Preparation and study of magnetic thin film based sub-micron structures

Due to its high Curie temperature of 420K and band structure calculations predicting 100% spin polarisation, Sr2FeMoO6 is a potential candidate for spintronic devices. However, the preparation of good quality thin films has proven to be a non-trivial task. Epitaxial Sr2FeMoO6 thin films were prepared by pulsed laser deposition on different substrates. Differing from previous reports a post-deposition annealing step at low oxygen partial pressure (10-5 mbar) was introduced and enabled the fabrication of reproducible, high quality samples. According to the structural properties of the substrates the crystal structure and morphology of the thin films are modified. The close interrelation between the structural, magnetic and electronic properties of Sr2FeMoO6 was studied. A detailed evaluation of the results allowed to extract valuable information on the microscopic nature of magnetism and charge transport. Smooth films with a mean roughness of about 2 nm have been achieved, which is a pre-requisite for a possible inclusion of this material in future devices. In order to establish device-oriented sub-micron patterning as a standard technique, electron beam lithography and focussed ion beam etching facilities have been put into operation. A detailed characterisation of these systems has been performed. To determine the technological prospects of new spintronics materials, the verification of a high spin polarisation is of vital interest. A popular technique for this task is point contact Andreev reflection (PCAR). Commonly, the charge transport in a transparent metal-superconductor contact of nanometer dimensions is attributed solely to coherent transport. If this condition is not fulfilled, inelastic processes in the constriction have to be considered. PCAR has been applied to Sr2FeMoO6 and the Heusler compound Co2Cr0.6Fe0.4Al. Systematic deviations between measured spectra and the standard models of PCAR have been observed. Therefore existing approaches have been generalised, in order to include the influence of heating. With the extended model the measured data was successfully reproduced but the analysis has revealed grave implications for the determination of spin polarisation, which was found to break down completely in certain cases.

Spectroscopic investigations of functional bulk and thin film Heusler alloys

Functional and smart materials have gained large scientific and practical interest in current research and development. The Heusler alloys form an important class of functional materials used in spintronics, thermoelectrics, and for shape memory alloy applications. An important aspect of functional materials is the adaptability of their physical properties. In this work functional polycrystalline bulk and epitaxial thin film Heusler alloys are characterized by means of spectroscopic investigation methods, X-ray magnetic circular dichroism (XMCD) and energy dispersive X-ray analysis (EDX). With EDX the homogeneity of the samples is studied extensively. For some cases of quaternary compounds, for example Co2(MnxTi1−x)Sn and Co2(Mn0.5Dy0.5)Sn, an interesting phase separation in two nearly pure ternary Heusler phases occurs. For these samples the phase separation leads to an improvement of thermoelectric properties. XMCD as the main investigation method was used to study Co2TiZ (Z = Si, Sn, and Sb), Co2(MnxTi1−x)Si, Co2(MnxTi1−x)Ge, Co2Mn(Ga1−xGex), Co2FeAl, Mn2VAl, and Ni2MnGa Heusler compounds. The element-specific magnetic moments are calculated. Also, the spin-resolved unoccupied density of states is determined, for example giving hints for half-metallic ferromagnetism for some Co-based compounds. The systematic change of the magnetic moments and the shift of the Fermi energy is a proof that Heusler alloys are suitable for a controlled tailoring of physical properties. The comparison of the experimental results with theoretical predictions improves the understanding of complex materials needed to optimize functional Heusler alloys.

Organic thin-film photovoltaics

Zusammenfassung Zur Verbesserung der Leistungsumwandlung in organischen Solarzellen sind neue Materialien von zentraler Bedeutung, die sämtliche Erfordernisse für organische Photovoltaik-Elemente erfüllen. In der vorliegenden Arbeit „Organic thin-film photovoltaics“ wurden im Hinblick auf ein besseres Verständnis der Zusammenhänge zwischen molekularer Struktur und der Leistungsfähigkeit neue Materialien in „bulk-heterojunction“ Solarzellen und in Festphasen-Farbstoffsensibilisierten Solarzellen untersucht. Durch die Anwendung selbstorganisierender Materialien, diskotischer Graphen-Derivate oder konjugierter Polymere in Verbindung mit entsprechenden Akzeptoren in den „bulk-heterojunction“ Solarzellen wurde gezeigt, dass mit einer Erhöhung der Ordnung durch thermische Behandlung eine verbesserte Leistung des Photovoltaik-Elements einhergeht. In den Festphasen-Farbstoffsensibilisierten Solarzellen wurden zwei neue Farbstoffe untersucht, und es konnte gezeigt werden, dass diese gute Leistung zeigten. Ferner ermöglicht das komplementäre Absorptionsvermögen der beiden Farbstoffe die Herstellung von Vollspektrum-Zellen.

