Ingegnerizzazione e design di nanoparticelle core-shell di magnetite/silice

In the past decade the study of superparamagnetic nanoparticles has been intensively developed for many biomedical applications such as magnetically assisted drug delivery, MRI contrast agents, cells separation and hyperthermia therapy. All of these applications require nanoparticles with high magnetization, equipped also with a suitable surface coating which has to be non-toxic and biocompatible. In this master thesis, the silica coating of commercially available magnetic nanoparticles was investigated. Silica is a versatile material with many intrinsic features, such as hydrophilicity, low toxicity, proper design and derivatization yields particularly stable colloids even in physiological conditions. The coating process was applied to commercial magnetite particles dispersed in an aqueous solution. The formation of silica coated magnetite nanoparticles was performed following two main strategies: the Stöber process, in which the silica coating of the nanoparticle was directly formed by hydrolysis and condensation of suitable precursor in water-alcoholic mixtures; and the reverse microemulsions method in which inverse micelles were used to confine the hydrolysis and condensation reactions that bring to the nanoparticles formation. Between these two methods, the reverse microemulsions one resulted the most versatile and reliable because of the high control level upon monodispersity, silica shell thickness and overall particle size. Moving from low to high concentration, within the microemulsion region a gradual shift from larger particles to smaller one was detected. By increasing the amount of silica precursor the silica shell can also be tuned. Fluorescent dyes have also been incorporated within the silica shell by linking with the silica matrix. The structure of studied nanoparticles was investigated by using transmission electron microscope (TEM) and dynamic light scattering (DLS). These techniques have been used to monitor the syntetic procedures and for the final characterization of silica coated and silica dye doped nanoparticles. Finally, field dependent magnetization measurements showed the magnetic properties of core-shell nanoparticles were preserved. Due to a very well defined structure that combines magnetic and luminescent properties together with the possibility of further functionalization, these multifunctional nanoparticles are potentially useful platforms in biomedical fields such as labeling and imaging.

New catalysts for the water gas shift reaction at middle-temperature

H2 demand is continuously increasing since its many relevant applications, for example, in the ammonia production, refinery processes or fuel cells. The Water Gas Shift (WGS) reaction (CO + H2O = CO2 + H2 DeltaH = -41.1 kJ.mol-1) is a step in the H2 production, reducing significantly the CO content and increasing the H2 one in the gas mixtures obtained from steam reforming. Industrially, the reaction is carried out in two stages with different temperature: the first stage operates at high temperature (350-450 °C) using Fe-based catalysts, while the second one is performed at lower temperature (190-250 °C) over Cu-based catalysts. However, recently, an increasing interest emerges to develop new catalytic formulations, operating in a single-stage at middle temperature (MTS), while maintaining optimum characteristics of activity and stability. These formulations may be obtained by improving activity and selectivity of Fe-based catalysts or increasing thermal stability of Cu-based catalysts. In the present work, Cu-based catalysts (Cu/ZnO/Al2O3) prepared starting from hydrotalcite-type precursors show good homogeneity and very interesting physical properties, which worsen by increasing the Cu content. Among the catalysts with different Cu contents, the catalyst with 20 wt.% of Cu represents the best compromise to obtain high catalytic activity and stability. On these bases, the catalytic performances seem to depend on both metallic Cu surface area and synergetic interactions between Cu and ZnO. The increase of the Al content enhances the homogeneity of the precursors, leading to a higher Cu dispersion and consequent better catalytic performances. The catalyst with 20 wt.% of Cu and a molar ratio M(II)/M(III) of 2 shows a high activity also at 250 °C and a good stability at middle temperature. Thus, it may be considered an optimum catalyst for the WGS reaction at middle temperature (about 300 °C). Finally, by replacing 50 % (as at. ratio) of Zn by Mg (which is not active in the WGS reaction), better physical properties were observed, although associate with poor catalytic performances. This result confirms the important role of ZnO on the catalytic performances, favoring synergetic interactions with metallic Cu.