Inorganic-organic hybrid polymers: Solution-processible coating materials for defined surface functionalization

A new class of inorganic-organic hybrid polymers could successfully been prepared by the combination of different polymerization techniques. The access to a broad range of organic polymers incorporated into the hybrid polymer was realized using two independent approaches.rnIn the first approach a functional poly(silsesquioxane) (PSSQ) network was pre-formed, which was capable to initiate a controlled radical polymerization to graft organic vinyl-type monomers from the PSSQ precursor. As controlled radical polymerization techniques atom transfer radical polymerization (ATRP), as well as reversible addition fragmentation chain transfer (RAFT) polymerization could be used after defined tuning of the PSSQ precursor either toward a PSSQ macro-initiator or to a PSSQ macro-chain-transfer-agent. The polymerization pathway, consisting of polycondensation of trialkoxy-silanes followed by grafting-from polymerization of different monomers, allowed synthesis of various functional hybrid polymers. A controlled synthesis of the PSSQ precursors could successfully be performed using a microreactor setup; the molecular weight could be adjusted easily while the polydispersity index could be decreased well below 2.rnThe second approach aimed to incorporate differently derived organic polymers. As examples, polycarbonate and poly(ethylene glycol) were end-group-modified using trialkoxysilanes. After end-group-functionalization these organic polymers could be incorporated into a PSSQ network.rnThese different hybrid polymers showed extraordinary coating abilities. All polymers could be processed from solution by spin-coating or dip-coating. The high amount of reactive silanol moieties in the PSSQ part could be cross-linked after application by annealing at 130° for 1h. Not only cross-linking of the whole film was achieved, which resulted in mechanical interlocking with the substrate, also chemical bonds to metal or metal oxide surfaces were formed. All coating materials showed high stability and adhesion onto various underlying materials, reaching from metals (like steel or gold) and metal oxides (like glass) to plastics (like polycarbonate or polytetrafluoroethylene).rnAs the material and the synthetic pathway were very tolerant toward different functionalities, various functional monomers could be incorporated in the final coating material. The incorporation of N-isopropylacrylamide yielded in temperature-responsive surface coatings, whereas the incorporation of redox-active monomers allowed the preparation of semi-conductive coatings, capable to produce smooth hole-injection layers on transparent conductive electrodes used in optoelectronic devices.rnThe range of possible applications could be increased tremendously by incorporation of reactive monomers, capable to undergo fast and quantitative conversions by polymer-analogous reactions. For example, grafting active esters from a PSSQ precursor yielded a reactive surface coating after application onto numerous substrates. Just by dipping the coated substrate into a solution of a functionalized amine, the desired function could be immobilized at the interface as well as throughout the whole film. The obtained reactive surface coatings could be used as basis for different functional coatings for various applications. The conversion with specifically tuned amines yielded in surfaces with adjustable wetting behaviors, switchable wetting behaviors or as recognition element for surface-oriented bio-analytical devices. The combination of hybrid materials with orthogonal reactivities allowed for the first time the preparation of multi-reactive surfaces which could be functionalized sequentially with defined fractions of different groups at the interface. rnThe introduced concept to synthesis functional hybrid polymers unifies the main requirements on an ideal coating material. Strong adhesion on a wide range of underlying materials was achieved by secondary condensation of the PSSQ part, whereas the organic part allowed incorporation of various functionalities. Thus, a flexible platform to create functional and reactive surface coatings was achieved, which could be applied to different substrates. rn

Biofunktionalisierung oxidischer Titanoberflächen über eine spezifische Anbindung von biotinyliertem Fibronektin für die medizinische Anwendung

