Synthesis and characterization of metal-chalcogenide MQ 2-Nanoparticles (M = Mo, W, Zr; Q = S, O)

Here, we present the adaptation and optimization of (i) the solvothermal and (ii) the metal-organic chemical vapor deposition (MOCVD) approach as simple methods for the high-yield synthesis of MQ2 (M=Mo, W, Zr; Q = O, S) nanoparticles. Extensive characterization was carried out using X-ray diffraction (XRD), scanning and transmission electron micros¬copy (SEM/TEM) combined with energy dispersive X-ray analysis (EDXA), Raman spectroscopy, thermal analyses (DTA/TG), small angle X-ray scattering (SAXS) and BET measurements. After a general introduction to the state of the art, a simple route to nanostructured MoS2 based on the decomposition of the cluster-based precursor (NH4)2Mo3S13∙xH2O under solvothermal conditions (toluene, 653 K) is presented. Solvothermal decomposition results in nanostructured material that is distinct from the material obtained by decomposition of the same precursor in sealed quartz tubes at the same temperature. When carried out in the presence of the surfactant cetyltrimethyl¬ammonium bromide (CTAB), the decomposition product exhibits highly disordered MoS2 lamellae with high surface areas. The synthesis of WS2 onion-like nanoparticles by means of a single-step MOCVD process is discussed. Furthermore, the results of the successful transfer of the two-step MO¬CVD based synthesis of MoQ2 nanoparticles (Q = S, Se), comprising the formation of amorphous precursor particles and followed by the formation of fullerene-like particles in a subsequent annealing step to the W-S system, are presented. Based on a study of the temperature dependence of the reactions a set of conditions for the formation of onion-like structures in a one-step reaction could be derived. The MOCVD approach allows a selective synthesis of open and filled fullerene-like chalcogenide nanoparticles. An in situ heating stage transmission electron microscopy (TEM) study was employed to comparatively investigate the growth mechanism of MoS2 and WS2 nanoparticles obtained from MOCVD upon annealing. Round, mainly amorphous particles in the pristine sample trans¬form to hollow onion-like particles upon annealing. A significant difference between both compounds could be demonstrated in their crystallization conduct. Finally, the results of the in situ hea¬ting experiments are compared to those obtained from an ex situ annealing process under Ar. Eventually, a low temperature synthesis of monodisperse ZrO2 nanoparticles with diameters of ~ 8 nm is introduced. Whereas the solvent could be omitted, the synthesis in an autoclave is crucial for gaining nano-sized (n) ZrO2 by thermal decomposition of Zr(C2O4)2. The n-ZrO2 particles exhibits high specific surface areas (up to 385 m2/g) which make them promising candidates as catalysts and catalyst supports. Co-existence of m- and t-ZrO2 nano-particles of 6-9 nm in diameter, i.e. above the critical particle size of 6 nm, demonstrates that the particle size is not the only factor for stabilization of the t-ZrO2 modification at room temperature. In conclusion, synthesis within an autoclave (with and without solvent) and the MOCVD process could be successfully adapted to the synthesis of MoS2, WS2 and ZrO2 nanoparticles. A comparative in situ heating stage TEM study elucidated the growth mechanism of MoS2 and WS2 fullerene-like particles. As the general processes are similar, a transfer of this synthesis approach to other layered transition metal chalcogenide systems is to be expected. Application of the obtained nanomaterials as lubricants (MoS2, WS2) or as dental filling materials (ZrO2) is currently under investigation.

High resolution study of local stress inside alumina - micro mechanical analysis using laser scanning confocal microscope

The aim of this work is to measure the stress inside a hard micro object under extreme compression. To measure the internal stress, we compressed ruby spheres (a-Al2O3: Cr3+, 150 µm diameter) between two sapphire plates. Ruby fluorescence spectrum shifts to longer wavelengths under compression and can be related to the internal stress by a conversion coefficient. A confocal laser scanning microscope was used to excite and collect fluorescence at desired local spots inside the ruby sphere with spatial resolution of about 1 µm3. Under static external loads, the stress distribution within the center plane of the ruby sphere was measured directly for the first time. The result agreed to Hertz’s law. The stress across the contact area showed a hemispherical profile. The measured contact radius was in accord with the calculation by Hertz’s equation. Stress-load curves showed spike-like decrease after entering non-elastic phase, indicating the formation and coalescence of microcracks, which led to relaxing of stress. In the vicinity of the contact area luminescence spectra with multiple peaks were observed. This indicated the presence of domains of different stress, which were mechanically decoupled. Repeated loading cycles were applied to study the fatigue of ruby at the contact region. Progressive fatigue was observed when the load exceeded 1 N. As long as the load did not exceed 2 N stress-load curves were still continuous and could be described by Hertz’s law with a reduced Young’s modulus. Once the load exceeded 2 N, periodical spike-like decreases of the stress could be observed, implying a “memory effect” under repeated loading cycles. Vibration loading with higher frequencies was applied by a piezo. Redistributions of intensity on the fluorescence spectra were observed and it was attributed to the repopulation of the micro domains of different elasticity. Two stages of under vibration loading were suggested. In the first stage continuous damage carried on until certain limit, by which the second stage, e.g. breakage, followed in a discontinuous manner.

