Investigation on performance characteristics of dense graded hot mix asphalt with RAP and Crumb Rubber

The use of recycled materials in asphalt mixtures such as reclaimed asphalt pavements (RAP) have become widely accepted as a replacement for virgin asphalt binder or virgin aggregates. In this study, the RAP content was 30%, and CR additives were blended with the soft unmodified binder by using dry processes. The objective of this study was to investigate and evaluate the engineering properties of dry method application of crumb rubber influences on reclaimed asphalt pavement (RAP) mixtures. To evaluate the effect of rubber-bitumen interaction on the mixture’s mechanical properties, a laboratory investigation has been conducted on a range of dense graded and 30% RAP by dry process crumb rubber modified (CRM) asphalt mixtures containing 0% (control), 1% crumb rubber by the total aggregate mass. The experimental program in this research include the binder extraction for estimating the amount of aged binder in the both fine and coarse RAP material. Before extracting the binder the RAP sieve analysis, have been done to provide the Black grading curve. In continue after the binder extraction the material sieved again to providing the white curve. The comparison of Black and White curve indicated that there is a remarkable difference between the aggregate grading even for the fine RAP. The experimental program was continued by fabricating 12 specimens in different 4 types of mixtures. For the first group no RAP, no rejuvenator and no crumb rubber were used. For the second group 30% of virgin aggregates substituted by RAP material and the third group was similar to the second group just with 0.01% rejuvenator. the forth group was the group, which in that the specimens contain RAP, rejuvenator and crumb rubber. Finally the specimens were tested for Indirect tensile strength. The results indicated that the addition of crumb rubber increased the optimum amount of binder in the mixture with 30% RAP.

Atmospheric corrosion of quaternary bronzes (Cu-Sn-Zn-Pb): laboratory tests (accelerated ageing in wet & dry conditions)and field studies (the Bottego monument in Parma, Italy).

The interactions between outdoor bronzes and the environment, which lead to bronze corrosion, require a better understanding in order to design effective conservation strategies in the Cultural Heritage field. In the present work, investigations on real patinas of the outdoor monument to Vittorio Bottego (Parma, Italy) and laboratory studies on accelerated corrosion testing of inhibited (by silane-based films, with and without ceria nanoparticles) and non-inhibited quaternary bronzes are reported and discussed. In particular, a wet&dry ageing method was used both for testing the efficiency of the inhibitor and for patinating bronze coupons before applying the inhibitor. A wide range of spectroscopic techniques has been used, for characterizing the core metal (SEM+EDS, XRF, AAS), the corroded surfaces (SEM+EDS, portable XRF, micro-Raman, ATR-IR, Py-GC-MS) and the ageing solutions (AAS). The main conclusions were: 1. The investigations on the Bottego monument confirmed the differentiation of the corrosion products as a function of the exposure geometry, already observed in previous works, further highlighting the need to take into account the different surface features when selecting conservation procedures such as the application of inhibitors (i.e. the relative Sn enrichment in unsheltered areas requires inhibitors which effectively interact not only with Cu but also with Sn). 2. The ageing (pre-patination) cycle on coupons was able to reproduce the relative Sn enrichment that actually happens in real patinated surfaces, making the bronze specimens representative of the real support for bronze inhibitors. 3. The non-toxic silane-based inhibitors display a good protective efficiency towards pre-patinated surfaces, differently from other widely used inhibitors such as benzotriazole (BTA) and its derivatives. 4. The 3-mercapto-propyl-trimethoxy-silane (PropS-SH) additivated with CeO2 nanoparticles generally offered a better corrosion protection than PropS-SH.