Optimising thin-film solar cells by computer simulations

CIGS-Dünnschichtsolarzellen verbinden hohe Effizienz mit niedrigen Kosten und sind damit eine aussichtsreiche Photovoltaik-Technologie. Das Verständnis des Absorbermaterials CIGS ist allerdings noch lückenhaft und benötigt weitere Forschung. In dieser Dissertation werden Computersimulationen vorgestellt, die erheblich zum besseren Verständnis von CIGS beitragen. Es wurden die beiden Systeme Cu(In,Ga)Se2 und (Cu,In,Vac)Se betrachtet. Die Gesamtenergie der Systeme wurde in Clusterentwicklungen ausgedrückt, die auf der Basis von ab initio Dichtefunktionalrechnungen erstellt wurden. Damit war es möglich Monte Carlo (MC)-Simulationen durchzuführen. Kanonische MC-Simulationen von Cu(In,Ga)Se2 zeigen das temperaturabhängige Verhalten der In-Ga-Verteilung. In der Nähe der Raumtemperatur findet ein Übergang von einer geordneten zu einer ungeordneten Phase statt. Unterhalb separiert das System in CuInSe2 und CuGaSe2. Oberhalb existiert eine gemischte Phase mit inhomogen verteilten In- und Ga-Clustern. Mit steigender Temperatur verkleinern sich die Cluster und die Homogenität nimmt zu. Bei allen Temperaturen, bis hin zur Produktionstemperatur der Solarzellen (¼ 870 K), ist In-reiches CIGS homogener als Ga-reiches CIGS. Das (Cu,In,Vac)Se-System wurde mit kanonischen und großkanonischen MC-Simulationen untersucht. Hier findet sich für das CuIn5Se8-Teilsystem ein Übergang von einer geordneten zu einer ungeordneten Phase bei T0 = 279 K. Großkanonische Simulationen mit vorgegebenen Werten für die chemischen Potentiale von Cu und In wurden verwendet, um die Konzentrations- Landschaft und damit die sich ergebenden Stöchiometrien zu bestimmen. Stabilitätsbereiche wurden für stöchiometrisches CuInSe2 und für die Defektphasen CuIn5Se8 und CuIn3Se5 bei einer Temperatur von 174 K identifiziert. Die Bereiche für die Defektphasen sind bei T = 696 K verschwunden. Die Konzentrations-Landschaft reproduziert auch die leicht Cu-armen Stöchiometrien, die bei Solarzellen mit guten Effizienzen experimentell beobachtet werden. Die Simulationsergebnisse können verwendet werden, um den industriellen CIGS-Produktionspr