Noble-metal nanoparticles produced with colloidal lithography: fabrication, optical properties and applications

In this work, metal nanoparticles produced by nanosphere lithography were studied in terms of their optical properties (in connection to their plasmon resonances), their potential application in sensing platforms - for thin layer sensing and bio-recognition events -, and for a particular case (the nanocrescents), for enhanced spectroscopy studies. The general preparation procedures introduced early in 2005 by Shumaker-Parry et al. to produce metallic nanocrescents were extended to give rise to more complex (isolated) structures, and also, by combining colloidal monolayer fabrication and plasma etching techniques, to arrays of them. The fabrication methods presented in this work were extended not only to new shapes or arrangements of particles, but included also a targeted surface tailoring of the substrates and the structures, using different thiol and silane compounds as linkers for further attachment of, i.e. polyelectrolyte layers, which allow for a controlled tailoring of their nanoenvironment. The optical properties of the nanocrescents were studied with conventional transmission spectroscopy; a simple multipole model was adapted to explain their behaviour qualitatively. In terms of applications, the results on thin film sensing using these particles show that the crescents present an interesting mode-dependent sensitivity and spatial extension. Parallel to this, the penetrations depths were modeled with two simplified schemes, obtaining good agreement with theory. The multiple modes of the particles with their characteristic decay lengths and sensitivities represent a major improvement for particle-sensing platforms compared to previous single resonance systems. The nanocrescents were also used to alter the emission properties of fluorophores placed close to them. In this work, green emitting dyes were placed at controlled distances from the structures and excited using a pulsed laser emitting in the near infrared. The fluorescence signal obtained in this manner should be connected to a two-photon processes triggered by these structures; obtaining first insight into plasmon-mediated enhancement phenomena. An even simpler and faster approach to produce plasmonic structures than that for the crescents was tested. Metallic nanodiscs and nanoellipses were produced by means of nanosphere lithography, extending a procedure reported in the literature to new shapes and optical properties. The optical properties of these particles were characterized by extinction spectroscopy and compared to results from the literature. Their major advantage is that they present a polarization-dependent response, like the nanocrescents, but are much simpler to fabricate, and the resonances can be tailored in the visible with relative ease. The sensing capabilities of the metallic nanodiscs were explored in the same manner as for the nanocrescents, meaning their response to thin layers and to bio-recognition events on their surface. The sensitivity of these nanostructures to thin films proved to be lower than that of the crescents, though in the same order of magnitude. Experimental information about the near field extension for the Au nanodiscs of different sizes was also extracted from these measurements. Further resonance-tailoring approaches based on electrochemical deposition of metals on the nanodiscs were explored, as a means of modifying plasmon resonances by changing surface properties of the nanoparticles. First results on these experiments would indicate that the deposition of Ag on Au on a submonolayer coverage level can lead to important blue-shifts in the resonances, which would open a simple way to tailor resonances by changing material properties in a local manner.

On the development of novel cocaine-analogues for in vivo imaging of the dopamine transporter status

