Uptake mechanism, intracellular trafficking and endo-lysosomal pH monitoring of polystyrene nanoparticles

What is the intracellular fate of nanoparticles (NPs) taken up by the cells? This question has been investigated for polystyrene NPs of different sizes with a set of molecular biological and biophysical techniques.rnTwo sets of fluorescent NPs, cationic and non-ionic, were synthesized with three different polymerization techniques. Non-ionic particles (132 – 846 nm) were synthesized with dispersion polymerization in an ethanol/water solution. Cationic NPs with 120 nm were synthesized by miniemulsion polymerization Particles with 208, 267 and 603 nm were produced by seeding the 120 nm particle obtained by miniemulsion polymerization with drop-wise added monomer and polymerization of such. The colloidal characterization of all particles showed a comparable amount of the surface groups. In addition, particles were characterized with regard to their size, morphology, solid content, amount of incorporated fluorescent dye and zeta potential. The fluorescent intensities of all particles were measured by fluorescence spectroscopy for calibration in further cellular experiments. rnThe uptake of the NPs to HeLa cells after 1 – 24 h revealed a much higher uptake of cationic NPs in comparison to non-ionic NPs. If the same amount of NPs with different sizes is introduced to the cell, a different amount of particles is present in the cell medium, which complicates a comparison of the uptake. The same conclusion is valid for the particles’ overall surface area. Therefore, HeLa cells were incubated with the same concentration, amount and surface area of NPs. It was found that with the same concentration always the same polymer amount is taking up by cells. However, the amount of particles taken up decreases for the biggest. A correlation to the surface area could not be found. We conclude that particles are endocytosed by an excavator-shovel like mechanism, which does not distinguish between different sizes, but is only dependent on the volume that is taken up. For the decreased amount of large particles, an overload of this mechanism was assumed, which leads to a decrease in the uptake. rnThe participation of specific endocytotic processes has been determined by the use of pharmacological inhibitors, immunocytological staining and immunofluorescence. The uptake of NPs into the endo-lysosomal machinery is dominated by a caveolin-mediated endocytosis. Other pathways, which include macropinocytosis and a dynamin-dependent mechanism but exclude clathrin mediated endocytosis, also occur as competing processes. All particles can be found to some extent in early endosomes, but only bigger particles were proven to localize in late endosomes. No particles were found in lysosomes; at least not in lysosomes that are labeled with Lamp1 and cathepsin D. However, based on the character of the performed experiment, a localization of particles in lysosomes cannot be excluded.rnDuring their ripening process, vesicles undergo a gradual acidification from early over late endosomes to lysosomes. It is hypothesized that NPs in endo-lysosomal compartments experience the same change in pH value. To probe the environmental pH of NPs after endocytosis, the pH-sensitive dye SNARF-4F was grafted onto amino functionalized polystyrene NPs. The pH value is a ratio function of the two emission wavelengths of the protonated and deprotonated form of the dye and is hence independent of concentration changes. The particles were synthesized by the aforementioned miniemulsion polymerization with the addition of the amino functionalized copolymer AEMH. The immobilization of SNARF-4F was performed by an EDC-coupling reaction. The amount of physically adsorbed dye in comparison to covalently bonded dye was 15% as determined by precipitation of the NPs in methanol, which is a very good solvent for SNARF-4F. To determine influences of cellular proteins on the fluorescence properties, a intracellular calibration fit was established with platereader measurements and cLSM imaging by the cell-penetrable SNARF-4F AM ester. Ionophores equilibrated the extracellular and intracellular pH.rnSNARF-4F NPs were taken up well by HeLa cells and showed no toxic effects. The pH environment of SNARF-4F NPs has been qualitatively imaged as a movie over a time period up to 1 h in pseudo-colors by a self-written automated batch program. Quantification revealed an acidification process until pH value of 4.5 over 24 h, which is much slower than the transport of nutrients to lysosomes. NPs are present in early endosomes after min. 1 h, in late endosomes at approx. 8 h and end up in vesicles with a pH value typical for lysosomes after > 24 h. We therefore assume that NPs bear a unique endocytotic mechanism, at least with regards to the kinetic involvedrn

Die Isolierung und Aufreinigung der Metalloendopeptidase LysN und die Evaluierung der Spezifität der LysN E157D-Mutante und ihr Einsatz in der Proteomik und die Mechanismen der Bildung von “dendritic cell aggresome- like induced structures“ (DALIS)

