Development and testing of a Fourier trasform based experimental system for Dynamic Mechanical Thermal Analysis tests

Altough nowadays DMTA is one of the most used techniques to characterize polymers thermo-mechanical behaviour, it is only effective for small amplitude oscillatory tests and limited to a single frequency analysis (linear regime). In this thesis work a Fourier transform based experimental system has proven to give hint on structural and chemical changes in specimens during large amplitude oscillatory tests exploiting multi frequency spectral analysis turning out in a more sensitive tool than classical linear approach. The test campaign has been focused on three test typologies: Strain sweep tests, Damage investigation and temperature sweep tests.

Natural Wax-Based Water Vapour Barrier Coatings on PLA for MAP Food Packaging

PLA is a bio-based polymer that is obtained from renewable resources and it is very promising for a sustainable packaging manufacturing. However, its gas and vapour barrier properties are not enough to comply with the requirements of MAP packaging of fresh foods, which need specific concentration of water and oxygen to avoid spoilage and to keep the organoleptic properties unaltered throughout their shelf-life. The use of waxes from natural renewable sources such as plants (e.g., candelilla wax, carnauba wax, rice bran wax, sunflower wax) or animals (e.g., beeswax) could tackle down the permeation of water vapour through the packaging without affecting its bio-based content. The core of this work is developing wax-based coatings with enhanced thermo-mechanical properties so that they can undergo thermoforming and a proper adhesion to the PLA substrate can be ensured. Chemical modifications and crosslinking of waxes are performed to produce wax-based alkyd resins. The synthesised materials are characterised both by DSC and FTIR. Films of the wax-based alkyds are produced in order to assess their water vapour permeability.

Cure Induced Residual Stresses on Thick Composite Components Manufactured by Additive Process

This study investigates the effect of an additive process in manufacturing of thick composites. Airstone 780 E epoxy resin and 785H Hardener system is used in the analysis since it is widely used wind turbine blade, namely thick components. As a fiber, fabric by SAERTEX (812 g/m2) with a 0-90 degrees layup direction is used. Temperature overshoot is a major issue during the manufacturing of thick composites. A high temperature overshoot leads to an increase in residual stresses. These residual stresses are causing warping, delamination, dimensional instability, and undesired distortion of composite structures. A coupled thermo-mechanical model capable of predicting cure induced residual stresses have been built using the commercial FE software Abaqus®. The possibility of building thick composite components by means of adding a finite number of sub-laminates has been investigated. The results have been compared against components manufactured following a standard route. The influence of pre-curing of the sub-laminates has also been addressed and results compared with standard practice. As a result of the study, it is found that introducing additive process can prevent temperature overshoot to occur and benefits the residual stresses generation during the curing process. However, the process time required increases by 50%, therefore increasing the manufacturing costs. An optimized cure cycle is required to minimize process time and cure induced defects simultaneously.