The present thesis is concerned with the development of novel cocaine-derived dopamine transporter ligands for the non-invasive exploration of the striatal and extra-striatal dopamine transporter (DAT) in living systems. The presynaptic dopamine transporter acquires an important function within the mediation of dopaminergic signal transduction. Its availability can serve as a measure for the overall integrity of the dopaminergic system. The DAT is upregulated in early Parkinson’s disease (PD), resulting in an increased availability of DAT-binding sites in the striatal DAT domains. Thereby, DAT imaging has become an important routine diagnostic tool for the early diagnosis of PD in patients, as well as for the differentiation of PD from symptomatically similar medical conditions. Furthermore, the dopaminergic system is involved in a variety of psychiatric diseases. In this regard, DAT-selective imaging agents may provide detailed insights into the scientific understanding of the biochemical background of both, the progress as well as the origins of the symptoms. DAT-imaging may also contribute to the determination of the dopaminergic therapeutic response for a given medication and thereby contribute to more convenient conditions for the patient. From an imaging point of view, the former demands a high availability of the radioactive probe to facilitate broad application of the modality, whereas the latter profits from short-lived probes, suitable for multi-injection studies. Therefore, labelling with longer-lived 18F-fluoride and in particular the generator nuclide 68Ga is worthwhile for clinical routine imaging. In contrast, the introduction of a 11C-label is a prerequisite for detailed scientific studies of neuronal interactions. The development of suitable DAT-ligands for medical imaging has often been complicated by the mixed binding profile of many compounds that that interact with the DAT. Other drawbacks have included high non-specific binding, extensive metabolism and slow accumulation in the DAT-rich brain areas. However, some recent examples have partially overcome the mentioned complications. Based on the structural speciality of these leads, novel ligand structures were designed and successfully synthesised in the present work. A structure activity relationship (SAR) study was conducted wherein the new structural modifications were examined for their influence on DAT-affinity and selectivity. Two of the compounds showed improvements in in vitro affinity for the DAT as well as selectivity versus the serotonin transporter (SERT) and norepinephrine transporter (NET). The main effort was focussed on the high-affinity candidate PR04.MZ, which was subsequently labelled with 18F and 11C in high yield. An initial pharmacological characterisation of PR04.MZ in rodents revealed highly specific binding to the target brain structures. As a result of low non-specific binding, the DAT-rich striatal area was clearly visualised by autoradiography and µPET. Furthermore, the radioactivity uptake into the DAT-rich brain regions was rapid and indicated fast binding equilibrium. No radioactive metabolite was found in the rat brain. [18F]PR04.MZ and [11C]PR04.MZ were compared in the primate brain and the plasma metabolism was studied. It was found that the ligands specifically visualise the DAT in high and low density in the primate brain. The activity uptake was rapid and quantitative evaluation by Logan graphical analysis and simplified reference tissue model was possible after a scanning time of 30 min. These results further reflect the good characteristics of PR04.MZ as a selective ligand of the neuronal DAT. To pursue 68Ga-labelling of the DAT, initial synthetic studies were performed as part of the present thesis. Thereby, a concept for the convenient preparation of novel bifunctional chelators (BFCs) was developed. Furthermore, the suitability of novel 1,4,7-triazacyclononane based N3S3-type BFCs for biomolecule-chelator conjugates of sufficient lipophilicity for the penetration of the blood-brain-barrier was elucidated.

A scanning electron microscope for ultracold quantum gases

This thesis presents a new imaging technique for ultracold quantum gases. Since the first observation of Bose-Einstein condensation, ultracold atoms have proven to be an interesting system to study fundamental quantum effects in many-body systems. Most of the experiments use optical imaging rnmethods to extract the information from the system and are therefore restricted to the fundamental limitation of this technique: the best achievable spatial resolution that can be achieved is comparable to the wavelength of the employed light field. Since the average atomic distance and the length scale of characteristic spatial structures in Bose-Einstein condensates such as vortices and solitons is between 100 nm and 500 nm, an imaging technique with an adequate spatial resolution is needed. This is achieved in this work by extending the method of scanning electron microscopy to ultracold quantum gases. A focused electron beam is scanned over the atom cloud and locally produces ions which are subsequently detected. The new imaging technique allows for the precise measurement of the density distribution of a trapped Bose-Einstein condensate. Furthermore, the spatial resolution is determined by imaging the atomic distribution in one-dimensional and two-dimensional optical lattices. Finally, the variety of the imaging method is demonstrated by the selective removal of single lattice site. rn

