Synthesis and characterization of metal-chalcogenide MQ 2-Nanoparticles (M = Mo, W, Zr; Q = S, O)

Here, we present the adaptation and optimization of (i) the solvothermal and (ii) the metal-organic chemical vapor deposition (MOCVD) approach as simple methods for the high-yield synthesis of MQ2 (M=Mo, W, Zr; Q = O, S) nanoparticles. Extensive characterization was carried out using X-ray diffraction (XRD), scanning and transmission electron micros¬copy (SEM/TEM) combined with energy dispersive X-ray analysis (EDXA), Raman spectroscopy, thermal analyses (DTA/TG), small angle X-ray scattering (SAXS) and BET measurements. After a general introduction to the state of the art, a simple route to nanostructured MoS2 based on the decomposition of the cluster-based precursor (NH4)2Mo3S13∙xH2O under solvothermal conditions (toluene, 653 K) is presented. Solvothermal decomposition results in nanostructured material that is distinct from the material obtained by decomposition of the same precursor in sealed quartz tubes at the same temperature. When carried out in the presence of the surfactant cetyltrimethyl¬ammonium bromide (CTAB), the decomposition product exhibits highly disordered MoS2 lamellae with high surface areas. The synthesis of WS2 onion-like nanoparticles by means of a single-step MOCVD process is discussed. Furthermore, the results of the successful transfer of the two-step MO¬CVD based synthesis of MoQ2 nanoparticles (Q = S, Se), comprising the formation of amorphous precursor particles and followed by the formation of fullerene-like particles in a subsequent annealing step to the W-S system, are presented. Based on a study of the temperature dependence of the reactions a set of conditions for the formation of onion-like structures in a one-step reaction could be derived. The MOCVD approach allows a selective synthesis of open and filled fullerene-like chalcogenide nanoparticles. An in situ heating stage transmission electron microscopy (TEM) study was employed to comparatively investigate the growth mechanism of MoS2 and WS2 nanoparticles obtained from MOCVD upon annealing. Round, mainly amorphous particles in the pristine sample trans¬form to hollow onion-like particles upon annealing. A significant difference between both compounds could be demonstrated in their crystallization conduct. Finally, the results of the in situ hea¬ting experiments are compared to those obtained from an ex situ annealing process under Ar. Eventually, a low temperature synthesis of monodisperse ZrO2 nanoparticles with diameters of ~ 8 nm is introduced. Whereas the solvent could be omitted, the synthesis in an autoclave is crucial for gaining nano-sized (n) ZrO2 by thermal decomposition of Zr(C2O4)2. The n-ZrO2 particles exhibits high specific surface areas (up to 385 m2/g) which make them promising candidates as catalysts and catalyst supports. Co-existence of m- and t-ZrO2 nano-particles of 6-9 nm in diameter, i.e. above the critical particle size of 6 nm, demonstrates that the particle size is not the only factor for stabilization of the t-ZrO2 modification at room temperature. In conclusion, synthesis within an autoclave (with and without solvent) and the MOCVD process could be successfully adapted to the synthesis of MoS2, WS2 and ZrO2 nanoparticles. A comparative in situ heating stage TEM study elucidated the growth mechanism of MoS2 and WS2 fullerene-like particles. As the general processes are similar, a transfer of this synthesis approach to other layered transition metal chalcogenide systems is to be expected. Application of the obtained nanomaterials as lubricants (MoS2, WS2) or as dental filling materials (ZrO2) is currently under investigation.

Kinetic modeling and experiments on gas uptake and chemical transformation of organic aerosol in the atmosphere

