Novel materials for direct X-ray detectors based on semiconducting organic polymers

Conventional inorganic materials for x-ray radiation sensors suffer from several drawbacks, including their inability to cover large curved areas, me- chanical sti ffness, lack of tissue-equivalence and toxicity. Semiconducting organic polymers represent an alternative and have been employed as di- rect photoconversion material in organic diodes. In contrast to inorganic detector materials, polymers allow low-cost and large area fabrication by sol- vent based methods. In addition their processing is compliant with fexible low-temperature substrates. Flexible and large-area detectors are needed for dosimetry in medical radiotherapy and security applications. The objective of my thesis is to achieve optimized organic polymer diodes for fexible, di- rect x-ray detectors. To this end polymer diodes based on two different semi- conducting polymers, polyvinylcarbazole (PVK) and poly(9,9-dioctyluorene) (PFO) have been fabricated. The diodes show state-of-the-art rectifying be- haviour and hole transport mobilities comparable to reference materials. In order to improve the X-ray stopping power, high-Z nanoparticle Bi2O3 or WO3 where added to realize a polymer-nanoparticle composite with opti- mized properities. X-ray detector characterization resulted in sensitivties of up to 14 uC/Gy/cm2 for PVK when diodes were operated in reverse. Addition of nanoparticles could further improve the performance and a maximum sensitivy of 19 uC/Gy/cm2 was obtained for the PFO diodes. Compared to the pure PFO diode this corresponds to a five-fold increase and thus highlights the potentiality of nanoparticles for polymer detector design. In- terestingly the pure polymer diodes showed an order of magnitude increase in sensitivity when operated in forward regime. The increase was attributed to a different detection mechanism based on the modulation of the diodes conductivity.

On the influence of polymeric nanofibers in laminated composite materials. Studio dell'influenza di nanofibre polimeriche in materiali compositi laminati

During the last years an increased interest about the reinforcement of laminated composites by means of polymeric nanofibers has been growth. During this master-degree-thesis work, unidirectional and plane-textile composites have been interleaved with Nylon 6.6, PCL and mixed (Nylon 6.6+PCL) nanofibrous mats and the DCB (mode I interlaminar fracture toughness), ENF (mode II interlaminar fracture toughness and DMA (damping capability) tests have been performed. Regarding the interlaminar fracture toughness, marked increases have been recorded; while further investigation about damping capability is requested.