Atmospheric corrosion of quaternary bronzes (Cu-Sn-Zn-Pb): laboratory tests (accelerated ageing in wet & dry conditions)and field studies (the Bottego monument in Parma, Italy).

The interactions between outdoor bronzes and the environment, which lead to bronze corrosion, require a better understanding in order to design effective conservation strategies in the Cultural Heritage field. In the present work, investigations on real patinas of the outdoor monument to Vittorio Bottego (Parma, Italy) and laboratory studies on accelerated corrosion testing of inhibited (by silane-based films, with and without ceria nanoparticles) and non-inhibited quaternary bronzes are reported and discussed. In particular, a wet&dry ageing method was used both for testing the efficiency of the inhibitor and for patinating bronze coupons before applying the inhibitor. A wide range of spectroscopic techniques has been used, for characterizing the core metal (SEM+EDS, XRF, AAS), the corroded surfaces (SEM+EDS, portable XRF, micro-Raman, ATR-IR, Py-GC-MS) and the ageing solutions (AAS). The main conclusions were: 1. The investigations on the Bottego monument confirmed the differentiation of the corrosion products as a function of the exposure geometry, already observed in previous works, further highlighting the need to take into account the different surface features when selecting conservation procedures such as the application of inhibitors (i.e. the relative Sn enrichment in unsheltered areas requires inhibitors which effectively interact not only with Cu but also with Sn). 2. The ageing (pre-patination) cycle on coupons was able to reproduce the relative Sn enrichment that actually happens in real patinated surfaces, making the bronze specimens representative of the real support for bronze inhibitors. 3. The non-toxic silane-based inhibitors display a good protective efficiency towards pre-patinated surfaces, differently from other widely used inhibitors such as benzotriazole (BTA) and its derivatives. 4. The 3-mercapto-propyl-trimethoxy-silane (PropS-SH) additivated with CeO2 nanoparticles generally offered a better corrosion protection than PropS-SH.

Corrosione atmosferica in area urbana-costiera di un acciaio Cor-Ten: studio del rilascio in ambiente dei metalli di lega

Cor-Ten is a particular kind of steel, belonging to low-alloyed steel; thanks to his aesthetic features and resistance to atmospheric corrosion, this material is largely used in architectural, artistic and infrastructural applications. After environmental exposure, Cor-Ten steel exhibits the characteristic ability to self-protect from corrosion, by the development of a stable and adherent protective layer. However, some environmental factors can influence the formation and stability of the patina. In particular, exposure of Cor-Ten to polluted atmosphere (NOx, SOx, O3) or coastal areas (marine spray) may cause problems to the protective layer and, as a consequence, a release of alloying metals, which can accumulate near the structures. Some of these metals, such as Cr and Ni, could be very dangerous for soils and water because of their large toxicity. The aim of this work was to study the corrosion behavior of Cor-Ten exposed to an urban-coastal site (Rimini, Italy). Three different kinds of commercial surface finish (bare and pre-patinated, with or without a beeswax covering) were examined, both in sheltered and unsheltered exposure conditions. Wet deposition brushing the specimens surface (leaching solutions) are monthly collected and analyzed to evaluate the extent of metal release and the form in which they leave the surface, for example, as water-soluble compounds or non-adherent corrosion products. Five alloying metals (Fe, Cu, Cr, Mn and Ni) and nine ions (Cl-, NO3-, NO2-, SO42-, Na+, Ca2+, K+, Mg2+, NH4+) are determined through Atomic Absorption Spectroscopy and Ion Chromatography, respectively. Furthermore, the evolution and the behaviour of the patina are periodically followed by surface investigations (SEM-EDS and Raman Spectroscopy). After two years of exposure, the results show that Bare Cor-Ten, cheaper than the other analyzed specimens, even though undergoes the greater mass variation, his metal release is comparable to the release of the pre-patinated samples. The behavior of pre-patinated steel, with or without beeswax covering, do not show particular difference. This exposure environment doesn’t allow a completely stabilization of the patina; nevertheless an estimate of metal release after 10 years of exposure points out that the environmental impact of Cor-Ten is very low: for example, the release of chromium in the soluble fraction is less than 10 mg if we consider an exposed wall of 10 m2.

A new method for continuous quality control of nsm cfrp systems

In the last decade the near-surface mounted (NSM) strengthening technique using carbon fibre reinforced polymers (CFRP) has been increasingly used to improve the load carrying capacity of concrete members. Compared to externally bonded reinforcement (EBR), the NSM system presents considerable advantages. This technique consists in the insertion of carbon fibre reinforced polymer laminate strips into pre-cut slits opened in the concrete cover of the elements to be strengthened. CFRP reinforcement is bonded to concrete with an appropriate groove filler, typically epoxy adhesive or cement grout. Up to now, research efforts have been mainly focused on several structural aspects, such as: bond behaviour, flexural and/or shear strengthening effectiveness, and energy dissipation capacity of beam-column joints. In such research works, as well as in field applications, the most widespread adhesives that are used to bond reinforcements to concrete are epoxy resins. It is largely accepted that the performance of the whole application of NSM systems strongly depends on the mechanical properties of the epoxy resins, for which proper curing conditions must be assured. Therefore, the existence of non-destructive methods that allow monitoring the curing process of epoxy resins in the NSM CFRP system is desirable, in view of obtaining continuous information that can provide indication in regard to the effectiveness of curing and the expectable bond behaviour of CFRP/adhesive/concrete systems. The experimental research was developed at the Laboratory of the Structural Division of the Civil Engineering Department of the University of Minho in Guimar\~aes, Portugal (LEST). The main objective was to develop and propose a new method for continuous quality control of the curing of epoxy resins applied in NSM CFRP strengthening systems. This objective is pursued through the adaptation of an existing technique, termed EMM-ARM (Elasticity Modulus Monitoring through Ambient Response Method) that has been developed for monitoring the early stiffness evolution of cement-based materials. The experimental program was composed of two parts: (i) direct pull-out tests on concrete specimens strengthened with NSM CFRP laminate strips were conducted to assess the evolution of bond behaviour between CFRP and concrete since early ages; and, (ii) EMM-ARM tests were carried out for monitoring the progressive stiffness development of the structural adhesive used in CFRP applications. In order to verify the capability of the proposed method for evaluating the elastic modulus of the epoxy, static E-Modulus was determined through tension tests. The results of the two series of tests were then combined and compared to evaluate the possibility of implementation of a new method for the continuous monitoring and quality control of NSM CFRP applications.