Hyperbranched polyether polyols as building blocks for complex macromolecular architectures

The present thesis deals with the development of new branched polymer architectures containing hyperbranched polyglycerol. Materials investigated include hyperbranched oligomers, hyperbranched polyglycerols containing functional initiator-cores at the focal point, well-defined linear-hyperbranched block copolymers and also negatively charged hyperbranched polyelectrolytes.rnHyperbranched oligoglycerols (DPn = 7 and 14) have been synthesized for the first time. The materials show narrow polydispersity (Mw/Mn ca. 1.45) and a very low content in cyclic homopolymers. 13C NMR evidences the dendritic structure of the oligomers and the DB could be calculated (44% and 52%). These new oligoglycerols were compared with the industrial products obtained by polycondensation which exhibit narrow polydispersity (Mw/Mn<1.3) butrnmultimodal distribution in SEC. Detailed 13C NMR and Maldi-ToF studies reveal the presence of branched units and cyclic compounds. In comparison, the hyperbranched oligoglycerols comprise a very low proportion of cyclic homopolymer which render them very interesting materials for biomedical applications for example.rnThe site isolation of the core moiety in dendritic structure offers intriguing potential with respect to peculiar electro-optical properties. Various initiator-cores (n-alkyl amines, UVabsorbing amines and benzophenone) for the ROMBP of glycidol have been tested. The bisglycidolized amine initiator-cores show the best control over the molecular weight and the molecular weight distribution. The photochemical analyses of the naphthalene containingrnhyperbranched polyglycerols show a slight red shift, a pronounced hypochromic effect (decrease of the intensity of the band) compared with the parent model compound and the formation of a relative compact structure. The benzophenone containing polymers adopt an open structure in polar solvents. The fluorescence measurements show a clear “dendritic effect” on the fluorescence intensities and the quantum yield of the encapsulated benzophenone.rnA convenient 3-step strategy has been developed for the preparation of well-defined amphiphilic, linear-hyperbranched block copolymers via hypergrafting. The procedure represents a combination of carbanionic polymerization with the alkoxide-based, controlled ring-opening multibranching polymerization of glycidol. Materials consisting of a polystyrene linear block and a hyperbranched polyglycerol block exhibit narrow polydispersity (1.01-1.02rnfor 5.4% to 27% wt. PG and 1.74 for 52% wt. PG) with a high grafting efficiency. The strategy was also extended to materials with a linear polyisoprene block.rnDetailed investigations of the solution properties of the block copolymers with linear polystyrene blocks show that block copolymer micelles are stabilized by the highly branched block. The morphology of the aggregates is depending on the solvent: in chloroform monodisperse spherical shape aggregates and in toluene ellipsoidal aggregates are formed. On graphite these aggregates show interesting features, giving promising potential applications with respect to the presence of a very dense, functional and stable hyperbranched block.rnThe bulk morphology of the linear-hyperbranched block copolymers has been investigated. The materials with a linear polyisoprene block only behave like complex liquids due to the low Tg and the disordered nature of both components. For the materials with polystyrene, only the sample with 27% wt. hyperbranched polyglycerol forms some domains showing lamellae.rnThe preparation of hyperbranched polyelectrolytes was achieved by post-modification of the hydroxyl groups via Michael addition of acrylonitrile, followed by hydrolysis. In aqueous solution materials form large aggregates with size depending on the pH value. After deposition on mica the structures observed by AFM show the coexistence of aggregates andrnunimers. For the low molecular weight sample (PG 520 g·mol-1) extended and highly ordered terrace structures were observed. Materials were also successfully employed for the fabrication of composite organic-inorganic multilayer thin films, using electrostatic layer-bylayer self-assembly coupled with chemical vapor deposition.