Inverse size exclusion chromatography (ISEC)

In this work, an improved protocol for inverse size-exclusion chromatography (ISEC) was established to assess important pore structural data of porous silicas as stationary phases in packed chromatographic columns. After the validity of the values generated by ISEC was checked by comparison with data obtained from traditional methods like nitrogen sorption at 77 K (Study A), the method could be successfully employed as valuable tool at the development of bonded poly(methacrylate)-coated silicas, while traditional methods generate partially incorrect pore structural information (Study B). Study A: Different mesoporous silicas were converted by a pseudomorphical transition into ordered MCM-41-type silica while maintaining the particle-size and -shape. The essential parameters like specific surface area, average pore diameter and specific pore volume, the pore connectivity from ISEC remained nearly the same which was reflected by the same course of the theoretical plate height vs. linear velocity curves. Study B: In the development of bonded poly(methacrylate)-coated silicas for the reversed phase separation of biopolymers, ISEC was the only method to generate valid pore structural information of the polymer-coated materials. Synthesis procedures were developed to obtain reproducibly covalently bonded poly(methacrylate) coatings with good thermal stability on different base materials, employing as well particulate and monolithic materials.

Self assembled monolayers for engineering of structured inorganic materials in the micrometer and submicrometer range

Deutsch:In der vorliegenden Arbeit konnten neue Methoden zur Synthese anorganischer Materialien mit neuartiger Architektur im Mikrometer und Nanometer Maßstab beschrieben werden. Die zentrale Rolle der Formgebung basiert dabei auf der templatinduzierten Abscheidung der anorganischen Materialien auf selbstorganisierten Monoschichten. Als Substrate eignen sich goldbedampfte Glasträger und Goldkolloide, die eine Mittelstellung in der Welt der Atome bzw. Moleküle und der makroskopischen Welt der ausgedehnten Festkörper einnehmen. Auf diesen Substraten lassen sich Thiole zu einer monomolekularen Schicht adsorbieren und damit die Oberflächeneigenschaften des Substrates ändern. Ein besonderer Schwerpunkt bei dieser Arbeit stellt die Synthese speziell auf die Bedürfnisse der jeweiligen Anwendung ausgerichteten Thiole dar.Im ersten Teil der Arbeit wurden goldbedampfte Glasoberflächen als Template verwendet. Die Abscheidung von Calciumcarbonat wurde in Abhängigkeit der Schichtdicke der adsorbierten Monolage untersucht. Aragonit, eine der drei Hauptphasen des Calciumcarbonat Systems, wurde auf polyaromatischen Amid - Oberflächen mit Schichtdicken von 5 - 400 nm Dicke unter milden Bedingung abgeschieden. Die einstellbaren Parameter waren dabei die Kettenlänge des Polymers, der w-Substituent, die Bindung an die Goldoberfläche über Verwendung verschiedener Aminothiole und die Kristallisationstemperatur. Die Schichtdickeneinstellung der Polymerfilme erfolgte hierbei über einen automatisierten Synthesezyklus.Titanoxid Filme