In der hier vorliegenden Dissertation wird die Entwicklung und Charakterisierung einer biomimetischen Beschichtung für Titanimplantatoberflächen, insbesondere Dentalimplantate, beschrieben. Ziel war es, die Adhäsion und Aktivität von Osteoblasten auf Titanoberflächen zu steigern und so eine Beschleunigung der Implantatintegration in das Knochengewebe zu erreichen. Hierfür wurde eine spezielle Art der biomimetischen Beschichtung entwickelt, bei der biotinyliertes Fibronektin (bFn) über Streptavidin auf eine biotinylierte TiOX-Modelloberfläche immobilisiert wurde. Die Biotinmodifizierung der TiOX-Oberfläche erfolgte hierbei über einen „Self-Assembly-Prozess“ durch sequenzielle Chemiesorption von N-(6-aminohexyl)aminopropyltrimethoxysilan sowie verschiedenen Sulfo-NHS-Biotin-Derivaten, welche den Aufbau einer Streptavidin-Monolage ermöglichten. Als ein wichtiges Resultat zeigte sich, dass die Streptavidin-Monolage effektiv die unspezifische Adsorption von Proteinen an die TiOX-Oberfläche unterbindet und hierdurch die Adhäsion von Osteoblasten auf dieser unterdrückt. Dies hat den Vorteil, dass auf eine antiadhäsive Basisbeschichtung, welche für eine spezifische Zellreaktion wichtig ist, verzichtet werden kann. Dieses osteoblastere Adhäsionsverhalten änderte sich signifikant nach Anbindung von bFn an die Streptavidin-Monolage, mit dem Ergebnis, einer drastischen Steigerung der Osteoblastenadhäsion. Weiterhin besaßen Osteoblasten auf diesen Oberflächen ein Proteinexpressionsmuster, das auf eine erhöhte Osteoinduktion schließen lässt. Es zeigte sich darüber hinaus eine verstärkte Zelladhäsion sowie eine Steigerung des osteoinduktiven Effekts auf Substraten, bei denen bFn über eine Streptavidin-Monolage immobilisiert wurde, gegenüber mit nativem Fibronektin (Fn) modifizierten TiOX-Oberflächen. Ein wesentlicher Schwerpunkt bestand daher in der Analyse der Zusammensetzung und Struktur der biomimetischen Beschichtung über „Surface Plasmon Spectroscopy“ und „Atomic Force Microscopy“. Diese ergab, dass bFn und natives Fn auf den jeweiligen Oberflächen eine unterschiedliche Konformation einnimmt. Im Gegensatz zu nativem Fn, das bei der Adsorption unter physiologischen Bedingungen auf TiOX-Oberflächen eine kompakte Konformation besitzt, nimmt bFn auf einer Streptavidin-Monolage eine entfaltete Konformation ein. Bei letzterer handelt es sich um dieselbe, welche Fn in vivo innerhalb der extrazellulären Matrix besitzt. Sie unterscheidet sich von der kompakten Fn-Konformation dahingehend, dass entlang der Fn-Achse weitere Proteinbindestellen zugänglich werden und hierdurch die Zellaffinität von Fn gesteigert wird. Die nachgewiesene Konformationsänderung kann somit als Grund für die gesteigerte Osteoblasten-Adhäsion und Aktivität auf Oberflächen mit bFn angenommen werden. Diese Kenntnisse konnten weiterhin für die Optimierung des biomimetischen Schichtsystems genutzt werden. So war es möglich, durch alternierendes Inkubieren der Biotin-aktivierten Oberfläche mit Streptavidin und bFn, ein Multilayersystem gezielt aufzubauen. Der Vorteil dieses Multilayersystems gegenüber einer einfachen Monolage aus bFn besteht in einer erhöhten Stabilität der biomimetischen Beschichtung, wodurch eine Anwendung in der Praxis erleichtert würde.

Stress & structure of thin polymer brush films

Polymer brushes have unique properties with a large variety of possible applications ranging from responsive coatings and drug delivery to lubrication and sensing. For further development a detailed understanding of the properties is needed. Established characterization methods, however, only supply information of the surface. Experimental data about the inner “bulk” structure of polymer brushes is still missing.rnScattering methods under grazing incidence supply structural information of surfaces as well as structures beneath it. Nanomechanical cantilevers supply stress data, which is giving information about the forces acting inside the polymer brush film. In this thesis these two techniques are further developed and used to deepen the understanding of polymer brushes. rnThe experimental work is divided into four chapters. Chapter 2 deals with the preparation of polymer brushes on top of nanomechanical cantilever sensors as well as large area sample by using a “grafting-to” technique. The further development of nanomechanical cantilever readout is subject of chapter 3. In order to simplify cantilever sensing, a method is investigated which allows one to perform multiple bending experiments on top of a single cantilever. To do so, a way to correlate different curvatures is introduced as well as a way to conveniently locate differently coated segments. In chapter 4 the change in structure upon solvent treatment of mixed polymer brushes is investigated by using scattering methods and nanomechanical cantilevers amongst others. This allows one to explain the domain memory effect, which is typically found in such systems. Chapter 5 describes the implementation of a phase shifting interferometer - used for readout of nanomechanical cantilevers - into the µ-focused scattering beamline BW4, allowing simultaneous measurements of stress and structure information. The last experimental chapter 6 deals with the roughness correlation in polymer brushes and its dependence on the chain tethered density.rnIn summary, the thesis deals with utilization of new experimental techniques for the investigation of polymer brushes and further development of the techniques themselves.rn

