new synthetic methods for the shape control of colloidal semiconductor nanocrystals remains an important goal. Accordingly, we have attempted to utilize a crystal phase control approach for the controllable synthesis of colloidal ZnE/CdSe (E = S, Se, Te) heterostructures in a variety of morphologies. The complex heterostructures obtained are presented in chapter 6. The unique optical properties of nanocrystals make them appealing as in vivo and in vitro fluorophores in a variety of biological and chemical investigations, in which traditional fluorescence labels based on organic molecules fall short of providing long-term stability and simultaneous detection of multiple emission colours [References]. The ability to prepare water soluble nanocrystals with high stability and quantum yield has led to promising applications in cellular labeling, [57, 58] deep-tissue imaging, [59, 60] and assay labeling [61, 62]. Furthermore, appropriately solubilized nanocrystals have been used as donors in fluorescence resonance energy transfer (FRET) couples. [63-65] Despite recent progress, much work still needs to be done to achieve reproducible and robust surface functionalization and develop flexible (bio-) conjugation techniques. Based on multi-shell CdSe nanocrystals, several new solubilization and ligand exchange protocols have been developed which are presented in chapter 7. The organization of this thesis is as follows: A short overview describing synthesis and properties of CdSe nanocrystals is given in chapter 2. Chapter 3 is the experimental part providing some background information about the optical and analytical methods used in this thesis. The following chapters report the results of this work: synthesis and characterization of type-I multi-shell and type-II core/shell nanocrystals are described in chapter 4 and chapter 5, respectively. In chapter 6, a high–yield synthesis of various CdSe architectures by crystal phase control is reported. Experiments about surface modification of nanocrystals are described in chapter 7. At last, a short summary of the results is given in chapter 8.

Unraveling efficiency-limiting processes in organic solar cells by ultrafast spectroscopy - impact of chemical structure and morphology on photophysics and efficiency

Diese Arbeit widmet sich der Untersuchung der photophysikalischen Prozesse, die in Mischungen von Elektronendonoren mit Elektronenakzeptoren zur Anwendung in organischen Solarzellen auftreten. Als Elektronendonoren werden das Copolymer PBDTTT-C, das aus Benzodithiophen- und Thienothiophene-Einheiten besteht, und das kleine Molekül p-DTS(FBTTh2)2, welches Silizium-überbrücktes Dithiophen, sowie fluoriertes Benzothiadiazol und Dithiophen beinhaltet, verwendet. Als Elektronenakzeptor finden ein planares 3,4:9,10-Perylentetracarbonsäurediimid-(PDI)-Derivat und verschiedene Fullerenderivate Anwendung. PDI-Derivate gelten als vielversprechende Alternativen zu Fullerenen aufgrund der durch chemische Synthese abstimmbaren strukturellen, optischen und elektronischen Eigenschaften. Das gewichtigste Argument für PDI-Derivate ist deren Absorption im sichtbaren Bereich des Sonnenspektrums was den Photostrom verbessern kann. Fulleren-basierte Mischungen übertreffen jedoch für gewöhnlich die Effizienz von Donor-PDI-Mischungen.rnUm den Nachteil der PDI-basierten Mischungen im Vergleich zu den entsprechenden Fulleren-basierten Mischungen zu identifizieren, werden die verschiedenen Donor-Akzeptor-Kombinationen auf ihre optischen, elektronischen und strukturellen Eigenschaften untersucht. Zeitaufgelöste Spektroskopie, vor allem transiente Absorptionsspektroskopie (TA), wird zur Analyse der Ladungsgeneration angewendet und der Vergleich der Donor-PDI Mischfilme mit den Donor-Fulleren Mischfilmen zeigt, dass die Bildung von Ladungstransferzuständen einen der Hauptverlustkanäle darstellt.rnWeiterhin werden Mischungen aus PBDTTT-C und [6,6]-Phenyl-C61-buttersäuremethylesther (PC61BM) mittels TA-Spektroskopie auf einer Zeitskala von ps bis µs untersucht und es kann gezeigt werden, dass der Triplettzustand des Polymers über die nicht-geminale Rekombination freier Ladungen auf einer sub-ns Zeitskala bevölkert wird. Hochentwickelte Methoden zur Datenanalyse, wie multivariate curve resolution (MCR), werden angewendet um überlagernde Datensignale zu trennen. Zusätzlich kann die Regeneration von Ladungsträgern durch Triplett-Triplett-Annihilation auf einer ns-µs Zeitskala gezeigt werden. Darüber hinaus wird der Einfluss des Lösungsmitteladditivs 1,8-Diiodooctan (DIO) auf die Leistungsfähigkeit von p-DTS(FBTTh2)2:PDI Solarzellen untersucht. Die Erkenntnisse von morphologischen und photophysikalischen Experimenten werden kombiniert, um die strukturellen Eigenschaften und die Photophysik mit den relevanten Kenngrößen des Bauteils in Verbindung zu setzen. Zeitaufgelöste Photolumineszenzmessungen (time-resolved photoluminescence, TRPL) zeigen, dass der Einsatz von DIO zu einer geringeren Reduzierung der Photolumineszenz führt, was auf eine größere Phasentrennung zurückgeführt werden kann. Außerdem kann mittels TA Spektroskopie gezeigt werden, dass die Verwendung von DIO zu einer verbesserten Kristallinität der aktiven Schicht führt und die Generation freier Ladungen fördert. Zur genauen Analyse des Signalzerfalls wird ein Modell angewendet, das den gleichzeitigen Zerfall gebundener CT-Zustände und freier Ladungen berücksichtigt und optimierte Donor-Akzeptor-Mischungen zeigen einen größeren Anteil an nicht-geminaler Rekombination freier Ladungsträger.rnIn einer weiteren Fallstudie wird der Einfluss des Fullerenderivats, namentlich IC60BA und PC71BM, auf die Leistungsfähigkeit und Photophysik der Solarzellen untersucht. Eine Kombination aus einer Untersuchung der Struktur des Dünnfilms sowie zeitaufgelöster Spektroskopie ergibt, dass Mischungen, die ICBA als Elektronenakzeptor verwenden, eine schlechtere Trennung von Ladungstransferzuständen zeigen und unter einer stärkeren geminalen Rekombination im Vergleich zu PCBM-basierten Mischungen leiden. Dies kann auf die kleinere Triebkraft zur Ladungstrennung sowie auf die höhere Unordnung der ICBA-basierten Mischungen, die die Ladungstrennung hemmen, zurückgeführt werden. Außerdem wird der Einfluss reiner Fullerendomänen auf die Funktionsfähigkeit organischer Solarzellen, die aus Mischungen des Thienothienophen-basierenden Polymers pBTTT-C14 und PC61BM bestehen, untersucht. Aus diesem Grund wird die Photophysik von Filmen mit einem Donor-Akzeptor-Mischungsverhältnis von 1:1 sowie 1:4 verglichen. Während 1:1-Mischungen lediglich eine co-kristalline Phase, in der Fullerene zwischen den Seitenketten von pBTTT interkalieren, zeigen, resultiert der Überschuss an Fulleren in den 1:4-Proben in der Ausbildung reiner Fullerendomänen zusätzlich zu der co kristallinen Phase. Transiente Absorptionsspektroskopie verdeutlicht, dass Ladungstransferzustände in 1:1-Mischungen hauptsächlich über geminale Rekombination zerfallen, während in 1:4 Mischungen ein beträchtlicher Anteil an Ladungen ihre wechselseitige Coulombanziehung überwinden und freie Ladungsträger bilden kann, die schließlich nicht-geminal rekombinieren.