Polymer nanoparticles : their functionalization for biomedical applications and dynamics near an electrode

In this work, a method for the functionalization of biocompatible, poly(lactic acid)-based nanoparticles with charged moieties or fluorescent labels is presented. Therefore, a miniemulsion solvent evaporation procedure is used in which prepolymerized poly(L-lactic acid) is used together with a previously synthesized copolymer of methacrylic acid or a polymerizable dye, respectively, and an oligo(lactic acid) macromonomer. Alternatively, the copolymerization has been carried out in one step with the miniemulsion solvent evaporation. The increased stability in salty solutions of the carboxyl-modified nanoparticles compared to nanoparticles consisting of poly(lactic acid) only has been shown in light scattering experiments. The properties of the nanoparticles that were prepared with the separately synthesized copolymer were almost identical to those in which the copolymerization and particle fabrication were carried out simultaneously. During the characterization of the fluorescently labeled nanoparticles, the focus was on the stable bonding between the fluorescent dye and the rest of the polymer chain to ensure that none of it is released from the particles, even after longer storage time or during lengthy experiments. In a fluorescence correlation spectroscopy experiment, it could be shown that even after two weeks, no dye has been released into the solvent. Besides biomedical research for which the above described, functionalized nanoparticles were optimized, nanoparticles also play a role in coating technology. One possibility to fabricate coatings is the electrophoretic deposition of particles. In this process, the mobility of nanoparticles near electrode interfaces plays a crucial role. In this thesis, the nanoparticle mobility has been investigated with resonance enhanced dynamic light scattering (REDLS). A new setup has been developed in which the evanescent electromagnetic eld of a surface plasmon that propagates along the gold-sample interface has been used as incident beam for the dynamic light scattering experiment. The gold layer that is necessary for the excitation of the plasmon doubles as an electrode. Due to the penetration depth of the surface plasmon into the sample layer that is limited to ca. 200 nm, insights on the voltage- and frequency dependent mobility of the nanoparticles near the electrode could be gained. Additionally, simultaneous measurements at four different scattering angles can be carried out with this setup, therefore the investigation of samples undergoing changes is feasible. The results were discussed in context with the mechanisms of electrophoretic deposition.

An alternative blocking layer for titanium dioxide (TiO 2) solar cell applications

In hybrid organic solar cells a blocking layer between transparent electrode and nanocrystalline titania particles is essential to prevent short-circuiting and current loss through recombination at the electrode interface. Here the preparation of a uniform hybrid blocking layer which is composed of conducting titania nanoparticles embedded in an insulating polymer derived ceramic is presented. This blocking layer is prepared by sol-gel chemistry where an amphiphilic block copolymer is used as a templating agent. A novel poly(dimethylsiloxane) containing amphiphilic block copolymer poly(ethyleneglycol)methylethermethacrylate-block-poly(dimethylsiloxane)-block-poly(ethyleneglycol)methylethermethacrylate has been synthesized to act as the templating agent. Plasma treatment uncovered titania surface from any polymer. Annealing at 450°C under nitrogen resulted in anatase titania with polymer derived silicon oxycarbide ceramic. Electrical characterization by conductive scanning probe microscopy experiments revealed a percolating titania network separated by an insulating ceramic matrix. Scanning Kelvin probe force microscopy showed predominant presence of titania particles on the surface creating a large surface area for dye absorption. The uniformity of the percolating structures was proven by microbeam grazing incidence small angle x-ray scattering. First applications in hybrid organic solar cells in comparison with conventional titanium dioxide blocking layer containing devices revealed 15 fold increases in corresponding efficiencies. Poly(dimethylsiloxane)-block-poly(ethyleneglycol)methylethermethacrylate and poly(ethyleneoxide)-poly(dimethylsiloxane)methylmethacrylate diblock copolymers were also synthesized. Their titania nanocomposite films were compared with the integrated blocking layer. Liner poly(ethyleneoxide) containing diblock copolymer resulted in highly ordered foam like structures. The effect of heating temperature rise to 600°C and 1000°C on titania morphology was investigated by scanning electron and force microscopy and x-ray scattering. Sol-gel contents, hydrochloric acid, titania precursor and amphiphilic triblock copolymer were altered to see their effect on titania morphology. Increase in block copolymer content resulted in titania particles of diameter 15-20 nm.

