Developments for transactinide chemistry experiments behind the gas-filled separator TASCA

Topic of this thesis is the development of experiments behind the gas-filled separator TASCA(TransActinide Separator and Chemistry Apparatus) to study the chemical properties of the transactinide elements.rnIn the first part of the thesis, the electrodepositions of short-lived isotopes of ruthenium and osmium on gold electrodes were studied as model experiments for hassium. From literature it is known that the deposition potential of single atoms differs significantly from the potential predicted by the Nernst equation. This shift of the potential depends on the adsorption enthalpy of therndeposited element on the electrode material. If the adsorption on the electrode-material is favoured over the adsorption on a surface made of the same element as the deposited atom, the electrode potential is shifted to higher potentials. This phenomenon is called underpotential deposition.rnPossibilities to automatize an electro chemistry experiment behind the gas-filled separator were explored for later studies with transactinide elements.rnThe second part of this thesis is about the in-situ synthesis of transition-metal-carbonyl complexes with nuclear reaction products. Fission products of uranium-235 and californium-249 were produced at the TRIGA Mainz reactor and thermalized in a carbon-monoxide containing atmosphere. The formed volatile metal-carbonyl complexes could be transported in a gas-stream.rnFurthermore, short-lived isotopes of tungsten, rhenium, osmium, and iridium were synthesised at the linear accelerator UNILAC at GSI Helmholtzzentrum für Schwerionenforschung, Darmstadt. The recoiling fusion products were separated from the primary beam and the transfer products in the gas-filled separator TASCA. The fusion products were stopped in the focal plane of TASCA in a recoil transfer chamber. This chamber contained a carbon-monoxide – helium gas mixture. The formed metal-carbonyl complexes could be transported in a gas stream to various experimental setups. All synthesised carbonyl complexes were identified by nuclear decay spectroscopy. Some complexes were studied with isothermal chromatography or thermochromatography methods. The chromatograms were compared with Monte Carlo Simulations to determine the adsorption enthalpyrnon silicon dioxide and on gold. These simulations based on existing codes, that were modified for the different geometries of the chromatography channels. All observed adsorption enthalpies (on silcon oxide as well as on gold) are typical for physisorption. Additionally, the thermalstability of some of the carbonyl complexes was studied. This showed that at temperatures above 200 °C therncomplexes start to decompose.rnIt was demonstrated that carbonyl-complex chemistry is a suitable method to study rutherfordium, dubnium, seaborgium, bohrium, hassium, and meitnerium. Until now, only very simple, thermally stable compounds have been synthesized in the gas-phase chemistry of the transactindes. With the synthesis of transactinide-carbonyl complexes a new compound class would be discovered. Transactinide chemistry would reach the border between inorganic and metallorganic chemistry.rnFurthermore, the in-situ synthesised carbonyl complexes would allow nuclear spectroscopy studies under low background conditions making use of chemically prepared samples.

Investigation of the lithium ion mobility in cyclic model compounds and their ion conducting properties

