Vortex dynamics in the high-temperature superconductors YBa 2 Cu 3 O 7 and Bi 2 Sr 2 CaCu 2 O 8 + delta in low- and high-dissipative transport measurements

This thesis investigates phenomena of vortex dynamics in type II superconductors depending on the dimensionality of the flux-line system and the strength of the driving force. In the low dissipative regime of Bi_2Sr_2CaCu_2O_{8+delta} (BSCCO) the influence of oxygen stoichiometry on flux-line tension was examined. An entanglement crossover of the vortex system at low magnetic fields was identified and a comprehensive B-T phase diagram of solid and fluid phases derived.In YBa_2Cu_3O_7 (YBCO) extremely long (>100 mm) high-quality measurement bridges allowed to extend the electric-field window in transport measurements by up to three orders of magnitude. Complementing analyses of the data conclusively produced dynamic exponents of the glass transition z~9 considerably higher than theoretically predicted and previously reported. In high-dissipative measurements a voltage instability appearing in the current-voltage characteristics of type II superconductors was observed for the first time in BSCCO and shown to result from a Larkin-Ovchinnikov flux-flow vortex instability under the influence of quasi-particle heating. However, in an analogous investigation of YBCO the instability was found to appear only in the temperature and magnetic-field regime of the vortex-glass state. Rapid-pulse measurements fully confirmed this correlation of vortex glass and instability in YBCO and revealed a constant rise time (~µs).

Pinning-Effekte kolumnarer Schwerionenspuren in Kuprat-Supraleiter-Dünnschichten

In this work the flux line dynamics in High-Temperature Superconductor (HTSC) thin films in the presence of columnar defects was studied using electronic transport measurements. The columnar defects which are correlated pinning centers for vortices were generated by irradiation with swift heavy ions at the Gesellschaft für Schwerionenforschung (GSI) in Darmstadt. In the first part, the vortex dynamics is discussed within the framework of the Bose-glass model. This approach describes the continuous transition from a vortex liquid to a Bose-glass phase which is characterized by the localization of the flux lines at the columnar defects. The critical behavior of the characteristic length and time scales for temperatures in the vicinity of this phase transition were probed by scaling properties of experimentally obtained current-voltage characteristics. In contrast to the predicted universal properties of the critical behavior the scaling analysis shows a strong dependence of the dynamic critical exponent on the experimentally accessible electric field range. In addition, the predicted divergence of the activation energy in the limit of low current densities was experimentally not confirmed.The dynamic behavior of flux lines in spatially resolved irradiation geometries is reported in the second part. Weak pinning channels with widths between 10 µm and 100 µm were generated in a strong pinning environment with the use of metal masks and the GSI microprobe, respectively. Measurements of the anisotropic transport properties of these structures show a striking resemblance to the results in YBCO single crystals with unidirected twin boundaries which were interpreted as a guided vortex motion effect. The use of two additional test bridges allowed to determine in parallel the resistivities of the irradiated and unirradiated parts as well as the respective current-voltage characteristics. These measurements provided the input parameters for a numerical simulation of the potential distribution in the spatially resolved irradiation geometry. The results are interpreted within a model that describes the hydrodynamic interaction between a Bose-glass phase and a vortex liquid. The interface between weakly pinned flux lines in the unirradiated channels and strongly pinned vortices leads to a nonuniform vortex velocity profile and therefore a variation of the local electric field. The length scale of these interactions was estimated for the first time in measuring the local variation of the electric field profile in a Bose-glass contact.Finally, a method for the determination of the true temperature in HTSC thin films at high dissipation levels is described. In this regime of electronic transport the occurrence of a flux flow instability is accompanied by heating effects in the vortex system. The heat propagation properties of the film/substrate system are deduced from the time dependent voltage response to a short high current density pulse of rectangular shape. The influence of heavy ion irradiation on the heat resistance at the film/substrate interface is studied.

Functional hydrogels: ferrogel thin films

Die Kombination magnetischer Nanopartikel (NP) mit temperatursensitiven Polymeren führt zur Bildung neuer Komposit-Materialien mit interessanten Eigenschaften, die auf vielfältige Weise genutzt werden können. Mögliche Anwendungsgebiete liegen in der magnetischen Trennung, der selektiven Freisetzung von Medikamenten, dem Aufbau von Sensoren und Aktuatoren. Als Polymerkomponente können z.B. Hydrogele dienen. Die Geschwindigkeit der Quellgradänderung mittels externer Stimuli kann durch eine Reduzierung des Hydrogelvolumens erhöht werden, da das Quellen ein diffusionskontrollierter Prozess ist. rnIm Rahmen dieser Arbeit wurde ein durch ultraviolettes Licht vernetzbares Hydrogel aus N-isopropylacrylamid, Methacrylsäure und dem Vernetzer 4-Benzoylphenylmethacrylat hergestellt (PNIPAAm-Hydrogel) und mit magnetischen Nanopartikeln aus Magnetit (Fe3O4) kombiniert. Dabei wurde die Temperatur- und die pH-Abhängigkeit des Quellgrades im Hinblick auf die Verwendung als nanomechanische Cantilever Sensoren (NCS) untersucht. Desweiteren erfolgte eine Charakterisierung durch Oberflächenplasmonen- und optischer Wellenleitermoden-Resonanz Spektroskopie (SPR/OWS). Die daraus erhaltenen Werte für den pKa-Wert und die lower critical solution Temperatur (LCST) stimmten mit den bekannten Literaturwerten überein. Es konnte gezeigt werden, dass eine stärkere Vernetzung zu einer geringeren LCST führt. Die Ergebnisse mittels NCS wiesen zudem auf einen skin-effect während des Heizens von höher vernetzten Polymeren hin.rnDie Magnetit Nanopartikel wurden ausgehend von Eisen(II)acetylacetonat über eine Hochtemperaturreaktion synthetisiert. Durch Variation der Reaktionstemperatur konnte die Größe der hergestellten Nanopartikel zwischen 3.5 und 20 nm mit einer Größenverteilung von 0.5-2.5 nm eingestellt werden. Durch geeignete Oberflächenfunktionalisierung konnten diese in Wasser stabilisiert werden. Dazu wurde nach zwei Strategien verfahren: Zum einen wurden die Nanopartikel mittels einer Silika-Schale funktionalisiert und zum anderen Zitronensäure als Tensid eingesetzt. Wasserstabilität ist vor allem für biologische Anwendungen wünschenswert. Die magnetischen Partikel wurden mit Hilfe von Transmissionselektronenmikroskopie (TEM), und superconductive quantum interference device (SQUID) charakterisiert. Dabei wurde eine Größenabhängigkeit der magnetischen Eigenschaften sowie superparamagnetisches Verhalten beobachtet. Außerdem wurde die Wärmeerzeugung der magnetischen Nanopartikel in einem AC Magnetfeld untersucht. rnDie Kombination beider Komponenten in Form eines Ferrogels wurde durch Mischen Benzophenon funktionalisierter magnetischer Nanopartikel mit Polymer erreicht. Durch Aufschleudern (Spin-Coaten) wurden dünne Filme erzeugt und diese im Hinblick auf ihr Verhalten in einem Magnetfeld untersucht. Dabei wurde eine geringes Plastikverhalten beobachtet. Die experimentellen Ergebnisse wurden anschließend mit theoretisch berechneten Erwartungswerten verglichen und mit den unterschiedlichen Werten für dreidimensionale Ferrogele in Zusammenhang gestellt. rn