Synthese und Strukturierung von funktionalisierten Oligothiophenen

AbstractIn this thesis t-BOC and methacrylate functionalisedoligothiophenes with 3 – 5 thiophene units where synthesizedby Stille coupling. The material was structured by methodslike stamping and photolithography.The polymerizability of the methacrylates was proved by thepolymerization in solution with AIBN and subsequent analysisby gel permeation chromatography and differential scanningcalorimetry. The conductivities of the doped polymer filmswere in the range published for oligothiophenes.The optical and electrochemical properties of the compoundswere measured and compared to known compounds.The cleavage of the t-BOC groups was followed bythermogravimetry and infrared spectroscopy. The cleavagetemperature can be lowered by up to 100 °C by the use ofphoto acid generators. The cleavage is complete after 2hours annealing.The methacrylates were structured by microinjection mouldingin capillaries (MIMIC), stamping with soft silicone moulds,filling of patterned substrates and preperation of an opalreplica. By MIMIC line patterns with 5- 50 µm line widthswere obtained. The stamping succeeded in structures with 500nm line width only, on which liquid crystals wereorientated. This shows the possible application asorientation layers in LED’s with polarized emission. Withsilica opal templates the three-dimensional structuring ofthe oligomers succeeded.ZusammenfassungIn dieser Arbeit wurden neue funktionalisierteOligothiophene hergestellt und unter Anwendung verschiedenerVerfahren wie Stempeltechniken oder Photolithographiestrukturiert. Dazu wurden Oligothiophene mit drei bis fünfThiopheneinheiten durch Stille-Kupplung synthetisiert. Alsfunktionelle Gruppen wurden t-BOC-Ester undMethacrylsäureester eingeführt.Die Polymerisierbarkeit der Methacrylate wurde durch diePolymerisation mit AIBN in Lösung und anschließendeGelpermeationschromatographie und Differentialkalorimetrienachgewiesen. Die Leitfähigkeiten der dotierten Polymerfilmelagen im Bereich der für Oligothiophene bekannten Werte.Die optischen und elektrochemischen Eigenschaften derVerbindungen wurden untersucht und mit den Eigenschaftenbekannter Verbindungen verglichen. Die Abspaltung der t-BOC-Gruppen wurde thermogravimetrischund infrarotspektroskopisch verfolgt. Es wurde gezeigt, daßdie Abspaltungstemperatur durch den Zusatz einesPhotosäuregenerators um bis zu 100°C gesenkt wird und dieAbspaltung nach zweistündigem Tempern vollständig ist.Die methacrylatfunktionalisierten Verbindungen wurdenstrukturiert durch Micro Injection Moulding in Capillaries(MIMIC), Prägen mit weichen Silikonstempeln, Füllen vonstrukturierten Substraten und die Herstellung einerOpalreplika. Durch die Strukturierung mit MIMIC wurdenLinienstrukturen mit Linienbreiten von 5-50 µm erhalten.Durch Prägen wurden Strukturen mit Linienbreiten von nur 500nm erreicht, auf diesen gelang die Orientierung vonFlüssigkristallen. Dies zeigt die mögliche Anwendung alsOrientierungsschichten in Leuchtdioden mit polarisierterEmission. Durch die Verwendung von Siliziumoxidopalen alsTemplate gelang die dreidimensionale Strukturierung derOligomere.