Efficient energy storage and conversion is playing a key role in overcoming the present and future challenges in energy supply. Batteries provide portable, electrochemical storage of green energy sources and potentially allow for a reduction of the dependence on fossil fuels, which is of great importance with respect to the issue of global warming. In view of both, energy density and energy drain, rechargeable lithium ion batteries outperform other present accumulator systems. However, despite great efforts over the last decades, the ideal electrolyte in terms of key characteristics such as capacity, cycle life, and most important reliable safety, has not yet been identified. rnrnSteps ahead in lithium ion battery technology require a fundamental understanding of lithium ion transport, salt association, and ion solvation within the electrolyte. Indeed, well-defined model compounds allow for systematic studies of molecular ion transport. Thus, in the present work, based on the concept of ‘immobilizing’ ion solvents, three main series with a cyclotriphosphazene (CTP), hexaphenylbenzene (HBP), and tetramethylcyclotetrasiloxane (TMS) scaffold were prepared. Lithium ion solvents, among others ethylene carbonate (EC), which has proven to fulfill together with pro-pylene carbonate safety and market concerns in commercial lithium ion batteries, were attached to the different cores via alkyl spacers of variable length.rnrnAll model compounds were fully characterized, pure and thermally stable up to at least 235 °C, covering the requested broad range of glass transition temperatures from -78.1 °C up to +6.2 °C. While the CTP models tend to rearrange at elevated temperatures over time, which questions the general stability of alkoxide related (poly)phosphazenes, both, the HPB and CTP based models show no evidence of core stacking. In particular the CTP derivatives represent good solvents for various lithium salts, exhibiting no significant differences in the ionic conductivity σ_dc and thus indicating comparable salt dissociation and rather independent motion of cations and ions.rnrnIn general, temperature-dependent bulk ionic conductivities investigated via impedance spectroscopy follow a William-Landel-Ferry (WLF) type behavior. Modifications of the alkyl spacer length were shown to influence ionic conductivities only in combination to changes in glass transition temperatures. Though the glass transition temperatures of the blends are low, their conductivities are only in the range of typical polymer electrolytes. The highest σ_dc obtained at ambient temperatures was 6.0 x 10-6 S•cm-1, strongly suggesting a rather tight coordination of the lithium ions to the solvating 2-oxo-1,3-dioxolane moieties, supported by the increased σ_dc values for the oligo(ethylene oxide) based analogues.rnrnFurther insights into the mechanism of lithium ion dynamics were derived from 7Li and 13C Solid- State NMR investigations. While localized ion motion was probed by i.e. 7Li spin-lattice relaxation measurements with apparent activation energies E_a of 20 to 40 kJ/mol, long-range macroscopic transport was monitored by Pulsed-Field Gradient (PFG) NMR, providing an E_a of 61 kJ/mol. The latter is in good agreement with the values determined from bulk conductivity data, indicating the major contribution of ion transport was only detected by PFG NMR. However, the μm-diffusion is rather slow, emphasizing the strong lithium coordination to the carbonyl oxygens, which hampers sufficient ion conductivities and suggests exploring ‘softer’ solvating moieties in future electrolytes.rn

Special Heusler compounds for spintronic applications

This work emphasizes the potential of Heusler compounds in a wide range of spintronic applications. Using electronic structure calculations it is possible to design compounds for specific applications. Examples for GMR and TMR applications, for spin injection into semiconductors, and for spin torque transfer applications will be shown. After a detailed introduction about spintronics and related materials chapter 5 reports about the investigation of new half-metallic compounds where the Fermi energy is tuned in the middle of the gap to result in more stable compounds for GMR and TMR applications. The bulk properties of the quaternary Heusler alloy Co2Mn(1-x)Fe(x)Si with the Fe concentration ranging from x=0 to 1 will be reported and the results suggest that the best candidate for applications may be found at an iron concentration of about 50%. Due to the effect that in the Co2Mn(1-x)Fe(x)Si series the transition metal carrying the localized moment is exchanged and this might lead to unexpected effects on the magnetic properties if the samples are not completely homogeneous chapter 6 reports about the optimization of the Heusler compounds for GMR and TMR applications. The structural and magnetic properties of the quaternary Heusler alloy Co2FeAl(1-x)Si(x) with varying Si concentration will be reported. From the combination of experimental (better order for high Si content) and theoretical findings (robust gap at x = 0.5) it is concluded that a compound with an intermediate Si concentration close to x=0.5-0.7 would be best suited for spintronic applications, especially for GMR and TMR applications. In chapter 7 the detailed investigation of compounds for spin injection into semiconductors will be reported. It will be shown that the diluted magnetic semiconductors based on CoTiSb with a very low lattice mismatch among each other are interesting materials for spintronics applications like Spin-LEDs or other spin injection devices. Chapter 8 refers about the investigation of the theoretically predicted half-metallic completely compensated-ferrimagnet Mn$_3$Ga as a suitable material for spin torque transfer applications. The Curie temperature is above 730~K and the electronic structure calculations indicate a nearly half-metallic ferrimagnetic order with 88% spin polarization at the Fermi energy.}