Molecular plating of thin lanthanide layers with improved material properties for nuclear applications

In der vorliegenden Arbeit werden Experimente beschrieben, die zu einem vertieften Verständnis fundamentaler Prozesse bei der elektrochemischen Herstellung von Dünnschichten, sog. Targets, für kernphysikalische und -chemische Studien führten. Targets wurden mittels 'Molecular Plating' (MP) hergestellt, indem eine Elektrodeposition aus organischem Medium in der Regel bei konstantem Strom in Zwei-Elektroden-Zellen. Die Resultate erlaubten, optimierte Herstellungs-bedingungen zu ermitteln, welche die Produktion deutlich verbesserter Targets erlaubten. MP bei konstantem Strom ist ein massentransportkontrollierter Prozess. Der angelegte Strom wird durch einen konstanten Fluss elektroaktiver Spezies zur Kathode – auf der die Schicht wächst – und Anode aufrechterhalten. Die Untersuchungen zeigten, dass das Zellenpotential des Elektrodepositionsystems immer durch den Ohm'schen Spannungsabfall auf Grund des Widerstandes der verwendeten Lösung dominiert wurde. Dies erlaubte die Herleitung einer Beziehung zwischen dem Zellenpotential und der Konzentration der elektroaktiven Spezies. Die Beziehung erlaubt die Erklärung des gemessenen zeitlichen Verlaufs des Zellenpotentials während der Abscheidung als Funktion der Elektrolytkonzentration. Dies dient als Basis, auf der nun ein umfassenderes Bild der Prozesse, die für die charakteristischen Minima im Potentialverlauf einer Abscheidung verantwortlich sind, gewonnen werden kann. Es konnte gezeigt werden, dass die Minima mit der fast vollständigen Entfernung (durch Abscheidung) der aus einem gelösten Salz erzeugten Nd-Ionen korrespondieren. Die abgeschiedene Spezies wurde als Nd3+ identifiziert, vermutlich als Carboxylat, Oxid oder Hydroxid, was auf Grund der hohen negative Werte des Standardredoxpotentials der Lanthanide verständlich erscheint. Von den vorliegenden elektroaktiven Spezies tragen die Nd3+ Ionen nur zu knapp 20% zum Gesamtstrom bei. Durch Elektrolyse tragen auch die Lösungsmittelkomponenten zu diese Strom bei. Die Gegenwart von elektrolysiertem Lösungsmittel wurde in Analysen der Dünnschichten bestätigt. Diese waren immer mit chemi- und physisorbierten Lösungsmittelmolekülen bedeckt. Die Analyse der Dünnschichten zeigte, dass die Oberflächen von einem furchenartiges Netz durchzogen waren, und dass diese während des Trocknen der Schichten nach dem MP entstanden. Ob die Schichten an Luft oder in inerter Atmosphäre trockneten, hatte keinen Einfluss. Es wurden Experimente mit mehreren Lösungsmitteln durchgeführt, die sich deutlich in ihren physikalischen Eigenschaften, v.a. dem Siedepunkt, unterschieden. Furchenfreie Dünnschichten konnten insbesondere bei MP in N,N-dimethylformamide (DMF) erzeugt werden. Die Verwendung von DMF in Kombination mit einer Abscheidung auf sehr glatten Substraten erlaubte die Produktion von sehr homogenen, glatten und defektfreien Schichten. Diese waren vermutlich geringeren inneren Spannungen während des Trocknens ausgesetzt, als Schichten auf raueren Substraten oder solche, die aus flüchtigeren Lösungsmitteln hergestellt wurden. Die Oberflächenrauigkeit des Substrats und das gewählte Lösungsmittel wurden so als Schlüsselfaktoren für die Produktion hochqualitativer Schichten identifiziert. Es konnte gezeigt werden, dass mit MP eine sehr effiziente Methode zur Herstellung homogener Schichten mit exzellenter Ausbeute ist. In weiteren Experimenten mit dem primordialen Alpha-Emitter 147Sm als Modellisotop wurde die Eignung solcher Schichten als Alpha-Quelle untersucht. Sowohl die Energieauflösung als auch der Anteil der Alpha-Teilchen, die den Detektor erreichten, waren von den Quelleneigenschaften abhängig. Die Effekte wurden verschiedenen Variablen der Dünnschicht zugeordnet, welche die Alpha-Spektren beeinflussten. Dominant war die Wahl des Lösungsmittels und die Rauigkeit des Substrats. Dies beeinflusste Schichtdicke und -morphologie sowie die Art des Schichtwachstums und veränderte die Detektionseffizienz in Alpha-Messungen bis zu 15%. Nur homogene, ebene Schichten, die aus DMF auf glatten Substraten abgeschieden wurden, eignen sich optimal als Alpha-Quelle. Die gewonnenen Ergebnisse erlauben die optimierte Herstellung nuklearer Targets durch MP. Künftige Anwendungen beinhalten insbesondere die Herstellung von Targets für neutroneninduzierte Spaltexperimente und untergrundarmeAlpha-Messungen sehr kleiner Aktivitäten.