The release of zinc and lead from mine tailings

Mining and processing of metal ores are important causes of soil and groundwater contamination in many regions worldwide. Metal contaminations are a serious risk for the environment and human health. The assessment of metal contaminations in the soil is therefore an important task. A common approach to assess the environmental risk emanating from inorganic contaminations to soil and groundwater is the use of batch or column leaching tests. In this regard, the suitability of leaching tests is a controversial issue. In the first part of this work the applicability and comparability of common leaching tests in the scope of groundwater risk assessment of inorganic contamination is reviewed and critically discussed. Soil water sampling methods (the suction cup method and centrifugation) are addressed as an alternative to leaching tests. Reasons for limitations of the comparability of leaching test results are exposed and recommendations are given for the expedient application of leaching tests for groundwater risk assessment. Leaching tests are usually carried out in open contact with the atmosphere disregarding possible changes of redox conditions. This can affect the original metal speciation and distribution, particularly when anoxic samples are investigated. The influence of sample storage on leaching test results of sulfide bearing anoxic material from a former flotation dump is investigated in a long-term study. Since the oxidation of the sulfide-bearing samples leads to a significant overestimation of metal release, a feasible modification for the conduction of common leaching tests for anoxic material is proposed, where oxidation is prevented efficiently. A comparison of leaching test results to soil water analyzes have shown that the modified saturation soil extraction (SSE) is found to be the only of the tested leaching procedures, which can be recommended for the assessment of current soil water concentrations at anoxic sites if direct investigation of the soil water is impossible due to technical reasons. The vertical distribution and speciation of Zn and Pb in the flotation residues as well as metal concentrations in soil water and plants were investigated to evaluate the environmental risk arising from this site due to the release of metals. The variations in pH and inorganic C content show an acidification of the topsoil with pH values down to 5.5 in the soil and a soil water pH of 6 in 1 m depth. This is due to the oxidation of sulfides and depletion in carbonates. In the anoxic subsoil pH conditions are still neutral and soil water collected with suction cups is in equilibrium with carbonate minerals. Results from extended x-ray absorption fine-structure (EXAFS) spectroscopy confirm that Zn is mainly bound in sphalerite in the subsoil and weathering reactions lead to a redistribution of Zn in the topsoil. A loss of 35% Zn and S from the topsoil compared to the parent material with 10 g/kg Zn has been observed. 13% of total Zn in the topsoil can be regarded as mobile or easily mobilizable according to sequential chemical extractions (SCE). Zn concentrations of 10 mg/L were found in the soil water, where pH is acidic. Electron supply and the buffer capacity of the soil were identified as main factors controlling Zn mobility and release to the groundwater. Variable Pb concentrations up to 30 µg/L were observed in the soil water. In contrast to Zn, Pb is enriched in the mobile fraction of the oxidized topsoil by a factor of 2 compared to the subsoil with 2 g/kg Pb. 80% of the cation exchange capacity in the topsoil is occupied by Pb. Therefore, plant uptake and bioavailability are of major concern. If the site is not prevented from proceeding acidification in the future, a significant release of Zn, S, and Pb to the groundwater has to be expected. Results from this study show that the assessment of metal release especially from sulfide bearing anoxic material requires an extensive comprehension of leaching mechanisms on the one hand and on weathering processes, which influence the speciation and the mobility of metals, on the other hand. Processes, which may change redox and pH conditions in the future, have to be addressed to enable sound decisions for soil and groundwater protection and remediation.

Synthesis and characterization of metal-chalcogenide MQ 2-Nanoparticles (M = Mo, W, Zr; Q = S, O)

Here, we present the adaptation and optimization of (i) the solvothermal and (ii) the metal-organic chemical vapor deposition (MOCVD) approach as simple methods for the high-yield synthesis of MQ2 (M=Mo, W, Zr; Q = O, S) nanoparticles. Extensive characterization was carried out using X-ray diffraction (XRD), scanning and transmission electron micros¬copy (SEM/TEM) combined with energy dispersive X-ray analysis (EDXA), Raman spectroscopy, thermal analyses (DTA/TG), small angle X-ray scattering (SAXS) and BET measurements. After a general introduction to the state of the art, a simple route to nanostructured MoS2 based on the decomposition of the cluster-based precursor (NH4)2Mo3S13∙xH2O under solvothermal conditions (toluene, 653 K) is presented. Solvothermal decomposition results in nanostructured material that is distinct from the material obtained by decomposition of the same precursor in sealed quartz tubes at the same temperature. When carried out in the presence of the surfactant cetyltrimethyl¬ammonium bromide (CTAB), the decomposition product exhibits highly disordered MoS2 lamellae with high surface areas. The synthesis of WS2 onion-like nanoparticles by means of a single-step MOCVD process is discussed. Furthermore, the results of the successful transfer of the two-step MO¬CVD based synthesis of MoQ2 nanoparticles (Q = S, Se), comprising the formation of amorphous precursor particles and followed by the formation of fullerene-like particles in a subsequent annealing step to the W-S system, are presented. Based on a study of the temperature dependence of the reactions a set of conditions for the formation of onion-like structures in a one-step reaction could be derived. The MOCVD approach allows a selective synthesis of open and filled fullerene-like chalcogenide nanoparticles. An in situ heating stage transmission electron microscopy (TEM) study was employed to comparatively investigate the growth mechanism of MoS2 and WS2 nanoparticles obtained from MOCVD upon annealing. Round, mainly amorphous particles in the pristine sample trans¬form to hollow onion-like particles upon annealing. A significant difference between both compounds could be demonstrated in their crystallization conduct. Finally, the results of the in situ hea¬ting experiments are compared to those obtained from an ex situ annealing process under Ar. Eventually, a low temperature synthesis of monodisperse ZrO2 nanoparticles with diameters of ~ 8 nm is introduced. Whereas the solvent could be omitted, the synthesis in an autoclave is crucial for gaining nano-sized (n) ZrO2 by thermal decomposition of Zr(C2O4)2. The n-ZrO2 particles exhibits high specific surface areas (up to 385 m2/g) which make them promising candidates as catalysts and catalyst supports. Co-existence of m- and t-ZrO2 nano-particles of 6-9 nm in diameter, i.e. above the critical particle size of 6 nm, demonstrates that the particle size is not the only factor for stabilization of the t-ZrO2 modification at room temperature. In conclusion, synthesis within an autoclave (with and without solvent) and the MOCVD process could be successfully adapted to the synthesis of MoS2, WS2 and ZrO2 nanoparticles. A comparative in situ heating stage TEM study elucidated the growth mechanism of MoS2 and WS2 fullerene-like particles. As the general processes are similar, a transfer of this synthesis approach to other layered transition metal chalcogenide systems is to be expected. Application of the obtained nanomaterials as lubricants (MoS2, WS2) or as dental filling materials (ZrO2) is currently under investigation.