Wasserfreie, polymere Protonenleiter für Brennstoffzellen durch Immobilisierung von Imidazol

Es werden neuartige, polymere Protonenleiter vorgestellt die nach dem 'Konzept des polymergebunden Protonensolvens' realisiert wurden. Sie zeigen protonische Leitfähigkeit als intrinsische Eigenschaft, sodass keine zweite, flüssige Phase zur Protonenleitung nötig ist. Verwirklicht wurde das Konzept anhand von kammartigen Siloxanoligomeren und -polymeren, wobei Imidazol als Protonensolvens durch flexible Spacer kovalent an das Rückgrat gebunden ist. Durch Pfropfung mit imidazoltragenden Spacereinheiten wurden ferner Kieselgelnanopartikel oberflächenmodifiziert. Um die Auswirkungen der Immobilisierung von Imidazol auf die Leitfähigkeit zu untersuchen, wurden neben unterschiedlichen Molekulargewichten, die Verbindungen auch jeweils mit verschiedenen Spacerlängen synthetisiert. Die Materialien wurden umfassend charakterisiert und auf ihr thermisches Verhalten, Stabilität, Leitfähigkeit, Diffusion und dielektrisches Verhalten sowie auch nach Dotierung mit Säure untersucht. Thermisch stabil sind die Materialien bis ca. 200°C. Die Leitfähigkeiten betragen bis zu 1,5E-3 S/cm bei 160°C, welche aufgrund der Immobilisierung des Imidazols ausschließlich auf Strukturdiffusion zurückzuführen sind. Die Strukturdiffusion ist vergleichbar mit dem Grotthus-Mechanismus in Wasser und wird durch die lokale Mobilität der Imidazolmoleküle, d.h. durch die Glasübergangstemperatur des Systems bestimmt. Entsprechend wird das für Glasbildner typische Vogel-Tamman-Fulcher-Verhalten für alle untersuchten Transportprozesse gefunden. Die mit abnehmender Glasübergangstemperatur abnehmende mechanische Stabilität der Materialien kann, wie gezeigt ist, durch Compoundierung mit Kieselgelnanopartikeln entscheidend verbessert werden, was eine kostengünstige und aussichtsreiche Möglichkeit zur Herstellung von Membranen für Brennstoffzellen darstellt.