konnten auf Oberflächen strukturiert werden. Dabei kam ein speziell synthetisiertes Thiol zum Einsatz, das die Funktionalität einer Styroleinheit an der Oberflächen Grenze als auch eine Möglichkeit zur späteren Entfernung von der Oberfläche in sich vereinte. Die PDMS Stempeltechnik erzeugte dabei Mikrostrukturen auf der Goldoberfläche im Bereich von 5 bis 10 µm, die ihrerseits über die Polymerisation und Abscheidung des Polymers in den Titanoxid Film überführt werden konnten. Drei dimensionale Strukturen wurden über Goldkolloid Template erhalten. Tetraethylenglykol konnte mit einer Thiolgruppe im Austausch zu einer Hydroxylgruppe monofunktionalisiert werden. Das erhaltene Molekül wurde auf kolloidalem Gold selbstorganisiert; es entstand dabei ein wasserlösliches Goldkolloid. Die Darstellung erfolgte dabei in einer Einphasenreaktion. Die so erhaltenen Goldkolloide wurden als Krstallisationstemplate für die drei dimensionale Abscheidung von Calciumcarbonat verwendet. Es zeigte sich, dass Glykol die Kristallisation bzw. den Habitus des krsitalls bei niedrigem pH Wert modifiziert. Bei erhöhtem pH Wert (pH = 12) jedoch agieren die Glykol belegten Goldkolloide als Template und führen zu sphärisch Aggregaten. Werden Goldkolloide langkettigen Dithiolen ausgesetzt, so führt dies zu einer Aggregation und Ausfällung der Kolloide aufgrund der Vernetzung mehrer Goldkolloide mit den Thiolgruppen der Alkyldithiole. Zur Vermeidung konnte in dieser Arbeit ein halbseitig geschütztes Dithiol synthetisiert werden, mit dessen Hilfe die Aggregation unterbunden werden konnte. Das nachfolgende Entschützten der Thiolfunktion führte zu Goldkolloiden, deren Oberfläche Thiol funktionalisiert werden konnte. Die thiolaktiven Goldkolloide fungierten als template für die Abscheidung von Bleisulfid aus organisch/wässriger Lösung. Die Funktionsweise der Schutzgruppe und die Entschützung konnte mittels Plasmonenresonanz Spektroskopie verdeutlicht werden. Titanoxid / Gold / Polystyrol Komposite in Röhrenform konnten synthetisiert werden. Dazu wurde ein menschliches Haar als biologisches Templat für die Formgebung gewählt.. Durch Bedampfung des Haares mit Gold, Assemblierung eines Stryrolmonomers, welches zusätzlich eine Thiolfunktionalität trug, Polymerisation auf der Oberfläche, Abscheidung des Titanoxid Films und anschließendem Auflösen des biologischen Templates konnte eine Röhrenstruktur im Mikrometer Bereich dargestellt werden. Goldkolloide fungierten in dieser Arbeit nicht nur als Kristallisationstemplate und Formgeber, auch sie selbst wurden dahingehend modifiziert, dass sie drahtförmige Agglormerate im Nanometerbereich ausbilden. Dazu wurden Template aus Siliziumdioxid benutzt. Zum einen konnten Nanoröhren aus amorphen SiO2 in einer Sol Gel Methode dargestellt werden, zum anderen bediente sich diese Arbeit biologischer Siliziumoxid Hohlnadeln aus marinen Schwämmen isoliert. Goldkolloide wurden in die Hohlstrukturen eingebettet und die Struktur durch Ausbildung von Kolloid - Thiol Netzwerken mittels Dithiol Zugabe gefestigt. Die Gold-Nanodrähte im Bereich von 100 bis 500 nm wurden durch Auflösen des SiO2 - Templates freigelegt.