Der proteolytische Verdau von Proteinen in Peptide ist ein wichtiger Schritt in der Tandem-Massenspektrometrie. Dabei werden Peptide fragmentiert und die sich ergebenden Fragmentionen geben Aufschluss über die Aminosäuresequenz des zu untersuchenden Proteins. Dabei sind für die Fragmentierung sowohl Länge und Sequenz, als auch der Ladungszustand des Peptids ungemein wichtig. Diese Parameter bedingen sich durch Endoproteasen, die für den proteolytischen Verdau eingesetzt werden. Eine Voraussetzung hierfür ist die Spezifität der Protease. Trypsin ist bei weitem die gebräuchlichste Protease zur massenspektrometrischen Probenvorbereitung. Allerdings bietet Trypsin keine Komplettlösung. Je nach Fragestellung und Applikation müssen weitere Proteasen eingesetzt werden, um eine komplette Sequenzabdeckung zu gewährleisten und möglichst alle posttranslationalen Modifikationen nachzuweisen, oder bestimmte Proteomklassen (z.B Phosphoproteom

Speciation of tetravalent plutonium in contact with humic substances and kaolinite under environmental conditions

Plutonium represents the major contribution to the radiotoxicity of spent nuclear fuel over storage times of up to several hundred thousand years. The speciation of plutonium in aquifer systems is important in order to assess the risks of high-level nuclear waste disposal and to acquire a deep knowledge of the mobilization and immobilization behavior of plutonium. In aqueous solutions, plutonium can coexist in four oxidation states and each one of them has different chemical and physical behavior. Tetravalent plutonium is the most abundant under natural conditions. Therefore, detailed speciation studies of tetravalent plutonium in contact with humic substances (HS) and kaolinite as a model clay mineral have been performed in this work. Plutonium is present in the environment at an ultratrace level. Therefore, speciation of Pu at the ultratrace level is mandatory. Capillary electrophoresis (CE) coupled to resonance ionization mass spectrometry (RIMS) was used as a new speciation method. CE-RIMS enables to improve the detection limit for plutonium species by 2 to 3 orders of magnitude compared to the previously developed CE-ICP-MS. For understanding the behavior of Pu(IV) in aqueous systems, redox reactions, complexation, and sorption behavior of plutonium were studied. The redox behavior of plutonium in contact with humic acid (HA) and fulvic acid (FA) was investigated. A relatively fast reduction of Pu(VI) in contact with HS was observed. It was mainly reduced to Pu(IV) and Pu(III) within a couple of weeks. The time dependence of the Pu(IV) complexation with Aldrich HA was investigated and a complex constant (logßLC) between 6.4 - 8.4 of Pu(IV) was determined by means of ultrafiltration taking into account the loading capacity (LC). The sorption of tetravalent plutonium onto kaolinite was investigated as a function of pH in batch experiments under aerobic and anaerobic conditions. The sorption edge was found at about pH = 1 and a maximum sorption at around pH = 8.5. In the presence of CO2 at pH > 8.5, the sorption of plutonium was decreased probably due to the formation of soluble carbonate complexes. For comparison, the sorption of Th(IV) onto kaolinite was also investigated and consistent results were found. The Pu(IV) sorption onto kaolinite was studied by XANES and EXAFS at pH 1, 4, 9 and the sorbed species on kaolinite surface was Pu(IV). Depending on the pH, only 1 - 10 % of the sorbed plutonium is desorbed from kaolinite and released into a fresh solution at the same pH value. Furthermore, the sorption of HS onto kaolinite was studied as a function of pH at varying concentrations of HS, as a prerequisite to understand the more complex ternary system. The sorption of HA onto kaolinite was found to be higher than that of FA. The investigation of the ternary systems (plutonium-kaolinite-humic substances) is performed as a function of pH, concentration of HS, and the sequences of adding the reactants. The presence of HS strongly influences the sorption of Pu(IV) onto kaolinite over the entire pH range. For comparison, the influence of HS on the sorption of Th(IV) onto kaolinite was also investigated and a good agreement with the results of Pu(IV) was obtained.

Sorption and direct speciation of neptunium(V) on aluminium oxide and montmorillonite