Poly(p-phenylen)-Derivate für die Anwendung in Leuchtdioden

Zusammenfassung Das 2,7-Polyfluoren (2,7-PF) wurde in neuer Zeit sowohl wegen seiner einfachen Synthese und hohen Fluoreszenzquantenausbeuten als auch seiner chemischen und thermischen Stabilität intensiv untersucht. Leider liegt das Emissionsmaximum von 2,7-PF in einem Bereich, bei dem das menschliche Auge nicht genügend Sensitivität aufweist. Das Leiter-Poly(p-phenylen) (LPPP) besitzt die optimale Wellenlänge. Jedoch zeigt das LPPP wegen seines steifen Rückgrates große Aggregationstendenz im Film auf, wodurch die Emissionsfarbe bathochrom verschoben und die Photolumineszenzquantenausbeute verringert wird. Es ist deshalb wünschenswert, Polymere zu synthetisieren, die eine längerwellige Emissionsbande als 2,7-PF und eine geringere Aggregationstendenz als LPPP 20 besitzen. Eine Reihe neuer blau emittierender Polymere auf der Basis von Indenofluoren- und Fluoren-Bausteinen mit geringer Aggregationstendenz, hoher thermischer und chemischer Stabilität sowie guter Verarbeitbarkeit wurden dargestellt. Die Polymere weisen eine hohe thermische Stabilität auf (Zersetzung ca.: 310 °C) und sind sehr gut löslich in organischen Lösungsmitteln. Das Absorptionsmaximum des 2,8-Polyindenofluoren (2,8-PIF) in Chloroform liegt bei 416 nm, das Emissionsmaximun bei 432 nm. Die Phasenumwandlungstemperatur beim PIF liegt ca. bei 260 °C. Leider zeigen 2,8-PIF Aggregationstendenzen im Film. Um die Aggregation komplett zu unterbinden, wurden Polyphenylene als Seitenketten an das Dibromfluoren angebracht. Anschließend wurde nach Yamamoto polymerisiert. Das dendritnische PF (DPF) weist die gleiche thermische Stabilität wie die PIFs 28 auf (Zersetzung: 340 °C). Das Polymer 62a ist sehr gut löslich in Toluol, Xylol und chlorierten organischen Lösungsmitteln. Die Absorptions- und Emissionsmaxima des DPFs in Lösung (Chloroform) weisen keine Veränderung gegenüber PF auf. Die Emissionsmaxima des DPFs im Film und nach dem Tempern (100 °C, 24 h) zeigen lediglich eine Verschiebung um 8 nm. Eine Aggregatenbande entsteht jedoch nicht. Dies unterstreicht die abschirmende Eigenschaft der dendritischen Substituenten. Durch Copolymerisation lassen sich die Eigenschaften von Polymeren variieren. Um die Aggregationstendenz der PIF-Derivate zu verringern, wurden die entsprechenden Monomere in verschiedenen Verhältnissen copolymerisiert. Durch die Copolymerisation wurde die PL-Quantenausbeute auf 50 % erhöht. Weiterhin wurden Copolymere von Indenofluoren und 9,10-Dibromanthracen, und erschiedenen Perylenen hergestellt, um zu blau, rot und grün emittierenden Polymeren zu gelangen. Alle blau emittierenden Polymeren wurden in Leuchtdioden untersucht. Das DPF und das Copolymer aus Indenofluoren und Anthracene wiesen die besten Eigenschaften hierfür auf.

Anhydrous proton conducting polymer electrolytes based on polymeric ionic liquids

Imidazolium types of ionic liquids were immobilized by tethering it to acrylate backbone. These imidazolium salt containing acrylate monomers were polymerize at 70oC by free radical polymerization to give polymers poly(AcIm-n) with n being the side chain lenght. The chemical structure of the polymer electrolytes obtained by the described synthetic routes was investigated by NMR-spectroscopy. The polymers were doped with various amounts of H3PO4 and LiN(SO2CF3)2, to obtain poly(AcIm-n) x H3PO4 and poly(AcIm-2-Li) x LiN(SO2CF3)2. The TG curves show that the polymer electrolytes are thermally stable up to about 200◦C. DSC results indicates the softening effect of the length of the spacers (n) as well as phosphoric acid. The proton conductivity of the samples increase with x and reaches to 10-2 Scm-1 at 120oC for both poly(AcIm-2)2H3PO4 and poly(AcIm-6)2H3PO4. It was observed that the lithium ion conductivity of the poly(AcIm-2-Li) x LiN(SO2CF3)2 increases with blends (x) up to certain composition and then leveled off independently from blend content. The conductivity reaches to about 10-5 S cm-1 at 30oC and 10-3 at 100oC for poly(AcIm-2-Li) x LiN(SO2CF3)2 where x is 10. The phosphate and phosphoric acid functionality in the resulting polymers, poly(AcIm-n) x H3PO4, undergoes condensation leading to the formation of cross-linked materials at elevated temperature which may improve the mechanical properties to be used as membrane materials in fuel cells. High resolution nuclear magnetic resonance (NMR) spectroscopy was used to obtain information about hydrogen bonding in solids. The low Tg enhances molecular mobility and this leads to better resolved resonances in both the backbone region and side chain region. The mobile and immobile protons can be distinguished by comparing 1H MAS and 1H-DQF NMR spectra. The interaction of the protons which may contribute to the conductivity is observed from the 2D double quantum correlation (DQC) spectra.