Bioinspired fabrication of biosilica-based bone substitution materials

Until today, autogenic bone grafts from various donor regions represent the gold standard in the field of bone reconstruction, providing both osteoinductive and osteoconductive characteristics. However, due to low availability and a disequilibrium between supply and demand, the risk of disease transfer and morbidity, usually associated with autogeneic bone grafts, the development of biomimic materials with structural and chemical properties similar to those of natural bone have been extensively studied. So far,rnonly a few synthetic materials, so far, have met these criteria, displaying properties that allow an optimal bone reconstitution. Biosilica is formed enzymatically under physiological-relevant conditions (temperature and pH) via silicatein (silica protein), an enzyme that was isolated from siliceous sponges, cloned, and prepared in a recombinant way, retaining its catalytic activity. It is biocompatible, has some unique mechanical characteristics, and comprises significant osteoinductive activity.rnTo explore the application of biosilica in the fields of regenerative medicine,rnsilicatein was encapsulated, together with its substrate sodium metasilicate, into poly(D,L-lactide)/polyvinylpyrrolidone(PVP)-based microspheres, using w/o/wrnmethodology with solvent casting and termed Poly(D,L-lactide)-silicatein silicacontaining-microspheres [PLASSM]. Both silicatein encapsulation efficiency (40%) and catalytic activity retention upon polymer encapsulation were enhanced by addition of an essential pre-emulsifying step using PVP. Furthermore, the metabolic stability, cytoxicity as well as the kinetics of silicatein release from the PLASSM were studied under biomimetic conditions, using simulated body fluid. As a solid support for PLASSM, a polyvinylpyrrolidone/starch/Na2HPO4-based matrix (termed plastic-like filler matrix containing silicic acid [PMSA]) was developed and its chemical and physical properties determined. Moreover, due to the non-toxicity and bioinactivity of the PMSA, it is suggested that PMSA acts as osteoconductive material. Both components, PLASSM and PMSA, when added together, form arnbifunctional 2-component implant material, that is (i)non-toxic(biocompatible), (ii)moldable, (iii) self-hardening at a controlled and clinically suitable rate to allows a tight insertion into any bone defect (iv) biodegradable, (v)forms a porous material upon exposure to body biomimetic conditions, and (vi)displays both osteoinductive (silicatein)and osteoconductive (PMSA) properties.rnPreliminary in vivo experiments were carried out with rabbit femurs, by creatingrnartificial bone defects that were subsequently treated with the bifunctional 2-component implant material. After 9 weeks of implantation, both computed tomography (CT) and morphological analyses showed complete resorption of the implanted material, concurrent with complete bone regeneration. The given data can be considered as a significant contribution to the successful introduction of biosilica-based implants into the field of bone substitution surgery.

Inorganic-organic hybrid polymers: Solution-processible coating materials for defined surface functionalization

A new class of inorganic-organic hybrid polymers could successfully been prepared by the combination of different polymerization techniques. The access to a broad range of organic polymers incorporated into the hybrid polymer was realized using two independent approaches.rnIn the first approach a functional poly(silsesquioxane) (PSSQ) network was pre-formed, which was capable to initiate a controlled radical polymerization to graft organic vinyl-type monomers from the PSSQ precursor. As controlled radical polymerization techniques atom transfer radical polymerization (ATRP), as well as reversible addition fragmentation chain transfer (RAFT) polymerization could be used after defined tuning of the PSSQ precursor either toward a PSSQ macro-initiator or to a PSSQ macro-chain-transfer-agent. The polymerization pathway, consisting of polycondensation of trialkoxy-silanes followed by grafting-from polymerization of different monomers, allowed synthesis of various functional hybrid polymers. A controlled synthesis of the PSSQ precursors could successfully be performed using a microreactor setup; the molecular weight could be adjusted easily while the polydispersity index could be decreased well below 2.rnThe second approach aimed to incorporate differently derived organic polymers. As examples, polycarbonate and poly(ethylene glycol) were end-group-modified using trialkoxysilanes. After end-group-functionalization these organic polymers could be incorporated into a PSSQ network.rnThese different hybrid polymers showed extraordinary coating abilities. All polymers could be processed from solution by spin-coating or dip-coating. The high amount of reactive silanol moieties in the PSSQ part could be cross-linked after application by annealing at 130° for 1h. Not only cross-linking of the whole film was achieved, which resulted in mechanical interlocking with the substrate, also chemical bonds to metal or metal oxide surfaces were formed. All coating materials showed high stability and adhesion onto various underlying materials, reaching from metals (like steel or gold) and metal oxides (like glass) to plastics (like polycarbonate or polytetrafluoroethylene).rnAs the material and the synthetic pathway were very tolerant toward different functionalities, various functional monomers could be incorporated in the final coating material. The incorporation of N-isopropylacrylamide yielded in temperature-responsive surface coatings, whereas the incorporation of redox-active monomers allowed the preparation of semi-conductive coatings, capable to produce smooth hole-injection layers on transparent conductive electrodes used in optoelectronic devices.rnThe range of possible applications could be increased tremendously by incorporation of reactive monomers, capable to undergo fast and quantitative conversions by polymer-analogous reactions. For example, grafting active esters from a PSSQ precursor yielded a reactive surface coating after application onto numerous substrates. Just by dipping the coated substrate into a solution of a functionalized amine, the desired function could be immobilized at the interface as well as throughout the whole film. The obtained reactive surface coatings could be used as basis for different functional coatings for various applications. The conversion with specifically tuned amines yielded in surfaces with adjustable wetting behaviors, switchable wetting behaviors or as recognition element for surface-oriented bio-analytical devices. The combination of hybrid materials with orthogonal reactivities allowed for the first time the preparation of multi-reactive surfaces which could be functionalized sequentially with defined fractions of different groups at the interface. rnThe introduced concept to synthesis functional hybrid polymers unifies the main requirements on an ideal coating material. Strong adhesion on a wide range of underlying materials was achieved by secondary condensation of the PSSQ part, whereas the organic part allowed incorporation of various functionalities. Thus, a flexible platform to create functional and reactive surface coatings was achieved, which could be applied to different substrates. rn