This study comprised batch experiments, direct speciation studies via EXAFS, and modelling with the 2SPNE SC/CE model to elucidate the mechanisms of Np(V) sorption on montmorillonite and, for reference, on γ-Al2O3. The sorption of pM 239Np(V) and µM 237Np(V) on montmorillonite (STx-1, 4 g/L) and γ-Al2O3 (0.5 g/L) was studied at room temperature in the presence and absence of ambient CO2 covering a pH-range from 2.5 (STx-1) or 5 (γ-Al2O3) to 10.5 with 0.01 or 0.1M NaClO4 as background electrolyte. The Np(V) uptake was determined by γ spectroscopy of the supernatants and calculated as percentage as well as distribution coefficient Kd. Sorption starts from pH ~6 and, under exclusion of CO2, increases continuously, while, in the presence of ambient air, it reaches a maximum at pH ~8.5 (γ-Al2O3: log Kd max ≈ 4 mL/g; STx-1: log Kd max ≈ 2.7 mL/g). Beyond that it decreases again due to the formation of queous neptunium carbonate complexes. Furthermore, neptunium sorption on montmorillonite is influenced by ionic strength at pH <6 through ion exchange processes pointing towards the formation of outer-sphere surface complexes there. Isotherms measured at the sorption maximum showed the precipitation of resumably neptunium carbonate complexes above 3∙10^-5 M under ambient air conditions. Additionally, they indicated progressive saturation of the sorption sites of γ-Al2O3. At selected pH (STx-1: 5.0, 7.0, 8.0, 8.5, 9.0, 9.5; γ-Al2O3: 8.5, 9.5) EXAFS samples were prepared as wet pastes with µM 237Np and measured at room temperature in fluorescence mode at ANKA and ESRF. Several spectra were averaged and analysed with EXAFSPAK and FEFF 8.20 employing models of NaNpO2(CO3) or soddyite, (UO2)2SiO4∙2(H2O). The shorter atomic distances of the neptunyl ion at pH 5 compared to the others hinted at the retention of the hydration shell and, thus, at outer-sphere sorption. On average the bond lengths for Np(V) sorbed on STx-1 at high pH were Oax ≈ 1.84 Å and Oeq ≈ 2.53 Å. At high pH, ternary neptunyl carbonate surface complexes could be identified for montmorillonite (C ≈ 3.00 Å), but not for γ-Al2O3, where an interaction of neptunium with the aluminium surface atoms according to the soddyite model gave better agreement with the experimental data. However, neither structure as suggested by the two models could be excluded for both systems rendering a combination most likely. Modelling of the sorption data provided further evidence for the existence of ternary neptunium carbonate surface complexes in both cases. The results of this study can aid environmental risk assessment for clay-based nuclear waste repositories by providing valuable input data for simulations of radionuclide migration from a final disposal site.

Identification and dissolution behavior of the secondary uranium minerals in the corrosion products of Depleted Uranium (DU) ammunition formed in soils