Cellulose based Lithium ion polymer electrolytes for Lithium batteries

The separator membrane in batteries and fuel cells is of crucial importance for the function of these devices. In lithium ion batteries the separator membrane as well as the polymer matrix of the electrodes consists of polymer electrolytes which are lithium ion conductors. To overcome the disadvantage of currently used polymer electrolytes which are highly swollen with liquids and thus mechanically and electrochemically unstable, the goal of this work is a new generation of solid polymer electrolytes with a rigid backbone and a soft side chain structure. Moreover the novel material should be based on cheap substrates and its synthesis should not be complicated aiming at low overall costs. The new materials are based on hydroxypropylcellulose and oligoethyleneoxide derivatives as starting materials. The grafting of the oligoethyleneoxide side chains onto the cellulose was carried out following two synthetic methods. One is based on a bromide derivative and another based on p-toluolsulfonyl as a leaving group. The side chain reagents were prepared form tri(ethylene glycol) monoethyl ether. In order to improve the mechanical properties the materials were crosslinked. Two different conceptions have been engaged based on either urethane chemistry or photosensitive dimethyl-maleinimide derivatives. PEO - graft - cellulose derivatives with a high degree of substitution between 2,9 and 3,0 were blended with lithium trifluoromethane-sulfonate, lithium bis(trifluorosulfone)imide and lithium tetrafluoroborate. The molar ratios were in the range from 0,02 to 0,2 [Li]/[O]. The products have been characterized with nuclear magnetic resonance (NMR), gel permeation chromatography (GPC) and laserlight scattering (LS) with respect to their degree of substitution and molecular weight. The effect of salt concentration on ionic conductivity, thermal behaviour and morphology has been investiga-ted with impedance spectroscopy, differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA). The crosslinking reactions were controlled with dynamic mechanical analysis (DMS). The degree of substitution of our products is varying between 2,8 and 3,0 as determined by NMR. PEO - graft - cellulose derivatives are highly viscous liquids at room temperature with glass transition temperatures around 215 K. The glass transition temperature for the Lithium salt complexes of PEO - graft - cellulose deri-vatives increase with increasing salt content. The maximum conductivity at room temperature is about 10-4 and at 100°C around 10-3 Scm-1. The presence of lithium salt decreases the thermal stability of the complexes in comparison to pure PEO - graft - cellulose derivatives. Complexes heated over 140 – 150°C completely lose their ionic conductivity. The temperature dependence of the conductivity presented as Arrhenius-type plots for all samples is similar in shape and follows a VTF behaviour. This proofs that the ionic transport is closely related to the segmental motions of the polymer chains. Novel cellulose derivatives with grafted oligoethylen-oxide side chains with well-defined chemical structure and high side chain grafting density have been synthesized. Cellulose was chosen as stiff, rod like macromolecule for the backbone while oligoethylen-oxides are chosen as flexible side chains. A maximum grafting density of 3.0 have been obtained. The best conductivity reaches 10-3 Scm-1 at 100°C for a Li-triflate salt complex with a [Li]/[O] ratio of 0.8. The cross-linked complexes containing the lithium salts form elastomeric films with convenient mechanical stability. Our method of cellulose modification is based on relatively cheap and commercially available substrates and as such appears to be a promising alternative for industrial applications.

Monitoring kinetic processes in polymeric colloids by fluorescence correlation spectroscopy

Polymerbasierte Kolloide mit Groen im Nanometerbereich werden als aussichts- reiche Kandidaten fur die Verkapselung und den Transport von pharmazeutischen Wirkstoen angesehen. Daher ist es wichtig die physikalischen Prozesse, die die Bil- dung, Struktur und kinetische Stabilitat der polymerbasierten Kolloide beein ussen, besser zu verstehen. Allerdings ist die Untersuchung dieser Prozesse fur nanome- tergroe Objekte kompliziert und erfordert fortgeschrittene Techniken. In dieser Arbeit beschreibe ich Untersuchungen, bei denen Zwei-Farben-Fluoreszenzkreuz- korrelationsspektroskopie (DC FCCS) genutzt wurde, um Informationen uber die Wechselwirkung und den Austausch von dispergierten, nanometergroen Kolloiden zu bekommen. Zunachst habe ich den Prozess der Polymernanopartikelherstellung aus Emul- sionstropfen untersucht, welcher einen der am haugsten angewendeten Prozesse der Nanopartikelformulierung darstellt. Ich konnte zeigen, dass mit DC FCCS eindeutig und direkt Koaleszenz zwischen Emulsionstropfen gemessen werden kann. Dies ist von Interesse, da Koaleszenz als Hauptgrund fur die breite Groenverteilung der nalen Nanopartikel angesehen wird. Weiterhin habe ich den Austausch von Mizellen bildenden Molekulen zwischen amphiphilen Diblock Kopolymermizellen untersucht. Als Modellsystem diente ein Linear-Burste Block Kopolymer, welches Mizellen mit einer dichten und kurzen Korona bildet. Mit Hilfe von DC FCCS konnte der Austausch in verschiedenen Losungsmitteln und bei verschiedenen Temperaturen beobachtet werden. Ich habe herausgefunden, dass in Abhangigkeit der Qualitat des Losungsmittels die Zeit des Austausches um Groenordnungen verschoben werden kann, was eine weitreichende Einstellung der Austauschkinetik ermoglicht. Eine Eigenschaft die all diese Kolloide gemeinsam haben ist ihre Polydispersitat. Im letzten Teil meiner Arbeit habe ich am Beispiel von Polymeren als Modellsystem untersucht, welchen Eekt Polydispersitat und die Art der Fluoreszenzmarkierung auf FCS Experimente haben. Eine Anpassung des klassischen FCS Modells kann die FCS Korrelationskurven dieser Systeme beschreiben. Die Richtigkeit meines Ansatzes habe ich mit dem Vergleich zur Gel-Permeations-Chromatographie und Brownschen Molekulardynamiksimulationen bestatigt.

