Structure and properties of composite polyolefin materials

This thesis is based on three main studies, all dealing with structure-property investigation of semicrystalline polyolefin-based composites. Low density poly(ethylene) (LDPE) and isotactic poly(propylene) (iPP) were chosen as parts of the composites materials and they were investigated either separately (as homoploymers), either in blend systems with the composition LDPE/iPP 80/20 or as filled matrix with layered silicate (montmorillonite). The beneficial influence of adding ethylene-co-propylene polymer of amorphous nature, to low density poly(ethylene)/isotactic poly(propylene) (80/20) blend is demonstrated. This effect is expressed by the major improvement of mechanical properties of ternary blends as examined at a macroscopic size scale by means of tensile measurements. The structure investigation also reveals a clear dependence of the morphology on adding ethylene-copropylene polymer. Both the nature and the content of ethylene-co-propylene polymer affect structure and properties. It is further demonstrated that the extent of improvement in mechanical properties is to be related to the molecular details of the compatibilizer. Combination of high molecular weight and high ethylene content is appropriate for the studied system where the poly(ethylene) plays the role of matrix. A new way to characterize semicrystalline systems by means of Brillouin spectroscopy is presented in this study. By this method based on inelastic light scattering, we were able to measure the high frequency elastic constant (c11) of the two microphases in the case where the spherulites size is exhibit size larger than the size of the probing phonon wavelength. In this considered case, the sample film is inhomogeneous over the relevant length scales and there is an access to the transverse phonon in the crystalline phase yielding the elastic constant c44 as well. Isotactic poly(propylene) is well suited for this type of investigation since its morphology can be tailored through different thermal treatment from the melt. Two distinctly different types of films were used; quenched (low crystallinity) and annealed (high crystallinity). The Brillouin scattering data are discussed with respect to the spherulites size, lamellae thickness, long period, crystallinity degree and well documented by AFM images. The structure and the properties of isotactic poly(propylene) matrix modified by inorganic layered silicate, montmorillonite, are discussed with respect to the clay content. Isotactic poly(propylene)-graft-maleic anhydride was used as compatibilizer. It is clearly demonstrated that the property enhancement is largely due to the ability of layered silicate to exfoliate. The intimate dispersion of the nanometer-thick silicate result from a delicate balance of the content ratio between the isotactic poly(propylene)-graft-maleic anhydride compatibilizer and the inorganic clay.

Proton-conducting copolymers, blends and composites with phosphonic acid as protogenic group

ABSTRACT: In this work, proton conducting copolymers, polymer blends and composites containing phosphonic acid groups have been prepared. Proton conduction mechanisms in these materials are discussed respectively in both, the anhydrous and humidified state. Atom transfer radical copolymerization (ATRCP) of diisopropyl-p-vinylbenzyl phosphonate (DIPVBP) and 4-vinyl pyridine (4VP) is studied for the first time in this work. The kinetic parameters are obtained by using the 1H-NMR online technique. Proton conduction in poly(vinylbenzyl phosphonic acid) (PVBPA) homopolymer and its statistical copolymers with 4-vinyl pyridine (poly(VBPA-stat-4VP)s) are comprehensively studied in both, the “dry” and “wet” state. Effects of temperature, water content and polymer composition on proton conductivities are studied and proton transport mechanisms under various conditions are discussed. The proton conductivity of the polymers is in the range of 10-6-10-8 S/cm in nominally dry state at 150 oC. However, proton conductivity of the polymers increases rapidly with water content in the polymers which can reach 10-2 S/cm at the water uptake of 25% in the polymers. The highest proton conductivity obtained from the polymers can even reach 0.3 S/cm which was measured at 85oC with 80% relative humidity in the measuring atmosphere. Poly(4-vinyl pyridine) was grafted from the surface of SiO2 nanoparticles using ATRP in this work for the first time. Following this approach, silica nanoparticles with a shell of polymeric layer are used as basic particles in a polymeric acidic matrix. The proton conductivities of the composites are studied under both, humidified and dry conditions. In dry state, the conductivity of the composites is in the range of 10-10~10-4 S/cm at 150 oC. While in humid state, the composites show much higher proton conductivity. The highest proton conductivity obtained with the composites is 0.5 S/cm measured at 85oC with 80% relative humidity in the measuring atmosphere. The miscibility of poly (vinyl phosphonic acid) and PEO is studied for the first time in this work and a phase diagram is plotted based on a DSC study and optical microscopy. With this knowledge, homogeneous PVPA/PEO mixtures are prepared as proton-conducting polymer blends. The mobility of phosphonic acid groups and PEO in the blends is determined by 1H-MAS-NMR in temperature dependent measurements. The effect of composition and the role of PEO on proton conduction are discussed.

Polymer-nanoparticle composites: from orientation phenomena to optoelectronic applications

Polymer-nanoparticle hybrids show synergistic effects, demonstrating both, the unique properties of nanosized structures and the good processability and functionalities of polymeric materials. This work shows the synthesis and application of block copolymers containing a soluble, functional block and a short anchor block, which efficiently binds to the surface of nanocrystals. We functionalized anisotropic, semiconducting nanoparticles, which can be dissolved in organic and polymeric matrices upon modification. The modified nanorods have the ability to form liquid crystalline phases, which behave similar to low molecular liquid crystals with a reversible clearing behaviour. These liquid crystalline phases could also be obtained in hole conducting matrices. For a macroscopic orientation of the nanorods, electric fields were applied and a switching (in analogy to known liquid crystals) to a homeotropic orientation was observed.rnBy introduction of dye molecules in the anchor block of a hole conducting block copolymer, all essential components of a solar cell can be combined in a single particle. Light absorption of the dye induces the injection of electrons into the particles, followed by a charging, that was monitored by a special AFM technique.rnLight emitting nanocrystals were functionalized analogously with a hole transporting polymer. The stability of the particles could be enhanced by the sterically stabilizing polymer corona and the particles showed improved properties in terms of processing. We applied these hybrid materials in light emitting devices, which showed better characteristics due to an improved hole injection and well dispersed emitting particles in the active device layer.rnThe work shows the broad spectrum of properties and applications based on the synergistic effects in hybrid and composite materials.

Graphene based electrode materials for solar cell and electrochemical oxygen reduction

Diese Arbeit hat viele beispiellose synthetische Ansätze für neuartige Verbundwerkstoffe Graphen-und stickstoffhaltigen graphitischen Materialien erforscht. Die erhaltenen Materialien wurden als den transparenten Elektroden der Solarzellen, die freistehenden Elektroden mit verbesserter mechanischer Festigkeit, und die Kathoden der Brennstoffzellen der Sauerstoffreduktion aufgebracht.rnAlle Ergebnisse haben eindeutig das große Potenzial von Graphen basierenden Materialien und stickstoffhaltigen graphitische Kohlenstoffe als neuartige Elektrodenmaterialien für neue Energie-Geräten demonstriert.