Aerosolpartikel beeinflussen das Klima durch Streuung und Absorption von Strahlung sowie als Nukleations-Kerne für Wolkentröpfchen und Eiskristalle. Darüber hinaus haben Aerosole einen starken Einfluss auf die Luftverschmutzung und die öffentliche Gesundheit. Gas-Partikel-Wechselwirkunge sind wichtige Prozesse, weil sie die physikalischen und chemischen Eigenschaften von Aerosolen wie Toxizität, Reaktivität, Hygroskopizität und optische Eigenschaften beeinflussen. Durch einen Mangel an experimentellen Daten und universellen Modellformalismen sind jedoch die Mechanismen und die Kinetik der Gasaufnahme und der chemischen Transformation organischer Aerosolpartikel unzureichend erfasst. Sowohl die chemische Transformation als auch die negativen gesundheitlichen Auswirkungen von toxischen und allergenen Aerosolpartikeln, wie Ruß, polyzyklische aromatische Kohlenwasserstoffe (PAK) und Proteine, sind bislang nicht gut verstanden.rn Kinetische Fluss-Modelle für Aerosoloberflächen- und Partikelbulk-Chemie wurden auf Basis des Pöschl-Rudich-Ammann-Formalismus für Gas-Partikel-Wechselwirkungen entwickelt. Zunächst wurde das kinetische Doppelschicht-Oberflächenmodell K2-SURF entwickelt, welches den Abbau von PAK auf Aerosolpartikeln in Gegenwart von Ozon, Stickstoffdioxid, Wasserdampf, Hydroxyl- und Nitrat-Radikalen beschreibt. Kompetitive Adsorption und chemische Transformation der Oberfläche führen zu einer stark nicht-linearen Abhängigkeit der Ozon-Aufnahme bezüglich Gaszusammensetzung. Unter atmosphärischen Bedingungen reicht die chemische Lebensdauer von PAK von wenigen Minuten auf Ruß, über mehrere Stunden auf organischen und anorganischen Feststoffen bis hin zu Tagen auf flüssigen Partikeln. rn Anschließend wurde das kinetische Mehrschichtenmodell KM-SUB entwickelt um die chemische Transformation organischer Aerosolpartikel zu beschreiben. KM-SUB ist in der Lage, Transportprozesse und chemische Reaktionen an der Oberfläche und im Bulk von Aerosol-partikeln explizit aufzulösen. Es erforder im Gegensatz zu früheren Modellen keine vereinfachenden Annahmen über stationäre Zustände und radiale Durchmischung. In Kombination mit Literaturdaten und neuen experimentellen Ergebnissen wurde KM-SUB eingesetzt, um die Effekte von Grenzflächen- und Bulk-Transportprozessen auf die Ozonolyse und Nitrierung von Protein-Makromolekülen, Ölsäure, und verwandten organischen Ver¬bin-dungen aufzuklären. Die in dieser Studie entwickelten kinetischen Modelle sollen als Basis für die Entwicklung eines detaillierten Mechanismus für Aerosolchemie dienen sowie für das Herleiten von vereinfachten, jedoch realistischen Parametrisierungen für großskalige globale Atmosphären- und Klima-Modelle. rn Die in dieser Studie durchgeführten Experimente und Modellrechnungen liefern Beweise für die Bildung langlebiger reaktiver Sauerstoff-Intermediate (ROI) in der heterogenen Reaktion von Ozon mit Aerosolpartikeln. Die chemische Lebensdauer dieser Zwischenformen beträgt mehr als 100 s, deutlich länger als die Oberflächen-Verweilzeit von molekularem O3 (~10-9 s). Die ROIs erklären scheinbare Diskrepanzen zwischen früheren quantenmechanischen Berechnungen und kinetischen Experimenten. Sie spielen eine Schlüsselrolle in der chemischen Transformation sowie in den negativen Gesundheitseffekten von toxischen und allergenen Feinstaubkomponenten, wie Ruß, PAK und Proteine. ROIs sind vermutlich auch an der Zersetzung von Ozon auf mineralischem Staub und an der Bildung sowie am Wachstum von sekundären organischen Aerosolen beteiligt. Darüber hinaus bilden ROIs eine Verbindung zwischen atmosphärischen und biosphärischen Mehrphasenprozessen (chemische und biologische Alterung).rn Organische Verbindungen können als amorpher Feststoff oder in einem halbfesten Zustand vorliegen, der die Geschwindigkeit von heterogenen Reaktionenen und Mehrphasenprozessen in Aerosolen beeinflusst. Strömungsrohr-Experimente zeigen, dass die Ozonaufnahme und die oxidative Alterung von amorphen Proteinen durch Bulk-Diffusion kinetisch limitiert sind. Die reaktive Gasaufnahme zeigt eine deutliche Zunahme mit zunehmender Luftfeuchte, was durch eine Verringerung der Viskosität zu erklären ist, bedingt durch einen Phasenübergang der amorphen organischen Matrix von einem glasartigen zu einem halbfesten Zustand (feuchtigkeitsinduzierter Phasenübergang). Die chemische Lebensdauer reaktiver Verbindungen in organischen Partikeln kann von Sekunden bis zu Tagen ansteigen, da die Diffusionsrate in der halbfesten Phase bei niedriger Temperatur oder geringer Luftfeuchte um Größenordnungen absinken kann. Die Ergebnisse dieser Studie zeigen wie halbfeste Phasen die Auswirkung organischeer Aerosole auf Luftqualität, Gesundheit und Klima beeinflussen können. rn