Magnetization dynamics in spin valves

Key technology applications like magnetoresistive sensors or the Magnetic Random Access Memory (MRAM) require reproducible magnetic switching mechanisms. i.e. predefined remanent states. At the same time advanced magnetic recording schemes push the magnetic switching time into the gyromagnetic regime. According to the Landau-Lifschitz-Gilbert formalism, relevant questions herein are associated with magnetic excitations (eigenmodes) and damping processes in confined magnetic thin film structures.rnObjects of study in this thesis are antiparallel pinned synthetic spin valves as they are extensively used as read heads in today’s magnetic storage devices. In such devices a ferromagnetic layer of high coercivity is stabilized via an exchange bias field by an antiferromagnet. A second hard magnetic layer, separated by a non-magnetic spacer of defined thickness, aligns antiparallel to the first. The orientation of the magnetization vector in the third ferromagnetic NiFe layer of low coercivity - the freelayer - is then sensed by the Giant MagnetoResistance (GMR) effect. This thesis reports results of element specific Time Resolved Photo-Emission Electron Microscopy (TR-PEEM) to image the magnetization dynamics of the free layer alone via X-ray Circular Dichroism (XMCD) at the Ni-L3 X-ray absorption edge.rnThe ferromagnetic systems, i.e. micron-sized spin valve stacks of typically deltaR/R = 15% and Permalloy single layers, were deposited onto the pulse leading centre stripe of coplanar wave guides, built in thin film wafer technology. The ferromagnetic platelets have been applied with varying geometry (rectangles, ellipses and squares), lateral dimension (in the range of several micrometers) and orientation to the magnetic field pulse to study the magnetization behaviour in dependence of these magnitudes. The observation of magnetic switching processes in the gigahertz range became only possible due to the joined effort of producing ultra-short X-ray pulses at the synchrotron source BESSY II (operated in the so-called low-alpha mode) and optimizing the wave guide design of the samples for high frequency electromagnetic excitation (FWHM typically several 100 ps). Space and time resolution of the experiment could be reduced to d = 100 nm and deltat = 15 ps, respectively.rnIn conclusion, it could be shown that the magnetization dynamics of the free layer of a synthetic GMR spin valve stack deviates significantly from a simple phase coherent rotation. In fact, the dynamic response of the free layer is a superposition of an averaged critically damped precessional motion and localized higher order spin wave modes. In a square platelet a standing spin wave with a period of 600 ps (1.7 GHz) was observed. At a first glance, the damping coefficient was found to be independent of the shape of the spin-valve element, thus favouring the model of homogeneous rotation and damping. Only by building the difference in the magnetic rotation between the central region and the outer rim of the platelet, the spin wave becomes visible. As they provide an additional efficient channel for energy dissipation, spin waves contribute to a higher effective damping coefficient (alpha = 0.01). Damping and magnetic switching behaviour in spin valves thus depend on the geometry of the element. Micromagnetic simulations reproduce the observed higher-order spin wave mode.rnBesides the short-run behaviour of the magnetization of spin valves Permalloy single layers with thicknesses ranging from 3 to 40 nm have been studied. The phase velocity of a spin wave in a 3 nm thick ellipse could be determined to 8.100 m/s. In a rectangular structure exhibiting a Landau-Lifschitz like domain pattern, the speed of the field pulse induced displacement of a 90°-Néel wall has been determined to 15.000 m/s.rn

Magnetic tunneling junctions with the Heusler compound Co 2 Cr 0.6 Fe 0.4 Al

Materialen mit sehr hoher Spinpolarisation werden für Anwendungen im Bereich der Spin-Elektronik benötigt. Deshalb werden große Forschungsanstrengungen zur Untersuchung der Eigenschaften von Verbindungen mit potentiell halbmetallischem Charakter, d. h.mit 100% Spinpolarisation, unternommen. In halbmetallischen Verbindungen, erwartet man eine Lücke in der Zustandsdichte an der Fermi Energie für Ladungsträger einer Spinrichtung, wahrend die Ladungsträger mit der anderen Spinrichtung sich metallisch verhalten. Eine Konsequenz davon ist, dass ein Strom, der durch solche Verbindung fließt, voll spinpolarisiert ist. Die hohe Curie-Temperatur Tc (800 K) und der theoretisch vorhergesagte halbmetallische Charakter machen Co2Cr0.6Fe0.4Al (CCFA) zu einem guten Kandidaten für Spintronik-Anwendungen wie magnetische Tunnelkontakte (MTJs = Magnetic Tunneling Junctions). In dieser Arbeit werden die Ergebnisse der Untersuchung der elektronischen und strukturellen Eigenschaften von dünnen CCFA Schichten dargestellt. Diese Schichten wurden in MTJs integriert und der Tunnel-Magnetowiderstands-Effekt untersucht. Hauptziele waren die Messung der Spinpolarisation und Untersuchungen der elektronischen Struktur von CCFA. Der Einfluss verschiedener Depositionsparameter auf die Eigenschaften der Schichten, speziell auf der Oberflächenordnung und damit letztlich auf den Tunnel-Magnetowiderstand (TMR), wurde bestimmt. Epitaktische d¨unne CCFA Schichten mit zwei verschiedenen Wachstumsrichtungen wurden auf verschiedene Substrate und Pufferschichten deponiert. Ein Temperverfahren wurde eingesetzt um die strukturelle Eigenschaften der dünnen Schichten zu verbessern. Für die MTJs wurde Al2O3 als Barrierenmaterial verwendet und Co als Gegenelektrode gewählt. Die Mehrschicht-Systeme wurden in Mesa-Geometrie mit lithographischen Methoden strukturiert. Eine maximal Jullière Spinpolarisation von 54% wurde an Tunnelkontakte mit epitaktischen CCFA Schichten gemessen. Ein starker Einfluss der Tempernbedingungen auf dem TMR wurde festgestellt. Eine Erhörung des TMR wurde mit einer Verbesserung der Oberflächenordung der CCFA Schichten korreliert. Spektroskopische Messungen wurden an den MTJs durchgeführt. Diesen Messungen liefern Hinweise auf inelastische Elektron-Magnon und Elektron-Phonon Stossprozesse an den Grenzflächen. Einige der beobachteten Strukturen konnten mit der berechneten elektronischen Struktur von CCFA korreliert worden.