Transport properties of YBa 2 Cu 3 O 7, PrBa 2 Cu 3 O 7-superlattices

The understanding of the coupling between superconducting YBa2Cu3O7 (YBCO) layers decoupled by non superconducting PrBa2Cu3O7 (PBCO) layers in c-axis oriented superlattices was the aim of this thesis. For this purpose two conceptually different kind of transport experiments have been performed. rnrnIn the first type of transport experiments the current is flowing parallel to the layers. Here the coupling is probed indirectly using magnetic vortex lines, which are penetrating the superlattice. Movement of the vortex segments in neighbouring YBCO layers is more or less coherent depending on the thickness of both the superconducting and non superconducting layers. This in-plane transport was measured either by sending an external current through bridges patterned in the superlattice or by an induced internal current. rnThe vortex-creep activation energy U was determined by analysis of the in-plane resistive transition in an external magnetic field B oriented along the c-axis. The activation energies for two series of superlattices were investigated. In one series the thickness of the YBCO layers was constant (nY=4 unit cells) and the number of the PBCO unit cells was varied, while in the other the number of PBCO layers was constant (nP=4) and nY varied. The correlation length of the vortex system was determined to be 80 nm along the c-axis direction. It was found that even a single PBCO unit cell in a superlattice effectively cuts the flux lines into shorter weakly coupled segments, and the coupling of the vortex systems in neighbouring layers is negligible already for a thickness of four unit cells of the PBCO layers. A characteristic variation of the activation energy for the two series of superlattices was found, where U0 is proportional to the YBCO thickness. A change in the variation of U0 with the current I in the specimen was observed, which can be explained in terms of a crossover in the vortex creep process, generated by the transport current. At low I values the dislocations mediated (plastic) vortex creep leads to thermally assisted flux-flow behaviour, whereas at high current the dc transport measurements are dominated by elastic (collective) creep.rnThe analysis of standard dc magnetization relaxation data obtained for a series superlattices revealed the occurrence of a crossover from elastic (collective) vortex creep at low temperature to plastic vortex creep at high T. The crossover is generated by the T dependent macroscopic currents induced in the sample. The existence of this creep crossover suggests that, compared with the well known Maley technique, the use of the normalized vortex creep activation energy is a better solution for the determination of vortex creep parameters.rnrnThe second type of transport experiments was to measure directly a possible Josephson coupling between superconducting CuO2 double planes in the superlattices by investigation of the transport properties perpendicular to the superconducting planes. Here three different experiments have been performed. The first one was to pattern mesa structures photolithographically as in previous works. The second used three-dimensional nanostructures cut by a focused ion beam. For the these two experiments insufficient patterning capabilities prevented an observation of the Josephson effect in the current voltage curves. rnA third experiment used a-axis and (110) oriented YBCO films, where in-plane patterning can in principle be sufficient to measure transport perpendicular to the superconducting planes. Therefore the deposition of films with this unusual growth orientation was optimized and investigated. The structural and microstructural evolution of c-axis to a-axis orientation was monitored using x-ray diffraction, scanning electron microscopy and magnetization measurements. Films with full a-axis alignment parallel to the substrate normal could be achieved on (100)SrTiO3. Due to the symmetry of the substrate the c-axis direction in-plane is twofold. Transferring the deposition conditions to films grown on (110)SrTiO3 allowed the growth of (110) oriented YBCO films with a unique in-plane c-axis orientation. While these films were of high quality by crystallographic and macroscopic visual inspection, electron microscopy revealed a coherent crack pattern on a nanoscale. Therefore the actual current path in the sample was not determined by the macroscopic patterning which prohibited investigations of the in-plane anisotropy in this case.rn

