DNA block copolymers – from micelles to machines

DNA block copolymer, a new class of hybrid material composed of a synthetic polymer and an oligodeoxynucleotide segment, owns unique properties which can not be achieved by only one of the two polymers. Among amphiphilic DNA block copolymers, DNA-b-polypropylene oxide (PPO) was chosen as a model system, because PPO is biocompatible and has a Tg < 0 °C. Both properties might be essential for future applications in living systems. During my PhD study, I focused on the properties and the structures of DNA-b-PPO molecules. First, DNA-b-PPO micelles were studied by scanning force microscopy (SFM) and fluorescence correlation spectroscopy (FCS). In order to control the size of micelles without re-synthesis, micelles were incubated with template-independent DNA polymerase TdT and deoxynucleotide triphosphates in reaction buffer solution. By carrying out ex-situ experiments, the growth of micelles was visualized by imaging in liquid with AFM. Complementary measurements with FCS and polyacrylamide gel electrophoresis (PAGE) confirmed the increase in size. Furthermore, the growing process was studied with AFM in-situ at 37 °C. Hereby the growth of individual micelles could be observed. In contrast to ex-situ reactions, the growth of micelles adsorbed on mica surface for in-situ experiments terminated about one hour after the reaction was initiated. Two reasons were identified for the termination: (i) block of catalytic sites by interaction with the substrate and (ii) reduced exchange of molecules between micelles and the liquid environment. In addition, a geometrical model for AFM imaging was developed which allowed deriving the average number of mononucleotides added to DNA-b-PPO molecules in dependence on the enzymatic reaction time (chapter 3). Second, a prototype of a macroscopic DNA machine made of DNA-b-PPO was investigated. As DNA-b-PPO molecules were amphiphilic, they could form a monolayer at the air-water interface. Using a Langmuir film balance, the energy released owing to DNA hybridization was converted into macroscopic movements of the barriers in the Langmuir trough. A specially adapted Langmuir trough was build to exchange the subphase without changing the water level significantly. Upon exchanging the subphase with complementary DNA containing buffer solution, an increase of lateral pressure was observed which could be attributed to hybridization of single stranded DNA-b-PPO. The pressure versus area/molecule isotherms were recorded before and after hybridization. I also carried out a series of control experiments, in order to identify the best conditions of realizing a DNA machine with DNA-b-PPO. To relate the lateral pressure with molecular structures, Langmuir Blodgett (LB) films were transferred to highly ordered pyrolytic graphite (HOPG) and mica substrates at different pressures. These films were then investigated with AFM (chapter 4). At last, this thesis includes studies of DNA and DNA block copolymer assemblies with AFM, which were performed in cooperation with different group of the Sonderforschungsbereich 625 “From Single Molecules to Nanoscopically Structured Materials”. AFM was proven to be an important method to confirm the formation of multiblock copolymers and DNA networks (chapter 5).

Synthesis and characterization of polymers containing oligothiophenes

In the present work a series of thiophene oligomers of three and six thiophene units were synthesized, starting from thiophene, and characterized. Polymers containing these electroative side groups were then prepared by two strategies. The oligomers were attached to existing polymer systems and were connected to a polymerizable unit leading to monomer containing the oligothiophenes as side groups. Subsequently the properties of the monomers and the polymers were investigated. A butylcellulose derivative carrying terthienyl side chains (BCTTE, 26) was synthesized starting from cellulose acetate and 5-(2-chloroethyl)-2,2':5',2'-terthiophene (4). The polymer had a degree of substitution (DS) of the butyl and terthienyl side chains of DSbutyl = 1.9 and DSterth = 0.35, respectively. It was successfully spread on a Langmuir-Blodgett (LB) trough and then transferred to several solid substrates. X-rays reflectometry showed an ordered architecture of the cellulose backbones. However, the terthiophene side groups were found as isotropically aligned by polarized UV-Vis spectroscopy. When used as anode material in the electropolymerization of 3-pentylthiophene (28), polythiophene was grafted onto the cellulose backbone through the terthienyl side groups. The polythiophene chains showed an average anisotropic alignment of 20 % along the LB dipping direction, calculated by means of polarized UV-Vis spectroscopy. A second butylcellulose derivative carrying sexithienyl side chains (BCST) was synthesized and investigated, starting from butylcellulose and 2-[b ', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2': 5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl p-toluensulfonate (7). The polymer showed formation of stable LB monolayers at the air-water interface, but its transfer onto solid substrates was not successful. A poly(p-phenylene-ethynylene) bearing sexithienyl side chains (BzAcST, 31) was prepared by reaction of the two monomers 2-[b ', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2': 5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl 2,5-diiodobenzoate (15) and 2-[b', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2':5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl 2,5-diethynylbenzoate (18). The polymer was obtained as insoluble product. Upon oxidation with FeCl3 (doping) of the polymer suspension, BzAcST showed an electrical conductivity of ó = 2.5 . 10 -6 S/cm, a typical value for semiconductors. The IR spectrum of the doped polymer presented the diagnostic bands of oxidized sexithiophene in good agreement with literature results. Along with the monomer and polymer synthesis, an a,a '-disubstituted sexithiophene, b ', b ''-dipentyl-5,5'''-bis-(2-hydroxyethyl)-2,2':5',2':5',2'':5'',2'':5'',2'''-sexithiophene (6a),was synthesized and characterized. The UV-Vis absorption of the chromophore wasinvestigated as a function of temperature and different solvents, showing a blue-shift of the absorption maximum with increasing temperature and a red-shift changing the solvent from hexane to ethanol to toluene. Monitoring the change of the UV-Vis spectrum upon electrochemical oxidation, the oxidized chromophore showed a new broad absorption band, red shifted with respect to the p -p* transition of the neutral state. Upon reduction, the new band disappeared and the UV-Vis spectrum of the chromophore was restored. Such oxidation-reduction cycles were totally reversible. This feature, together with the absorption maximum falling in the visible region, makes this chromophore a suitable compound for the development of an electrochemical sensor.Attempts to polymerize acrylic monomers carrying sexythienyl side chains both via radical polymerization, as in the case of 2-[b ', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2': 5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl acrylate (8), and anionic polymerization, as in the case of 2-{b ', b ''-dipentyl-5'''-[2-(tertbutyldimethylsiloxy)ethyl]-2,2':5',2':5',2'':5'',2'': 5'',2''' -sexithiophen-5-yl}-ethylacrylate (29), were not successful, probably due to the steric hindrance of the oligothiophene side group. However, due to the time consuming and therefore restricted availability of the monomers, a screening of the polymerization conditions towards the formation of polymeric material was not possible.