Vibrational spectroscopy on thermally and optically switchable spin crossover compounds

Oktaedrisch koordinierte Übergangsmetalle mit der Elektronenkonfiguration [Ar]3d4 - 3d7 können in zwei unterschiedlichen elektronischen Zuständen existieren: im High-Spin (HS) oder im Low-Spin (LS) Zustand. Zum Beispiel kann Fe(II) in 1A1g (LS) oder 5T2g (HS) Konfiguration auftreten.Besonderes Interesse besteht in der Aufklärung des Mechanismus der kooperativen Wechselwirkung, die den Spinübergang im Festkörper bestimmt. Hierzu müssen zunächst die internen Freiheitsgrade der molekularen Einheiten bekannt sein. Besonders der Beitrag der molekularen Schwingungen zur Entropiedifferenz, die die Triebkraft des Spinübergangs darstellt, ist von entscheidender Bedeutung. Bisher existieren nur wenige detaillierte Untersuchungen zu den Schwingungseigenschaften der Spincrossovermoleküle.In Rahmen der vorliegenden Arbeit wurden die Schwingungseigenschaften einiger Komplexverbindungen, die Spincrossover zeigen, im Detail untersucht. Dazu wurden temperaturabhängige Raman-, Fern- und Mittel-Infrarot-Spektroskopie, Isotopensubstitution und Normalkoordinatenanalysen (NKA) in Verbindung mit Dichtefunktional-Rechnungen (DFT) verwendet.Die gewonnenen Werte der zugeordneten Schwingungsfrequenzen und die bestimmten Kraftkonstantenänderungen können nun zur Verfeinerung von theoretischen Modellen zur Beschreibung des Spinübergangs verwendet werden.

Computational studies on the structure and stabilities of magnetic inter-metallic compounds

The purpose of this thesis is to further the understanding of the structural, electronic and magnetic properties of ternary inter-metallic compounds using density functional theory (DFT). Four main problems are addressed. First, a detailed analysis on the ternary Heusler compounds is made. It has long been known that many Heusler compounds ($X_2YZ$; $X$ and $Y$ transition elements, $Z$ main group element) exhibit interesting half-metallic and ferromagnetic properties. In order to understand these, the dependence of magnetic and electronic properties on the structural parameters, the type of exchange-correlation functional and electron-electron correlation was examined. It was found that almost all Co$_2YZ$ Heusler compounds exhibit half-metallic ferromagnetism. It is also observed that $X$ and $Y$ atoms mainly contribute to the total magnetic moment. The magnitude of the total magnetic moment is determined only indirectly by the nature of $Z$ atoms, and shows a trend consistent with Slater-Pauling behaviour in several classes of these compounds. In contrast to experiments, calculations give a non-integer value of the magnetic moment in certain Co$_2$-based Heusler compounds. To explain deviations of the calculated magnetic moment, the LDA+$U$ scheme was applied and it was found that the inclusion of electron-electron correlation beyond the LSDA and GGA is necessary to obtain theoretical description of some Heusler compounds that are half-metallic ferromagnets. The electronic structure and magnetic properties of substitutional series of the quaternary Heusler compound Co$_2$Mn$_{1-x}$Fe$_x$Si were investigated under LDA+$U$. The calculated band structure suggest that the most stable compound in a half-metallic state will occur at an intermediate Fe concentration. These calculated findings are qualitatively confirmed by experimental studies. Second, the effect of antisite disordering in the Co$_2$TiSn system was investigated theoretically as well as experimentally. Preservation of half-metallicity for Co$_2$TiSn was observed with moderate antisite disordering and experimental findings suggest that the Co and Ti antisites disorder amounts to approximately 10~% in the compound. Third, a systematic examination was carried out for band gaps and the nature (covalent or ionic) of bonding in semiconducting 8- and 18-electron or half-metallic ferromagnet half-Heusler compounds. It was found that the most appropriate description of these compounds from the viewpoint of electronic structures is one of a $YZ$ zinc blende lattice stuffed by the $X$ ion. Simple valence rules are obeyed for bonding in the 8- and 18-electron compounds. Fourth, hexagonal analogues of half-Heusler compounds have been searched. Three series of compounds were investigated: GdPdSb, GdAutextit{X} (textit{X} = Mn, Cd and In) and EuNiP. GdPdSb is suggested as a possible half-metallic weak ferromagnet at low temperature. GdAutextit{X} (textit{X} = Mn, Cd and In) and EuNiP were investigated because they exhibit interesting bonding, structural and magnetic properties. The results qualitatively confirm experimental studies on magnetic and structural behaviour in GdPdSb, GdAutextit{X} (textit{X} = Mn, Cd and In) and EuNiP compounds. ~