Biochemische Untersuchungen des Lichtsammlerprotein (LHCP) im Komplex mit seinem Chaperon, dem plastidären Signalerkennungspartikel cpSRP

Das Lichtsammlerprotein (light harvesting chlorophyll a/b-binding protein, LHCP) ist das Apoprotein des Haupt-Lichtsammelkomplexes (LHCII) und stellt das häufigste Membranprotein der Erde dar. Nicht nur aufgrund seiner Abundanz, sondern auch wegen seiner speziellen Translokation als stark hydrophobes Membranprotein durch hauptsächlich wässrige Milieus von cytosolischen Ribosomen bis in die Thylakoidmembran der Chloroplasten ist der Biogeneseweg dieses Proteins von besonderem Interesse. LHCP ist kernkodiert und wird nach seinem Import in Chloroplasten als Transitkomplex mit dem stromalen Signalerkennungsprotein (cpSRP) zur Thylakoide geleitet. Der cpSRP-Komplex besteht aus dem cpSRP43 mit Chaperonfunktion für das LHCP sowie dem Co-Chaperon cpSRP54, welches eine entscheidende Rolle in der stromalen Zielführung des Transitkomplexes spielt. Sowohl die Proteinkonformation des LHCP während seiner Biogenese als auch der in vivo Faltungsablauf während der Thylakoidinsertion sind noch völlig unklar. Mithilfe der Elektronen-paramagnetischen Resonanz (EPR-)Spektroskopie sollte in dieser Arbeit der Faltungszustand des LHCP im Transitkomplex mit dem cpSRP oder in Teilkomplexen davon ermittelt werden.rnKopplungen von cpSRP43 und LHCP bestätigten, dass das Chaperon als Minimaleinheit zur quantitativen Solubilisierung des Membranproteins genügt. Gelfiltrationschromatographische (GFC-) Untersuchungen solcher Komplexe wiesen jedoch mit einem apparenten MW von ≥ 600 kDa ein sehr hochmolekulares Laufverhalten auf. Variierende Proteinstöchiometrien im Komplex zeigten in densitometrischen Auswertungen eine undefinierte Aggregation. Zusätze von Agenzien zur Vermeidung unspezifischer Wechselwirkungen wie z.B. Detergentien oder auch Salzzugabe zeigten keinen Einfluss auf die Aggregate. Volllängen-Transitkomplexe dagegen wiesen trotz unterschiedlichem Angebot von Einzelproteinen reproduzierbar definierte Stöchiometrien auf. Diese zeigten eine LHCP:cpSRP43-Stöchiometrie von 1,25. Dennoch hatten diese Komplexe mit einem apparenten MW von > 300 kDa einen mindestens dimeren Assemblierungsgrad. Eine Voraussetzung für eindeutige EPR-spektroskopische Distanzmessungen zwischen definierten Positionen im LHCP ist jedoch dessen monomolekularisiertes Vorliegen im Chaperonkomplex. Die Darstellung von ternären Transitkomplexen mit einem zu erwartenden apparenten MW von ~175 kDa war auch durch Zusatz verschiedener Proteinaggregationshemmer nicht möglich. Transitkomplexe mit einer verkürzten Version des cpSRP54 zeigten schließlich eine definierte 1:1-Komplexstöchiometrie bei gleichzeitiger polydisperser Komplexzusammensetzung. Es konnten ~60% dieser sogenannten 54M-Transitkomplexe nach GFC-Daten und densitometrischer Auswertung als potentiell ternär eingeschätzt werden. Darüber hinaus gelang es solche Ansätze durch GFC-Fraktionierung zusätzlich von oligomerisierten Spezies aufzureinigen. Dennoch zeigten die Präparate vor GFC-Fraktionierung ein (noch) zu hohes Aggregationssignal im Hintergrund und nach Fraktionierung ein zu schwaches Signal, um eine eindeutige Aussage der EPR-Daten zuzulassen. Dennoch bietet dieses ausgearbeitete Komplexbildungsprotoll in Verbindung mit der Verwendung von verkürztem cpSRP54 eine solide Basis, um weitere Versuche zu EPR-Messungen an cpSRP-gebundenem LHCP durchzuführen. rn