Functional hydrogels: ferrogel thin films

Die Kombination magnetischer Nanopartikel (NP) mit temperatursensitiven Polymeren führt zur Bildung neuer Komposit-Materialien mit interessanten Eigenschaften, die auf vielfältige Weise genutzt werden können. Mögliche Anwendungsgebiete liegen in der magnetischen Trennung, der selektiven Freisetzung von Medikamenten, dem Aufbau von Sensoren und Aktuatoren. Als Polymerkomponente können z.B. Hydrogele dienen. Die Geschwindigkeit der Quellgradänderung mittels externer Stimuli kann durch eine Reduzierung des Hydrogelvolumens erhöht werden, da das Quellen ein diffusionskontrollierter Prozess ist. rnIm Rahmen dieser Arbeit wurde ein durch ultraviolettes Licht vernetzbares Hydrogel aus N-isopropylacrylamid, Methacrylsäure und dem Vernetzer 4-Benzoylphenylmethacrylat hergestellt (PNIPAAm-Hydrogel) und mit magnetischen Nanopartikeln aus Magnetit (Fe3O4) kombiniert. Dabei wurde die Temperatur- und die pH-Abhängigkeit des Quellgrades im Hinblick auf die Verwendung als nanomechanische Cantilever Sensoren (NCS) untersucht. Desweiteren erfolgte eine Charakterisierung durch Oberflächenplasmonen- und optischer Wellenleitermoden-Resonanz Spektroskopie (SPR/OWS). Die daraus erhaltenen Werte für den pKa-Wert und die lower critical solution Temperatur (LCST) stimmten mit den bekannten Literaturwerten überein. Es konnte gezeigt werden, dass eine stärkere Vernetzung zu einer geringeren LCST führt. Die Ergebnisse mittels NCS wiesen zudem auf einen skin-effect während des Heizens von höher vernetzten Polymeren hin.rnDie Magnetit Nanopartikel wurden ausgehend von Eisen(II)acetylacetonat über eine Hochtemperaturreaktion synthetisiert. Durch Variation der Reaktionstemperatur konnte die Größe der hergestellten Nanopartikel zwischen 3.5 und 20 nm mit einer Größenverteilung von 0.5-2.5 nm eingestellt werden. Durch geeignete Oberflächenfunktionalisierung konnten diese in Wasser stabilisiert werden. Dazu wurde nach zwei Strategien verfahren: Zum einen wurden die Nanopartikel mittels einer Silika-Schale funktionalisiert und zum anderen Zitronensäure als Tensid eingesetzt. Wasserstabilität ist vor allem für biologische Anwendungen wünschenswert. Die magnetischen Partikel wurden mit Hilfe von Transmissionselektronenmikroskopie (TEM), und superconductive quantum interference device (SQUID) charakterisiert. Dabei wurde eine Größenabhängigkeit der magnetischen Eigenschaften sowie superparamagnetisches Verhalten beobachtet. Außerdem wurde die Wärmeerzeugung der magnetischen Nanopartikel in einem AC Magnetfeld untersucht. rnDie Kombination beider Komponenten in Form eines Ferrogels wurde durch Mischen Benzophenon funktionalisierter magnetischer Nanopartikel mit Polymer erreicht. Durch Aufschleudern (Spin-Coaten) wurden dünne Filme erzeugt und diese im Hinblick auf ihr Verhalten in einem Magnetfeld untersucht. Dabei wurde eine geringes Plastikverhalten beobachtet. Die experimentellen Ergebnisse wurden anschließend mit theoretisch berechneten Erwartungswerten verglichen und mit den unterschiedlichen Werten für dreidimensionale Ferrogele in Zusammenhang gestellt. rn

