The effect of poly(lactide)-poly(carbonate) based block copolymers on the morphology and crystallization of double crystalline poly(lactide)/poly(ε-caprolactone) blends

Block copolymers of poly(lactide) and poly(carbonate) were synthetized in three different compositions and characterized by 1H-NMR and ATR analyses. The compatibilization effect of this copolymers on 80/20 (w/w%) PLA/PCL blend was evaluated. SEM micrographs show that all the blends exhibit the typical sea-island morphology characteristic of immiscible blends with PCL finely dispersed in droplets on a PLA matrix. Upon the addiction of the copolymers a reduction on PCL droplets size is observable. At the same time, a Tg depression of the PLA phase is detected when the copolymers are added in the blend. These results indicate that these copolymers are effective as compatibilizers. The copolymer that acts as the best compatibilizer is the one characterized by the same amount of PLA and PC as repeating units. As result, in the blend containing this copolymer PLA phase exhibits the highest spherulitic growth rate. An analyses on PLA phase crystallization behaviour from the glassy state within the blends was evaluated by DSC experiments. Isothermal cold crystallization of the PLA phase is enhanced up an order of magnitude upon the blending with PCL. Annealing experiments demonstrated that the crystallization of the PCL phase induces the formation of active nuclei in PLA when cooled above cooled below Tg. When the crystallization rate of PCL is retarded, a reduction on PLA nucleation is observed.

Crystallization and morphology of the PLLA phase within random poly (L-lactide-ran-ɛ-caprolactone)

This work has mainly focused on the poly (L-lactide) (PLLA) which is a material for multiple applications with performances comparable to those of petrochemical polymers (PP, PS, PET, etc. ...), readily recyclable and also compostable. However, PLLA has certain shortcomings that limit its applications. It is a brittle, hard polymer with a very low elongation at break, hydrophobic, exhibits low crystallization kinetics and takes a long time to degrade. The properties of PLLA may be modified by copolymerization (random, block, and graft) of L-lactide monomers with other co-monomers. In this thesis it has been studied the crystallization and morphology of random copolymers poly (L-lactide-ran-ε-caprolactone) with different compositions of the two monomers since the physical, mechanical, optical and chemical properties of a material depend on this behavior. Thermal analyses were performed by differential scanning calorimetry (DSC) and thermogravimetry (TGA) to observe behaviors due to the different compositions of the copolymers. The crystallization kinetics and morphology of poly (L-lactide-ran-ε-caprolactone) was investigated by polarized light optical microscopy (PLOM) and differential scanning calorimetry (DSC). Their thermal behavior was observed with crystallization from melt. It was observed that with increasing amounts of PCL in the copolymer, there is a decrease of the thermal degradation. Studies on the crystallization kinetics have shown that small quantities of PCL in the copolymer increase the overall crystallization kinetics and the crystal growth rate which decreases with higher quantities of PCL.

Bionanocomposites based on Plla, Pcl and montmorillonite: synthesis, characterization and crystallization

Poly(lactide) is one of the best candidate to replace conventional petroleum-based polymers, since it is biobased, biocompatible and biodegradable. However, commercial PLA materials typically have low crystallization rate resulting in long processing time and low production efficiency. In this work the effects of two nanofillers MMT30B and MMT30B-g-P(LA-co-CL) on the crystallization rate of neat PLA and PLA/PCL blend were investigated. MMT30B-g-P(LA-co-CL) was synthetized by in situ grafting reaction. The synthesis was carried in xylene at 140°C, upon the results of a screening. The grafted copolymers were evaluated by 1H-NMR ,ATR–IR and TGA. Solvent casted films were obtained by mixing MMT30B-g-P(LA-co-CL) at 5% (w/w) with neat PLA and PLA/PCL blend, comparing the properties with the corresponding blends with and without a 5% of (w/w) unmodified clay. SEM images on PLA based blends shows that MMT30B is aggregated into larger particles compared to MMT30B-g-P(LLA-co-CL). This behavior is correlated to the better exfoliation of MMT30B-g-P(LA-co-CL) clay layers. SEM images on PLA/PCL based blends exhibit the typical sea-island morphology, characteristic of immiscible blends. PLA is the matrix while PCL is finely dispersed in droplets. MMT30B does not reduce PCL droplets size, while MMT30B-g-P(LA-co-CL) reduces the size of PCL droplets. This means that MMT30B-g-P(LA-co-CL) can migrate to the PLA-PCL interface, acting as a compatibilizer. Non-isothermal DSC cooling scans show a fractionated crystallization of the PCL phase in PLA/PCL/MMT30B-g-P(LA-co-CL), confirming the compatibilizer effect of MMT30B-g-P(LA-co-CL). At the same timeMMT30B-g-P(LA-co-CL) can better nucleate the PLA phase, both in neat PLA and PLA/PCL blend, promoting the crystallization during the heating scans. In isothermal condition, both the nanofillers increase the crystallization rate of PLA phase in neat PLA, while in PLA/PCL blends the effect is covered by the nucleating effect of PCL.