Wet chemistry synthesis towards nanostructures of thermoelectric antimonides

Die vorliegende Arbeit befasst sich mit der Synthese von nanostrukturierten Antimoniden, wobei die folgenden beiden Themen bearbeitet wurden: rnAus chemischer Sicht wurden neue Synthesewege entwickelt, um Nanopartikel der Verbindungen in den binären Systemen Zn-Sb und Fe-Sb herzustellen (Zn4Sb3, ZnSb, FeSb2, Fe1+xSb). Anders als in konventionellen Festkörperreaktionen, die auf die Synthese von Bulk-Materialien oder Einkristallen zielen, muss die Synthese von Nanopartikeln Agglomerate und Ostwald-Wachstum vermeiden. Daher benötigen annehmbare Reaktionszeiten und vergleichsweise tiefe Reaktionstemperaturen kurze Diffusionswege und tiefe Aktivierungsbarrieren. Demzufolge bedient sich die Synthese der Reaktion von Antimon-Nanopartikeln und geeigneten molekularen oder nanopartikulären Edukten der entsprechenden Übergangsmetalle. Zusätzlich wurden anisotrope ZnSb Strukturen synthetisiert, indem eine Templat-Synthese mit Hilfe von anodisierten Aluminiumoxid- oder Polycarbonat-Membranen angewandt wurde. rnDie erhaltenen Produkte wurden hauptsächlich durch Röntgen-Diffraktion und Elektronenmikroskopie untersucht. Die Auswertung der Pulver Röntgendiffraktions-Daten stellte eine Herausforderung dar, da die Nanostrukturierung und die Anwesenheit von mehreren Phasen zu verbreiterten und überlagernden Reflexen führen. Zusätzliche Fe-Mößbauer Messungen wurden im Falle der Fe-Sb Produkte vorgenommen, um detailliertere Informationen über die genaue Zusammensetzung zu erhalten. Die erstmals hergestellte Phase Zn1+xSb wurde einer detaillierten Kristallstrukturanalyse unterzogen, die mit Hilfe einer neuen Diffraktionsmethode, der automatisierten Elektronen Diffraktions Tomographie, durchgeführt wurde.rnrnAus physikalischer Sicht sind Zn4Sb3, ZnSb und FeSb2 interessante thermoelektrische Materialien, die aufgrund ihrer Fähigkeit thermische in elektrische Energie umzuwandeln, großes Interesse geweckt haben. Nanostrukturierte thermoelektrische Materialien zeigen dabei eine höhere Umwandlungseffizienz zu erhöhen, da deren thermische Leitfähigkeit herabgesetzt ist. Da thermoelektrische Bauteile aus dichten Bulk-Materialien gefertigt werden, spielte die Verfestigung der synthetisierten nanopartikulären Pulver eine große Rolle. Die als „Spark Plasma Sintering“ bezeichnete Methode wurde eingesetzt, um die Proben zu pressen. Dies ermöglicht schnelles Heizen und Abkühlen der Probe und kann so das bei klassischen Heißpress-Methoden unvermeidliche Kristallitwachstum verringern. Die optimalen Bedingungen für das Spark Plasma Sintern zu finden, ist Inhalt von bestehender und weiterführender Forschung. rnEin Problem stellt die Stabilität der Proben während des Sinterns dar. Trotz des schnellen Pressens wurde eine teilweise Zersetzung im Falle des Zn1+xSb beobachtet, wie mit Hilfe von Synchrotrondiffraktionsuntersuchungen aufgedeckt wurde. Morphologie und Dichte der verschiedenen verfestigten Materialien wurden mittels Rasterelektronenmikroskopie und Lasermikroskopie bestimmt. Die Gitterdynamik wurde mit Hilfe von Wärmekapazitätsmessungen- und inelastischer Kern-Streuung untersucht. Die Wärmeleitfähigkeit der nanostrukturierten Materialien ist im Vergleich zu den Festkörpern ist drastisch reduziert - im Falle des FeSb2 um mehr als zwei Größenordnungen. Abhängig von der Zusammensetzung und mechanischen Härte wurden für einen Teil der verfestigten Nanomaterialien die thermoelektrische Eigenschaften, wie Seebeck Koeffizient, elektrische und Wärmeleitfähigkeit, gemessen.rn

Drainage of thin aqueous films between solid surfaces measured with the colloidal probe technique

Understanding liquid flow at the vicinity of solid surfaces is crucial to the developmentrnof technologies to reduce drag. One possibility to infer flow properties at the liquid-solid interface is to compare the experimental results to solutions of the Navier-Stokes equations assuming the no-slip boundary condition (BC) or the slip BC. There is no consensus in the literature about which BC should be used to model the flow of aqueous solutions over hydrophilic surfaces. Here, the colloidal probe technique is used to systematically address this issue, measuring forces acting during drainage of water over a surface. Results show that experimental variables, especially the cantilever spring constant, lead to the discrepancy observed in the literature. Two different parameters, calculated from experimental variables, could be used to separate the data obtained in this work and those reported in the literature in two groups: one explained with the no-slip BC, and another with the slip BC. The observed residual slippage is a function of instrumental variables, showing a trend incompatible with the available physical justifications. As a result, the no-slip is the more appropriate BC. The parameters can be used to avoid situations where the no-slip BC is not satisfied.

Detektion von Nickel- und Cobaltspezies in einzelnen lebenden Zellen mit hoher lateraler Auflösung