Controlled wetting on silica-based nano- and microstructured surfaces

Der Fokus dieser Doktorarbeit liegt auf der kontrollierten Benetzung von festen Oberflächen, die in vielen Bereichen, wie zum Beispiel in der Mikrofluidik, für Beschichtungen und in biologischen Studien von Zellen oder Bakterien, von großer Bedeutung ist.rnDer erste Teil dieser Arbeit widmet sich der Frage, wie Nanorauigkeit das Benetzungsverhalten, d.h. die Kontaktwinkel und die Pinningstärke, von hydrophoben und superhydrophoben Beschichtungen beeinflusst. Hierfür wird eine neue Methode entwickelt, um eine nanoraue Silika-Beschichtung über die Gasphase auf eine superhydrophobe Oberfläche, die aus rauen Polystyrol-Silika-Kern-Schale-Partikeln besteht, aufzubringen. Es wird gezeigt, dass die Topographie und Dichte der Nanorauigkeiten bestimmt, ob sich die Superhydrophobizität verringert oder erhöht, d.h. ob sich ein Flüssigkeitstropfen im Nano-Wenzel- oder Nano-Cassie-Zustand befindet. Das verstärkte Pinning im Nano-Wenzel-Zustand beruht auf dem Eindringen von Flüssigkeitsmolekülen in die Nanoporen der Beschichtung. Im Nano-Cassie-Zustand dagegen sitzt der Tropfen auf den Nanorauigkeiten, was das Pinning vermindert. Die experimentellen Ergebnisse werden mit molekulardynamischen Simulationen in Bezug gesetzt, die den Einfluss der Oberflächenbeschichtungsdichte und der Länge von fluorinierten Silanen auf die Hydrophobizität einer Oberfläche untersuchen. rnEs wurden bereits verschiedenste Techniken zur Herstellung von transparenten superhydrophoben, d.h. extrem flüssigkeitsabweisenden, Oberflächen entwickelt. Eine aktuelle Herausforderung liegt darin, Funktionalitäten einzuführen, ohne die superhydrophoben Eigenschaften einer Oberfläche zu verändern. Dies ist extrem anspruchsvoll, da funktionelle Gruppen in der Regel hydrophil sind. In dieser Arbeit wird eine innovative Methode zur Herstellung von transparenten superhydrophoben Oberflächen aus Janus-Mikrosäulen mit variierenden Dimensionen und Topographien entwickelt. Die Janus-Säulen haben hydrophobe Seitenwände und hydrophile Silika-Oberseiten, die anschließend selektiv und ohne Verlust der superhydrophoben Eigenschaften der Oberfläche funktionalisiert werden können. Diese selektive Oberflächenfunktionalisierung wird mittels konfokaler Mikroskopie und durch das chemische Anbinden von fluoreszenten Molekülen an die Säulenoberseiten sichtbar gemacht. Außerdem wird gezeigt, dass das Benetzungsverhalten durch Wechselwirkungen zwischen Flüssigkeit und Festkörper in der Nähe der Benetzungslinie bestimmt wird. Diese Beobachtung widerlegt das allgemein akzeptierte Modell von Cassie und Baxter und beinhaltet, dass hydrophile Flächen, die durch mechanischen Abrieb freigelegt werden, nicht zu einem Verlust der Superhydrophobizität führen müssen, wie allgemein angenommen.rnBenetzung kann auch durch eine räumliche Beschränkung von Flüssigkeiten kontrolliert werden, z.B. in mikrofluidischen Systemen. Hier wird eine modifizierte Stöber-Synthese verwendet, um künstliche und natürliche Faser-Template mit einer Silika-Schicht zu ummanteln. Nach der thermischen Zersetzung des organischen Templat-Materials entstehen wohldefinierte Silika-Kanäle und Kanalkreuzungen mit gleichmäßigen Durchmessern im Nano- und Mikrometerbereich. Auf Grund ihrer Transparenz, mechanischen Stabilität und des großen Länge-zu-Durchmesser-Verhältnisses sind die Kanäle sehr gut geeignet, um die Füllgeschwindigkeiten von Flüssigkeiten mit variierenden Oberflächenspannungen und Viskositäten zu untersuchen. Konfokale Mikroskopie ermöglicht es hierbei, die Füllgeschwindigkeiten über eine Länge von mehreren Millimetern, sowie direkt am Kanaleingang zu messen. Das späte Füllstadium kann sehr gut mit der Lucas-Washburn-Gleichung beschrieben werden. Die anfänglichen Füllgeschwindigkeiten sind jedoch niedriger als theoretisch vorhergesagt. Wohingegen die vorhergehenden Abschnitte dieser Arbeit sich mit der quasistatischen Benetzung beschäftigen, spielt hier die Dynamik der Benetzung eine wichtige Rolle. Tatsächlich lassen sich die beobachteten Abweichungen durch einen geschwindigkeitsabhängigen Fortschreitkontaktwinkel erklären und durch dynamische Benetzungstheorien modellieren. Somit löst diese Arbeit das seit langem diskutierte Problem der Abweichungen von der Lucas-Washburn-Gleichung bei kleinen Füllgeschwindigkeiten.