Stable isotope fractionation of selenium by biomethylation in soil

Selen ist in geringen Mengen ein essentielles Nährelement, das aber in höheren Gehalten toxisch wird. Der Se-Kreislauf in der Umwelt ist eng mit Redoxreaktionen wie der Reduktion von Se-Oxyanionen zu Methylselenid verknüpft. Flüchtige Methylselenide sind weit verbreitet und stellen einen wichtigen Se-Fluss in der Umwelt dar. Das übergeordnete Ziel meiner Dissertation war, die Stabilisotopenfraktionierung von Se durch Biomethylierung verschiedener oxidierter Se-Spezies (Se[IV] und Se[VI]) im Boden aufzuklären. Zunächst wurde eine Methode entwickelt, die es erlaubte flüchte Methylselenide quantitativ zurückzuhalten. Es zeigte sich, dass alkalische Peroxid-Lösung dafür geeignet war. Mit alkalischer Peroxid-Lösung wurde eine Wiederfindung von 95,6 ± Standardabweichung 5,4% in Verflüchtigungsexperimenten mit Methylselenid-Standards erreicht. Bei Einsatz von alkalischer Peroxid-Lösung in geschlossenen Mikrokosmos-Experimenten kam es zu keinen Se-Verlusten und ausgeglichenen Se-Isotopenbilanzen. Die massengewichteten δ82/76Se-Werte lagen für Se(IV) und Se(VI) am Ende der Mikrokosmos-Inkubationen bei -0,31 ± 0,05‰ (n = 3) und -0,76 ± 0,07‰ (n = 3) verglichen mit -0,20 ± 0,05‰ und -0,69 ± 0,07‰ im jeweils zugegebenen Se. Im zweiten Teil meiner Dissertation wurde die Pilzart Alternaria alternata mit Se(VI) und Se(IV) in geschlossenen Mikrokosmen für 11-15 und Se(IV) zusätzlich für 3-5 Tage bei 30°C inkubiert. In 11-15 Tagen wurden 2,9-11% des Se(VI) und 21-29% des Se(IV) und in 3-5 Tagen, 3-5% des Se(IV) methyliert. Die anfänglichen δ82/76Se-Werte von Se(VI) und Se(IV) lagen bei -0,69 ± 0,07‰, und -0,20 ± 0,05‰. Die δ82/76Se-Werte der Methylselenide unterschieden sich nach 11-15 Tagen Inkubation signifikant zwischen Se(VI) (-3,97 bis -3,25 ‰) und Se(IV) (-1,44 bis -0,16‰) als Quellen. Die δ82/76Se-Werte der Methylselenide zeigen also die Quellen der Biomethylierung von Se an. Die kürzere Inkubation von Se(IV) für 3-5 Tage führte zu einer ausgeprägten Se-Isotopenfraktonierung von mindestens -6‰, bevor ein Fließgleichgewicht erreicht wurde. Im dritten Teil bestimmte ich die Bindungsformen von Se mit drei operativ definierten sequentiellen Extraktionen und die δ82/76S-Werte des gesamten Selens in zehn urbanen Oberböden mit 0,09-0,52 mg/kg Se, die fünf verschiedene Landnutzungstypen repräsentierten (Überschwemmungsgrünland, Garten, Park, Straßenrand und Wald). Nur ein kleiner Teil des Seleniums lag in austauschbarer und damit direkt bioverfügbarer und in residualer, wenig reaktiver Form vor. Das meiste Se war an die organische Substanz und Fe-(Hydr-)Oxide gebunden (42-77% des gesamten Selens). Der mittlere δ82/76Se-Wert des gesamten Selens in den Oberböden lag mit -0,03 ± 0,38‰ nahe beim Mittelwert der gesamten Erde. Geringfügig niedrigere Se-Isotopensignale von -0,59 bis -0,35‰ v.a. in Waldböden und geringfügig höhere von 0,26 to 0,45‰ in Überschwemmungsgrünland wurden vermutlich durch Boden-Pflanze-Recycling und Se-Kontaminationen durch das Flusswasser verursacht. Der vierte Teil umfasste ein “Natural Attenuation”-Experiment und Mikrokosmos-Inkubationen von Bodenproben mit A. alternata. Die Equilibrierung von zum Boden gegebenem Se(IV) und Se(VI) für drei Tage führte zu abnehmenden wasserlöslichen Se-Gehalten um 32-44% bzw. 8-14, die mit kleinen Isotopenfraktionierung (ε = -0,045 bis -0,12 ‰ and -0,05 to -0,07‰ verbunden waren. In zwei der inkubierten Böden mit mäßig sauren pH-Werten wurden zwischen 9,1 und 30% des zugefügten Se(IV) und 1,7% des zugefügten Se(VI) methyliert während in einem stark sauren Boden keine Methylierung auftrat. Das aus Se(IV) entstandene Methylselenid war deutlich gegenüber dem zugegebenen Se-Standard (0,20‰) an 82Se verarmt (δ82/76Se = -3,3 bis -4,5‰). Meine Ergebnisse zeigen, dass die stabilen Isotopenverhältnisse von Se neue Einblicke in Se-Transformationsprozesse erlauben.rn