Übergangsmetallen wie Nickel und Cobalt kommt meist eine große Bedeutung als Cofaktor in Enzymen oder Metallkomplexen im Metabolismus von Lebewesen zu. Da eine sehr geringe Konzentration dieser Übergangsmetalle in einer Zelle für deren Funktionalität ausreicht, ist eine konstante Konzentration der Spurenelemente in einer Zelle angestrebt. Durch meist anthropogene Einflüsse sind Pflanzen und Menschen zunehmend hohen Konzentrationen von Übergangsmetallen ausgesetzt, die in Abhängigkeit von ihrer Spezies, der Konzentration und der Lokalisation unterschiedliche Toxizitäten aufweisen können. Die Speziation von Metallen wurde bisher mittels gängiger Analyseverfahren, wie der ICP-MS und ähnlicher Verfahren, anhand von bulk-Material durchgeführt. Durch die Entwicklung von optischen Sensoren für Metallionen war es möglich, diese Metalle auch in lebenden Zellen mittels Fluoreszenzmikroskopie zu lokalisieren. Ke und Kollegen (2006, 2007) nutzten einen solchen optischen Sensor - Newport Green DCF, um die Aufnahme von Nickel in humane A543 Lungenbronchialepithelzellen nach Inkubation mit dem wasserlöslichen NiCl2 (0,5 mM und 1 mM) sowie den wasserunlöslichen Verbindungen Ni3S2 (0,5 µg/cm2 und 1 µg/cm2) und NiS (2,5 µg/cm2) nachzuweisen und zu lokalisieren und konnten damit eine Akkumulation von Nickel im Zytoplasma und im Zellkern aufzeigen. Dabei war bei wasserlöslichen und wasserunlöslichen Nickelverbindungen Nickel nach 24 h im Zytoplasma und erst nach 48 h im Zellkern zu beobachten.rnrnDa Nickel und Cobalt keine detektierbare Eigenfluoreszenz unter den gegebenen Bedingungen zeigten, wurde für den optischen Nachweis von Nickel und Cobalt mit dem konfokalen Laser-Raster Mikroskop (CLSM) nach der Zugabe der verschiedenen wasserlöslichen und wasserunlöslichen Metallverbindungen NiCl2, NiSO4, Ni3S2 und CoCl2 in einzelnen lebenden humanen Gingiva-Fibroblasten, sowie in Pflanzenzellen in dieser Arbeit ebenfalls der optische Sensor Newport Green DCF genutzt. Korrespondierend zu den Ergebnissen früherer Arbeiten von Ke et al. (2006, 2007), in denen die Nickelaufnahme bei Konzentrationen von >0,5 mM NiCl2 bzw. >0,5 µg/cm2 Ni3S2 gezeigt wurde, wurde Nickel in Fibroblasten in Abhängigkeit von der Spezies mit steigender Metallkonzentration von 100 µM bis 500 µM nach 16 h im Zytoplasma und zunehmend nach 24 h bis 48 h im Zellkern detektiert. Bei der wasserunlöslichen Verbindung Ni3S2 war der Nachweis von Nickel im Zellkern bereits nach 16 h bis 24 h erfolgreich. Zusätzlich wurden weitere Strukturen wie das Endoplasmatische Retikulum, die Mitochondrien und die Nukleoli durch eine starke Fluoreszenz des optischen Sensors bei Colokalisationsexperimenten mit Organell-spezifischen Fluoreszenzfarbstoffen als target für die Nickelbindung vermutet. Die Lokalisation von Cobalt in den Fibroblasten entsprach weitgehend der Lokalisation von Nickel. Im Zellkern war die Cobaltlokalisation jedoch auf die Nukleoli beschränkt. Weiterführende Versuche an humanen Gingiva-Fibroblasten zeigten, dass die Aufnahme der Metalle in die Fibroblasten pH-Wert abhängig war. Niedrige pH-Werte im sauren pH-Bereich verringerten die Aufnahme der Metalle in die Zellen, wobei ein pH-Wert im basischen Bereich keinen bedeutenden Unterschied zum neutralen pH-Bereich aufwies. Im Vergleich zu den Fibroblasten war in Pflanzenzellen zu jedem Zeitpunkt, auch bei geringen Konzentrationen der Metallverbindungen sowie des optischen Sensors, Nickel und Cobalt in den Zellkernen detektierbar. Durch die Eigenschaft der Pflanzenzellen eine Vakuole zu besitzen, war Nickel und Cobalt hauptsächlich in den Vakuolen lokalisiert. Weitere Strukturen wie das Endoplasmatische Retikulum, die Mitochondrien oder auch die Zellwand kamen bei Pflanzenzellen als target in Frage.rnrnDie Fluoreszenz und Lokalisation der Metalle in den Fibroblasten waren unabhängig von der Spezies sehr ähnlich, sodass in den Zellen die Spezies anhand der fluoreszenzmikroskopischen Aufnahmen kaum unterschieden werden konnten. Lambda-Scans in verschiedenen regions of interest (ROI) wurden durchgeführt, um durch die Fluoreszenzspektren Hinweise auf eine charakteristische Beeinflussung der Bindungspartner von Nickel und Cobalt oder dieser Metalle selbst in den Zellen auf den optischen Sensor zu bekommen und diese dadurch identifizieren zu können. Das Ziel der parallelen Detektion bzw. Lokalisation und gleichzeitigen Speziation bestimmter Nickel- und Cobaltpezies in einzelnen lebenden Zellen konnte in dieser Arbeit durch den optischen Sensor Newport Green DCF nicht erreicht werden.

