Synthesis, characterization and chemical modification of a cationic polyelectrolyte poly(methylene amine)

Polyamine polymers have attracted attention due to their ability to demonstrate pH dependent cationic nature and presence of highly reactive pendant amino groups. These amino groups make them suitable for a host of applications through cross-linking and derivatization. As a result the end use application of a polyamine is largely driven by the number of amino groups and the way they are attached to the polymer backbone. Thus, this piece of work describes the synthesis and investigation of properties of a novel aliphatic polyamine, poly(methylene amine); that carries maximum number of amino group on its backbone. The target polymer, poly(methylene amine); was synthesized via two major steps viz.1.synthesis of precursor polymers of poly(methylene amine) and 2. Hydrolysis of the precursor polymers to obtain poly(methylene amine). The precursor polymers poly (1,3-diacetylimidazole-2-one)(6) and poly(1,3-diformyldihydroimidazol-2-one)(7) were synthesized via radical polymerization of their respective monomers. The monomers were polymerized in bulk as well as in solution at different reaction conditions. The maximum molecular weights were achieved by polymerizing the monomers in bulk (Mn = 6.5 x 104 g/mol and Mw = 2.13 x 105 g/mol) of 6. The precursor polymers were hydrolyzed under strong reaction conditions in ethanol in presence of NaOH, LiCl at 170°C to yield poly(methylene amine). The process of hydrolysis was monitored by IR spectroscopy. The solution properties of poly(methylene amine) and its hydrochloride were investigated by viscosimetry and light scattering. The reduced viscosity of poly (methylene amine) hydrochloride as a function of polymer concentration demonstrated a behavior typical of cationic polyelectrolyte. With decrease in polymer concentration the reduced viscosity of poly(methylene amine) hydrochloride increased gradually. The dynamic light scattering studies also revealed behaviors of a polyelectrolyte. Poly(methylene amine) was reacted with electrophiles to yield novel materials. While the attachment of alkyl group onto the nitrogen would increase nucleophilicity, it would also impose steric hindrance. As a result the degree of substitution on poly(methylene amine) would be governed by both the factors. Therefore, few model reactions with electrophiles were performed on polvinylamine under similar reaction conditions in order to make a comparative evaluation. It was found that under similar reaction conditions the degree of substitution was higher in case of polyvinylamine in comparison with poly (methylene amine).This shows that the steric hindrance outweighs nucleophilicity while deciding degree of substitution of electrophiles on poly(methylene amine). The modification was further extended to its use as an initiator for ring opening polymerization of benzyloxy protected N-carboxyanhydride of z-Lysine. The resulting polymer had an interesting brush like architecture. The solid state morphology of this polymer was investigated by SAXS. The 2D-WAXS diffractograms revealed hexagonal morphology of peptide segments without formation of alpha helices.

Chemical composition measurements of cloud condensation nuclei and ice nuclei by aerosol mass spectrometry

In this study the Aerodyne Aerosol Mass Spectrometer (AMS) was used during three laboratory measurement campaigns, FROST1, FROST2 and ACI-03. The FROST campaigns took place at the Leipzig Aerosol Cloud Interaction Simulator (LACIS) at the IfT in Leipzig and the ACI-03 campaign was conducted at the AIDA facility at the Karlsruhe Institute of Technology (KIT). In all three campaigns, the effect of coatings on mineral dust ice nuclei (IN) was investigated. During the FROST campaigns, Arizona Test Dust (ATD) particles of 200, 300 and 400 nm diameter were coated with thin coatings (< 7 nm) of sulphuric acid. At these very thin coatings, the AMS was operated close to its detection limits. Up to now it was not possible to accurately determine AMS detection limits during regular measurements. Therefore, the mathematical tools to analyse the detection limits of the AMS have been improved in this work. It is now possible to calculate detection limits of the AMS under operating conditions, without losing precious time by sampling through a particle filter. The instrument was characterised in more detail to enable correct quantification of the sulphate loadings on the ATD particle surfaces. Correction factors for the instrument inlet transmission, the collection efficiency, and the relative ionisation efficiency have been determined. With these corrections it was possible to quantify the sulphate mass per particle on the ATD after the condensation of sulphuric acid on its surface. The AMS results have been combined with the ice nucleus counter results. This revealed that the IN-efficiency of ATD is reduced when it is coated with sulphuric acid. The reason for this reduction is a chemical reaction of sulphuric acid with the particle's surface. These reactions are increasingly taking place when the aerosol is humidified or heated after the coating with sulphuric acid. A detailed analysis of the solubility and the evaporation temperature of the surface reaction products revealed that most likely aluminium sulphate is produced in these reactions.