Synthesis of new xanthene derivatives

Xanthene dyes, including fluorescein, are a well-known class of fluorescent dyes, which have widespread applications in natural sciences. The synthesis of xanthene derivatives via acid catalyzed condensation of substituted phenols with phthalic anhydride, to afford the asymmetric derivatives, is well established. The high temperature, harsh reaction conditions and often low yields make this method less convenient. The synthesis of xanthene dyes by direct modification of the fluorophore moiety is a great option to circumvent the above mentioned drawbacks. rnOur new synthetic strategy for the preparation of novel asymmetric xanthene dyes via direct conversion of hydroxyl groups on 3'- and 6'-positions into leaving groups by mesylation is reported. It was discovered that 3',6'-di-mesylated fluorescein underwent a nucleophilic aromatic substitution with sulfur nucleophiles and afforded new asymmetric xanthene sulfides. rnThe impact of substituents possessing an electron-withdrawing character such as chlorines and bromines was investigated with the aim to improve the aromatic substitution on the electron-rich fluorescein structure. It was observed that the incorporation of these groups did not considerably affect the substitution reaction and the yields were comparable with the unsubstituted fluorescein. rnThis strategy provided novel fluorescent probes with the linker suitable to further modifications. The modifications of the linker delivered fluorescein derivatives that could be used as fluorescent labels in peptides, oligonucleotides and for cell imaging. rnThe hydroxyl group on the linker was modified to achieve potent bioconjugate functionality such as azide. The new fluorescent azides were obtained in a 4-step synthesis, namely 2-(6-(2-azidoethylthio)-3-oxo-3H-xanthen-9-yl)benzoic acid with an overall yield of 13%, its 2',7'-dichloro derivative with an overall yield of 10% and its 2',4',5'-tribromo derivative with an overall yield of 1%, respectively. rnAn asymmetric xanthene sulfide with an amino functionality placed on the aliphatic linker, namely 2-(6-((2-aminoethyl)thio)-3-oxo-3H-xanthen-9-yl)benzoic acid, was obtained in a 3-step synthesis with an overall yield of 33%. rnThe impact of the substitution with sulfur nucleophiles on the 6'-position of the xanthene moiety on its fluorescent characteristics was investigated. In comparison with fluorescein new asymmetric xanthene sulfides afforded lower extinction coefficients and fluorescent quantum yields. On the other hand, the substitution with a sulfur nucleophile significantly improved the photostability of xanthene dyes. It was shown that after 10 hours of continuous excitation, the asymmetric sulfur-containing xanthene fluorophores exhibited 58-94% of their initial fluorescent intensities. This observation suggested that the novel dyes were 1-2 orders of magnitude more stable than fluorescein. rnThe azido-modified xanthenes were “clicked” via Cu(I)-catalyzed azide-alkyne cycloaddition with an oligonucleotide, which contained the terminal alkyne residue. rn

Sulfur-containing polymers for surface attachment

Different concepts for the synthesis of sulfur-containing polymers as well as their adsorption onto gold surfaces were studied. The present work is divided into three parts. The main part focuses on the synthesis of poly(1,2-alkylene sulfides) (“polysulfides”) with complex architectures on the basis of polyether-based macroinitiators by the anionic ring-opening polymerization of ethylene sulfide and propylene sulfide. This synthetic tool kit allowed the synthesis of star-shaped, brush-like, comb-like and pom-pom-like polysulfides, the latter two with an additional poly(ethylene glycol) chain. Additionally, the number of polysulfide arms as well as the monomer composition could be varied over a wide range to obtain copolymers with multiple thioether functionalities.rnThe second section deals with the synthesis of a novel lipoic acid-based initiator for ring-opening polymerizations for lactones and epoxides. A straightforward approach was selected to accomplish the ability to obtain tailored polymers with a common used disulfide-anchoring group, without the drawbacks of post-polymerization functionalization. rnIn the third part, a new class of block-copolymers consisting of polysulfides and polyesters were investigated. For the first time this approach enabled the use of hydroxyl-terminated poly(propylene sulfide) as macroinitiator for the synthesis of a second block.rnThe adsorption efficiency of those different polymer classes onto gold nanoparticles as well as gold rnsupports was studied via different methods.rn