In der vorliegenden Studie wurden verschiedene Techniken eingesetzt um drei Proben (4, 7, and 8) die aus denrnKorrosionsprodukten von aus dem Kosovo Krieg stammenden Munitionskugeln, bestehend aus abgereichertem Uranrn(Depleted Uranium - DU), zu untersuchen. Als erstes Verfahren wurde die Raman-Spektroskopie eingesetzt. Hierbeirnzeigte sichin den Proben, charakterisiert durch einen Doppelpeak, die Anwesenheit von Schoepitrn(UO2)8O2(OH)12(H2O)12. Der erste und zweite Peakzeigte sich im Spektralbereich von 840,3-842,5 cm-1rnbeziehungsweise 853,6-855,8 cm-1. Diese Werte stimmen mit den Literaturwerten für Raman-Peaks für Schoepitrnüberein. Des Weiteren wurde bei dieser Untersuchungsmethode Becquerelite Ca(UO2)6O4(OH)6(H2O)8 mit einemrnPeak im Bereich zwischen 829 to 836 cm-1 gefunden. Aufgrund des Fehlens des Becquerelitespektrums in derrnSpektralbibliothek wurde eine in der Natur vorkommende Variante analysiert und deren Peak bei 829 cm-1 bestimmt,rnwas mit den Ergebnissen in den Proben korrespondiert. Mittels Röntgenbeugung (X-Ray Diffraction, XRD) zeigtenrnsich in allen Proben ähnliche Spektren. Das lässt darauf schließen, dass das pulverisierte Material in allen Probenrndas gleiche ist. Hierbei zeigte sich eine sehr gute Übereinstimmung mit Schoepit und/oder meta-rnSchoepit(UO2)8O2(OH)12(H2O)10, sowie Becquerelite. Weiterhin war weder Autunit, Sabugalit noch Uranylphosphatrnanwesend, was die Ergebnisse einer anderen Studie, durchgeführt an denselben Proben, wiederlegt. DiernAnwesenheit von P, C oder Ca im Probenmaterial konnte ausgeschlossen werden. Im Falle von Calciumkann diesrnmit der Anwesenheit von Uran erklärt werden, welches aufgrund seines Atomradius bevorzugt in Becquerelite (1:6)rneingebaut wird. Die beiden Hauptpeaks für Uran lagen im Falle von U 4f 7/2 bei 382.0 eV und im Falle von U 4f 5/2rnbei 392 eV. Diese Werte mit den Literaturwerten für Schoepit und meta-Schoepitüberein. Die Ergebnissernelektronenmikroskopischen Untersuchung zeigen U, O, Ca, Ti als dominante Komponenten in allen Messungen.rnElemente wie Si, Al, Fe, S, Na, und C wurden ebenfalls detektiert; allerdings kann nicht ausgeschlossen werden,rndass diese Elemente aus dem Boden in der unmittelbaren Umgebung der Munitionsgeschosse stammen. Gold wurdernebenfalls gemessen, was aber auf die Goldarmierung in den Probenaufbereitungsbehältern zurückgeführt werdenrnkann. Die Elektronenmikroskopie zeigte außerdem einige Stellen in denen elementares Uran und Bodenmineralernsowie sekundäre Uranminerale auftraten. Die Elementübersicht zeigt einen direkten Zusammenhang zwischen U andrnCa und gleichzeitig keine Korrelation zwischen U und Si, oder Mg. Auf der anderen Seite zeigte sich aber einrnZusammenhang zwischen Si und Al da beide Konstituenten von Bodenmineralen darstellen. Eine mit Hilfe derrnElektronenstrahlmikroanalyse durchgeführte quantitative Analyse zeigte den Massenanteil von Uran bei ca. 78 - 80%,rnwas mit den 78,2% and 79,47% für Becquerelite beziehungsweise Schoepit aufgrund ihrer Summenformelrnkorrespondiert. Zusätzlich zeigt sich für Calcium ein Massenanteil von 2% was mit dem Wert in Becquerelite (2.19%)rnrecht gut übereinstimmt. Der Massenanteil von Ti lag in einigen Fällen bei 0,77%, was auf eine noch nicht korrodierternDU-Legierung zurückzuführen ist. Ein Lösungsexperiment wurde weiterhin durchgeführt, wobei eine 0,01 M NaClO4-rnLösung zum Einsatz kam in der die verbliebene Probensubstanz der Korrosionsprodukte gelöst wurde;rnNatriumperchlorate wurde hierbei genutzt um die Ionenstärke bei 0,01 zu halten. Um Verunreinigungen durchrnatmosphärisches CO2 zu vermeiden wurden die im Versuch für die drei Hauptproben genutzten 15 Probenbehälterrnmit Stickstoffgas gespült. Eine Modelkalkulation für den beschriebenen Versuchsaufbau wurde mit Visual MINTEQrnv.3.0 für die mittels vorgenannten Analysemethoden beschriebenen Mineralphasen im pH-Bereich von 6 – 10 imrnFalle von Becquerelite, und Schoepit berechnet. Die modellierten Lösungskurven wurden unter An- und Abwesenheitrnvon atmosphärischem CO2 kalkuliert. Nach dem Ende des Lösungsexperiments (Dauer ca. 6 Monate) zeigten diernKonzentrationen des gelösten Urans, gemessen mittels ICP-OES, gute Übereinstimmung mit den modelliertenrnSchoepit und Becquerelite Kurven. Auf Grund des ähnlichen Löslichkeitverhaltens war es nicht möglich zwichen denrnbeiden Mineralen zu unterscheiden. Schoepit kontrolliert im sauren Bereich die Löslichkeit des Urans, währendrnbecquerelit im basichen am wenigsten gelöst wird. Des Weiteren bleibt festzuhalten, dass ein Anteil an CO2 in diernverschlossenen Probenbehälter eingedrungen ist, was sich mit der Vorhersage der Modeldaten deckt. Die Löslichkeitrnvon Uran in der Lösung als Funktion des pH-Wertes zeigte die niedrigsten Konzentrationen im Falle einer Zunahmerndes pH-Wertes von 5 auf 7 (ungefähr 5,1 x 10-6 mol/l) und einer Zunahme des pH-Wertes auf 8 (ungefähr 1,5 x 10-6rnmol/l bei). Oberhalb dieses Bereichs resultiert jeder weitere Anstieg des pH-Wertes in einer Zunahme gelösten Uransrnin der Lösung. Der ph-Wert der Lösung wie auch deren pCO2-Wert kontrollieren hier die Menge des gelösten Urans.rnAuf der anderen Seite zeigten im Falle von Becquerelite die Ca-Konzentrationen höhere Werte als erwartet, wobeirnwahrscheinlich auf eine Vermischung der Proben mit Bodensubstanz zurückgeführt werden kann. Abschließendrnwurde, unter Berücksichtigung der oben genannten Ergebnisse, eine Fallstudie aus Basrah (Irak) diskutiert, wo inrnzwei militärischen Konflikten Uranmunition in zwei Regionen unter verschiedenen Umweltbedingungen eingesetztrnwurden.