Structure and properties of quaternary and tetragonal Heusler compounds for spintronics and spin transfer torque applications

Diese Dissertation ist in zwei Teile aufgeteilt: Teil 1 befasst sich mit der Vorhersage von Halb-Metallizität in quarternären Heuslerverbindungen und deren Potential für Spintronik-Anwendungen. Teil 2 befasst sich mit den strukturellen Eigenschaften der Mn2-basierenden Heuslerverbindungen und dem Tuning von ihrer magnetischen Eigenschaften bzgl. Koerzitivfeldstärke und Remanenz. Diese Verbindungen sind geeignet für Spin-Transfer Torque-Anwendungen.rnrnIn Teil 1 wurden die folgenden drei Probenserien quarternärer Heuslerverbindungen untersucht: XX´MnGa (X = Cu, Ni und X´ = Fe, Co), CoFeMnZ (Z = Al, Ga, Si, Ge) und Co2−xRhxMnZ (Z = Ga, Sn, Sb). Abgesehen von CuCoMnGa wurden alle diese Verbindungen mittels ab-initio Bandstrukturrechnungen als halbmetallische Ferromagnete prognostiziert. In der XX´MnGa-Verbindungsklasse besitzt NiFeMnGa zwar eine zu niedrige Curie-Temperatur für technologische Anwendungen, jedoch NiCoMnGa mit seiner hohen Spinpolarisation, einem hohen magnetischen Moment und einer hohen Curie-Temperatur stellt ein neues Material für Spintronik-Anwendungen dar. Alle CoFeMnZ-Verbindungen kristallisieren in der kubischen Heuslerstruktur und ihre magnetischen Momente folgen der Slater-Pauling-Regel, was Halbmetalizität und eine hohe Spinpolarisation impliziert. Die ebenfalls hohen Curie-Temperaturen ermöglichen einen Einsatz weit über Raumtemperatur hinaus. In der strukturellen Charakterisierung wurde festgestellt, dass sämtliche Co2−xRhxMnZ abgesehen von CoRhMnSn verschiedene Typen von Unordnung aufweisen; daher war die ermittelte Abweichung von der Slater-Pauling-Regel sowie von der 100%-igen Spinpolarisation dieser Verbindungen zu erwarten. Die Halbmetallizität der geordneten CoRhMnSn-Verbindung sollte nach den durchgeführten magnetischen Messungen vorhanden sein.rnrnIm zweiten Teil wurden Mn3−xCoxGa und Mn2−xRh1+xSn synthetisiert und charakterisiert. Es wurde gezeigt, dass Mn3−xCoxGa im Bereich x = 0.1 − 0.4 in einer tetragonal verzerrten inversen Heuslerstruktur kristallisiert und im Bereich x = 0.6−1 in einer kubisch inversen Heuslerstruktur. Während die tetragonalen Materialien hartmagnetisch sind und Charakeristika aufweisen, die typischerweise für Spin-Transfer Torque-Anwengungen attraktiv sind, repräsentieren die weichmagnetischen kubischen Vertreter die 100% spinpolarisierten Materialien, die der Slater-Pauling-Regel folgen. Mn2RhSn kristallisiert in der inversen tetragonal verzerrten Heuslerstruktur, weist einernhartmagnetische Hystereseschleife auf und folgt nicht der Slater-Pauling-Regel. Bei hohen Rh-Gehalt wird die kubische inverse Heuslerstruktur gebildet. Alle kubischen Proben sind weichmagnetisch und folgen der Slater-Pauling-Regel.