Chemical exfoliation of graphene and its application in organic electronics and energy storage devices

Graphene, the thinnest two-dimensional material possible, is considered as a realistic candidate for the numerous applications in electronic, energy storage and conversion devices due to its unique properties, such as high optical transmittance, high conductivity, excellent chemical and thermal stability. However, the electronic and chemical properties of graphene are highly dependent on their preparation methods. Therefore, the development of novel chemical exfoliation process which aims at high yield synthesis of high quality graphene while maintaining good solution processability is of great concern. This thesis focuses on the solution production of high-quality graphene by wet-chemical exfoliation methods and addresses the applications of the chemically exfoliated graphene in organic electronics and energy storage devices.rnPlatinum is the most commonly used catalysts for fuel cells but they suffered from sluggish electron transfer kinetics. On the other hand, heteroatom doped graphene is known to enhance not only electrical conductivity but also long term operation stability. In this regard, a simple synthetic method is developed for the nitrogen doped graphene (NG) preparation. Moreover, iron (Fe) can be incorporated into the synthetic process. As-prepared NG with and without Fe shows excellent catalytic activity and stability compared to that of Pt based catalysts.rnHigh electrical conductivity is one of the most important requirements for the application of graphene in electronic devices. Therefore, for the fabrication of electrically conductive graphene films, a novel methane plasma assisted reduction of GO is developed. The high electrical conductivity of plasma reduced GO films revealed an excellent electrochemical performance in terms of high power and energy densities when used as an electrode in the micro-supercapacitors.rnAlthough, GO can be prepared in bulk scale, large amount of defect density and low electrical conductivity are major drawbacks. To overcome the intrinsic limitation of poor quality of GO and/or reduced GO, a novel protocol is extablished for mass production of high-quality graphene by means of electrochemical exfoliation of graphite. The prepared graphene shows high electrical conductivity, low defect density and good solution processability. Furthermore, when used as electrodes in organic field-effect transistors and/or in supercapacitors, the electrochemically exfoliated graphene shows excellent device performances. The low cost and environment friendly production of such high-quality graphene is of great importance for future generation electronics and energy storage devices. rn

Unraveling efficiency-limiting processes in organic solar cells by ultrafast spectroscopy - impact of chemical structure and morphology on photophysics and efficiency