Microstructure of epitaxial thin films of the ferromagnetic shape memory alloy Ni 2 MnGa

Gegenstand dieser Arbeit ist die Präparation und die ausführliche Charakterisierung epitaktischer Dünnschicht-Proben der Heusler Verbindung Ni2MnGa. Diese intermetallische Verbindung zeigt einen magnetischen Formgedächtnis-Effekt (MFG), der sowohl im Bezug auf mögliche Anwendungen, als auch im Kontext der Grundlagenforschung äußerst interessant ist. In Einkristallen nahe der Stöchiometrie Ni2MnGa wurden riesige magnetfeldinduzierte Dehnungen von bis zu 10 % nachgewiesen. Der zugrundeliegende Mechanismus basiert auf einer Umverteilung von kristallographischen Zwillings-Varianten, die eine tetragonale oder orthorhombische Symmetrie besitzen. Unter dem Einfluss des Magnetfeldes bewegen sich die Zwillingsgrenzen durch den Kristall, was eine makroskopische Formänderung mit sich bringt. Die somit erzeugten reversiblen Längenänderungen können mit hoher Frequenz geschaltet werden, was Ni2MnGa zu einem vielversprechenden Aktuatorwerkstoff macht. rnDa der Effekt auf einem intrinsischen Prozess beruht, eignen sich Bauteile aus MFG Legierungen zur Integration in Mikrosystemen (z.B. im Bereich der Mikrofluidik). rnrnBislang konnten große magnetfeldinduzierte Dehnungen nur für Einkristalle und Polykristalle mit hoher Porosität („foams") nachgewiesen werden. Um den Effekt für Anwendungen nutzbar zu machen, werden allerdings Konzepte zur Miniaturisierung benötigt. Eine Möglichkeit bieten epitaktische dünne Filme, die im Rahmen dieser Arbeit hergestellt und untersucht werden sollen. Im Fokus stehen dabei die Optimierung der Herstellungsparameter, sowie die Präparation von freitragenden Schichten. Zudem werden verschiedene Konzepte zur Herstellung freistehender Mikrostrukturen erprobt. Mittels Röntgendiffraktometrie konnte die komplizierte Kristallstruktur für verschiedene Wachstumsrichtungen verstanden und die genaue Verteilung der Zwillingsvarianten aufgedeckt werden. In Verbindung mit Mikroskopie-Methoden konnte so die Zwillingsstruktur auf verschiedenen Längenskalen geklärt werden. Die Ergebnisse erklären das Ausbleiben des MFG Effekts in den Proben mit (100) Orientierung. Andererseits wurde für Schichten mit (110) Wachstum eine vielversprechende Mikrostruktur entdeckt, die einen guten Ausgangspunkt für weitere Untersuchungen bietet.rnDurch die spezielle Geometrie der Proben war es möglich, Spektroskopie-Experimente in Transmission durchzuführen. Die Ergebnisse stellen den ersten experimentellen Nachweis der Änderungen in der elektronischen Struktur einer metallischen Verbindung während des martensitischen Phasenübergangs dar. Durch Messen des magnetischen Zirkulardichroismus in der Röntgenabsorption konnten quantitative Aussagen über die magnetischen Momente von Ni und Mn getroffen werden. Die Methode erlaubt überdies die Beiträge von Spin- und Bahn-Moment separat zu bestimmen. Durch winkelabhängige Messungen gelang es, die mikroskopische Ursache der magnetischen Anisotropie aufzuklären. Diese Ergebnisse tragen wesentlich zum Verständnis der komplexen magnetischen und strukturellen Eigenschaften von Ni2MnGa bei.rn