Optimised polyolefin branch quantification by 13 C NMR spectroscopy

Quantitative branch determination in polyolefins by solid- and melt-state 13C NMR has been investigated. Both methods were optimised toward sensitivity per unit time. While solid-state NMR was shown to give quick albeit only qualitative results, melt-state NMR allowed highly time efficient accurate branch quantification. Comparison of spectra obtained using spectrometers operating at 300, 500 and 700 MHz 1H Larmor frequency, with 4 and 7~mm MAS probeheads, showed that the best sensitivity was achieved at 500 MHz using a 7 mm 13C-1H optimised high temperature probehead. For materials available in large quantities, static melt-state NMR, using large diameter detection coils and high coil filling at 300 MHz, was shown to produce comparable results to melt-state MAS measurements in less time. While the use of J-coupling mediated polarisation transfer techniques was shown to be possible, direct polarisation via single-pulse excitation proved to be more suitable for branch quantification in the melt-state. Artificial line broadening, introduced by FID truncation, was able to be reduced by the use of π pulse-train heteronuclear dipolar decoupling. This decoupling method, when combined with an extended duty-cycle, allowed for significant improvement in resolution. Standard setup, processing and analysis techniques were developed to minimise systematic errors contributing to the measured branch contents. The final optimised melt-state MAS NMR method was shown to allow time efficient quantification of comonomer content and distribution in both polyethylene- and polypropylene-co-α-olefins. The sensitivity of the technique was demonstrated by quantifying branch concentrations of 8 branches per 100,000 CH2 for an industrial ‘linear’ polyethylene in only 13 hours. Even lower degrees of 3–8 long-chain branches per 100,000 carbons were able to be estimated in just 24 hours for a series of γ-irradiated polypropylene homopolymers.