Coating of surfaces of composite materials with enzymatically formed biosilica

Die Bildung kieselsäurehaltiger Spicula in marinen Schwämmen ist nur möglich durch die enzymatische Aktivität des Silicatein- in Verbindung mit der stöchiometrischen Selbstassemblierung des Enzyms mit anderen Schwammproteinen. Die vorliegende Arbeit basiert auf einem biomimetischen Ansatz mit dem Ziel, unterschiedliche Oberflächen für biotechnologische und biomedizinische Anwendungen mit Biosilica und Biotitania zu beschichten und zu funktionalisieren. Für biotechnologische Anwendungen ist dabei das Drucken von Cystein-getaggtem Silicatein auf Gold-Oberflächen von Bedeutung, denn es ermöglichte die Bildung definierter Biotitania-Strukturen (Anatas), welche als Photokatalysator den Abbau eines organischen Farbstoffs bewirkten. Des Weiteren zeigte sich die bio-inspirierte Modifikation von Tyrosin-Resten an rekombinantem Silicatein-(via Tyrosinase) als vielversprechendes Werkzeug zur Beschleunigung der Selbstassemblierung des Enzyms zu mesoskaligen Filamenten. Durch eine solche Modifikation konnte Silicatein auch auf der Oberfläche von anorganischen Partikeln immobilisiert werden, welches die Assemblierung von anorganisch-organischen Verbundwerkstoffen in wäßriger Umgebung förderte. Die resultierenden supramolekularen Strukturen könnten dabei in bio-inspirierten und biotechnologischen Anwendungen genutzt werden. Weiterhin wurde in der vorliegenden Arbeit die Sekundärstruktur von rekombinantem Silicatein- (Monomer und Oligomer) durch Raman Spektroskopie analysiert, nachdem das Protein gemäß einer neu etablierten Methode rückgefaltet worden war. Diese Spektraldaten zeigten insbesondere Änderungen der Proteinkonformation durch Solubilisierung und Oligomerisierung des Enzyms. Außerdem wurden die osteoinduzierenden und osteogenen Eigenschaften unterschiedlicher organischer Polymere, die herkömmlich als Knochenersatzmaterial genutzt werden, durch Oberflächenmodifikation mit Silicatein/Biosilica verbessert: Die bei der Kultivierung knochenbildender Zellen auf derart oberflächenbehandelten Materialien beobachtete verstärkte Biomineralisierung, Aktivierung der Alkalischen Phosphatase, und Ausbildung eines typischen zellulären Phänotyps verdeutlichen das Potential von Silicatein/Biosilica für der Herstellung neuartiger Implantat- und Knochenersatzmaterialien.

