Studio del comportamento meccanico e tribologico della lega AlSi10Mg prodotta mediante Laser-based Powder Bed Fusion sottoposta ad un ciclo tecnologico ottimizzato

AlSi10Mg alloy is one of the most widely used alloys for producing structural components by Laser-based Powder Fusion (L-PBF) technology due to the high mechanical and technological properties. The present work aims to characterize mechanically and tribologically the L-PBF AlSi10Mg alloy subjected to both heat treatment and surface modification cycles. Specifically, the effects of three heat treatments on the tribological and mechanical properties of the alloy were analyzed: T5 (artificial aging at 160 °C for 4 h), T6 rapid solution heat treatment (solution heat treatment at 510 °C for 1h and aging at 160 °C for 6 h), and T6 benchmark (solution heat treatment at 540 °C for 1h and aging at 160 °C for 4 h), the latter used as a benchmark. The study highlighted how the better balance between strength and ductility properties induced by the introduction of heat treatments leads to lower wear resistance and not significant variations in the friction coefficient of the alloy. The tribological and mechanical behavior of the alloy coated with two different coating structures, consisting of (i) chemical Ni (Ni-P) and (ii) Ni-P + DLC, was also evaluated. The goal was the identification of a deposition cycle such as to guarantee the optimization of the mechanical and tribological behavior of the alloy. The Ni-P coating provided good wear resistance but an increase in the coefficient of friction. In contrast, using the DLC top coating resulted in excellent tribological performance in wear resistance and friction coefficient. The samples characterized by the Ni-P + DLC multilayer coating were subsequently subjected to mechanical characterization. The results obtained highlighted problems of adhesion and incipient breaking of the material due to the different mechanical behavior of the coating, considerably reducing the mechanical performance of the alloy coated with Ni-P+DLC multilayer solution compared to the specimens in the un-coated condition.