Diese Arbeit widmet sich der Untersuchung der photophysikalischen Prozesse, die in Mischungen von Elektronendonoren mit Elektronenakzeptoren zur Anwendung in organischen Solarzellen auftreten. Als Elektronendonoren werden das Copolymer PBDTTT-C, das aus Benzodithiophen- und Thienothiophene-Einheiten besteht, und das kleine Molekül p-DTS(FBTTh2)2, welches Silizium-überbrücktes Dithiophen, sowie fluoriertes Benzothiadiazol und Dithiophen beinhaltet, verwendet. Als Elektronenakzeptor finden ein planares 3,4:9,10-Perylentetracarbonsäurediimid-(PDI)-Derivat und verschiedene Fullerenderivate Anwendung. PDI-Derivate gelten als vielversprechende Alternativen zu Fullerenen aufgrund der durch chemische Synthese abstimmbaren strukturellen, optischen und elektronischen Eigenschaften. Das gewichtigste Argument für PDI-Derivate ist deren Absorption im sichtbaren Bereich des Sonnenspektrums was den Photostrom verbessern kann. Fulleren-basierte Mischungen übertreffen jedoch für gewöhnlich die Effizienz von Donor-PDI-Mischungen.rnUm den Nachteil der PDI-basierten Mischungen im Vergleich zu den entsprechenden Fulleren-basierten Mischungen zu identifizieren, werden die verschiedenen Donor-Akzeptor-Kombinationen auf ihre optischen, elektronischen und strukturellen Eigenschaften untersucht. Zeitaufgelöste Spektroskopie, vor allem transiente Absorptionsspektroskopie (TA), wird zur Analyse der Ladungsgeneration angewendet und der Vergleich der Donor-PDI Mischfilme mit den Donor-Fulleren Mischfilmen zeigt, dass die Bildung von Ladungstransferzuständen einen der Hauptverlustkanäle darstellt.rnWeiterhin werden Mischungen aus PBDTTT-C und [6,6]-Phenyl-C61-buttersäuremethylesther (PC61BM) mittels TA-Spektroskopie auf einer Zeitskala von ps bis µs untersucht und es kann gezeigt werden, dass der Triplettzustand des Polymers über die nicht-geminale Rekombination freier Ladungen auf einer sub-ns Zeitskala bevölkert wird. Hochentwickelte Methoden zur Datenanalyse, wie multivariate curve resolution (MCR), werden angewendet um überlagernde Datensignale zu trennen. Zusätzlich kann die Regeneration von Ladungsträgern durch Triplett-Triplett-Annihilation auf einer ns-µs Zeitskala gezeigt werden. Darüber hinaus wird der Einfluss des Lösungsmitteladditivs 1,8-Diiodooctan (DIO) auf die Leistungsfähigkeit von p-DTS(FBTTh2)2:PDI Solarzellen untersucht. Die Erkenntnisse von morphologischen und photophysikalischen Experimenten werden kombiniert, um die strukturellen Eigenschaften und die Photophysik mit den relevanten Kenngrößen des Bauteils in Verbindung zu setzen. Zeitaufgelöste Photolumineszenzmessungen (time-resolved photoluminescence, TRPL) zeigen, dass der Einsatz von DIO zu einer geringeren Reduzierung der Photolumineszenz führt, was auf eine größere Phasentrennung zurückgeführt werden kann. Außerdem kann mittels TA Spektroskopie gezeigt werden, dass die Verwendung von DIO zu einer verbesserten Kristallinität der aktiven Schicht führt und die Generation freier Ladungen fördert. Zur genauen Analyse des Signalzerfalls wird ein Modell angewendet, das den gleichzeitigen Zerfall gebundener CT-Zustände und freier Ladungen berücksichtigt und optimierte Donor-Akzeptor-Mischungen zeigen einen größeren Anteil an nicht-geminaler Rekombination freier Ladungsträger.rnIn einer weiteren Fallstudie wird der Einfluss des Fullerenderivats, namentlich IC60BA und PC71BM, auf die Leistungsfähigkeit und Photophysik der Solarzellen untersucht. Eine Kombination aus einer Untersuchung der Struktur des Dünnfilms sowie zeitaufgelöster Spektroskopie ergibt, dass Mischungen, die ICBA als Elektronenakzeptor verwenden, eine schlechtere Trennung von Ladungstransferzuständen zeigen und unter einer stärkeren geminalen Rekombination im Vergleich zu PCBM-basierten Mischungen leiden. Dies kann auf die kleinere Triebkraft zur Ladungstrennung sowie auf die höhere Unordnung der ICBA-basierten Mischungen, die die Ladungstrennung hemmen, zurückgeführt werden. Außerdem wird der Einfluss reiner Fullerendomänen auf die Funktionsfähigkeit organischer Solarzellen, die aus Mischungen des Thienothienophen-basierenden Polymers pBTTT-C14 und PC61BM bestehen, untersucht. Aus diesem Grund wird die Photophysik von Filmen mit einem Donor-Akzeptor-Mischungsverhältnis von 1:1 sowie 1:4 verglichen. Während 1:1-Mischungen lediglich eine co-kristalline Phase, in der Fullerene zwischen den Seitenketten von pBTTT interkalieren, zeigen, resultiert der Überschuss an Fulleren in den 1:4-Proben in der Ausbildung reiner Fullerendomänen zusätzlich zu der co kristallinen Phase. Transiente Absorptionsspektroskopie verdeutlicht, dass Ladungstransferzustände in 1:1-Mischungen hauptsächlich über geminale Rekombination zerfallen, während in 1:4 Mischungen ein beträchtlicher Anteil an Ladungen ihre wechselseitige Coulombanziehung überwinden und freie Ladungsträger bilden kann, die schließlich nicht-geminal rekombinieren.