Multifunctional polyether architectures : versatile materials for surface attachment and functionalization

Chapter 1 of this thesis comprises a review of polyether polyamines, i.e., combinations of polyether scaffolds with polymers bearing multiple amino moieties. Focus is laid on controlled or living polymerization methods. Furthermore, fields in which the combination of cationic, complexing, and pH-sensitive properties of the polyamines and biocompatibility and water-solubility of polyethers promise enormous potential are presented. Applications include stimuli-responsive polymers with a lower critical solution temperature (LCST) and/or the ability to gel, preparation of shell cross-linked (SCL) micelles, gene transfection, and surface functionalization.rnIn Chapter 2, multiaminofunctional polyethers relying on the class of glycidyl amine comonomers for anionic ring-opening polymerization (AROP) are presented. In Chapter 2.1, N,N-diethyl glycidyl amine (DEGA) is introduced for copolymerization with ethylene oxide (EO). Copolymer microstructure is assessed using online 1H NMR kinetics, 13C NMR triad sequence analysis, and differential scanning calorimetry (DSC). The concurrent copolymerization of EO and DEGA is found to result in macromolecules with a gradient structure. The LCSTs of the resulting copolymers can be tailored by adjusting DEGA fraction or pH value of the environment. Quaternization of the amino moieties by methylation results in polyelectrolytes. Block copolymers are used for PEGylated gold nanoparticle formation. Chapter 2.2 deals with a glycidyl amine monomer with a removable protecting group at the amino moiety, for liberation of primary amines at the polyether backbone, which is N,N-diallyl glycidyl amine (DAGA). Its allyl groups are able to withstand the harsh basic conditions of AROP, but can be cleaved homogeneously after polymerization. Gradient as well as block copolymers poly(ethylene glycol)-PDAGA (PEG-PDAGA) are obtained. They are analyzed regarding their microstructure, LCST behavior, and cleavage of the protecting groups. rnChapter 3 describes applications of multi(amino)functional polyethers for functionalization of inorganic surfaces. In Chapter 3.1, they are combined with an acetal-protected catechol initiator, leading to well-defined PEG and heteromultifunctional PEG analogues. After deprotection, multifunctional PEG ligands capable of attaching to a variety of metal oxide surfaces are obtained. In a cooperative project with the Department of Inorganic and Analytical Chemistry, JGU Mainz, their potential is demonstrated on MnO nanoparticles, which are promising candidates as T1 contrast agents in magnetic resonance imaging. The MnO nanoparticles are solubilized in aqueous solution upon ligand exchange. In Chapter 3.2, a concept for passivation and functionalization of glass surfaces towards gold nanorods is developed. Quaternized mPEG-b-PqDEGA diblock copolymers are attached to negatively charged glass surfaces via the cationic PqDEGA blocks. The PEG blocks are able to suppress gold nanorod adsorption on the glass in the flow cell, analyzed by dark field microscopy.rnChapter 4 highlights a straightforward approach to poly(ethylene glycol) macrocycles. Starting from commercially available bishydroxy-PEG, cyclic polymers are available by perallylation and ring-closing metathesis in presence of Grubbs’ catalyst. Purification of cyclic PEG is carried out using α-cyclodextrin. This cyclic sugar derivative forms inclusion complexes with remaining unreacted linear PEG in aqueous solution. Simple filtration leads to pure macrocycles, as evidenced by SEC and MALDI-ToF mass spectrometry. Cyclic polymers from biocompatible precursors are interesting materials regarding their increased blood circulation time compared to their linear counterparts.rnIn the Appendix, A.1, a study of the temperature-dependent water-solubility of polyether copolymers is presented. Macroscopic cloud points, determined by turbidimetry, are compared with microscopic aggregation phenomena, monitored by continuous wave electron paramagnetic resonance (CW EPR) spectroscopy in presence of the amphiphilic spin probe and model drug (2,2,6,6-tetramethylpiperidin-1-yl)oxyl (TEMPO). These thermoresponsive polymers are promising candidates for molecular transport applications. The same techniques are applied in Chapter A.2 to explore the pH-dependence of the cloud points of PEG-PDEGA copolymers in further detail. It is shown that the introduction of amino moieties at the PEG backbone allows for precise manipulation of complex phase transition modes. In Chapter A.3, multi-hydroxyfunctional polysilanes are presented. They are obtained via copolymerization of the acetal-protected dichloro(isopropylidene glyceryl propyl ether)methylsilane monomer. The hydroxyl groups are liberated through acidic work-up, yielding versatile access to new multifunctional polysilanes.