Thermoelectric performance of p-type TiCoSb half-Heusler compounds - Intrinsic phase separation and charge carrier concentration optimization as key to high efficiency

The world's rising demand of energy turns the development of sustainable and more efficient technologies for energy production and storage into an inevitable task. Thermoelectric generators, composed of pairs of n-type and p-type semiconducting materials, di¬rectly transform waste heat into useful electricity. The efficiency of a thermoelectric mate¬rial depends on its electronic and lattice properties, summarized in its figure of merit ZT. Desirable are high electrical conductivity and Seebeck coefficients, and low thermal con¬ductivity. Half-Heusler materials are very promising candidates for thermoelectric applications in the medium¬ temperature range such as in industrial and automotive waste heat recovery. The advantage of Heusler compounds are excellent electronic properties and high thermal and mechanical stability, as well as their low toxicity and elemental abundance. Thus, the main obstacle to further enhance their thermoelectric performance is their relatively high thermal conductivity.rn rnIn this work, the thermoelectric properties of the p-type material (Ti/Zr/Hf)CoSb1-xSnx were optimized in a multistep process. The concept of an intrinsic phase separation has recently become a focus of research in the compatible n-type (Ti/Zr/Hf)NiSn system to achieve low thermal conductivities and boost the TE performance. This concept is successfully transferred to the TiCoSb system. The phase separation approach can form a significant alternative to the previous nanostructuring approach via ball milling and hot pressing, saving pro¬cessing time, energy consumption and increasing the thermoelectric efficiency. A fundamental concept to tune the performance of thermoelectric materials is charge carrier concentration optimization. The optimum carrier concentration is reached with a substitution level for Sn of x = 0.15, enhancing the ZT about 40% compared to previous state-of-the-art samples with x = 0.2. The TE performance can be enhanced further by a fine-tuning of the Ti-to-Hf ratio. A correlation of the microstructure and the thermoelectric properties is observed and a record figure of merit ZT = 1.2 at 710°C was reached with the composition Ti0.25Hf0.75CoSb0.85Sn0.15.rnTowards application, the long term stability of the material under actual conditions of operation are an important issue. The impact of such a heat treatment on the structural and thermoelectric properties is investigated. Particularly, the best and most reliable performance is achieved in Ti0.5Hf0.5CoSb0.85Sn0.15, which reached a maximum ZT of 1.1 at 700°C. The intrinsic phase separation and resulting microstructure is stable even after 500 heating and cooling cycles.