Outdoor bronze conservation: assessment of protective treatments by accelerated aging and of treatment removal procedures by laser cleaning

Outdoor bronzes exposed to the environment form naturally a layer called patina, which may be able to protect the metallic substrate. However, since the last century, with the appearance of acid rains, a strong change in the nature and properties of the copper based patinas occurred [1]. Studies and general observations have established that bronze corrosion patinas created by acid rain are not only disfiguring in terms of loss of detail and homogeneity, but are also unstable [2]. The unstable patina is partially leached away by rainwater. This leaching is represented by green streaking on bronze monuments [3]. Because of the instability of the patina, conservation techniques are usually required. On a bronze object exposed to the outdoor environment, there are different actions of the rainfall and other atmospheric agents as a function of the monument shape. In fact, we recognize sheltered and unsheltered areas as regards exposure to rainwater [4]. As a consequence of these different actions, two main patina types are formed on monuments exposed to the outdoor environment. These patinas have different electrochemical, morphological and compositional characteristics [1]. In the case of sheltered areas, the patina contains mainly copper products, stratified above a layer strongly enriched in insoluble Sn oxides, located at the interface with the uncorroded metal. Moreover, different colors of the patina result from the exposure geometry. The surface color may be pale green for unsheltered areas, and green and mat black for sheltered areas [4]. Thus, in real outdoor bronze monuments, the corrosion behavior is strongly influenced by the exposure geometry. This must be taken into account when designing conservation procedures, since the patina is in most cases the support on which corrosion inhibitors are applied. Presently, for protecting outdoor bronzes against atmospheric corrosion, inhibitors and protective treatments are used. BTA and its derivatives, which are the most common inhibitors used for copper and its alloy, were found to be toxic for the environment and human health [5, 6]. Moreover, it has been demonstrated that BTA is efficient when applied on bare copper but not as efficient when applied on bare bronze [7]. Thus it was necessary to find alternative compounds. Silane-based inhibitors (already successfully tested on copper and other metallic substrates [8]), were taken into consideration as a non-toxic, environmentally friendly alternative to BTA derivatives for bronze protection. The purpose of this thesis was based on the assessment of the efficiency of a selected compound, to protect the bronze against corrosion, which is the 3-mercapto-propyl-trimethoxy-silane (PropS-SH). It was selected thanks to the collaboration with the Corrosion Studies Centre “Aldo Daccò” at the Università di Ferrara. Since previous studies [9, 10, 11] demonstrated that the addition of nanoparticles to silane-based inhibitors leads to an increase of the protective efficiency, we also wanted to evaluate the influence of the addition of CeO2, La2O3, TiO2 nanoparticles on the protective efficiency of 3-mercapto-propyl-trimethoxy-silane, applied on pre-patinated bronze surfaces. This study is the first section of the thesis. Since restorers have to work on patinated bronzes and not on bare metal (except for contemporary art), it is important to be able to recreate the patina, under laboratory conditions, either in sheltered or unsheltered conditions to test the coating and to obtain reliable results. Therefore, at the University of Bologna, different devices have been designed to simulate the real outdoor conditions and to create a patina which is representative of real application conditions of inhibitor or protective treatments. In particular, accelerated ageing devices by wet & dry (simulating the action of stagnant rain in sheltered areas [12]) and by dropping (simulating the leaching action of the rain in unsheltered areas [1]) tests were used. In the present work, we used the dropping test as a method to produce pre-patinated bronze surfaces for the application of a candidate inhibitor as well as for evaluating its protective efficiency on aged bronze (unsheltered areas). In this thesis, gilded bronzes were also studied. When they are exposed to the outside environment, a corrosion phenomenon appears which is due to the electrochemical couple gold/copper where copper is the anode. In the presence of an electrolyte, this phenomenon results in the formation of corrosion products than will cause a blistering of the gold (or a break-up and loss of the film in some cases). Moreover, because of the diffusion of the copper salts to the surface, aggregates and a greenish film will be formed on the surface of the sample [13]. By coating gilded samples with PropS-SH and PropS-SH containing nano-particles and carrying out accelerated ageing by the dropping test, a discussion is possible on the effectiveness of this coating, either with nano-particles or not, against the corrosion process. This part is the section 2 of this thesis. Finally, a discussion about laser treatment aiming at the assessment of reversibility/re-applicability of the PropS-SH coating can be found in section 3 of this thesis. Because the protective layer loses its efficiency with time, it is necessary to find a way of removing the silane layer, before applying a new one on the “bare” patina. One request is to minimize the damages that a laser treatment would create on the patina. Therefore, different laser fluences (energy/surface) were applied on the sample surface during the treatment process in order to find the best range of fluence. In particular, we made a characterization of surfaces before and after removal of PropS-SH (applied on a naturally patinated surface, and subsequently aged by natural exposure) with laser methods. The laser removal treatment was done by the CNR Institute of Applied Physics “Nello Carrara” of Sesto Fiorentino in Florence. In all the three sections of the thesis, a range of non-destructive spectroscopic methods (Scanning Electron Microscopy with Energy Dispersive Spectroscopy (SEM-EDS), μ-Raman spectroscopy, X-Ray diffractometry (XRD)) were used for characterizing the corroded surfaces. AAS (Atomic Absorption Spectroscopy) was used to analyze the ageing solutions from the dropping test in sections 1 and 2.