Diffusion in heterogeneous systems studied by laser scanning confocal microscopy and fluorescence correlation spectroscopy

Understanding and controlling the mechanism of the diffusion of small molecules, macromolecules and nanoparticles in heterogeneous environments is of paramount fundamental and technological importance. The aim of the thesis is to show, how by studying the tracer diffusion in complex systems, one can obtain information about the tracer itself, and the system where the tracer is diffusing. rnIn the first part of my thesis I will introduce the Fluorescence Correlation Spectroscopy (FCS) which is a powerful tool to investigate the diffusion of fluorescent species in various environments. By using the main advantage of FCS namely the very small probing volume (<1µm3) I was able to track the kinetics of phase separation in polymer blends at late stages by looking on the molecular tracer diffusion in individual domains of the heterogeneous structure of the blend. The phase separation process at intermediate stages was monitored with laser scanning confocal microscopy (LSCM) in real time providing images of droplet coalescence and growth. rnIn a further project described in my thesis I will show that even when the length scale of the heterogeneities becomes smaller than the FCS probing volume one can still obtain important microscopic information by studying small tracer diffusion. To do so, I will introduce a system of star shaped polymer solutions and will demonstrate that the mobility of small molecular tracers on microscopic level is nearly not affected by the transition of the polymer system to a “glassy” macroscopic state. rnIn the last part of the thesis I will introduce and describe a new stimuli responsive system which I have developed, that combines two levels of nanoporosity. The system is based on poly-N-isopropylacrylamide (PNIPAM) and silica inverse opals (iOpals), and allows controlling the diffusion of tracer molecules. rn

Multifunctional polyether architectures : versatile materials for surface attachment and functionalization

Chapter 1 of this thesis comprises a review of polyether polyamines, i.e., combinations of polyether scaffolds with polymers bearing multiple amino moieties. Focus is laid on controlled or living polymerization methods. Furthermore, fields in which the combination of cationic, complexing, and pH-sensitive properties of the polyamines and biocompatibility and water-solubility of polyethers promise enormous potential are presented. Applications include stimuli-responsive polymers with a lower critical solution temperature (LCST) and/or the ability to gel, preparation of shell cross-linked (SCL) micelles, gene transfection, and surface functionalization.rnIn Chapter 2, multiaminofunctional polyethers relying on the class of glycidyl amine comonomers for anionic ring-opening polymerization (AROP) are presented. In Chapter 2.1, N,N-diethyl glycidyl amine (DEGA) is introduced for copolymerization with ethylene oxide (EO). Copolymer microstructure is assessed using online 1H NMR kinetics, 13C NMR triad sequence analysis, and differential scanning calorimetry (DSC). The concurrent copolymerization of EO and DEGA is found to result in macromolecules with a gradient structure. The LCSTs of the resulting copolymers can be tailored by adjusting DEGA fraction or pH value of the environment. Quaternization of the amino moieties by methylation results in polyelectrolytes. Block copolymers are used for PEGylated gold nanoparticle formation. Chapter 2.2 deals with a glycidyl amine monomer with a removable protecting group at the amino moiety, for liberation of primary amines at the polyether backbone, which is N,N-diallyl glycidyl amine (DAGA). Its allyl groups are able to withstand the harsh basic conditions of AROP, but can be cleaved homogeneously after polymerization. Gradient as well as block copolymers poly(ethylene glycol)-PDAGA (PEG-PDAGA) are obtained. They are analyzed regarding their microstructure, LCST behavior, and cleavage of the protecting groups. rnChapter 3 describes applications of multi(amino)functional polyethers for functionalization of inorganic surfaces. In Chapter 3.1, they are combined with an acetal-protected catechol initiator, leading to well-defined PEG and heteromultifunctional PEG analogues. After deprotection, multifunctional PEG ligands capable of attaching to a variety of metal oxide surfaces are obtained. In a cooperative project with the Department of Inorganic and Analytical Chemistry, JGU Mainz, their potential is demonstrated on MnO nanoparticles, which are promising candidates as T1 contrast agents in magnetic resonance imaging. The MnO nanoparticles are solubilized in aqueous solution upon ligand exchange. In Chapter 3.2, a concept for passivation and functionalization of glass surfaces towards gold nanorods is developed. Quaternized mPEG-b-PqDEGA diblock copolymers are attached to negatively charged glass surfaces via the cationic PqDEGA blocks. The PEG blocks are able to suppress gold nanorod adsorption on the glass in the flow cell, analyzed by dark field microscopy.rnChapter 4 highlights a straightforward approach to poly(ethylene glycol) macrocycles. Starting from commercially available bishydroxy-PEG, cyclic polymers are available by perallylation and ring-closing metathesis in presence of Grubbs’ catalyst. Purification of cyclic PEG is carried out using α-cyclodextrin. This cyclic sugar derivative forms inclusion complexes with remaining unreacted linear PEG in aqueous solution. Simple filtration leads to pure macrocycles, as evidenced by SEC and MALDI-ToF mass spectrometry. Cyclic polymers from biocompatible precursors are interesting materials regarding their increased blood circulation time compared to their linear counterparts.rnIn the Appendix, A.1, a study of the temperature-dependent water-solubility of polyether copolymers is presented. Macroscopic cloud points, determined by turbidimetry, are compared with microscopic aggregation phenomena, monitored by continuous wave electron paramagnetic resonance (CW EPR) spectroscopy in presence of the amphiphilic spin probe and model drug (2,2,6,6-tetramethylpiperidin-1-yl)oxyl (TEMPO). These thermoresponsive polymers are promising candidates for molecular transport applications. The same techniques are applied in Chapter A.2 to explore the pH-dependence of the cloud points of PEG-PDEGA copolymers in further detail. It is shown that the introduction of amino moieties at the PEG backbone allows for precise manipulation of complex phase transition modes. In Chapter A.3, multi-hydroxyfunctional polysilanes are presented. They are obtained via copolymerization of the acetal-protected dichloro(isopropylidene glyceryl propyl ether)methylsilane monomer. The hydroxyl groups are liberated through acidic work-up, yielding versatile access to new multifunctional polysilanes.

