Decay of imprinted surface waves in polymers

CONCLUSIONS The focus of this work was the investigation ofanomalies in Tg and dynamics at polymer surfaces. Thethermally induced decay of hot-embossed polymer gratings isstudied using laser-diffraction and atomic force microscopy(AFM). Monodisperse PMMA and PS are selected in the Mwranges of 4.2 to 65.0 kg/mol and 3.47 to 65.0 kg/mol,respectively. Two different modes of measurement were used:the one mode uses temperature ramps to obtain an estimate ofthe near-surface glass temperature, Tdec,0; the other modeinvestigates the dynamics at a constant temperature aboveTg. The temperature-ramp experiments reveal Tdec,0 valuesvery close to the Tg,bulk values, as determined bydifferential scanning calorimetry (DSC). The PMMA of65.0 kg/mol shows a decreased value of Tg, while the PS samples of 3.47 and 10.3 kg/mol (MwT_g,bulk(c1=16)tend to be smaller than Tdec,0 and Tg,bulk fromtemperature-ramp and DSC measurements, but confirm thecourse of the values with increasing Mw. The comparison of the fragilities (temperaturedependence of the polymer properties at Tg) near the surfaceand in the bulk shows a higher fragility for PS near thesurface, a lower one for PMMA with molecular weights of 4.2and 65.0 kg/mol. The different surface behavior of PS istraced back to a lower degree of cooperation and a largerfree volume fraction.