Coating of surfaces of composite materials with enzymatically formed biosilica

Die Bildung kieselsäurehaltiger Spicula in marinen Schwämmen ist nur möglich durch die enzymatische Aktivität des Silicatein- in Verbindung mit der stöchiometrischen Selbstassemblierung des Enzyms mit anderen Schwammproteinen. Die vorliegende Arbeit basiert auf einem biomimetischen Ansatz mit dem Ziel, unterschiedliche Oberflächen für biotechnologische und biomedizinische Anwendungen mit Biosilica und Biotitania zu beschichten und zu funktionalisieren. Für biotechnologische Anwendungen ist dabei das Drucken von Cystein-getaggtem Silicatein auf Gold-Oberflächen von Bedeutung, denn es ermöglichte die Bildung definierter Biotitania-Strukturen (Anatas), welche als Photokatalysator den Abbau eines organischen Farbstoffs bewirkten. Des Weiteren zeigte sich die bio-inspirierte Modifikation von Tyrosin-Resten an rekombinantem Silicatein-(via Tyrosinase) als vielversprechendes Werkzeug zur Beschleunigung der Selbstassemblierung des Enzyms zu mesoskaligen Filamenten. Durch eine solche Modifikation konnte Silicatein auch auf der Oberfläche von anorganischen Partikeln immobilisiert werden, welches die Assemblierung von anorganisch-organischen Verbundwerkstoffen in wäßriger Umgebung förderte. Die resultierenden supramolekularen Strukturen könnten dabei in bio-inspirierten und biotechnologischen Anwendungen genutzt werden. Weiterhin wurde in der vorliegenden Arbeit die Sekundärstruktur von rekombinantem Silicatein- (Monomer und Oligomer) durch Raman Spektroskopie analysiert, nachdem das Protein gemäß einer neu etablierten Methode rückgefaltet worden war. Diese Spektraldaten zeigten insbesondere Änderungen der Proteinkonformation durch Solubilisierung und Oligomerisierung des Enzyms. Außerdem wurden die osteoinduzierenden und osteogenen Eigenschaften unterschiedlicher organischer Polymere, die herkömmlich als Knochenersatzmaterial genutzt werden, durch Oberflächenmodifikation mit Silicatein/Biosilica verbessert: Die bei der Kultivierung knochenbildender Zellen auf derart oberflächenbehandelten Materialien beobachtete verstärkte Biomineralisierung, Aktivierung der Alkalischen Phosphatase, und Ausbildung eines typischen zellulären Phänotyps verdeutlichen das Potential von Silicatein/Biosilica für der Herstellung neuartiger Implantat- und Knochenersatzmaterialien.