Proprietà optoelettroniche di film nanoporosi ottenuti per impiantazione ionica.

In questo elaborato vengono studiate le proprietà optoelettroniche di film sottili di germanio nanoporosi ottenuti per impiantazione ionica. Viene trattata la tecnica sperimentale della Surface Photovoltage Spectroscopy nella configurazione Metal-Insulator-Semiconductor. Viene osservato che la presenza di struttura nanoporosa provoca due effetti: il primo è l’innalzamento del bandgap energetico dovuta al confinamento quantistico degli elettroni all’interno dei pori; il secondo è l’incremento del segnale SPV per quei film in cui è maggiore il rapporto tra superficie e volume.

Proposta di traduzione dello script di Brat 2, di Aleksej Balabanov

Il seguente elaborato si propone di fornire un esempio di traduzione del film Brat 2 di Aleksej Balabanov, che possa fungere da base per un eventuale sottotitolaggio. Il lavoro è suddiviso in quattro sezioni: in primo luogo, una breve nota alla traduzione, pensata per favorire una lettura diretta delle battute, in cui ci si soffermerà su alcuni aspetti della lingua e della cultura russe. Le linee orizzontali demarcano i cambi di scena, ovvero il passaggio da un ambiente ad un altro. La seconda sezione si concentra in parte sull'analisi di alcuni temi e caratteristiche del film in questione (anche in relazione con il suo antecedente Brat), in parte sul regista e sull'attore protagonista Sergej Badrov. La terza sezione fornirà invece una breve delucidazione riguardo la traduzione audiovisiva. Infine, la quarta sezione è composta da una tabella a due colonne, all'interno della quale sono inserite le battute tradotte con testo a fronte. La scelta è ricaduta sull'opera in questione data la sua rilevanza all'interno del panorama cinematografico russo, ma soprattutto, data la sua originalità. Brat 2 [Fratello 2] ha la capacità di mostrare, con poche ed efficaci pennellate, le immagini di un'America diversa da quella che si è soliti rappresentare sugli schermi occidentali.

Sviluppo di un protettivo a base di benzotriazolo per il rivestimento di superfici metalliche e beni culturali

Il BTA (benzotriazolo), largamente impiegato nei protettivi per metalli utilizzati commercialmente, in particolare per la conservazione dei beni culturali, presenta problematiche riguardo il progressivo impoverimento di quest'ultimo legato alla sua volatilità, con conseguente perdita di efficacia antiossidante del film e rischi per la salute e per l'ambiente, data la tossicità del composto. Lo scopo di questo lavoro è stato di mettere a punto un polimero per il coating ecofriendly (PLA, polimero proveniente da materie prime rinnovabili) ed efficiente (polimero funzionalizzato con BTA, il quale essendo legato chimicamente alla catena di polimero, è maggiormente trattenuto all'interno del materiale) come valida alternativa a quelli reperibili commercialmente. In questo lavoro di tesi è stato sintetizzato un derivato funzionalizzato del benzotriazolo, molto usato per la conservazione dei beni culturali, in modo da essere utilizzato come iniziatore di polimerizzazione ROP di rac-lattide. In questo modo sono stati messi a punto, modulandone il peso molecolare attraverso la variazione della quantità di iniziatore, alcuni polimeri di poli-acido lattico con una molecola di benzotriazolo legata alla estremità carbossilica di ogni catena, legame che ne limita molto la fuoriuscita dal film. In seguito è stata testata l'efficacia di questi polimeri come alternativa a quelli utilizzati commercialmente nel campo della conservazione dei beni culturali, applicando uno strato di essi su dei provini di bronzo e sottoponendoli a diversi processi di invecchiamento, confrontando il loro comportamento con quello di un prodotto commerciale preso a paragone e con quello di PLA privo di funzionalizzazioni additivato di benzotriazolo. Particolare attenzione è stata posta, non solo sul tasso di degradazione al quale sono andati in contro, ma, visto l'ambito artistico, anche le modificazioni estetiche che i provini hanno subito dopo l'applicazione e dopo l'invecchiamento servendosi di misure di colore e foto che ne monitorassero i cambiamenti.