Synthesis and characterization of metal-chalcogenide MQ 2-Nanoparticles (M = Mo, W, Zr; Q = S, O)

Here, we present the adaptation and optimization of (i) the solvothermal and (ii) the metal-organic chemical vapor deposition (MOCVD) approach as simple methods for the high-yield synthesis of MQ2 (M=Mo, W, Zr; Q = O, S) nanoparticles. Extensive characterization was carried out using X-ray diffraction (XRD), scanning and transmission electron micros¬copy (SEM/TEM) combined with energy dispersive X-ray analysis (EDXA), Raman spectroscopy, thermal analyses (DTA/TG), small angle X-ray scattering (SAXS) and BET measurements. After a general introduction to the state of the art, a simple route to nanostructured MoS2 based on the decomposition of the cluster-based precursor (NH4)2Mo3S13∙xH2O under solvothermal conditions (toluene, 653 K) is presented. Solvothermal decomposition results in nanostructured material that is distinct from the material obtained by decomposition of the same precursor in sealed quartz tubes at the same temperature. When carried out in the presence of the surfactant cetyltrimethyl¬ammonium bromide (CTAB), the decomposition product exhibits highly disordered MoS2 lamellae with high surface areas. The synthesis of WS2 onion-like nanoparticles by means of a single-step MOCVD process is discussed. Furthermore, the results of the successful transfer of the two-step MO¬CVD based synthesis of MoQ2 nanoparticles (Q = S, Se), comprising the formation of amorphous precursor particles and followed by the formation of fullerene-like particles in a subsequent annealing step to the W-S system, are presented. Based on a study of the temperature dependence of the reactions a set of conditions for the formation of onion-like structures in a one-step reaction could be derived. The MOCVD approach allows a selective synthesis of open and filled fullerene-like chalcogenide nanoparticles. An in situ heating stage transmission electron microscopy (TEM) study was employed to comparatively investigate the growth mechanism of MoS2 and WS2 nanoparticles obtained from MOCVD upon annealing. Round, mainly amorphous particles in the pristine sample trans¬form to hollow onion-like particles upon annealing. A significant difference between both compounds could be demonstrated in their crystallization conduct. Finally, the results of the in situ hea¬ting experiments are compared to those obtained from an ex situ annealing process under Ar. Eventually, a low temperature synthesis of monodisperse ZrO2 nanoparticles with diameters of ~ 8 nm is introduced. Whereas the solvent could be omitted, the synthesis in an autoclave is crucial for gaining nano-sized (n) ZrO2 by thermal decomposition of Zr(C2O4)2. The n-ZrO2 particles exhibits high specific surface areas (up to 385 m2/g) which make them promising candidates as catalysts and catalyst supports. Co-existence of m- and t-ZrO2 nano-particles of 6-9 nm in diameter, i.e. above the critical particle size of 6 nm, demonstrates that the particle size is not the only factor for stabilization of the t-ZrO2 modification at room temperature. In conclusion, synthesis within an autoclave (with and without solvent) and the MOCVD process could be successfully adapted to the synthesis of MoS2, WS2 and ZrO2 nanoparticles. A comparative in situ heating stage TEM study elucidated the growth mechanism of MoS2 and WS2 fullerene-like particles. As the general processes are similar, a transfer of this synthesis approach to other layered transition metal chalcogenide systems is to be expected. Application of the obtained nanomaterials as lubricants (MoS2, WS2) or as dental filling materials (ZrO2) is currently under investigation.

Ontogenetic studies on the determination of the apical meristem in racemose inflorescences

This thesis presents a comparative developmental study of inflorescences and focuses on the production of the terminal flower (TF). Morphometric attributes of inflorescence meristems (IM) were obtained throughout the ontogeny of inflorescence buds with the aim of describing possible spatial constraints that could explain the failure in developing the TF. The study exposes the inflorescence ontogeny of 20 species from five families of the Eudicots (Berberidaceae, Papaveraceae-Fumarioideae, Rosaceae, Campanulaceae and Apiaceae) in which 745 buds of open (i.e. without TF) and closed (i.e. with TF) inflorescences were observed under the scanning electron microscope.rnThe study shows that TFs appear on IMs which are 2,75 (se = 0,38) times larger than the youngest lateral reproductive primordium. The shape of these IMs is characterized by a leaf arc (phyllotactic attribute) of 91,84° (se = 7,32) and a meristematic elevation of 27,93° (se = 5,42). IMs of open inflorescences show a significant lower relative surface, averaging 1,09 (se=0,26) times the youngest primordium size, which suggests their incapacity for producing TFs. The relative lower size of open IMs is either a condition throughout the complete ontogeny (‘open I’) or a result from the drastic reduction of the meristematic surface after flower segregation (‘open II’). rnIt is concluded that a suitable bulge configuration of the IM is a prerequisite for TF formation. Observations in the TF-facultative species Daucus carota support this view, as the absence of the TF in certain umbellets is correlated with a reduction of their IM dimensions. A review of literature regarding histological development of IMs and genetic regulation of inflorescences suggests that in ‘open I’ inflorescences, the histological composition and molecular activity at the tip of the IM could impede the TF differentiation. On the other side, in ‘open II’ inflorescences, the small final IM bulge could represent a spatial constraint that hinders the differentiation of the TF. The existence of two distinct kinds of ontogenies of open inflorescences suggests two ways in which the loss of the TF could have occurred in the course of evolution.rn