Thermoelektrische und strukturelle Eigenschaften gefüllter Skutterudite, sowie Verbesserung ihres Gütefaktors durch Nanostrukturierung

Gefüllte Skutterudite mit der Summenformel MxCo4Sb12 sind vielversprechende thermoelektrische Materialien. Die Standardsynthese führt jedoch oft zur Bildung von MSbx, Sb, CoSb oder CoSb2 als Nebenphasen. In dieser Arbeit wird eine neue zweistufige Synthese vorgestellt, bei der die Bildung des Kieftits (CoSb3) getrennt von dem topotaktischen Füllen mit dem Metallatom M erfolgt. Dieser Ansatz erlaubt eine Durchführung der Reaktion bei niedrigeren Temperaturen mit kürzeren Reaktionszeiten. Ein geringer Antimon-Unterschuss im so erhaltenen Kieftit erhöht die Anzahl der Ladungsträger und unterdrückt die Bildung von Verunreinigungsphasen. Zunächst wurden Skutteruditproben mit der nominellen Zusammensetzung InxCo4Sb12 mit x = 0,12; 0,15; 0,18 und 0,20 in hoher Reinheit hergestellt und mit Spark Plasma Sintering (SPS) kompaktiert. Messaufnahmen mit Potential- und Seebeck-Mikrosonde und Rasterelektronenmikroskop zeigten eine hohe Probenhomogenität. Produkte waren nahezu phasenrein, was eine Untersuchung der Transporteigenschaften ohne Verfälschung durch Nebenphasen ermöglichte. Die quantitative Phasenanalyse mittels Synchrotron-Beugungsdaten zeigte < 0,1 % InSb bei In0,18Co4Sb12 und In0,20Co4Sb12, sowie eine lineare Korrelation zwischen dem wahren Füllgrad und der Gitterkonstante. Die Bindung von < 0,1 % InSb verringerte den Füllgrad der nominellen In0,20Co4Sb12-Probe auf x = 0,144. Die nominelle In0,18Co4Sb12-Probe mit dem wahren Gehalt x = 0,160 hatte den höchsten zT-Wert nahe eins bei 420 °C. Es konnte anschließend die Anwendbarkeit der Synthesemethode für Barium- und mehrfach gefüllte (Na+In) Skutterudite gezeigt werden. Die Na-gefüllte Probe war gegenüber der thermischen Behandlung in der SPS oder der Charakterisierung instabil. Alle Verbindungen wurden gesintert und ihre Transporteigenschaften wurden charakterisiert. Des weiterem wurde der Einfluss der Konzentration der Korngrenzen bei den Mischungen von zu Nanomaßstab vermahlenem In0,18Co4Sb12 (Partikelgrößen zwischen 20 und 100 nm) mit dem ursprünglichen Bulk untersucht. Proben mit verschiedenen Anteilen von Nanopulver wurden gesintert, ihre thermoelektrischen und strukturellen Eigenschaften wurden untersucht. Die Gütezahl zT von 1,39 bei 375 °C wurde bei der Probe mit gleichen Anteilen des Nano- und des unbehandelten Pulvers erreicht. Die Komposite mit Anteilen <10 % oder >75 % des Nanopulvers zeigten keine Verbesserung gegenüber der unbehandelten Verbindung.rn